玻璃纤维针刺滤料耐高温性能研究

玻璃纤维针刺滤料耐高温性能研究
赵振兴;汪黎明
【期刊名称】《科技视界》
【年(卷),期】2014(000)001
【摘要】本文利用三种不同直径的玻璃纤维与轶纶、芳纶混合制成复合滤料，测试了在经过160℃、200℃、240℃和280℃高温处理24h后的力学性能和透气性的变化。

结果表明：直径4μm的玻璃纤维制成的复合滤料经280℃处理24h后经向断裂强力仍保持在93.06%；由于针刺过程对纬向纤维的破坏较大，纬向断裂强力经高温处理后的下降趋势明显；经高温处理后透气性均保持在90%以上，说明处理温度对滤料透气性的影响较小。

%Yilun , Aramid fiber and three different diameter of glass fibers are used to make composite filter material. The change of mechanical properties and permeability of the material can be tested by 160℃, 200℃, 240℃and 280℃high temperature treatment for 24 h. The results indicated that the needled filter material that made of 4 microns in diameter glass fiber, its breaking force in warp remained at 93.06% by 280℃ high temperature treatment for 24 h. The weft-wise breaking force is obvious downward trend by high temperature treatment. Three filter material permeabilities are kept at more than 90% by high temperature treatment. The impact of processing temperature on filter material permeability is smaller.
【总页数】3页(P220-222)
【作者】赵振兴;汪黎明
【作者单位】青岛大学纺织学院，山东青岛266071;青岛大学纺织学院，山东青岛266071
【正文语种】中文
【相关文献】
1.不同水泥基材玻璃纤维混凝土耐高温性能的研究 [J], 王艳琼;孟云芳
2.玻璃纤维针刺复合滤料耐高温性能研究 [J], 赵振兴;汪黎明;聂换换;蒋树军
3.PSA/BAS水刺滤料耐高温性能研究 [J], 王立波;沈恒根;王振华;王锋华;汪晓峰;薛惠心;王君
4.玻璃纤维滤材的发展及玻璃纤维针刺毡的加工技术 [J], 王小兵;朱平
5.基于PTFE乳液改性的P84/超细玻璃纤维复合针刺滤料的性能研究 [J], 关欣;高晶;劳继红
因版权原因，仅展示原文概要，查看原文内容请购买。