高热稳定性聚膦腈亚微米球的室温快速合成

高热稳定性聚膦腈亚微米球的室温快速合成
付建伟;王明环;王旭哲;袁金苹;许群
【期刊名称】《应用化学》
【年(卷),期】2011(028)008
【摘要】Polyphosphazene(PPZ) sub-micrometer spheres were prepared rapidly under room temperature via precipitation polymerization of hexachlorocyclotriphosphazene ( HCCP) with 4, 4'-sulfonyldiphenol ( BPS) , using acetonitrile as the solvent and triethylamine (TEA) as the acid-acceptor. The PPZ sub-micrometer spheres were characterized by FT-IR, elemental analysis and EDX, and their highly cross-linked structures were identified. SEM and TEM results indicated that the PPZ sub-micrometer spheres had diameter of about 410 nm, solid structure and smooth surface. TCA result showed that the thermal decomposition temperature of the PPZ sub-micrometer spheres was about 531 t. In addition, the formation mechanism of the PPZ sub-micrometer spheres was proposed.%以六氯环三膦腈(HCCP)和4,4'-二羟基二苯砜(BPS)为共缩聚单体,乙腈为溶剂,三乙胺为缚酸剂,在室温条件下,采用沉淀聚合的方法快速合成了一种聚膦腈亚微米球.红外光谱、元素分析及X射线能谱分析(EDX)测试表明,该聚膦腈亚微米球具有高度交联的化学
结构；扫描电子显微镜和透射电子显微镜测试表明,该聚膦腈亚微米球粒径分布在410nm附近,而且具有光滑的表面和实心的结构；热重分析(TGA)测试表明,该聚膦腈亚微米球的热分解温度达到531℃.并推测了该聚膦腈亚微米球的形成机理.
【总页数】5页(P864-868)
【作者】付建伟;王明环;王旭哲;袁金苹;许群
【作者单位】郑州大学材料科学与工程学院郑州450001;郑州大学材料科学与工程学院郑州450001;郑州大学材料科学与工程学院郑州450001;郑州大学材料科学与工程学院郑州450001;郑州大学材料科学与工程学院郑州450001
【正文语种】中文
【中图分类】O634
【相关文献】
1.微波法合成含咔唑聚膦腈接枝偶氮硝基苯及其光电导性能研究 [J], 张文龙;姜文影;赵春山;蒋强;赵成龙;王暄
2.高温高残留聚环三膦腈-芳酰胺材料的合成与热性能 [J], 孙金亮;张经毅;郭强;赵正平;聂智军;罗唯力
3.由八氯环四膦腈制备高弹性聚二乙氧基膦腈及其构象的研究 [J], 张腾;蔡晴;吴战鹏;金日光
4.新型星形聚膦腈基杂臂聚合物的合成 [J], 蔡湘雯;肖安国
5.聚膦腈-g-聚己内酯共聚物的合成与表征 [J], 邓林;蔡晴;刘文博;金日光
因版权原因，仅展示原文概要，查看原文内容请购买。