四氧化三铁磁性纳米微粒表面的氨基化修饰

四氧化三铁磁性纳米微粒表面的氨基化修饰

胡玮;娄兆文

【期刊名称】《化学研究》

【年(卷),期】2013(024)002

【摘要】以3-氨丙基三乙氧基硅烷(APTES)作为氨基化试剂,通过硅烷化反应使其键合于Fe3O4纳米颗粒表面,制备了表面氨基化的磁性Fe3O4纳米复合颗粒；利用红外光谱分析了产物的化学键合特征,利用电位滴定测定了合成产物表面的-NH2含量,探讨了活化方式、反应溶剂、投料比、温度、时间等因素对氨基化修饰效果的影响.结果表明,APTES成功地包覆在磁性Fe3O4纳米微粒表面；在乙醇-水体系中,在Fe3O4与APTES投料比3:8、温度60℃下反应12 h,得到的Fe3O4纳米颗粒表面APTES修饰效果最佳,表面-NH2含量高达1 400±50 μmol ·g-1.%3-Aminopropyl triethoxysilane (APTES) was used as the animation agent and coated onto the surface of ferriferous oxide (Fe3O4) magnetite nanoparticles via silanization reaction. The chemical bonding feature of as-synthesized APTES-coated Fe3 O4 nanoparticles was analyzed by Fourier transform infrared spectrometry, and its surface -NH2 content was determined by potentiometric titration technology. Furthermore, the influences of activation method, solvent, feeding ratio, reaction temperature, and reaction time on the modification effect of Fe3O4 nanoparticles by -NH2 group were investigated. Results show that Fe3 O4 nanoparticles have been successfully coated by APTES. The best surface-modification effect is reached after Fe3O4 nanoparticles are coated with

APTES at a feeding ratio of 3 : 8 and a temperature of 60 ℃ for 12 h in the presence of ethanol/water as the solvent. Resultant surface-modified

Fe3O4 nanoparticles have a surface -NH2 content of about 1400 ±

50μmol·g-1.

【总页数】5页(P144-148)

【作者】胡玮;娄兆文

【作者单位】湖北大学化学化工学院,湖北武汉430062;湖北大学化学化工学院,湖北武汉430062

【正文语种】中文

【中图分类】O621

【相关文献】

1.氨基化修饰介孔Fe3O4@SiO2@mSiO2磁性吸附剂的制备及吸附性能的研究[J], 成岳;肖治国;余宏伟;万梦影;鲁莽

2.磁性四氧化三铁纳米粒子的表面修饰与应用 [J], 孙镇镇;

3.单分散双相可溶四氧化三铁纳米微粒的多醇法制备及磁性 [J], 王现红;贺攀科;程文正;刘晓;李雪梅;吴君华;刘红玲

4.纳米碳纤维表面四氧化三铁磁性修饰 [J], 周文;郝春成

5.磁性四氧化三铁纳米微粒的研究进展 [J], 张恒;郑娇;许宁侠;余佩

因版权原因，仅展示原文概要，查看原文内容请购买