抗拉强度与硬度对照表

抗拉强度Rm N/mm2维氏硬度HV
布氏硬度HB 洛氏硬度HRC 抗拉强度Rm N/mm2维氏硬度HV 布氏硬度HB 洛氏硬度HRC 25080
76112535033335.527085
80.7111536034236.628590
85.2119037035237.730595
90.2122038036138.8320100
95125539037139.8335105
99.8129040038040.8350110
105132041039041.8370115
109135042039942.7380120
114138543040943.6400125
119142044041844.5415130
124145545042845.3430135
128148546043746.1450140
133152047044746.9465145
138155548045647480150
143159549046648.4490155
147163050047549.1510160
152166551048549.8530165
156170052049450.5545170
162174053050451.1560175
166177554051351.7575180
171181055052352.3595185
176184556053253610190
181188057054253.6625195
185192058055154.1640200
190195559056154.7660205
195199560057055.2675210
199203061058055.7690215
204207062058956.3705220
209210563059956.8720225
214214564060857.3740230
219218065061857755235
22366058.3770240
22820.367058.8785245
23321.368059.2800250
23822.269059.7820255
24223.170060.1835260
2472472061850265
25224.874061.886527025725.676062.5
根据德国标准DIN50150,以下是常用范围的钢材抗拉强度与维氏硬度、布氏硬度、洛氏硬度的对照表
88027526126.478063.3 90028026627.180064 91528527127.882064.7 93029027628.584065.3 95029528029.286065.9 96530028529.888066.4 9953102953190067 103032030432.292067.5 106033031433.394068 109534032334.4
* HRB St12=65St13=55St14=50硬度试验是机械性能试验中最简单易行的一种试验方法。

为了能用硬度试验。

代替某些机械性能试验，生产上需要一个比较准确的硬度和强度的换算关系。

实践证明，金属材料的各种硬度值之间，硬度值与强度值之间具有近似的相应关系。

因为硬度值是由起始塑性变形抗力和继续塑性变形抗力决定的，材料的强度越高，塑性变形抗力越高，硬度值也就越高。

HBS就是用淬火钢球做压头的布氏硬度，HBW则是用硬质合金球做压头时的布氏硬度；
当其示值小于320时，就标度为HB，当其标度值高于320时，就不能省略后面的S或W。

据说新标准已规定只允许使用硬质合金球做压头。

1.HBS与σb之间的近似换算
（1）轧制及锻钢件：σb=3.4"3.6HBS；
（2）铸钢件：σb=3"4HBS；
（3）铬钼硅钢：σb=3.5HBS；
（4）铬钼钢：σb=3.3HBS；
（5）硬铝：σb=3.7HBS；
（6）黄铜：σb=5.3HBS；
（7）纯铜：σb=4.8HBS；
（8）灰铁：1.63HBS-65.3；
2.HRC与σb（Mpa）的换算
σb=-801.24+50.8HRC
以上近似换算公式，只能用于参考，在要求比较精确的时候，便不能采用。