ZrO2纤维加入量对莫来石-10vol.％SiC晶须复合材料机械性能和抗热震稳定性的影响

ZrO2纤维加入量对莫来石-10vol.％SiC晶须复合材料机械
性能和抗热震稳定性的影响
彭子钧;安迪;罗旭东;张国栋;谢志鹏
【期刊名称】《陶瓷学报》
【年(卷),期】2017(038)005
【摘要】为了提高莫来石复合材料的机械性能和抗热震稳定性,将ZrO2纤维引入到莫来石-SiC晶须复合材料体系中,在N2气氛中常压烧结制备莫来石-SiC晶须复合材料.结果表明,ZrO2纤维可以促进了莫来石复合材料的烧结,提高复合材料的断裂韧性和抗热震稳定性.ZrO2纤维的加入量为15wt.%时,材料的断裂韧性和抗热震稳定性到峰值,其断裂韧性为5.73 MPa?m1/2,抗热震次数达到47次.过量加入ZrO2纤维导致其促烧结能力降低会对莫来石-SiC晶须复合材料的机械性能和抗热震稳定性产生不利影响.%In order to improve the mechanical property and the thermal shock resistance of the mullite composite, the ZrO2fiber was introduced into the system of the mullite-SiC whisker composite which was prepared with the method of pressureless sintering in nitrogen. The result shows that introduction of ZrO2fiber can promote the sintering of the mullite composite,and enhance the fracture toughness property and the thermal shock resistance of the mullite composite.When the addition of ZrO2fiber was 15wt.%,the fracture toughness property of the composite that reached the highest,was 5.73MPa?m1/2,and the thermal shock resistance of the composite that was maximum value,attained 47 times.The poor sintering resulted from the overmuch addition of ZrO2fiber has a
negative performance impact of the mechanical property and the thermal shock resistance of the mullite-SiC whisker composite.
【总页数】5页(P706-710)
【作者】彭子钧;安迪;罗旭东;张国栋;谢志鹏
【作者单位】辽宁科技大学高温材料与镁资源工程学院,辽宁鞍山 114051;辽宁科技大学高温材料与镁资源工程学院,辽宁鞍山 114051;清华大学新型陶瓷与精细工艺国家重点实验室,北京 100084;辽宁科技大学高温材料与镁资源工程学院,辽宁鞍山 114051;清华大学新型陶瓷与精细工艺国家重点实验室,北京 100084;辽宁科技大学高温材料与镁资源工程学院,辽宁鞍山 114051;清华大学新型陶瓷与精细工艺国家重点实验室,北京 100084
【正文语种】中文
【中图分类】TQ174.75
【相关文献】
1.SiC晶须增韧Al2O3及ZrO2（Y2O3）基陶瓷复合材料的抗热震行为 [J], 周玉等;田磊
2.莫来石加入量对SiC-莫来石材料性能的影响 [J], 石锦雄;李楠
3.SiC晶须对ZrO2-莫来石陶瓷烧结性能及抗热震性能的影响 [J], 杨孟孟;安迪;罗旭东;谢志鹏;冯东;韩露
4.SiC晶须（Al2O3纤维）对氧化锆增韧莫来石陶瓷力学行为的影响 [J], 李秀华;杨正方
5.锆莫来石加入量对刚玉质耐火浇注料抗热震性的影响 [J], 陈杨;王永辉;朱冬冬因版权原因，仅展示原文概要，查看原文内容请购买。