硬度与钻杆钢级对照表
硬度对照表（详细）
硬度换算表 (以HRC硬度为基准) 1—前桥教育Brinell (布氏)Rockwell Hardness(洛氏硬度)Rockwell Superficial Hardness(罗克韦尔表面硬度)Rockwell C (洛氏C)3000 kgfRockwell A(洛氏A)Rockwell B(洛氏B)Rockwell D(洛氏D)Approximate近似Rockwell C(洛氏C)150 kgf Vickers10 mm 60 kgf100 kgf100 kgf15 kgf30 kgf45 kgf Tensile(拉伸)150 kgfDiamond (钻石)Hardness(硬度)Ball(球)Diamond(钻石)1//16" ball(1//16球)Diamond(钻石)1/16" ball(1/16球)1/16" ball(1/16球)1/16" ball(1/16球)Strength(强度)Diamond(钻石)HRC HV HB HRA HRB HRD HR15N HR30N HR45N ksi (MPa)HRC 68 940 --- 85.6 --- 76.9 93.2 84.4 75.4 --- 68 67 900 --- 85.0 --- 76.1 92.9 83.6 74.2 --- 67 66 865 --- 84.5 --- 75.4 92.5 82.8 73.3 --- 66 65 832 739 83.9 --- 74.5 92.2 81.9 72.0 --- 65 64 800 722 83.4 --- 73.8 91.8 81.1 71.0 --- 6463 772 705 82.8 --- 73.0 91.4 80.1 69.9 --- 63 62 746 688 82.3 --- 72.2 91.1 79.3 68.8 --- 62 61 720 670 81.8 --- 71.5 90.7 78.4 67.7 --- 61 60 697 654 81.2 --- 70.7 90.2 77.5 66.6 --- 60 59 674 634 80.7 --- 69.9 89.8 76.6 65.5 --- 5958 653 615 80.1 --- 69.2 89.3 75.7 64.3 --- 58 57 633 595 79.6 --- 68.5 88.9 74.8 63.2 --- 57 56 613 577 79.0 --- 67.7 88.3 73.9 62.0 --- 56 55 595 560 78.5 --- 66.9 87.9 73.0 60.9 2075 55 54 577 543 78.0 --- 66.1 87.4 72.0 59.8 2015 5453 560 525 77.4 --- 65.4 86.9 71.2 58.6 1950 53 52 544 512 76.8 --- 64.6 86.4 70.2 57.4 1880 52 51 528 496 76.3 --- 63.8 85.9 69.4 56.1 1820 51 50 513 481 75.9 --- 63.1 85.5 68.5 55.0 1760 50 49 498 469 75.2 --- 62.1 85.0 67.6 53.8 1695 49硬度换算表 (以HRC硬度为基准) 2前桥教育Brinell (布氏)Rockwell Hardness(洛氏硬度)Rockwell Superficial Hardness(罗克韦尔表面硬度)Rockwell C (洛氏C)3000 kgfRockwell A(洛氏A)Rockwell B(洛氏B)Rockwell D(洛氏D)Approximate近似Rockwell C(洛氏C)150 kgf Vickers10 mm 60 kgf100 kgf100 kgf15 kgf30 kgf45 kgf Tensile(拉伸)150 kgfDiamond (钻石)Hardness(硬度)Ball(球)Diamond(钻石)1//16" ball(1//16球)Diamond(钻石)1/16" ball(1/16球)1/16" ball(1/16球)1/16" ball(1/16球)Strength(强度)Diamond(钻石)HRC HV HB HRA HRB HRD HR15N HR30N HR45N ksi (MPa)HRC 48 484 455 74.7 --- 61.4 84.5 66.7 52.5 1635 48 47 471 443 74.1 --- 60.8 83.9 65.8 51.4 1580 47 46 458 432 73.6 --- 60.0 83.5 64.8 50.3 1530 46 45 446 421 73.1 --- 59.2 83.0 64.0 49.0 1480 45 44 434 409 72.5 --- 58.5 82.5 63.1 47.8 1435 4443 423 400 72.0 --- 57.7 82.0 62.2 46.7 1385 43 42 412 390 71.5 --- 56.9 81.5 61.3 45.5 1340 42 41 402 381 70.9 --- 56.2 80.9 60.4 44.3 1295 41 40 392 371 70.4 --- 55.4 80.4 59.5 43.1 1250 40 39 382 362 69.9 --- 54.6 79.9 58.6 41.9 1215 3938 372 353 69.4 --- 53.8 79.4 57.7 40.8 1180 38 37 363 344 68.9 --- 53.1 78.8 56.8 39.6 1160 37 36 354 336 68.4 (109.0) 52.3 78.3 55.9 38.4 1115 36 35 345 327 67.9 (108.5) 51,5 77.7 55.0 37.2 1080 35 34 336 319 67.4 (108.0) 50.8 77.2 54.2 36.1 1055 3433 327 311 66.8 (107.5) 50.0 76.6 53.3 34.9 1025 33 32 318 301 66.3 (107.0) 49.2 76.1 52.1 33.7 1000 32 31 310 294 65.8 (106.0) 48.4 75.6 51.3 32.5 980 31 30 302 286 65.3 (105.5) 47.7 75.0 50.4 31.3 950 30 29 294 279 64.7 (104.5) 47.0 74.5 49.5 30.1 930 29硬度换算表 (以HRC硬度为基准) 3Brinell (布氏)Rockwell Hardness(洛氏硬度)Rockwell Superficial Hardness(罗克韦尔表面硬度)Rockwell C (洛氏C)3000 kgfRockwell A(洛氏A)Rockwell B(洛氏B)Rockwell D(洛氏D)Approximate近似150 kgf Vickers10 mm 60 kgf100 kgf100 kgf15 kgf30 kgf45 kgf Tensile (拉伸)Diamond (钻石)Hardness(硬度)Ball(球)Diamond(钻石)1//16" ball(1//16球)Diamond(钻石)1/16" ball(1/16球)1/16" ball(1/16球)1/16" ball(1/16球)Strength(强度)HRC HV HB HRA HRB HRD HR15N HR30N HR45N ksi (MPa)28 286 271 64.3 (104.0) 46.1 73.9 48.6 28.9 910 28 27 279 264 63.8 (103.0) 45.2 73.3 47.7 27.8 880 27 26 272 258 63.3 (102.5) 44.6 72.8 46.8 26.7 860 26 25 266 253 62.8 (101.5) 43.8 72.2 45.9 25.5 840 25 24 260 247 62.4 (101.0) 43.1 71.6 45.0 24.3 825 2423 254 243 62.0 100.0 42.1 71.0 44.0 23.1 805 23 22 248 237 61.5 99.0 41.6 70.5 43.2 22.0 785 22 21 243 231 61.0 98.5 40.9 69.9 42.3 20.7 770 21 20 238 226 60.5 97.8 40.1 69.4 41.5 19.6 760 20 (18) 230 219 --- 96.7 --- --- --- --- 730 (18)(16) 222 212 --- 95.5 --- --- --- --- 705 (16) (14) 213 203 --- 93.9 --- --- --- --- 675 (14) (12) 204 194 --- 92.3 --- --- --- --- 650 (12) (10) 196 187 --- 90.7 --- --- --- --- 620 (10) (8) 188 179 --- 89.5 --- --- --- --- 600 (8)---(6) 180 171 --- 87.1 --- --- --- --- 580 (6) (4) 173 165 --- 85.5 --- --- --- --- 550 (4) (2) 166 158 --- 83.5 --- --- --- --- 530 (2) (0) 160 152 --- 81.7 --- --- --- --- 510 (0)42CrMo：材料采用调质工艺一般840淬火，620～680之间回火，硬度控制在261～304HB。
硬度对照表2
硬度对照表金属材料抵抗硬的物体压陷表面的能力，称为硬度。
根据试验方法和适用范围不同，硬度又可分为布氏硬度、洛氏硬度、维氏硬度、肖氏硬度、显微硬度和高温硬度等。
对于管材一般常用的有布氏、洛氏、维氏硬度三种。
A、布氏硬度（HB）用一定直径的钢球或硬质合金球，以规定的试验力（F）压入式样表面，经规定保持时间后卸除试验力，测量试样表面的压痕直径（L）。
布氏硬度值是以试验力除以压痕球形表面积所得的商。
以HBS （钢球）表示，单位为N/mm2（MPa）。
其计算公式为：式中：F--压入金属试样表面的试验力，N;D--试验用钢球直径，mm ;d--压痕平均直径，mm。
测定布氏硬度较准确可靠，但一般HBS只适用于450N/mm2（MPa）以下的金属材料，对于较硬的钢或较薄的板材不适用。
在钢管标准中，布氏硬度用途最广，往往以压痕直径d来表示该材料的硬度，既直观，又方便。
举例：120HBS10/1000130 :表示用直径10mm钢球在1000Kgf（9.807KN ）试验力作用下，保持30s（秒）测得的布氏硬度值为120N/ mm2 （MPa）。
B、洛氏硬度（HK）洛氏硬度试验同布氏硬度试验一样，都是压痕试验方法。
不同的是，它是测量压痕的深度。
即，在初邕试验力（Fo）及总试验力（F）的先后作用下，将压头（金钢厂圆锥体或钢球）压入试样表面，经规定保持时间后，卸除主试验力，用测量的残余压痕深度增量（e）计算硬度值。
其值是个无名数，以符号HR表示，所用标尺有A、B、C、D、E、F、G、H、K等9个标尺。
其中常用于钢材硬度试验的标尺一般为A、B、C,即卩HRA、HRB、HRC。
硬度值用下式计算：当用A和C标尺试验时，HR=100-e当用B标尺试验时，HR=130-e式中e--残余压痕深度增量，其什系以规定单位0.002mm表示，即当压头轴向位移一个单位（0.002mm）时，即相当于洛氏硬度变化一个数。
e值愈大，金属的硬度愈低，反之则硬度愈高。
钢材牌号对照表 主要钢材的硬度和对应工具表pdf
RS3
D3 D2
X210Cr12 X210Cr12 X210Cr12W12
合金工具钢
QF3
其他
ACD8
ICS22 MCR1 SKH9 HM35 HS53M HS93R HS98M FM38V MDS1 MDS3 MDS7 MATRIX2 ATM3 FAX38
K190
SKH51 SKH55类 高速 工具钢 SKH57类
M2
H6.5.2 S6.2.5
HS6-5-2 HS6-5-2-5
YXM1 YXM4 XVC5 YXR33 YXR3 YXR7
S600 S705 S700
S10-4-3-10 HS10-4-3-10
烧结类 SKH40 烧结类 HS6-5-3-8
QHZ KHA30 KHA3VN KHA32 SPM23 SPM60
(Be-Cu) SCM435 HPM2T
工
质
SKD61 STAVAX ESR RIGOR (SKD12类)
HPM7 NAK55 PX5 HPM1 NAK80 HPM38 HPM50 S-STAR FDAC STAVAX ESR DH2F 30 40
(电铸-外) (电铸-内) ORAVAR SUPREME (时效处理)MAS1C HPM38 S-STAR STAVAX ESR 50
E D M
WEDM
电极丝
电极丝
2726
鋼材ブランド対照表 / 主な鋼材の硬度と対応工具表
钢材牌号对照表 / 主要钢材的硬度和对应工具表
■ 钢材牌号对照表
分 类 碳素工具钢 JIS SK105(旧SK3) SKS93 SKS3 SKD1 SKD11 SKD11(改) 烧结类中的CrSKD SKD12 预硬钢40HRC 预硬钢50HRC以上 火焰淬火钢 低温空冷钢 耐冲击钢 X100CrMoV5 A2 国际标准相关牌号 AISI DIN W1-10 ISO TC105 日立金属 YC3 YCS3 SGT CRD SLD SLD8 SLD10 ARK1 SCD HPM2T PRE2 HMD5 HMD1 ACD37 YSM 爱知制钢 神户制钢所 山阳特殊钢 大同特殊钢 日本高频 钢业 SK3 QK3 YK3 K3 SK301 QKSM YK30 K3M SKS3 QKS3 GOA KS3 SKD1 SKD11 AUD15 SXACE SKD12 SX105V SX4 AKS3 AKS4 AUD11 SX5 SX44 QH51 MH51 MH55 MH8 H51 HM35 MV10 KXM KMX2 KMX3 QC1 QC11 QCM8 QCM10 QCM7 DC1 DC11 DC53 DCX DC12 GO40F CX1 GO5 GO4 QF1 GS5 KD1 KD11 KD11S KD21 KD12 KAP65 RC55 FH5 KSM KTV5 SRS6 PREGA COMPAX CALMAX VIKING ELMAX VANADIS4 VANADIS6 VANADIS10 RHM1 RHM5 RHM7 K630 CDS11 MDS9 RD11 不二越 SK3M SKS3 理研制钢 UDDEHOLM BOHRER (瑞典) (德国) K990 ARNE SVERKER3 SVERKER21 SLEIPNER RIGOR IMPAX FERNO K460 K100 K107 K105 K110 K340 K305
金属材料硬度对照表
硬度知识一、硬度简介：硬度表示材料抵抗硬物体压入其表面的能力。
它是金属材料的重要性能指标之一。
一般硬度越高，耐磨性越好。
常用的硬度指标有布氏硬度、洛氏硬度和维氏硬度。
1.布氏硬度(HB)以一定的载荷(一般3000kg)把一定大小(直径一般为10mm)的淬硬钢球压入材料表面，保持一段时间，去载后，负荷与其压痕面积之比值，即为布氏硬度值(HB)，单位为公斤力/mm2 (N/mm2)。
2.洛氏硬度(HR)当HB>450或者试样过小时，不能采用布氏硬度试验而改用洛氏硬度计量。
它是用一个顶角120°的金刚石圆锥体或直径为1.59、3.18mm的钢球，在一定载荷下压入被测材料表面，由压痕的深度求出材料的硬度。
根据试验材料硬度的不同，分三种不同的标度来表示：∙HRA：是采用60kg载荷和钻石锥压入器求得的硬度，用于硬度极高的材料(如硬质合金等)。
∙HRB：是采用100kg载荷和直径1.58mm淬硬的钢球，求得的硬度，用于硬度较低的材料(如退火钢、铸铁等)。
∙HRC：是采用150kg载荷和钻石锥压入器求得的硬度，用于硬度很高的材料(如淬火钢等)。
3 维氏硬度(HV)以120kg以内的载荷和顶角为136°的金刚石方形锥压入器压入材料表面，用材料压痕凹坑的表面积除以载荷值，即为维氏硬度HV值(kgf/mm2)。
#############################################################################################注：洛氏硬度中HRA、HRB、HRC等中的A、B、C为三种不同的标准，称为标尺A、标尺B、标尺C。
洛氏硬度试验是现今所使用的几种普通压痕硬度试验之一，三种标尺的初始压力均为98.07N(合10kgf)，最后根据压痕深度计算硬度值。
标尺A使用的是球锥菱形压头，然后加压至588.4N(合60kgf)；标尺B使用的是直径为1.588mm(1/16英寸)的钢球作为压头，然后加压至980.7N(合100kgf)；而标尺C使用与标尺A相同的球锥菱形作为压头，但加压后的力是1471N(合150kgf)。
钻杆性能参数表
表A.1新钻杆性能（API标准钻杆）代号1代号2公称壁厚（mm）钢级加厚型式钻杆接头连接代号新钻杆内螺纹外径(mm)外螺纹内径(mm)近似重量(kg/m)上扣扭矩(kN.m)管体拉伸屈服(t)接头拉伸屈服(t)管体扭转屈服(kN.m)接头扭转屈服(kN.m)管体挤毁压力(MPa)管体最大内部压力(MPa)23/8 6.657.11G EU NC2685.7344.4510.58 5.5987.77142.2811.869.32150.57149.3627/810.409.19G EU NC31104.7850.8016.5010.70136.11224.8621.9317.84159.35159.52 27/810.409.19S EU NC31111.1341.2817.1913.67175.01282.9728.2022.79204.88205.10 31/213.309.35G EU NC38127.0061.9121.9117.93172.45321.1735.2129.88136.23133.21 31/213.309.35S EU NC38127.0053.9822.2221.56221.73382.1245.2735.93175.15171.27 414.008.38G IU NC40139.7061.9123.6224.21181.21406.9544.2040.35109.60104.52 414.008.38S IU NC40139.7050.8024.0229.50232.99489.9456.8349.16138.87134.39 41/216.608.56G IEU NC46158.7576.2027.7231.72209.91475.5658.4852.8795.3294.88 41/216.608.56S IEU NC46158.7569.8528.0436.09269.89537.0175.1860.14115.65121.99 519.509.19G IEU NC50168.2882.5532.9541.66251.21575.5978.1469.4489.6291.73 519.509.19S IEU NC50168.2869.8533.6051.57322.99703.84100.4785.95108.05117.93 51/221.909.17G IEU51/2FH184.1588.9037.6258.74277.58734.4796.2597.9174.1483.1651/221.909.17S IEU51/2FH190.5076.2039.2770.58356.89873.41123.76117.6487.42106.9251/224.7010.54G IEU51/2FH184.1588.9041.3358.74315.75734.47107.3997.9196.6295.6051/224.7010.54S IEU51/2FH190.5076.2042.9670.58405.96873.41138.07117.64117.37122.911表A.2一级钻杆性能（API标准钻杆）代号1代号2公称壁厚（mm）钢级钻杆接头连接代号一级钻杆最小接头外径(mm)最大接头内径(mm)偏磨内螺纹最小台肩宽度(mm)最小外径&最大内径上扣扭矩(kN.m)管体拉伸屈服(t)接头拉伸屈服(t)管体扭转屈服(kN.m)接头扭转屈服(kN.m)管体挤毁压力(MPa)管体最大内部压力(MPa)23/8 6.657.11G NC2683.3449.21 3.97 4.4468.34112.739.137.40129.13136.56 27/810.409.19G NC31100.0157.94 5.168.12105.75173.3816.8113.53137.29145.84 27/810.409.19S NC31103.1951.59 6.7510.43135.97219.4721.6217.39176.52187.52 31/213.309.35G NC38118.2770.64 6.3513.40134.72244.4827.2622.33115.97121.79 31/213.309.35S NC38122.2463.508.3317.10173.21307.9835.0528.51149.11156.59 414.008.38G NC40127.0074.617.1417.03142.36292.0534.5428.3980.1395.56 414.008.38S NC40131.7666.689.5321.66183.04366.3744.4136.1095.40122.86 41/216.608.56G NC46142.0888.907.5422.02165.21336.6245.8236.7065.2786.74 41/216.608.56S NC46146.8480.179.9228.79212.42434.4458.9147.9975.59111.53 519.509.19G NC50154.7896.048.7329.56197.83415.9161.2849.2760.4383.86 519.509.19S NC50160.3486.5211.5138.27254.36531.1378.7963.7869.15107.82 51/221.909.17G51/2FH170.66108.749.1337.07218.95474.5975.6761.7947.3376.03 51/221.909.17S51/2FH176.21100.0111.9147.06281.50595.3797.2978.4451.6897.75 51/224.7010.54G51/2FH172.24105.579.9240.46248.48519.6884.1367.4466.3787.40 51/224.7010.54S51/2FH178.5995.2513.1052.22319.47656.99108.1687.0377.06112.372表A.3二级钻杆性能（API标准钻杆）代号1代号2公称壁厚（mm）钢级钻杆接头连接代号二级钻杆最小接头外径(mm)最大接头内径(mm)偏磨内螺纹最小台肩宽度(mm)最小外径&最大内径上扣扭矩(kN.m)管体拉伸屈服(t)接头拉伸屈服(t)管体扭转屈服(kN.m)接头扭转屈服(kN.m)管体挤毁压力(MPa)管体最大内部压力(MPa)23/8 6.657.11G NC2682.5551.59 3.97 3.8358.9896.827.84 6.38117.16119.49 27/810.409.19G NC3198.4360.33 4.377.1991.16154.7214.4111.99124.88127.62 27/810.409.19S NC31101.6055.56 5.959.01117.21191.2918.5215.02160.57164.08 31/213.309.35G NC38116.6873.82 5.5611.66116.46214.0923.4719.43103.71106.57 31/213.309.35S NC38119.8668.267.1414.70149.74266.4030.1824.50126.84137.01 414.008.38G NC40124.6278.58 5.9514.56123.43251.7729.8724.2662.9883.62 414.008.38S NC40128.5972.237.9418.47158.69315.2238.4130.7872.53107.51 41/216.608.56G NC46139.7092.08 6.3519.38143.37298.5539.6932.3049.5475.90 41/216.608.56S NC46143.6785.738.3324.52184.33373.3651.0240.8754.6397.59 519.509.19G NC50152.40100.017.5425.71171.73364.3553.1042.8645.1773.38 519.509.19S NC50157.1692.089.9233.29220.80465.3868.2755.4748.8194.35 51/221.909.17G51/2FH167.48112.717.5431.67190.21416.3565.6452.7833.7866.53 51/221.909.17S51/2FH173.04105.5710.3240.79244.56519.6884.4067.9837.6885.53 51/224.7010.54G51/2FH169.86110.338.7335.18215.61451.5472.8658.6450.5376.48 51/224.7010.54S51/2FH174.63101.6011.1145.00277.22574.1693.6774.9955.9598.333表 B.1新钻杆性能(非API标准钻杆)代号1代号2公称壁厚（mm）钢级加厚型式钻杆接头连接代号新钻杆内螺纹外径(mm)外螺纹内径(mm)近似重量(kg/m)上扣扭矩(kN.m)管体拉伸屈服(t)接头拉伸屈服(t)管体扭转屈服(kN.m)接头扭转屈服(kN.m)管体挤毁压力(MPa)管体最大内部压力(MPa)27/810.409.19G EU NT2995.0050.8015.8812.06136.20154.0021.9020.10159.35159.52 27/810.409.19S EU NT2995.0050.8015.8812.06175.10154.0028.2020.10204.88205.10 27/810.409.19S EU NC31104.8050.8016.5010.70175.01224.8628.2017.84204.88205.10 31/213.309.35G EU PD29101.6050.8019.7712.00172.50216.9035.2020.00136.23133.21 31/213.309.35S EU PD29101.6050.8019.7712.00221.80216.9045.2020.00175.15171.27 414.008.38G IU PD39130.0065.1022.7123.32181.30339.0044.2038.87109.60104.52 414.008.38S IU PD39130.0061.9022.7925.20233.80366.9056.8042.00138.87134.39 519.509.19S IEU NC50168.2882.5532.9541.66323.20575.90100.4069.44108.05117.93 519.509.19G EUE NC52173.0488.9032.9544.52251.21592.0078.1474.2089.6291.73 521.909.65S EUE NC52172.0088.9036.6244.73337.9592.79104.2974.55118.96123.77 524.1010.92V EUE NC52172.0088.9041.0148.46420.26642.19127.1880.77162.57155.63 519.509.19S IEU BHDS50168.3082.6034.9753.47322.99575.98100.4789.11108.05117.93 51/223.909.65S IEU BHDS55184.20101.6040.9656.8374.47574.55128.8894.6697.88112.52 51/223.909.65S IEU BHDS55184.2095.3041.1566.3374.47657.43128.88110.597.88112.524表B.2一级钻杆性能(非API标准钻杆)代号1代号2公称壁厚（mm）钢级钻杆接头连接代号一级钻杆最小接头外径(mm)最大接头内径(mm)偏磨内螺纹最小台肩宽度(mm)最小外径&最大内径上扣扭矩(kN.m)管体拉伸屈服(t)接头拉伸屈服(t)管体扭转屈服(kN.m)接头扭转屈服(kN.m)管体挤毁压力(MPa)管体最大内部压力(MPa)27/810.409.19G NT2990.0052.00 3.809.30105.75145.0016.8115.50137.29145.84 27/810.409.19S NT2992.0052.00 4.8010.50135.97145.0021.6117.50176.52187.52 27/810.409.19S NC31103.2050.807.7510.68135.97220.7221.6217.80176.52187.52 31/213.309.35G PD2998.0053.00 5.409.70134.72201.0027.2616.17115.97121.79 31/213.309.35S PD2998.0053.00 5.409.70173.21201.0035.0416.17149.11156.59 414.008.38G PD39124.0067.007.2019.40142.36323.0034.5332.3380.1395.56 414.008.38S PD39126.0065.108.2021.80183.04339.0044.4036.3395.40122.86 519.509.19S NC50160.3486.5211.5138.27254.36531.1378.7963.7869.15107.82 519.509.19G NC52165.1092.5010.8539.40197.83549.0061.2865.6760.4383.86 521.909.65S NC52162.4088.9011.135.89265.87475.3381.6959.8278.41113.16 524.1010.92V NC52162.4088.9011.138.88329.88514.9499.2464.81118.85125.74 519.509.19S BHDS50155.1082.6010.142.77254.36416.6778.7971.2969.15107.82 51/223.909.65S BHDS55168.50101.609.2545.44295.13422.12101.275.7360.52102.88 51/223.909.65S BHDS55170.8095.3010.453.04295.13473.86101.288.460.52102.885表B.2二级钻杆性能(非API标准钻杆)代号1代号2公称壁厚（mm）钢级钻杆接头连接代号二级钻杆最小接头外径(mm)最大接头内径(mm)偏磨内螺纹最小台肩宽度(mm)最小外径&最大内径上扣扭矩(kN.m)管体拉伸屈服(t)接头拉伸屈服(t)管体扭转屈服(kN.m)接头扭转屈服(kN.m)管体挤毁压力(MPa)管体最大内部压力(MPa)27/810.409.19G NT2989.0053.00 3.308.5091.16138.9014.4114.17124.88127.62 27/810.409.19S NT2991.0053.00 4.309.60117.21138.9018.5216.00160.57164.08 27/810.409.19S NC31101.6050.80 6.959.64117.21198.9918.5216.07160.57164.08 31/213.309.35G PD2995.0055.00 3.907.50116.46187.0023.4712.50103.71106.57 31/213.309.35S PD2996.0055.00 4.408.20149.74187.0030.1813.67126.84137.01 414.008.38G PD39122.0069.00 6.2017.10123.43305.0029.8728.5062.9883.62 414.008.38S PD39124.0067.007.2019.40158.69323.0038.4132.3372.53107.51 519.509.19S NC50157.1692.089.9233.29220.80465.3868.2755.4748.8194.35 519.509.19G NC52161.9295.009.9233.90220.8465.3861.2856.5045.1773.38 521.909.65S NC52159.7088.909.7531.38230.7417.2870.7452.2957.1699.02 524.1010.92V NC52159.7088.909.7533.99285.88452.0585.7856.6592.49110.02 519.509.19S BHDS50151.2082.608.1537.43220.8337.4768.2762.3848.8194.34 51/223.909.65S BHDS55165.10101.607.5539.76256.29346.9187.7466.2642.9190.02 51/223.909.65S BHDS55166.8095.308.4046.41256.29384.3187.7477.3542.9190.026注：1、代号1为钻杆管体规格的无量纲名称；代号2为钻杆管体单位长度质量的无量纲名称；2、一级钻杆其壁厚最小为公称壁厚的80%；二级钻杆其壁厚最小为公称壁厚的70%；3、表中所列的性能值不包括安全因素，通常基于单一载荷条件，例如只受拉力。
硬度对照表(包括比例)
硬度简介：
硬度表示材料抵抗硬物体压入其表面的能力。
它是金属材料的重要性能指标之一。
一般硬度越高，耐磨性越好。
常用的硬度指标有布氏硬度、洛氏硬度和维氏硬度。
1.布氏硬度(HB)
以一定的载荷(一般3000kg)把一定大小(直径一般为10mm)的淬硬钢球压入材料表面，保持一段时间，去载后，负荷与其压痕面积之比值，即为布氏硬度值(HB)，单位为公斤力/mm2 (N/mm2)。
2.洛氏硬度(HR)
当HB>450或者试样过小时，不能采用布氏硬度试验而改用洛氏硬度计量。
它是用一个顶角120°的金刚石圆锥体或直径为1.59、3.18mm的钢球，在一定载荷下压入被测材料表面，由压痕的深度求出材料的硬度。
根据试验材料硬度的不同，分三种不同的标度来表示：
HRA：是采用60kg载荷和钻石锥压入器求得的硬度，用于硬度极高的材料(如硬质合金等)。
HRB：是采用100kg载荷和直径1.58mm淬硬的钢球，求得的硬度，用于硬度较低的材料(如退火钢、铸铁等)。
HRC（一般使用）：是采用150kg载荷和钻石锥压入器求得的硬度，用于硬度很高的材料(如淬火钢等)。
3 维氏硬度(HV)
以120kg以内的载荷和顶角为136°的金刚石方形锥压入器压入材料表面，用材料压痕凹坑的表面积除以载荷值，即为维氏硬度HV值(kgf/mm2)。
硬度对照表：
根据德国标准DIN50150,以下是常用范围的钢材抗拉强度与维氏硬度、布氏硬度、洛氏硬度的对照表。
硬度对照表(详细)
51.4
1580
47
46
458
432
73.6
---
60.0
83.5
64.8
50.3
1530
46
45
446
421
73.1
---
59.2
83.0
64.0
49.0
1480
45
44
434
409
72.5
---
58.5
82.5
63.1
47.8
1435
44
43
423
400
72.0
---
57.7
82.0
62.2
37.2
1080
35
34
336
319
67.4
(108.0)
50.8
77.2
54.2
36.1
1055
34
33
327
311
66.8
(107.5)
50.0
76.6
53.3
34.9
1025
33
32
318
301
66.3
(107.0)
49.2
76.1
52.1
33.7
1000
32
31
310
294
65.8
(106.0)
(1/16球)
1/16" ball
(1/16球)
Strength
(强度)
Diamond
(钻石)
HRC
HV
HB
HRA
HRB
HRD
HR15N
HR30N
各种硬度关系对照表
各种硬度关系对照表
钢的布氏硬度的近似换算值
硬度试验是机械性能试验中最简单易行的一种试验方法。
为了能用硬度试验代替某些机械性能试验，生产上需要一个比较准确的硬度和强度的换算关系。
时间证明，金属材料的各种硬度值之间，硬度值与强度值之间具有近似的相应关系。
因为硬度值是由起始塑性变形抗力和继续塑性变形抗力决定的，材料的强度越高，塑性变形抗力越高，硬度值也就越高。
以上资料仅供参考、详细技术参数请登录本站“产品目录或资料下载”中查询。
硬度及钢号换算表
45
S45C
S48C
50 S53C 55 S55C C55(1.0535) , CK55(1.1181 ), Cm55(1.1209 ) C60(1.0601) , CK60(1.1221 ), Cm60(1.1223 )
1050, 1053 1055 1055
60
S58C
65 70
1065 1070
［返回］
优质碳素结构钢
项目 (1)普通含锰 中国 GB,YB 05F 日本 JIS 德国 DIN(W-Nr.) ASTM 1005 美国 AISI SAE 1005 英国 BS 015A03 法国 NF
量钢组
08F 8 S09CK(S9CK) C10(1.0301) , CK10(1.1121 ) S10C CK10(1.1121 )
1065 1070
1065 1070
060A67, 080A67 060A72, 070A72, 080A72
XC65 XC70
75
1074
1074
1074
060A78, 070A78, 080A78
80 85
1080 1084
1080 1084
1080 1084
060A82, 080A83 060A86, 080A86
1335 1340 1345 1052
1335 1340 1345 1052
1335 1340 1345 1552 -1052
150M36
40Cr 45Cr 50Cr (5)铬硅钢组 (6)铬锰钢组 38CrSi 40CrSi 38CrMn 15CrMn 40CrMn 项目 中国 GB,YB
5140 5147, 5145 5150
详细的材料硬度对照表
硬度对照表硬度试验是机械性能试验中最简单易行的一种试验方法。
为了能用硬度试验代替某些机械性能试验，生产上需要一个比较准确的硬度和强度的换算关系。
实践证明，金属材料的各种硬度值之间，硬度值与强度值之间具有近似的相应关系。
因为硬度值是由起始塑性变形抗力和继续塑性变形抗力决定的，材料的强度越高，塑性变形抗力越高，硬度值也就越高。
下面是本站根据由实验得到的经验公式制作的快速计算器，有一定的实用价值，但在要求数据比较精确时，仍需要通过试验测得。
抗拉强度N/mm2维氏硬度布氏硬度洛氏硬度Rm HV HB HRC250 80 76.0270 85 80.7285 90 85.2305 95 90.2320 100 95.0335 105 99.8350 110 105370 115 109380 120 114400 125 119415 130 124430 135 128450 140 133465 145 138480 150 143490 155 147510 160 152530 165 156545 170 162560 175 166575 180 171595 185 176610 190 181625 195 185抗拉强度N/mm2维氏硬度布氏硬度洛氏硬度640 200 190660 205 195675 210 199690 215 204705 220 209720 225 214740 230 219755 235 223770 240 228 20.3785 245 233 21.3800 250 238 22.2820 255 242 23.1835 260 247 24.850 265 252 24.8865 270 257 25.6880 275 261 26.4900 280 266 27.1915 285 271 27.8930 290 276 28.5950 295 280 29.2965 300 285 29.8995 310 295 31.01030 320 304 32.21060 330 314 33.31095 340 323 34.41125 350 333 35.51115 360 342 36.61190 370 352 37.7 抗拉强度N/mm2维氏硬度布氏硬度洛氏硬度1220 380 361 38.81255 390 371 39.81290 400 380 40.81320 410 390 41.81350 420 399 42.71385 430 409 43.61420 440 418 44.51455 450 428 45.31485 460 437 46.11520 470 447 46.915557 480 (456) 47.1595 490 (466) 48.41630 500 (475) 49.11665 510 (485) 49.81700 520 (494) 50.51740 530 (504) 51.11775 540 (513) 51.71810 550 (523) 52.31845 560 (532) 53.01880 570 (542) 53.61920 580 (551) 54.11955 590 (561) 54.71995 600 (570) 55.22030 610 (580) 55.72070 620 (589) 56.32105 630 (599) 56.82145 640 (608) 57.32180 650 (618) 57.8 抗拉强度N/mm2维氏硬度布氏硬度洛氏硬度660 58.3670 58.8680 59.2690 59.7700 60.1720 61.0740 61.8760 62.5780 63.3800 64.0820 64.7840 65.3860 65.9880 66.4900 67.0920 67.5940布氏硬度：测定布氏硬度较准确可靠，但一般HBS只适用于450N/mm2（MPa）以下的金属材料，对于较硬的钢或较薄的板材不适用。