复合硫化剂和硫化温度对氢化丁腈橡胶性能的影响

复合硫化剂和硫化温度对氢化丁腈橡胶性能的影响

张武建;谈金祝;潘龙;贺日东;胡雪东

【期刊名称】《合成橡胶工业》

【年(卷),期】2017(040)006

【摘要】以硫黄与过氧化二异丙苯(DCP)为复合硫化剂,考察了DCP用量和硫化温度对氢化丁腈橡胶(HNBR)硫化特性及物理机械性能、压缩应力弛豫特性的影响.结果表明,随着DCP用量的增大,HNBR混炼胶的转矩差值增大,焦烧时间延长,正硫化时间先延长后缩短;随着硫化温度的升高,HNBR混炼胶的转矩差值先增大后减小,焦烧时间和正硫化时间均缩短;当DCP用量为7份、硫化温度为160℃时,HNBR硫化胶的物理机械性能和压缩应力弛豫特性最佳.%With sulfur and dicumyl peroxide (DCP) as compound curing agent,the effects of DCP amount and curing temperature on the curing characteristics,mechanical properties and compression stress relaxation characteristics of hydrogenated nitrile rubber (HNBR) were investigated.The results showed that with the increase of DCP amount,the torque difference of HNBR compound increased,the scorch time prolonged,and the optimum curing time prolonged first and then shortened.With the increase of the curing temperature,the torque difference of the HNBR compound increased first and then decreased,both the scorch time and the optimum curing time shortened.When DCP was 7 phr and the curing temperature was 160 ℃,the mechanical properties and compression stress relaxation characteristics of HNBR vulcanizates were the best.

【总页数】5页(P448-452)

【作者】张武建;谈金祝;潘龙;贺日东;胡雪东

【作者单位】南京工业大学机械与动力工程学院,南京211816;南京工业大学机械与动力工程学院,南京211816;南京工业大学机械与动力工程学院,南京211816;南京工业大学机械与动力工程学院,南京211816;南京工业大学机械与动力工程学院,南京211816

【正文语种】中文

【中图分类】TQ333.7

【相关文献】

1.用多壁碳纳米管/炭黑复合填料提高氢化丁腈橡胶/氢化羧基丁腈橡胶共混胶的力学性能 [J], 殷标;温彦威;张旭敏;陈杰;贾红兵

2.硫化剂BIPB硫化氢化丁腈橡胶性能的研究 [J], 鲍刚;张秀娥;杨显峰;王军

3.单甲基丙烯酸锌对氢化丁腈橡胶复合材料性能的影响 [J], 王增林;田帅承;孙宝全;孙卫朝;王冠中;李再峰

4.聚合物包覆型纳米片层粒子对氢化丁腈橡胶复合材料性能的影响 [J], 罗明艳;陈建斌;辛晨;赵洪祥;周京福;赵天宝;李再峰

5.芳纶短纤维对氢化丁腈橡胶复合材料性能的影响 [J], 马岩;逄见光;朱超;史新妍因版权原因，仅展示原文概要，查看原文内容请购买