高分子质量聚L-乳酸-乙醇酸的制备及其性能

高分子质量聚L-乳酸-乙醇酸的制备及其性能
陈德辉;王锐;朱志国;张诚
【期刊名称】《纺织学报》
【年(卷),期】2011(032)009
【摘要】以六亚甲基二异氰酸酯(HDI)为扩链剂,对自制的双端羟基L-乳酸-乙醇酸预聚物(OLGA-OH)进行熔融扩链,进一步提高其分子质量.主要研究了HDI用量对扩链产物(PLGA)分子量及性能的影响.采用凝胶渗透色谱(GPC)、差示扫描量热(DSC)、热重分析(TGA)、傅里叶红外光谱(FT-IR)以及核磁共振谱(1H-NMR)对聚合物的相关结构与性能进行了表征.结果表明,当n(-NCO)∶n(-OH)=2∶l时,扩链效果最好,所得PLGA的分子质量最大,其数均分子质量和重均分子质量分别可达
5.6×104和15.0×104,玻璃化转变温度亦由36℃提高到53℃.%High molecular weight poly ( L-lactic-glycolic acid) (PLGA) was successfully synthesized by chain extension of hydroxyl terminated prepolymer ( OLGA-OH ) with 1 ,6-hexamethylene diisocyanate (HDI) as the chain extender. The impact of HDI dosage on the molecular weight and property of the chain extended product PLGA was investigated. The structure and properties were characterized using Fourier transform infrared spectroscopy ( FT-IR) , gel permeation chromatography ( GPC ) , differential scanning calorimetry ( DSC ) , thermal gravimetric analysis ( TGA) and nuclear magnetic resonance ( NMR). The results showed that the obtained PLGA appeared the best chain extension result and had the maximum molecular weight with Mn of 5. 6 × 104 and Mw of 15. 0 × 104 when n(-NCO)/n(-OH) = 2:1.
The glass transition temperature of the PLGA was increased from 36 ℃ to 53 ℃ after chain extension.
【总页数】5页(P15-19)
【作者】陈德辉;王锐;朱志国;张诚
【作者单位】北京服装学院材料科学与工程学院,北京 100029;北京服装学院材料科学与工程学院,北京 100029;北京服装学院材料科学与工程学院,北京 100029;北京服装学院材料科学与工程学院,北京 100029
【正文语种】中文
【中图分类】TQ316.33
【相关文献】
1.制备聚(L-乳酸-CO-乙醇酸)/聚D-乳酸共混物立构复合物的新方法 [J], 董军;白威;黄冬玲;熊成东
2.聚(ε-己内酯-co-L-丙交酯)/聚L-乳酸复合材料的制备与性能研究 [J], 吴艾;陈龙;熊左春;熊成东;陈栋梁
3.高分子量聚L-乳酸制备及性能研究 [J], 欧阳春平;曾祥斌;姚逸;董学腾;熊凯;王超军;卢昌利;张尔杰;郭志龙;焦建
4.L-丙交酯和聚L-乳酸的制备与性能 [J], 娄玲;尹静波;高战团;梁奇志;董丽松;陈学思;景遐斌
5.高分子质量聚(L-丙交酯-co-己内酯)无规共聚物的制备及性能 [J], 申雄军;陈晓峰;李贤
因版权原因，仅展示原文概要，查看原文内容请购买。