铝合金机械性能表
铝合金的典型机械性能
铝合金的典型机械性能(Typical Mechanical Properties)铝合金牌号及状态拉伸强度(25°C MPa)屈服强度(25°C MPa)硬度500kg力10mm球延伸率1.6mm(1/16in)厚度5052-H112 175 195 60 125083-H112 180 211 65 146061-T651 310 276 95 127050-T7451 510 455 135 107075-T651 572 503 150 112024-T351 470 325 120 20铝合金的典型物理性能(Typical Physical Properties)铝合金牌号及状态热膨胀系数(20-100℃)μm/m•k熔点范围(℃)电导率20℃(68℉)(%IACS) 电阻率20℃(68℉)Ωmm2/m 密度(20℃)(g/cm3)2024-T351 23.2 500-635 30 0.058 2.825052-H112 23.8 607-650 35 0.050 2.725083-H112 23.4 570-640 29 0.059 2.726061-T651 23.6 580-650 43 0.040 2.737050-T7451 23.5 490-630 41 0.0415 2.827075-T651 23.6 475-635 33 0.0515 2.82铝合金的化学成份(Chemical Composition Limit Of Aluminum )合金牌号硅Si 铁Fe 铜Cu 锰Mn 镁Mg 铬Cr 锌Zn 钛Ti 其它铝每个合计最小值2024 23.2 0.5 3.8-4.9 0.3-0.9 1.2-1.8 0.1 0.25 0.15 0.05 0.15 余量5052 25 0.4 0.1 0.1 2.2-2.8 0.15-0.35 0.1 -- 0.05 0.15 余量5083 23.8 0.4 0.1 0.3-1.0 4.0-4.9 0.05-0.25 0.25 0.15 0.05 0.15 余量6061 23.6 0.7 0.15-0.4 0.15 0.8-1.2 0.04-0.35 0.25 0.15 0.05 0.15 余量7050 23.5 0.15 20.-2.6 0.1 1.9-2.6 0.04 5.7-6.7 0.06 0.05 0.15 余量7075 23.6 0.5 1.2-2.0 0.3 2.1-2.9 0.18-0.28 5.1-6.1 0.2 0.05 0.15 余量美铝典型应用领域用途 2024 5052 5083 6061 7050 7075农业 -- ● -- ● -- --航空器● -- -- ●●●模具 -- ● -- ● -- ●机械设备●● -- ●●●五金零件 -- -- -- ● -- --建筑 -- ● -- ● -- --机动车● -- -- ● -- -- 建筑产品 -- ● -- ● -- -- 化学设备 -- -- -- ● -- -- 集装箱 -- -- -- -- -- -- 烹饪用具 -- -- -- -- -- -- 圆筒或活塞● -- -- ● -- -- 泵体 -- -- -- ● -- --电子 -- -- -- ● -- --电工 -- ● -- ● -- --紧固件●● -- ●●●屏蔽线 -- -- -- ● -- --风叶 -- -- -- ● -- --家具 -- -- -- ● -- --筒状容器 -- -- -- -- -- -- 硬件装置● -- -- ●●●医疗设备● -- -- ● -- -- 厨房设备 -- ● -- ● -- -- 灯座 -- -- -- -- -- --水上用途 -- ● -- ● -- -- 机械配件● -- -- ●●●名称招牌 -- -- -- -- -- -- 军火用品● -- -- ●●●管道 -- -- -- ● -- --车体 -- ● -- ● -- --娱乐设施● -- -- ●●●储存箱 -- ● -- ● -- --架构 -- -- -- ● -- --卡车与拖车 -- ● -- ● -- -- 拉链 -- -- -- -- -- --现货供应型号板材圆棒扁条/方条6061 T6 ●●●6061 T651 ● -- --6061 T6511 -- ● --7075 T651 ● -- --7075 T6 ●● --5052 H112 精度板● -- --5052 H32 冲压板● -- --5083 H112 ● -- --Alumould ● -- --Mic-6 ● -- --2024 ● -- --K-100 ● -- --产品参数中、美常用铝合金牌号对照表中国 CHINA 美国 THE UNITED STATESL1-L6 、 L5-1 1070 、1060 、 1050 、 1030 、 1100LY11 、 LY12 、 LY1 2017 、 2024 、 2117LD10 、 LD5 2014 、 2214LD7 2618LD9 、 LD8 2018 、 2218LY16 、 LY17 2219 、 2021LF21 3003LF2 、 LF3 、 LF4 5052 、 5154 、 5083LF5 、 LF11 、 LF6 、 LF5-1 5456 、 5056LD2 、 LD2-1 、 LD2-2 、 LD30 、 LD31 6165 、 6061 、 6055 、 6063 LC6 、 LC4 、 LC9 7001 、 7178 、 7075LC5 、 LC10 7076 、 7175 、 7079LD11 4032中国新旧合金牌号对照表（GB/T 3190-1996）新牌号旧牌号新牌号旧牌号新牌号旧牌号1A99 原LG5 2B12 原LY9 3003 －1A97 原LG4 2A13 原LY13 3103 －1A95 － 2A14 原LD10 3004 －1A93 原LG3 2A16 原LY16 3005 －1A90 原LG2 2B16 曾用Ly16-1 3105 －1A85 原LG1 2A17 原LY17 4A01 原LT11080 － 2A20 曾用LY20 4A11 原LD111080A － 2A21 曾用214 4A13 原LT131070 － 2A25 曾用225 4A17 原LT171070A 代L1 2A49 曾用149 4004 －1370 － 2A50 原LD5 4032 －1060 代L2 2B50 原LD6 4043 －1050 － 2A70 原LD7 4043A －1050A 代L3 2B70 曾用LD7－1 4047 －1A50 原LB2 2A80 原LD8 4047A －1350 － 2A90 原LD9 5A01 曾用2101、LF151145 － 2004 － 5A02 原LF21035 代L4 2011 － 5A03 原LF31A30 原L4－1 2014 － 5A05 原LF51100 代LF5－1 2014A － 5B05 原LF101200 代L5 2214 － 5A06 原LF61235 － 2017 － 5B06 原LF142A01 原LY1 2017A － 5A12 原LF122A02 原LY2 2117 － 5A13 原LF132A04 原LY4 2218 － 5A30 曾用2103、LF162A06 原LY6 2618 － 5A33 原LF332A10 原LY10 2219 曾用LY19、147 5A41 原LT412A11 原LY11 2024 － 5A43 原LF432B11 原LY8 2124 － 5A66 原LT662A12 原LY12 3A21 原LF21 5005 －5019 － 6B02 原LD2－1 7A09 原LC95050 － 6A51 曾用651 7A10 原LC105251 － 6101 － 7A15 曾用LC15、1575052 － 6101A － 7A19 曾用919、LC195154 － 6005 － 7A31 曾用183-15154A － 6005A － 7A33 曾用LB7335454 － 6351 － 7A52 曾用LC52、52105554 － 6060 － 7003 原LC125754 － 6061 原LD30 7005 －5056 原LF5－1 6063 原LD31 7020 －5356 － 6063A － 7022 －5456 － 6070 原LD2－2 7050 －5082 － 6181 － 7075 －5182 － 6082 － 7475 －5083 原LF4 7A01 原LB1 8A06 原L65183 － 7A03 原LC3 8011 曾用LT985086 － 7A04 原LC4 8090 －6A02 原LD2 7A05 曾用705 －－注意：（1）“原”是指化学成分与新牌号等同，且都符合GB3190－82规定的旧牌号。
铝机械性能
－
6005A
－
7A33
曾用LB733
5454
－
6351
－
7A52
曾用LC52、5210
5554
－
6060
－
7003
原LC12
5754
－
6061
原LD30
7005
－
5056
原LF5－1
6063
原LD31
7020
－
5356
－
6063A
－
7022
－
5456
－
6070
原LD2－2
7050
－
5082
43
0.040
2.73
7050-T7451
23.5
490-630
41
0.0415
2.82
7075-T651
23.6
475-635
33
0.0515
2.82
铝合金的化学成份(Chemical Composition Limit Of Aluminum )
合金
牌号
硅Si
铁Fe
铜Cu
锰Mn
镁Mg
铬Cr
锌Zn
O
退火状态
适用于经完全退火获得最低强度的加工产品
H
加工硬化状态
适用于通过加工硬化提高强度的产品，产品在加工硬化后可经过（也可不经过）使强度有所降低的附加热处理H代号后面必须 跟有两位或三位阿拉伯数字
W
固溶热处理状态
一种不稳定状态，仅适用于经固溶热处理后，室温下自然时效的合金，该状态代号仅表示产品处于自然时效阶段
●
--
●
--
部分铝合金典型机械性能参考值
315 230 —
14
260 115
22
—
290 205
12
—
325 255
10
—
270 130
14
—
240 115
27
—
270 205
15
—
290 230
13
—
310 250
12
—
330 270
10
—
240 115
25
—
235 170
11
—
285 240
5
—
240 115
27
—
270 205
15
—
拉
伸
强度，MPa
伸长率，%
50 毫米 5D
强度 屈服 厚
直径
极限 极限 1.60mm 12.5mm
试样 试样
420 315 —
10
185 75
20
20
485 345
18
—
470 325
20
17
495 395
13
—
180 75
20
—
450 310
18
—
440 290
19
—
460 36511 Nhomakorabea—
450 415
典型机械性能值表强度mpa铝合金牌号和状态强度极限7085100115130901101251451658595110125185380405185425485170435421470180425屈服极限30759010512535105115140150308595110165295310952904157027525541570275伸伸长率50毫米5d硬度剪切疲劳疲劳极限mpa20303545453540506060501251259014012590125模量弹性模量gpa6969696969696969696969696969697070737373737373737373布氏负荷极限500kgf抗剪厚直径10mm强度160mm125mm钢球mpa试样试样431612863512965212022104222181513131016181120201923263035232832384495100451051354510550556070756070758590556070751052202401252602901252552552851252601060o1016h121016h141016h161016h181100o1100h121100h141100h161100h181350o1350h121350h141350h161350h192011t32011t82014o2014t4t4512014t6t651包铝2014o包铝2014t32014t4t451包铝2014t6t6512017o2017t4t451强度mpa铝合金牌号和状态强度极限420185485470495180450440460450485400340295330170360360395415455475110130150175200110130150175200伸伸长率50毫米5d硬度剪切表续1疲劳模量弹性模量gpa7473737373737373737373727171747373737373737369696969696969696969屈服厚极限160mm试样3157534532539575310290365415455255195165255751852503152903503954012514517018540125145170185201820132018191166241820171110101030108543
铝机械性能
铝合金的典型机械性能(Typical Mecha ni cal Properties)铝合金的典型物理性能(Typical Physical Properties)铝合金的化学成份(Chemical Composition Limit Of Aluminum )产品参数中、美常用铝合金牌号对照表中国CHINA 美国THE UNITED STATESL1-L6、L5-1 1070 、1060 、1050 、1030 、1100 LY11、LY12、LY1 2017 、2024 、2117LD10 、LD5 2014、2214LD7 2618LD9 、LD8 2018、2218LY16、LY17 2219、2021LF21 3003LF2 、LF3 、LF4 5052、5154、5083LF5、LF11、LF6、LF5-1 5456、5056 LD2、LD2-1、LD2-2、LD30、LD31 6165、6061、6055、6063LC6、LC4、LC9 7001、7178、7075LC5 、LC10 7076、7175、70794032LD11中国新旧合金牌号对照表(GB/T 3190-1996 )新牌号旧牌号新牌号旧牌号新牌号旧牌号1A99 原LG5 2B12 原LY9 3003 —1A97 原LG4 2A13 原LY13 3103 —1A95 —2A14 原LD10 3004 —1A93 原LG3 2A16 原LY16 3005 —1A90 原LG2 2B16 曾用Ly16-1 3105 —1A85 原LG1 2A17 原LY17 4A01 原LT1 1080 —2A20 曾用LY20 4A11 原LD11 1080A —2A21 曾用214 4A13 原LT13 1070 —2A25 曾用225 4A17 原LT17 1070A 代L1 2A49 曾用149 4004 —1370 —2A50 原LD5 4032 —1060 代L2 2B50 原LD6 4043 —1050 —2A70 原LD7 4043A —1050A 代L3 2B70 曾用LD7- 1 4047 —1A50 原LB2 2A80 原LD8 4047A —1350 —2A90 原LD9 5A01 曾用2101、LF151145 —2004 —5A02 原LF2 1035 代L4 2011 —5A03 原LF31A30 原L4 —1 2014 —5A05 原LF5 1100 代LF5—1 2014A —5B05 原LF10 1200 代L5 2214 —5A06 原LF6 1235 —2017 —5B06 原LF142A01 原LY1 2017A —5A12 原LF122A02 原LY2 2117 —5A13 原LF132A04 原LY4 2218 —5A30 曾用2103、LF162A06 原LY6 2618 —5A33 原LF332A10 原LY10 2219 曾用LY19、147 5A41 原LT412A11 原LY11 2024 —5A43 原LF432B11 原LY8 2124 —5A66 原LT662A12 原LY12 3A21 原LF21 5005 —5019 —6B02 原LD2—1 7A09 原LC9 5050 —6A51 曾用651 7A10 原LC10 5251 —6101 —7A15 曾用LC15、157 5052 —6101A —7A19 曾用919、LC19 5154 —6005 —7A31 曾用183-1 5154A —6005A —7A33 曾用LB7335454 —6351 —7A52 曾用LC52、52105554 —6060 —7003 原LC12 5754 —6061 原LD30 7005 —5056 原LF5—1 6063 原LD31 7020 —5356 —6063A —7022 —5456 —6070 原LD2—2 7050 —5082 —6181 —7075 —5182 —6082 —7475 —5083 原LF4 7A01 原LB1 8A06 原L65183 —7A03 原LC3 8011 曾用LT985086 —7A04 原LC4 8090 —6A02 原LD2 7A05 曾用705 ——注意:(1)“原”是指化学成分与新牌号等同，且都符合GB3190- 82规定的旧牌号。
(完整版)铝合金的机械性能
产品参数中、美常用铝合金牌号对照表中国CHINA 美国THE UNITED STATESL1-L6 、L5-1 1070 、1060 、1050 、030 、1100LY11 、LY12 、LY1 2017、2024 、2117LD10 、LD5 2014 、2214 LD7 2618LD9 、LD8 2018 、2218 LY16 、LY17 2219 、2021 LF21 3003LF2 、LF3 、LF4 5052、5154 、5083LF5 、LF11 、LF6 、LF5-1 5456、5056LD2 、LD2-1 、LD2-2 、LD30 、LD31 6165 、6061 、6055 、6063LC6 、LC4 、LC9 7001、7178 、7075LC5 、LC10 7076、7175 、7079LD11 4032中国新旧合金牌号对照表( GB/T 3190-1996 )新牌号旧牌号新牌号旧牌号新牌号旧牌号1A99 原LG5 2B12 原LY9 3003 －1A97 原LG4 2A13 原LY13 3103 －1A95 －2A14 原LD10 3004 －1A93 原LG3 2A16 原LY16 3005 －1A90 原LG2 2B16 曾用Ly16-1 3105 －1A85 原LG1 2A17 原LY17 4A01 原LT1 1080 －2A20 曾用LY20 4A11 原LD11 1080A －2A21 曾用214 4A13 原LT13 1070 －2A25 曾用225 4A17 原LT17 1070A 代L1 2A49 曾用149 4004 －1370 －2A50 原LD5 4032 －1060 代L2 2B50 原LD6 4043 －1050 －2A70 原LD7 4043A －1050A 代L3 2B70 曾用LD7 － 1 4047 －1A50 原LB2 2A80 原LD8 4047A －1350 －2A90 原LD9 5A01曾用2101 、LF151145 －2004 －5A02 原LF21035 代L4 2011 －5A03 原LF3 1A30 原L4 － 1 2014 －5A05 原LF51100 代LF5 － 1 2014A －5B05 原LF101200 代L5 2214 －5A06 原LF61235 －2017－5B06 原LF142A01 原LY1 2017A －5A12 原LF12 2A02 原LY2 2117 －5A13 原LF132A04 原LY42218 －5A30曾用2103 、LF162A06 原LY6 2618 －5A33 原LF332A10 原LY10 2219 曾用LY19 、1475A41 原LT412A11 原LY11 2024 －5A43 原LF43 2B11 原LY8 2124 －5A66 原LT66 2A12 原LY12 3A21 原LF21 5005 －5019 －6B02 原LD2 － 1 7A09 原LC9 5050 －6A51 曾用651 7A10 原LC105251 －6101 －7A15 曾用LC15 、1575052 －6101A －7A19 曾用919 、LC195154 －6005 －7A31 曾用183-1 5154A －6005A －7A33 曾用LB7335454 －6351－7A52曾用LC52、52105554 －6060 －7003 原LC12 5754 －6061 原LD30 7005 －5056 原LF5 － 1 6063 原LD31 7020 －5356 －6063A －7022 －5456 －6070 原LD2 － 2 7050 －5082 －6181 －7075 －5182 －6082 －7475 －5083 原LF4 7A01 原LB1 8A06 原L6 5183 －7A03 原LC3 8011 曾用LT98 5086 －7A04 原LC4 8090 －6A02 原LD2 7A05 曾用705 －－注意：（1）“原”是指化学成分与新牌号等同，且都符合GB3190－82 规定的旧牌号。
BS EN 1706：1998 铝及铝合金铸件化学成分和机械性能
在凝固过程中由于内部压力的增加形成的一个铸件的破裂趋向。 3.9、气密性
在压力测试中没有漏气的趋向。
第 5 页 共 17 页
BS EN 1706：1998
4、命名系统
4.1、数字命名系统：数字命名系统必须与 EN 1780-1 一致。 4.2、以命名系统为基的化学符号：以命名系统为基的化学符号必须与 EN 1780-2 一致。 4.3、回火热处理标注：以下的缩写应用于热处理中，与表格 2，3，4 和 A.1 相关。
BS EN 1706：1998
铝及铝合金-铸件-化学成分和机械性能
欧洲标准 EN 1760:1998 具有英国标准的身份。 ICS 77.120.10； 77.150.10
未经 BSI 的同意不得擅自复印，除非符合版权法。
本件由重庆小舟翻译事务所(67722576)译自日语原文，2006 年 10 月
该欧洲标准由铝及铝合金技术委员会 CEN/TC 132 准备，该委员会的秘书处由法国标准化协会主 持。
该欧洲标准应该拥有一个国家标准的地位，不管是相同文本的发布或者认可，最迟不能超过 1998 年的 9 月。而与此相冲突的国家标准也应最迟在 1998 年的 9 月被撤消。
根据 CEN/CENELEC 的内部规章，国家标准组织的下列国家必须执行此欧洲标准：奥地利，比利 时，捷克共和国，丹麦，芬兰，法国，德国，希腊，冰岛，爱尔兰，意大利，卢森堡，荷兰，挪威，葡 萄牙，西班牙，瑞典，瑞士和英国。
和购买商协商同意的情况下才进行。这特别适用于变质处理或者精炼合金的元素，比如钠、锶、锑和磷。
掺杂元素和杂质要按照以下的顺序表述：硅，铁，铜，锰，镁，铬，镍，锌和钛，其余元素全部为铝。
(完整版)铝合金的机械性能
热处理状态
（不同于F、O、H）
适用于热处理后，经过（或不经过）加工硬化达到稳定状态的产品T代号后面必须跟有一个或多位阿拉伯数字
中国新旧原始状态代号对照表（GB/T16475－1996）
旧代号
新代号
旧代号
新代号
M
O
CYS
TX51、TX52
R
H112或F
CZY
T0
Y
HX8
CSY
T9
Y1
HX6
MCS
T62
(%IACS)
电阻率20℃(68℉)
Ωmm2/m
密度(20℃)(g/cm3)
2024-T351
23.2
500-635
30
0.058
2.82
5052-H112
23.8
607-650
35
0.050
2.72
5083-H112
23.4
570-640
29
0.059
2.72
6061-T651
23.6
580-650
原LY13
3103
－
1A95
－
2A14
原LD10
3004
－
1A93
原LG3
2A16
原LY16
3005
－
1A90
原LG2
2B16
曾用Ly16-1
3105
－
1A85
原LG1
2A17
原LY17
4A01
原LT1
1080
－
2A20
曾用LY20
4A11
原LD11
1080A
－
2A21
曾用214
铝合金技术参数
理论上是2.7，要看成型方法i: 压铸的2.6-2.63 左右，挤压的2.68-2.7，锻造的2.69-2.72 铝合金的典型机械性能(Typical Mechanical Properties)铝合金牌号及状态拉伸强度(25°C MPa)屈服强度(25°C MPa)硬度500kg力10mm球延伸率1.6mm(1/16in)厚度5052-H1121751956012 5083-H1121802116514 6061-T6513102769512 7050-T745151045513510 7075-T65157250315011 2024-T35147032512020铝合金的典型物理性能(Typical Physical Properties)铝合金牌号及状态热膨胀系数(20-100℃)μm/m·k熔点范围(℃)电导率20℃(68℉)(%IACS)电阻率20℃(68℉)Ωmm2/m密度(20℃)(g/cm3)2024-T35123.2500-635300.058 2.82 5052-H11223.8607-650350.050 2.72 5083-H11223.4570-640290.059 2.72 6061-T65123.6580-650430.040 2.73 7050-T745123.5490-630410.0415 2.82 7075-T65123.6475-635330.0515 2.82铝合金的化学成份(Chemical Composition Limit Of Aluminum )合金牌号硅Si铁Fe铜Cu锰Mn镁Mg铬Cr锌Zn钛Ti其它铝每个合计最小值202 423.20.5 3.8-4.90.3-0.91.2-1.80.10.250.150.050.15余量505 2250.40.10.12.2-2.80.15-0.350.1--0.050.15余量508 323.80.40.10.3-1.4.0-4.90.05-0.250.250.150.050.15余量60623.0.70.15-0.0.150.8-1.0.04-0.30.250.10.00.1余量16425555705 023.50.1520.-2.60.11.9-2.60.045.7-6.70.060.050.15余量707 523.60.5 1.2-2.00.32.1-2.90.18-0.285.1-6.10.20.050.15余量1050 食品、化学和酿造工业用挤压盘管，各种软管，烟花粉1060 要求抗蚀性与成形性均高的场合，但对强度要求不高，化工设备是其典型用途1100 用于加工需要有良好的成形性和高的抗蚀性但不要求有高强度的零件部件，例如化工产品、食品工业装置与贮存容器、薄板加工件、深拉或旋压凹形器皿、焊接零部件、热交换器、印刷板、铭牌、反光器具1145 包装及绝热铝箔，热交换器1199 电解电容器箔，光学反光沉积膜1350电线、导电绞线、汇流排、变压器带材2011 螺钉及要求有良好切削性能的机械加工产品2014 应用于要求高强度与硬度（包括高温）的场合。
铝合金的机械性能
5A01
曾用2101、LF15
1145
－
2004
－
5A02
原LF2
1035
代L4
2011
－
5A03
原LF3
1A30
原L4－1
2014
－
5A05
原LF5
1100
代LF5－1
2014A
－
5B05
原LF10
1200
代L5
2214
－
5A06
原LF6
1235
－
2017
－
5B06
原LF14
2A01
原LY1
●
●
--
5052 H112精度板
●
--
--
5052 H32冲压板
●
--
--
5083 H112
●
--
--
Alumould
●
--
--
Mic-6
●
--
--
2024
●
--
--
K-100
●
--
--
产品参数
中、美常用铝合金牌号对照表
中国CHINA
美国THE UNITED STATES
L1-L6、L5-1
1070、1060、1050、1030、1100
6165、6061、6055、6063
LC6、LC4、LC9
7001、7178、7075
LC5、LC10
7076、7175、7079
LD11
4032
中国新旧合金牌号对照表（GB/T 3190-1996）
新牌号
旧牌号
新牌号
铝合金的典型机械性能
Aluminum 7475-T651Categories: Metal; Nonferrous Metal; Aluminum Alloy; 7000 Series Aluminum AlloyMaterial Notes: Data points with the AA note have been provided by the Aluminum Association, Inc. and are NOT FOR DESIGN.Composition Notes:Composition information provided by the Aluminum Association and is not for design.Key Words: UNS A97475; ISOu(A); Aluminium 7475-T651; AA7475-T651UNS A97475; ISO AlZn5.5MgCu(A); Aluminium 7475-T7651; AA7475-T7651Vendors: Click here to view all available suppliers for this material.Please click here if you are a supplier and would like information on how to add yourlisting to this material.Printer friendly versionDownload as PDFDownload to Excel(requires Excel and Windows)PropertiesDensity 2.81 g/cc 0.102 lb/in³AA; Typical MechanicalPropertiesMetric English CommentsHardness, Brinell 150 150 500 kg load with 10 mm ball.Calculated value.Hardness, Knoop 190 190 Converted from Brinell HardnessValueHardness, Rockwell A 53.5 53.5 Converted from Brinell HardnessValueHardness, Rockwell B 87 87 Converted from Brinell HardnessValueHardness, Vickers 175 175 Converted from Brinell HardnessValueTensileStrength,Ultimate586 MPa 85000 psi AA; TypicalTensileStrength,Yield510 MPa 74000 psi AA; TypicalElongation at Break13.0 %@Diameter 12.7 mm13.0 %@Diameter 0.500 inAA; TypicalModulus of Elasticity 71.7 GPa 10400 ksi AA; Typical; Average of tension andcompression. Compression modulusis about 2% greater than tensilemodulus.PoissonsRatio0.330 0.330FractureToughness29.7 MPa-m½ 27.0 ksi-in½ plate; S-L37.4 MPa-m½ 34.0 ksi-in½ plate; T-L42.9 MPa-m½ 39.0 ksi-in½ plate; L-T Machinability 70 % 70 % 0-100 Scale of Aluminum Alloys ShearModulus27.0 GPa 3920 ksiShearStrength350 MPa 50800 psi Calculated value.Electrical Properties Metric English Comments ElectricalResistivity0.00000499 ohm-cm @Temperature 20.0 °C 0.00000499 ohm-cm@Temperature 68.0 °F AA; TypicalThermal Properties Metric English CommentsCTE, linear21.6 µm/m-°C @Temperature -50.0 - 20.0 °C 12.0 µin/in-°F@Temperature -58.0 - 68.0 °F23.2 µm/m-°C @Temperature 20.0 - 100 °C 12.9 µin/in-°F@Temperature 68.0 - 212 °FAA; Typical; average over range23.4 µm/m-°C @Temperature 20.0 - 100 °C 13.0 µin/in-°F@Temperature 68.0 - 212 °F24.3 µm/m-°C @Temperature 20.0 - 200 °C 13.5 µin/in-°F@Temperature 68.0 - 392 °F25.2 µm/m-°C @Temperature 20.0 - 300 °C 14.0 µin/in-°F@Temperature 68.0 - 572 °F25.2 µm/m-°C @Temperature 20.0 - 300 °C 14.0 µin/in-°F@Temperature 68.0 - 572 °FaverageSpecific Heat Capacity 0.880 J/g-°C 0.210 BTU/lb-°F Estimated from trends in similar Alalloys.Thermal Conductivity 138 W/m-K 960 BTU-in/hr-ft²-°F AA; Typical at 77°FMelting Point 477 - 635.0 °C 890 - 1175 °F AA; Typical range based on typicalcomposition for wrought products 1/4inch thickness or greaterSolidus 477 °C 890 °F AA; Typical Liquidus 635.0 °C 1175 °F AA; TypicalProcessing Properties Metric English CommentsAnnealing Temperature 413 °C 775 °FSolutionTemperature 516 °C 960 °F must be preceded by soak at 870 to890°FAgingTemperature 121 - 177 °C250 - 350 °FComponent Elements Properties MetricEnglish Comments Aluminum, Al88.5 - 91.5 % 88.5 - 91.5 % As remainderChromium, Cr0.18 - 0.25 % 0.18 - 0.25 % Copper, Cu 1.20 - 1.90 % 1.20 - 1.90 % Iron, Fe <= 0.12 % <= 0.12 % Magnesium, Mg1.90 -2.60 % 1.90 - 2.60 % Manganese, Mn<= 0.060 % <= 0.060 % Other, each <= 0.050 % <= 0.050 % Other, total <= 0.15 % <= 0.15 % Silicon, Si <= 0.10 % <= 0.10 % Titanium, Ti <= 0.060 % <= 0.060 % Zinc, Zn5.20 -6.20 %5.20 -6.20 %References for this datasheet.Aluminum 7075-T6; 7075-T651 Categories: M etal; Nonferrous Metal; Aluminum Alloy; 7000 Series Aluminum AlloyMaterial Notes: General 7075 characteristics and uses (from Alcoa): Very high strength material used for highly stressed structural parts. The T7351 temper offers improved stress-corrosion cracking resistance.Applications: Aircraft fittings, gears and shafts, fuse parts, meter shafts and gears, missile parts, regulating valve parts, worm gears, keys, aircraft, aerospace and defense applications; bike frames, all terrain vehicle (ATV) sprockets.Data points with the AA note have been provided by the Aluminum Association, Inc. and are NOT FOR DESIGN.Composition Notes:A Zr + Ti limit of 0.25 percent maximum may be used with this alloy designation for extruded and forged products only, but only when the supplier or producer and the purchaser have mutually so agreed. Agreement may be indicated, for example, by reference to a standard, by letter, by order note, or other means which allow the Zr + Ti limit.Composition information provided by the Aluminum Association and is not for design.Key Words: A luminium 7075-T6; Aluminium 7075-T651, UNS A97075; ISO AlZn5.5MgCu; Aluminium 7075-T6; Aluminium 7075-T651; AA7075-T6Vendors: Click here to view all available suppliers for this material.Please click here if you are a supplier and would like information on how to add yourlisting to this material.Printer friendly versionDownload as PDFDownload to Excel(requires Excel and Windows)PropertiesDensity 2.81 g/cc 0.102 lb/in³AA; TypicalMechanicalPropertiesMetric English CommentsHardness,Brinell150 150 AA; Typical; 500 g load; 10 mm ballHardness, Knoop 191 191 Converted from Brinell HardnessValueHardness, Rockwell A 53.5 53.5 Converted from Brinell HardnessValueHardness, Rockwell B 87 87 Converted from Brinell HardnessValueHardness, Vickers 175 175 Converted from Brinell HardnessValueTensileStrength,Ultimate572 MPa 83000 psi AA; Typical41.0 MPa @Temperature 371 °C5950 psi @Temperature 700 °F55.0 MPa @Temperature 316 °C7980 psi @Temperature 601 °F76.0 MPa @Temperature 260 °C11000 psi @Temperature 500 °F110 MPa @Temperature 204 °C16000 psi @Temperature 399 °F214 MPa@Temperature 149 °C31000 psi@Temperature 300 °F483 MPa@Temperature 100 °C70100 psi@Temperature 212 °F572 MPa@Temperature 24.0 °C83000 psi@Temperature 75.2 °F593 MPa@Temperature -28.0 °C86000 psi@Temperature -18.4 °F621 MPa@Temperature -80.0 °C90100 psi@Temperature -112 °F703 MPa@Temperature -196 °C102000 psi@Temperature -321 °F>= 462 MPa@Thickness 88.93 - 102 mm>= 67000 psi@Thickness 3.501 - 4.00 inPlate; T62, T651>= 490 MPa@Thickness 76.23 - 88.9 mm>= 71100 psi@Thickness 3.001 - 3.50 inPlate; T62, T651>= 496 MPa@Thickness 63.53 - 76.2 mm>= 71900 psi@Thickness 2.501 - 3.00 inPlate; T62, T651>= 510 MPa@Thickness 0.203 - 0.279 mm>= 74000 psi@Thickness 0.00800 - 0.0110 inSheet>= 524 MPa@Thickness 0.305 - 0.991 mm>= 76000 psi@Thickness 0.0120 - 0.0390 inSheet>= 524 MPa@Thickness 50.83 - 63.5 mm>= 76000 psi@Thickness 2.001 - 2.50 inPlate; T62, T651>= 531 MPa@Thickness 25.43 - 50.8 mm>= 77000 psi@Thickness 1.001 - 2.00 inPlate; T62, T651>= 538 MPa@Thickness 1.02 - 3.17 mm>= 78000 psi@Thickness 0.0400 - 0.125 inSheet>= 538 MPa@Thickness 3.20 - 6.32 mm>= 78000 psi@Thickness 0.126 - 0.249 inSheet>= 538 MPa@Thickness 6.35 - 12.7 mm>= 78000 psi@Thickness 0.250 - 0.499 inPlate; T62, T651>= 538 MPa@Thickness 12.7 - 25.4 mm>= 78000 psi@Thickness 0.500 - 1.00 inPlate; T62, T651 TensileStrength,Yield503 MPa 73000 psi AA; Typical>= 372 MPa@Thickness 88.93 - 102 mm>= 54000 psi@Thickness 3.501 - 4.00 inPlate; T62, T651>= 400 MPa@Thickness 76.23 - 88.9 mm>= 58000 psi@Thickness 3.001 - 3.50 inPlate; T62, T651>= 421 MPa@Thickness 63.53 - 76.2 mm>= 61100 psi@Thickness 2.501 - 3.00 inPlate; T62, T651>= 434 MPa@Thickness 0.203 - 0.279 mm>= 62900 psi@Thickness 0.00800 - 0.0110 inSheet>= 441 MPa@Thickness 50.83 - 63.5 mm>= 64000 psi@Thickness 2.001 - 2.50 inPlate; T62, T651>= 462 MPa@Thickness 0.305 - 0.991 mm>= 67000 psi@Thickness 0.0120 - 0.0390 inSheet>= 462 MPa@Thickness 6.35 - 12.7 mm>= 67000 psi@Thickness 0.250 - 0.499 inPlate; T62, T651>= 462 MPa@Thickness 25.43 - 50.8 mm>= 67000 psi@Thickness 1.001 - 2.00 inPlate; T62, T651>= 469 MPa@Thickness 1.02 - 3.17 mm>= 68000 psi@Thickness 0.0400 - 0.125 inSheet>= 469 MPa@Thickness 12.7 - 25.4 mm>= 68000 psi@Thickness 0.500 - 1.00 inPlate; T62, T651>= 476 MPa@Thickness 3.20 - 6.32 mm>= 69000 psi@Thickness 0.126 - 0.249 inSheet32.0 MPa@Strain 0.200 %,Temperature 271 °C4640 psi@Strain 0.200 %,Temperature 520 °F45.0 MPa@Strain 0.200 %,Temperature 316 °C6530 psi@Strain 0.200 %,Temperature 601 °F62.0 MPa@Strain 0.200 %,Temperature 260 °C8990 psi@Strain 0.200 %,Temperature 500 °F87.0 MPa12600 psi@Strain 0.200 %, Temperature 204 °C@Strain 0.200 %, Temperature 399 °F186 MPa @Strain 0.200 %, Temperature 149 °C27000 psi @Strain 0.200 %, Temperature 300 °F448 MPa @Strain 0.200 %, Temperature 100 °C65000 psi @Strain 0.200 %, Temperature 212 °F503 MPa @Strain 0.200 %, Temperature 24.0 °C73000 psi @Strain 0.200 %, Temperature 75.2 °F517 MPa @Strain 0.200 %, Temperature -28.0 °C75000 psi @Strain 0.200 %, Temperature -18.4 °F545 MPa @Strain 0.200 %, Temperature -80.0 °C79000 psi @Strain 0.200 %, Temperature -112 °F634 MPa @Strain 0.200 %, Temperature -196 °C92000 psi @Strain 0.200 %, Temperature -321 °FElongation atBreak9.00 %@Temperature -196 °C9.00 %@Temperature -321 °F11.0 %@Temperature -80.0 °C11.0 %@Temperature -112 °F11.0 %@Temperature -28.0 °C11.0 %@Temperature -18.4 °F11.0 %@Temperature 24.0 °C11.0 %@Temperature 75.2 °F14.0 %@Temperature 100 °C14.0 %@Temperature 212 °F30.0 %@Temperature 149 °C30.0 %@Temperature 300 °F55.0 %@Temperature 204 °C55.0 %@Temperature 399 °F65.0 %@Temperature 260 °C65.0 %@Temperature 500 °F70.0 %@Temperature 316 °C70.0 %@Temperature 601 °F70.0 %@Temperature 371 °C70.0 %@Temperature 700 °F>= 3.00 % @Thickness 88.93 - 102 mm>= 3.00 %@Thickness 3.501 - 4.00 inPlate; T62, T651>= 5.00 % @Thickness 0.203 - 0.279 mm>= 5.00 %@Thickness 0.00800 - 0.0110 inSheet>= 5.00 % @Thickness 50.83 - 63.5 mm>= 5.00 %@Thickness 2.001 - 2.50 inPlate; T62, T651>= 5.00 % @Thickness 63.53 - 76.2 mm>= 5.00 %@Thickness 2.501 - 3.00 inPlate; T62, T651>= 5.00 % @Thickness 76.23 - 88.9 mm>= 5.00 %@Thickness 3.001 - 3.50 inPlate; T62, T651>= 6.00 % @Thickness 25.43 - 50.8 mm>= 6.00 %@Thickness 1.001 - 2.00 inPlate; T62, T651>= 7.00 % @Thickness 0.305 - 0.991 mm>= 7.00 %@Thickness 0.0120 - 0.0390 inSheet>= 7.00 % @Thickness 12.7 - 25.4 mm>= 7.00 %@Thickness 0.500 - 1.00 inPlate; T62, T651>= 8.00 % @Thickness 1.02 - 3.17 mm>= 8.00 %@Thickness 0.0400 - 0.125 inSheet>= 8.00 % @Thickness 3.20 - 6.32 mm>= 8.00 %@Thickness 0.126 - 0.249 inSheet>= 9.00 % @Thickness 6.35 - 12.7 mm>= 9.00 %@Thickness 0.250 - 0.499 inPlate; T62, T65111.0 % @Thickness 1.59 mm11.0 %@Thickness 0.0625 inAA; Typical11.0 % @Diameter 12.7 mm11.0 %@Diameter 0.500 inAA; TypicalModulus of Elasticity 71.7 GPa 10400 ksi AA; Typical; Average of tensionand compression. Compressionmodulus is about 2% greater thantensile modulus. PoissonsRatio0.330 0.330Fatigue Strength159 MPa@# of Cycles 5.00e+823000 psi@# of Cycles 5.00e+8completely reversed stress; RRMoore machine/specimenFractureToughness17.6 MPa-m½ 16.0 ksi-in½ T651; Plate; S-L; average16.5 - 19.8 MPa-m½ 15.0 - 18.0 ksi-in½ T651; Plate; S-L18.7 MPa-m½ 17.0 ksi-in½ T651; Forgings; S-L20.0 MPa-m½ 18.2 ksi-in½ K(IC) in S-L Direction22.0 - 25.3 MPa-m½ 20.0 - 23.0 ksi-in½ T651; Plate; T-L24.2 MPa-m½ 22.0 ksi-in½ T651; Plate; T-L; average25.0 MPa-m½ 22.8 ksi-in½ K(IC) in T-L Direction28.6 MPa-m½ 26.0 ksi-in½ T651; Plate; L-T; average27.5 - 29.7 MPa-m½ 25.0 - 27.0 ksi-in½ T651; Plate; L-T29.0 MPa-m½ 26.4 ksi-in½ K(IC) in L-T Direction Machinability 70 % 70 % 0-100 Scale of Aluminum Alloys ShearModulus26.9 GPa 3900 ksiShearStrength331 MPa 48000 psi AA; TypicalElectricalPropertiesMetric English CommentsElectrical Resistivity 0.00000515 ohm-cm@Temperature 20.0 °C0.00000515 ohm-cm@Temperature 68.0 °FAA; TypicalThermalPropertiesMetric English CommentsCTE, linear21.6 µm/m-°C@Temperature -50.0 - 20.0 °C12.0 µin/in-°F@Temperature -58.0 - 68.0 °F23.4 µm/m-°C@Temperature 20.0 - 100 °C13.0 µin/in-°F@Temperature 68.0 - 212 °F23.6 µm/m-°C@Temperature 20.0 - 100 °C13.1 µin/in-°F@Temperature 68.0 - 212 °FAA; Typical; average over range24.3 µm/m-°C@Temperature 20.0 - 200 °C13.5 µin/in-°F@Temperature 68.0 - 392 °F25.2 µm/m-°C@Temperature 20.0 - 300 °C14.0 µin/in-°F@Temperature 68.0 - 572 °F25.2 µm/m-°C@Temperature 20.0 - 300 °C14.0 µin/in-°F@Temperature 68.0 - 572 °FaverageSpecific HeatCapacity0.960 J/g-°C 0.229 BTU/lb-°FThermalConductivity130 W/m-K 900 BTU-in/hr-ft²-°F AA; Typical at 77°F Melting Point 477 - 635.0 °C 890 - 1175 °F AA; Typical range based on typicalcomposition for wrought products1/4 inch thickness or greater.Homogenization may raise eutecticmelting temperature 20-40°F butusually does not eliminate eutecticmelting. Solidus 477 °C 890 °F AA; Typical Liquidus 635.0 °C 1175 °F AA; Typical ProcessingPropertiesMetric English Comments AnnealingTemperature413 °C 775 °FSolutionTemperature466 - 482 °C 870 - 900 °FAgingTemperature121 °C 250 °FComponentMetric English Comments ElementsProperties87.1 - 91.4 % 87.1 - 91.4 % As remainder Aluminum,AlChromium,0.18 - 0.280 % 0.18 - 0.280 %CrCopper, Cu 1.20 - 2.0 % 1.20 - 2.0 %Iron, Fe <= 0.50 % <= 0.50 %Magnesium,2.10 - 2.90 % 2.10 - 2.90 %Mg<= 0.30 % <= 0.30 %Manganese,MnOther, each <= 0.050 % <= 0.050 %Other, total <= 0.15 % <= 0.15 %Silicon, Si <= 0.40 % <= 0.40 %Titanium, Ti <= 0.20 % <= 0.20 %Zinc, Zn 5.10 - 6.10 % 5.10 - 6.10 %References for this datasheet.。
铝合金的系列和机械性能
一JIS A.A 1000 系列－－纯铝系1、1060作为导电材料IACS保证61%，需要强度时使用6061 电线2、1085 1080 1070 1050 1N30 1085 1080 1070 1050 —成形性、表面处理性良好，在铝合金中其耐蚀性最佳。
因为是纯铝、其强度较低，纯度愈高其强度愈低。
日用品、铝板、照明器具、反射板、装饰品、化学工业容器、散热片、溶接线、导电材3、1100 1200 AL纯度99.0%以上之一般用途铝材，阳极氧化处理后之外观略呈白色外与上记相同。
一般器物、散热片、瓶盖、印刷板、建材、热交换器组件1N00 －强度比1100略高，成形性良好，其化特性与1100相同。
二日用品2000 系列－－AL x Cu 系铝铜1、2011快削合金，切削性好强度也高。
但耐蚀性不佳。
要求耐蚀性时，使用6062系合金音量轴、光学组件、螺丝头。
2、2014 2017 2024 含有多量的Cu，耐蚀性不佳，但强度高，可作为构造用材使用，锻造品亦可适用，航空器、齿轮、油、压组件、轮轴。
3、2117固溶化热处理后，作为铰钉用材，为延迟常温时效速度之合金。
4、2018 2218 锻造用合金。
锻造性良好且高温强度较高，因此使用于需要耐热性之锻造品，耐蚀性不佳，汽缸头、活塞、VTR汽缸。
5、2618锻造用合金。
高温强度优越但耐蚀性不佳。
活塞、橡胶成形用模具、一般耐热用途组件。
6、2219强度高，低温及高温特性良好，溶接性也优越，但耐蚀性不佳。
低温用容器、航太机器。
7、2025 锻造用合金。
锻造性良好且强度高，但耐蚀性不佳。
螺旋桨、磁气桶。
2N01－锻造用合金。
具耐热性，强度也高，但耐蚀性不佳。
航空器引擎、油压组件。
三3000 系列－－AL x Mn 系铝锰1、3003 3203 强度比1100约高10%，成形性、溶接性、耐蚀性均良好。
一般器物、散热片、化妆板、影印机滚筒、船舶用材2、3004 3104 强度比3003高，成形性优越，耐蚀性也良好。
铝合金adc12材料参数
铝合金adc12材料参数
铝合金ADC12是一种常用的铝合金材料，它具有良好的机械性能和加工性能，被广泛应用于汽车、航空航天、电子等领域。
以下是关于铝合金ADC12材料参数的详细介绍。
1. 化学成分
铝合金ADC12的化学成分如下：
- 铝（Al）：余量
- 硅（Si）：9.6%-12%
- 铜（Cu）：1.5%-3.5%
- 镁（Mg）：0.3%-0.6%
- 锰（Mn）：不超过0.5%
- 锌（Zn）：不超过1%
- 铁（Fe）：不超过0.9%
- 钛（Ti）：不超过0.2%
2. 机械性能
铝合金ADC12的机械性能如下：
- 抗拉强度：≥320MPa
- 屈服强度：≥160MPa
- 延伸率：≥3%
- 冲击韧性：≥6J/cm²
3. 物理性质
铝合金ADC12的物理性质如下：
- 密度：2.7g/cm³
- 热膨胀系数：23×10^-6/K
- 热导率：96W/(m·K)
- 电导率：23.8MS/m
- 比热容：0.9J/(g·K)
4. 加工性能
铝合金ADC12具有良好的加工性能，可以通过压铸、挤压、锻造等加工方法进行加工。
其中，压铸是最常用的加工方法，可以生产出各种形状的零件。
5. 应用领域
由于铝合金ADC12具有良好的机械性能和加工性能，被广泛应用于汽车、航空航天、电子等领域。
在汽车领域中，它被用于制造发动机零件、转向器零件、变速器壳体等；在航空航天领域中，它被用于制造飞机结构零件、发动机零件等；在电子领域中，它被用于制造电脑外壳、手机外壳等。
铝合金技术参数
理论上是2.7，要看成型方法i: 压铸的2.6-2.63 左右，挤压的2.68-2.7，锻造的2.69-2.72 铝合金的典型机械性能(Typical Mechanical Properties)铝合金牌号及状态拉伸强度(25°CMPa)屈服强度(25°CMPa)硬度500kg力10mm球延伸率1.6mm(1/16in)厚度5052-H1121751956012 5083-H1121802116514 6061-T6513102769512 7050-T745151045513510 7075-T65157250315011 2024-T35147032512020铝合金的典型物理性能(Typical Physical Properties)铝合金牌号及状态热膨胀系数(20-100℃)μm/m·k熔点范围(℃)电导率20℃(68℉)(%IACS)电阻率20℃(68℉)Ωmm2/m密度(20℃)(g/cm3)2024-T35123.2500-635300.058 2.82 5052-H11223.8607-650350.050 2.72 5083-H11223.4570-640290.059 2.72 6061-T65123.6580-650430.040 2.73 7050-T745123.5490-630410.0415 2.82 7075-T65123.6475-635330.0515 2.82铝合金的化学成份(Chemical Composition Limit Of Aluminum )合金牌号硅Si铁Fe铜Cu锰Mn镁Mg铬Cr锌Zn钛Ti其它铝每个合计最小值202 423.20.5 3.8-4.90.3-0.91.2-1.80.10.250.150.050.15余量505 2250.40.10.12.2-2.80.15-0.350.1--0.050.15余量50823.0.40.10.3-1. 4.0-4.0.05-0.20.250.10.00.1余量38095555606 123.60.70.15-0.40.150.8-1.20.04-0.350.250.150.050.15余量705 023.50.1520.-2.60.11.9-2.60.045.7-6.70.060.050.15余量707 523.60.5 1.2-2.00.32.1-2.90.18-0.285.1-6.10.20.050.15余量1050 食品、化学和酿造工业用挤压盘管，各种软管，烟花粉1060 要求抗蚀性与成形性均高的场合，但对强度要求不高，化工设备是其典型用途1100 用于加工需要有良好的成形性和高的抗蚀性但不要求有高强度的零件部件，例如化工产品、食品工业装置与贮存容器、薄板加工件、深拉或旋压凹形器皿、焊接零部件、热交换器、印刷板、铭牌、反光器具1145 包装及绝热铝箔，热交换器1199 电解电容器箔，光学反光沉积膜1350电线、导电绞线、汇流排、变压器带材2011 螺钉及要求有良好切削性能的机械加工产品2014 应用于要求高强度与硬度（包括高温）的场合。
部分铝合金典型机械性能参考值
拉
伸
强度，MPa
伸长率，%
50 毫米 5D
强度 屈服 厚
直径
极限 极限 1.60mm 12.5mm
试样 试样
420 315 —
10
185 75
20
20
485 345
18
—
470 325
20
17
495 395
13
—
180 75
20
—
450 310
18
—
440 290
19
—
460 365
11
—
450 415
110 105
12
22
28
125 115
9
18
32
145 140
6
15
38
165 150
5
13
44
85 30
—
—⑤
—
95 85
—
—
—
110 95
—
—
—
125 110
—
—
—
185 165
—
—⑥
—
380 295
—
13
95
405 310
—
10
100
185 95
—
16
45
425 290
—
18
105
485 415
5
5
115 55
24
—
150 130
7
—
170 150
5
—
195 170
4
—
215 195
3
—
180 160
铝机械性能
M
O
CYS
TX51、TX52
R
H112或F
CZY
T0
Y
HX8
CSY
T9
Y1
HX6
MCS
T62
Y2
HX4
MCZ
T42
Y4
HX2
CGS1
T73
T
HX9
CGS2
T76
CZ
T4
CGS3
T74
CS
T6
RCS
T5
注：原以R状态交货的、提供CZ、CS试样性能的产品，其状态可分别对应新代号T62、T42。
HXY细分状态代号与加工硬化程度
T62
适用于自O或F状态固溶热处理后，进行人工时效的产品，也适用于需方对任何状态的加工产品热处理后，力学性能达到了T62状态的产品
T73
适用于固溶热处理后，经过时效以达到规定的力学性能和抗应力腐蚀性能指标的产品
T74
与T73状态定义相同。该状态的抗拉强度大于T73状态，但小于T76状态
T76
与T73状态定义相同。该状态的抗拉强度分别高于T73、T74状态，抗应力腐蚀断裂性能分别低于T73、T74状态，但其抗剥落腐蚀性能仍较好
T4
固溶热处理后自然时效至基本稳定的状态适用于固溶热处理后，不再进行冷加工（可进行矫直、矫平，但不影响力学性能极限）的产品
T5
由高温成型过程冷却，然后进行人工时效的状态，适用于由高温成型过程冷却后，不经过冷加工（可进行矫直、矫平，但不影响力学性能极限），予以人工时效的产品
T6
固溶热处理后进行人工时效的状态适用于固溶热处理后，不再进行冷加工（可进行矫直、矫平，但不影响力学性能极限）的产品
铝合金的机械性能
0.05
0.15
余量
6061
23.6
0.7
0.15-0.4
0.15
0.8-1.2
0.04-0.35
0.25
0.15
0.05
0.15
余量
7050
23.5
0.15
20.-2.6
0.1
1.9-2.6
0.04
5.7-6.7
0.06
0.05
0.15
余量
7075
23.6
0.5
1.2-2.0
0.3
2.1-2.9
O
退火状态
适用于经完全退火获得最低强度的加工产品
H
加工硬化状态
适用于通过加工硬化提高强度的产品，产品在加工硬化后可经过（也可不经过）使强度有所降低的附加热处理H代号后面必须 跟有两位或三位阿拉伯数字
W
固溶热处理状态
一种不稳定状态，仅适用于经固溶热处理后，室温下自然时效的合金，该状态代号仅表示产品处于自然时效阶段
注：当按上表确定的HX1～HX9状态的抗拉强度极限值，不是0或5结尾时，应修约至以0或5结尾的相邻较大值。
TX细分状态代号说明与应用
状态代号
说明与应用
T0
固溶热处理后、经自然时效再通过冷加工的状态，适用于经冷加工提高强度的产品
T1
由高温成型过程冷却，然后自然时效至基本稳定的状态，适用于由高温成型过程冷却后，不再进行冷加工（可进行矫直、矫平，但不影响力学性能极限）的产品
T2
由高温成型过程冷却，经冷加工后自然时效至基本稳定的状态，适用于由高温成型过程冷却后，进行冷加工、或矫直、矫平以提高强度的产品
T3
固溶热处理后进行冷加工，再经自然时效至基本稳定的状态，适用于在固溶热处理后，进行冷加工、或矫直。矫平以提高强度的产品