某高磷铁矿降磷技术研究

合集下载

云南某高磷鲕状赤铁矿提铁降磷试验研究

云南某高磷鲕状赤铁矿提铁降磷试验研究

云南某高磷鲕状赤铁矿提铁降磷试验研究徐兴鸿;蒋彦;简胜;杨林【摘要】云南某鲕状赤铁矿磷含量高达0.87%,铁品位为45.14%.对此矿石进行单一的强磁选及反浮选试验研究,结果表明都不能获得磷品位低于0.2%,铁品位较高的铁精矿.采用强磁-反浮选及脱泥-反浮选均能获得磷品位低于0.2%,铁品位高于52%的铁精矿.脱泥-反浮选具有投资成本低,流程结构简单的优势,推荐采用此流程处理该矿石.该研究对开发此类高磷鲕状赤铁矿具有一定的借鉴意义.%Hie simplex experimental study on high intensity magnetic separation or reveree flotation of an oolitic Kematite ore in Yunnan in which the contents of phosphonis and iron are respectively 0.87% and 45.14% was conducted. The result showed that the concentrate with higher iron grade and phosphorus content of less than 0.2% can not be obtained. In view of above, by adopting the process of high intensity magnetic separation-reverse flotation or the desliming-reverse flotation, the concentrate with iron of higher than 52% and phosphorus of less than 0.2% can be got. Therefore, the desliming-reverse flotation is proposed to process the mentioned ore due to its superiorities of low cost of investment and simple process structure. The study can be used for reference to developing this kind of high-phosphorus oolitic hematite ore.【期刊名称】《云南冶金》【年(卷),期】2012(041)003【总页数】5页(P17-20,51)【关键词】鲕状赤铁矿;脱磷;强磁选;反浮选【作者】徐兴鸿;蒋彦;简胜;杨林【作者单位】云南文山铝业有限公司,云南文山663000;昆明冶研新材料股份有限公司,云南昆明650031;昆明冶金研究院,云南昆明650031;昆明冶金研究院,云南昆明650031【正文语种】中文【中图分类】TD92高磷鲕状赤铁矿由于其嵌布粒度极细,且含磷高,目前,还没有得到有效的开发利用;在我国,此类矿石的储量巨大,约占我国铁矿资源的1/9[1~2]。

高磷铁矿石脱磷技术研究现状及发展趋势

高磷铁矿石脱磷技术研究现状及发展趋势
艾光 华 L 李 晓 波 , 周 源 ,
(. 理 工大 学 资源 与 环境 工 程 学 院 , 西 赣 州 3 10 ;2中 国 矿 业 大 学 化 工学 院 , 1江西 江 400 . 江苏 徐 州 2 10 ) 2 0 8
摘 要 :高磷 铁 矿石 的 选矿 已成 为 国 内外 的一 大选 矿技 术 难题 , 文 总结 了当前 国 内外 高磷 铁 矿脱 本
Ab t a t h s p p r s r e s t e r s a c tt s a d t c n l g e f t e d p 0 p 0 ia in p o e s s o i h— sr c :T i a e u v y h e e r h sau n e h oo i s o h e h s h r t r c s e f h g z o p o p o u io o e h e it g p o lms r a ay e b r d ci g t e d v l p n t n o h s h r s h s h r s r n r .T e x si r b e a e n l z d y p e it h e e o me t r d f p o p o n n e u r d c in a d io x r c in t c n l g . e u t n r n e ta t e h oo y o o Ke r s ih p o p o u r n o e r d c h s h r s a d e t c r n d v lp n r n y wo d :h g - h s h r s i r ; e u e p o p o n x r ti ; e eo me t e d o u a o t
AIGu n _ u L , a - o , a g h a LI Xi o b ZH OU a 2 Yu n

鄂西某高磷铁矿石浸出脱磷试验研究

鄂西某高磷铁矿石浸出脱磷试验研究

i s e n Hu e i n g a e 4 . 0 ,p o p o u o t n . 5 ) Th e u t h we h t n e h n we t r b i(r r d 3 5 o h s h r s c n e t0 8 . e r s ls s o d t a :u d rt e
磷 ,浸 出后 固体 中磷 含 量分 别 为 0 2 、0 2 。 .5 .2 关 键 词 : 磷铁 矿 石 ;酸 浸 ;生 物 浸 出 ;除 磷 高 中图 分类 号 :T 9 1 D 5 文 献标 识 码 :B 文 章编 号 :1 0 —4 5 (0 0 9 0 8 4 0 4 0 1 2 1 )0 —0 7 —0
(2 O) C H2 、柠 檬 酸 ( 6 O ) H2 O 、HN 。 HC 中 ,无 机 酸 提 铁 降 磷 效 果 优 于 有 机 酸 。 其 中 , C H8 7 、 S O、 1
H S 的提 铁除 磷 效 果 最佳 ,处 理后 矿 石 铁 品 位 为 4 . 8 , 铁 回 收 率 为 9. 7 , 除 磷 率 为 9 . 1 ; O 9 O 9 5 39
P — ,GONG W e — i d Yu b a IKeWU 一 n q ,I — io
( . Sc oo s r e nd Envr m e a gi e ig,W u n U ni r iy o e hn o 1 h lofRe ou c s a ion nt lEn ne rn ha ve st fT c olgy,W uh n 4 00 a 3 70,Chia; n 2 Sc o fCh m ia nd En r m e t lEng n e i g,H u iU nve st e h ol y,W uha 0 8, Chi ) . ho lo e c la vion n a i e rn be i r iy ofT c n og n 43 06 na

鄂西某高磷鲕状赤铁矿提铁降磷试验研究

鄂西某高磷鲕状赤铁矿提铁降磷试验研究

鄂西某高磷鲕状赤铁矿提铁降磷试验研究高磷鲕状赤铁矿是我国主要的复杂难选铁矿石之一,矿石储量较大,占铁矿资源储量的11%左右。

我国现已探明的高磷鲕状赤铁矿石储量约37.2亿吨,可勘探新资源量预计达上百亿吨。

高磷鲕状赤铁矿具有复杂的化学成分以及独特的结构构造,富集难度极大,其选别是选矿界公认的难题。

本论文首先通过XRF、XRD、物相分析、岩矿鉴定等手段对原矿进行工艺矿物学研究,得知该矿石中铁品位为43.13%,有害元素磷的含量高达0.86%,主要脉石矿物Si O2含量为17.20%。

该矿石是典型的高磷鲕状赤铁矿,本试验针对该矿石嵌布关系复杂、嵌布粒度极细且有害杂质磷含量高等特征,围绕“提铁降磷”,进行了工艺流程探索性试验研究。

首先采用高梯度磁选处理原矿。

在粗磨条件下,采用一粗一精一扫高梯度磁选流程进行选别,确定最佳磨矿细度为-0.074mm含量占65%,最佳磁场强度为粗选0.8T、精选0.5T、扫选0.9T。

粗磨选别后,将中矿(精选尾矿和扫选精矿)再磨后进行一粗一精磁选,确定最佳再磨细度为-0.074mm含量占90%,最佳磁场强度为粗选0.8T、精选0.4T。

进行高梯度磁选闭路试验,将中矿再磨精选尾矿返回再磨球磨机,获得磁选精矿铁品位为53.06%,相对于原矿提高9.94个百分点,回收率为78.53%,磁选尾矿产率为36.18%、铁品位为25.59%。

可见高梯度磁选精矿指标较好,且抛尾能力较强。

以磁选精矿为处理对象,采用反浮选进行提铁降杂。

试验研究表明,磁选精矿细磨—直接反浮选效果不好,引入脱泥流程后反浮选效果明显增强。

确定最佳磨矿细度为-0.038mm含量占95%,选择性絮凝脱泥最佳条件为分散剂用量12kg/t、矿浆p H值11、苛性淀粉用量0.3kg/t,反浮粗选最佳条件为矿浆p H值11、苛性淀粉用量1.0kg/t、氯化钙用量0.12kg/t、捕收剂PL用量0.8kg/t、浮选时间4min。

通过细磨—选择性絮凝脱泥—阴离子反浮选闭路试验,反浮选采用一粗二精一扫流程,中矿合并返回粗选,获得反浮选精矿铁品位为56.75%,相对于磁选精矿提高了3.63个百分点,整体回收率为72.26%,取得了良好的提铁降杂效果。

宜昌某高磷赤铁矿反浮选提铁降磷试验

宜昌某高磷赤铁矿反浮选提铁降磷试验
反浮选技术具有选择性高、适应性强等优点,在处理复杂难选矿石时具有较明 显的优势。
试验目的和意义
试验目的
本次试验旨在验证反浮选技术在宜昌高磷赤铁矿上的应用效 果,探究最佳工艺条件,为工业应用提供科学依据。
试验意义
成功应用反浮选技术提质宜昌高磷赤铁矿,将有助于提高铁 资源利用率,降低选矿成本,推动当地矿业经济持续发展。 同时,本次试验结果还可为类似矿石的选矿提供借鉴和参考 。
优化工艺流程和操作参数
01
优化磨矿细度和矿浆浓度
通过调整磨矿细度和矿浆浓度,找到最佳的工艺条件,以提高反浮选效
果。
02
精确控制药剂制度和用量
根据不同矿石性质,精确调整药剂制度和用量,降低药剂消耗,同时保
证良好的反浮选效果。
03
强化操作流程的自动化和智能化
通过引入先进的自动化和智能化技术,提高操作流程的稳定性和可控性
数据分析方法
采用了多种数据分析方法,如对 比分析、回归分析等,对试验数
据进行了深入挖掘。
结果展示与讨论
通过图表、图像等形式展示了数 据分析结果,并结合前人研究成 果进行了讨论,为后续研究提供
了借鉴。
04 试验结论与讨论
试验成果总结
提铁降磷效果显著
经过反浮选处理,宜昌某高磷赤铁矿中的铁品位得到有效提升, 同时磷含量明显降低,满足了工业生产的要求。
矿石特点
高磷赤铁矿中磷含量较高,直接 影响铁的品位和利用效率,因此 需要通过选矿手段进行提质。
反浮选提铁降磷技术简介
反浮选原理
与传统的正浮选不同,反浮选是通过捕收剂将不需要的矿物浮选出来,留下目 标矿物。在宜昌高磷赤铁矿的处理中,利用反浮选技术可以将高磷矿物浮选出 来,实现提铁降磷的目的。

澳大利亚某地高磷铁矿石降磷工艺研究

澳大利亚某地高磷铁矿石降磷工艺研究

文章 编 号 : 1 0 4 22 1) 20 2—6 0 11 1 (0 10 —2 90
0 引言
高磷 矿石 的 降 磷 工 艺 在 选 矿 领 域 一 直 是 个 难 题 。我 国的锰 矿资 源 中有相 当多 的锰 矿石 因为 磷 的 含 量 较高 而不 能 利用 ; 大 利亚 的高 磷 铁 矿 目前 也 澳
性 溶解 、 淘析 、 学 分 析 及 X射 线 衍 射 分 析 等 方 法 化
进行 综合 研究 。 1 1 高磷 铁 矿 的化学 组成 .
图 中显 示 除 主要 元 素 F e以外 , 尚含 一定 数 量 的杂 质 s、 l有 害 iA , 杂 质 P、 量 很 低 , 谱 中不 能 有 效 显 示 。 S含 能
Ta l P c n e t r n d fe e tg an sz b e2 o t n sFe o e i if r n r i ie
胶体 状态 产 出而没 有独 立矿 物存 在 的结论 相 吻合 。
2 2 化 学 选 矿 试 验 .
粒级/ mm > 0 0 4 0 O 4 0 0 3 . 4 tO 0 0 . 7 . 7 ~ . 4 0 0 3 . 3
2 2 2 焙 烧 一 酸 浸 试 验 ..
把粒 度 一2 0目占 9 . 的铁矿 样用 马弗 炉 焙 0 76 烧 2h 焙烧 温度 分别 为 5 0℃ 和 7 0℃ , 出介 质 , 0 0 浸 为 1 6 硫 酸 、 酸 、 酸 及 乙 酸 , 浆 浓 度 为 O/的 9 盐 硝 矿 2 , 出环 境 为 9 ℃ 的 水浴 , 出 时 间 为 2h 试 5 浸 5 浸 ,
显变 化 。
增 加 , 明在褐 铁矿 中磷 元素 有 富集 的趋势 。 表

微波作用高磷铁矿提铁脱磷的研究

微波作用高磷铁矿提铁脱磷的研究
[ 6] 0 0 0 0
式 ¦ 中 : N - 阿伏伽德罗常数 ; B - 比例系数 , 经 1 ; r - 相邻异号离子间的平衡距离即正负 4P 0
*
离子半径之和, m; Z+ - 阳离子的有效电荷; A+ - 阳 离子的极化率。 经过假设简化, F eO 晶格能 U 可由下式计算 :
0 Fe O 活
x y
+ $f GC活 。
0 0 0 0
¦
由于 $f GF e xO y活 + $f GC活 > 0 , 所以当 $f GC理 = 0 时, 表明微波可使在传统加热时已处于化学平衡的 铁氧化物碳热还原反应活化 , 反应继续自发进行 ; 当 $rG理 > 0且 $ f GFe xO y活 + $f GC活 > $rG理 时, 表明经典 热力学认为不可能进行的反应, 在微波场中反应可 能自发进 行 。所以微波可 以使铁氧化物 碳热还 原进行的更加彻底。
[ 2]
行业承受的极限 , 优质、 低价的铁矿资源供应问题已 成为中国钢铁企业发展的瓶颈。要解决铁矿石资源 短缺问题, 必须着眼于低品位、 复合共生矿的利用 , 这也是解决我国铁矿石资源安全稳定供给的根本途 径
[ 1]
。高磷铁 矿经微
。分布于湖北、 湖南、 江西、 云南、 广西、 贵州、
波加热碳热还原和磁选两种工艺作用后 , 其脱磷率 达到 87 . 8 % , 収铁率达到 90 % 。本文从晶格能、 热 力学和动力学分析微波强化高磷铁矿提铁脱磷的作 用机理。微波能应用于 髙磷铁矿提铁脱磷具有重要 的意义。
1
引言
近年来 , 国际矿价飞速上涨 , 涨幅直逼中国钢铁
微波是频率位于 0 . 3~ 300 GH z的电磁波, 其热 效应是依靠物质自身能量 的耗散来选择性 加热物 料。微波的热效应和非热效应, 使得微波加热相对 于传统加热具有无可比拟的优势。 F e2 O 3、 F e3 O 4和 无烟煤粉均对微波具有良好的吸收性能 , 磷灰石和 硅酸盐对 微波的吸收能力较差

高磷铁矿石的提质降磷技术探讨

高磷铁矿石的提质降磷技术探讨

高磷铁矿石的提质降磷技术探讨近年来,国内外针对不同的矿石性质,进行了较为深入的铁矿石脱磷工艺研究。

标签:降磷;铁矿石;技术现状铁矿石中的磷主要以磷灰石或碳氟磷灰石形态与其它矿物共生,浸染于氧化铁矿物的颗粒边缘,嵌布于石英或碳酸盐矿物中,少量赋存于铁矿物的晶格中。

且磷灰石晶体主要呈柱状、针状、集晶或散粒状嵌布于铁矿物及脉石矿物中,粒度较小,有时甚至是在2微米以下,不易分离,属于难选矿石。

针对不同的矿石性质,近年来国内外进行了较为深入的铁矿石脱磷工艺研究。

主要工艺有:反浮选、选择性聚团、酸浸、高梯度磁选、氧化焙烧一酸浸、微生物脱磷。

1 高磷铁矿石提质降磷技术现状1.1 反浮选脱磷或磁选一反浮选联合工艺随着新型高效浮选药剂的不断出现,反浮选仍然是目前最主要的铁矿石脱磷方法。

为了降低反浮选成本或进一步降低含磷量,磁选一反浮选联合降磷已显示出优势。

例如:长沙矿冶研究总院以RA-3巧捕收剂,采用反浮选工艺,对美国Toshi 公司提供的Tilden高磷铁矿综合样进行了实验室小型试验研究。

以Cα2+为石英活化剂,淀粉为铁矿物抑制剂,RA-3巧为捕收剂进行磷硅混合反浮选,取得了铁品位65.50%,含磷0.030%,铁回收率79.67%的闭路试验指标;梅山铁矿与马鞍山矿山研究院采用浮选(脱硫)一磁选一浮选(脱磷)工艺流程处理梅山铁矿高磷磁铁矿取得了较好的工业试验指标,可将磷降至0.25%以下。

试验以H-907为捕收剂,水玻璃为抑制剂,浮磷作业铁回收率可达96.45%。

1.2 选择性聚团分选由于磷灰石等杂质矿物嵌布粒度极细,为使其单体解离,往往需要细磨,从而使常规方法捕集困难,回收率低。

近年来,迅速发展起来的选择性聚团分选工艺为微细粒矿物分离提供了更为广阔的前景。

选择性聚团分选工艺主要有:高分子絮凝分选、疏水聚团分选、磁团聚与磁种聚团分选以及复合聚团分选。

自1964年开始,选择性聚团分选工艺曾用于加拿大斯奈克雷文矿床的高磷铁矿石脱磷研究。

高磷鲕状赤铁矿提铁降磷研究综述

高磷鲕状赤铁矿提铁降磷研究综述

高磷鲕状赤铁矿提铁降磷研究综述周文涛1,2韩跃新1,2孙永升1,2高鹏1,2李艳军1,2(1.东北大学资源与土木工程学院,辽宁沈阳110819;2.难采选铁矿资源高效开发利用技术国家地方联合工程研究中心,辽宁沈阳110819)摘要为提高我国铁矿资源的高效开发利用水平,提高铁矿石自给率,基于高磷鲕状赤铁矿石的矿物特性,对高磷鲕状赤铁矿的资源利用现状、提铁降磷工艺方法和机理进行了综述。

指出采用传统选矿方法,如单一浮选、选择性絮凝—反浮选、浮磁联合等常规选矿方法虽然操作简单易行,但得到的铁精矿铁品位和回收率等选别指标较低,去磷率低,难以达到理想的提铁降磷效果;化学浸出法、生物浸出法以及冶炼法虽然去磷效果显著,但存在成本和环境问题;东北大学相关课题组在总结已有提铁降磷研究成果和大量试验研究的基础上提出了一种低耗、高效的提铁降磷的工艺方法,即深度还原短流程熔炼工艺技术,该技术以铁矿石→金属铁→铁水→铁水除杂→成型钢材为流程路线,具有工艺流程短、热量利用率高等优势,可以实现高磷鲕状赤铁矿石的高效选别。

关键词高磷鲕状赤铁矿提铁降磷磁选浮选浸出深度还原短流程中图分类号TD925.7文献标志码A文章编号1001-1250(2019)-02-010-05DOI 10.19614/ki.jsks.201902002Research Prospect of Enriched Iron and Dephosphorization of High Phosphorus Oolitic HematiteZhou Wentao 1,2Han Yuexin 1,2Sun Yongsheng 1,2Gao Peng 1,2Li Yanjun 1,2(1.School of Resources and Civil Engineering,Northeastern University ,Shenyang 110819,China ;2.National -Local Joint Engineering Research Center of Refractory Iron Ore Resources Efficient Utilization Technology ,Shenyang 110819,China )AbstractTo increase the development and utilization level of iron resources in our country ,increase the iron self -suffi⁃ciency degree ,based on the mineral properties of high -phosphorus oolitic hematite ,the present high phosphorus oolitic hema⁃tite utilization situation ,the process and mechanism of iron extraction and phosphorus reduction were reviewed.It was pointedout that although conventional mineral processing methods such as single flotation ,selective flocculation -reverse flotation and flotation -magnetic combination are easy to operate ,the separation indexes such as grade and recovery of iron concentrate arelow ,and the dephosphorization rate is low ,which makes it difficult to achieve the ideal effect of iron extraction and dephos⁃phorization ;chemical leaching ,biological leaching and smelting methods have costs and environmental problems ,althoughthe dephosphorization effect is remarkable.On the basis of summarizing the existing research results and a large number of ex⁃perimental studies ,the relevant research group of Northeast University proposed a low -consumption and high -efficiency pro⁃cess for iron extraction and phosphorus reduction ,i.e.deep reduction short -process smelting technology ,which takes iron ore→metal iron→hot Metal→hot metal impurity removal→forming steel as the process route ,with short process flow and high heat utilization rate.The principle and Prospect of this technology are also discussed.The process has the advantages of short process flow and high heat utilization rate ,can realize the high -efficiency separation of high -phosphorus oolitic hematite.KeywordsHigh phosphorus oolitic hematite ,Iron increase and phosphorus removal ,Magnetic separation ,Flotation ,Leaching ,Deep reduction short -process smelting technology收稿日期2018-11-25基金项目国家自然科学基金项目(编号:51604063)。

高磷铁精矿降磷试验研究

高磷铁精矿降磷试验研究
摘 要 :本文 针 对 某 高 磷 铁 精 矿 进 行 降 磷 试 验 研 究 ,采 用 了 细磨 一 次磁 选 ,反 浮 选 ,化 学 浸 出等 多 多
种 方 法 降磷 。研 究 结 果 表 明 :该铁 精 矿 采用 常规 分 选 法 难 以获 得 符 合 冶 炼 要 求 的产 品 ,而 化 学 浸 出法 可 以有 效 降 磷 ,但 碱 浸 成 本 较 高 ,酸 浸 降磷 则 较 为 经 济 可 行 。盐 酸 、硝 酸 、硫 酸浸 出 均 可 获 得 磷 含 量 合 格
S HEN i i g,HUANG a — i AO —i ,QI a Hu — n t Xio y ,B Xil n N Hu
( l g fRe o r e n t l r y,Gu n x ie st ,Na n n 3 0 4,Ch n ) Co l eo s u c s a d Me a l g e u ag i Un v r iy n ig5 0 0 ia
I ss w n t tt wo c ve to ls p r to e ho r t e fc i e w he e s c e ia e c ng i f ti ho ha he t on n ina e a a in m t ds a e no fe tv r a h m c 11a hi s e — f c ie f r r m o lo os ho u e tv o e va fph p r s,a c d la hig i o e c t ef c i d fasb et n akaila h n nd a i e c n s m r os— fe tvean e i l ha l l e c i g.
铁 精 矿 ,但 硝 酸 价 格 较 高 ,因此 采 用 盐 酸 和 硫 酸 为 浸 出剂 。在 适 当 条 件 下 ,硫 酸 和 盐 酸 浸 出 均 可 获 得 铁 品位 6 . 以上 、磷 含 量 0 1 的铁 精矿 产 品 。 05 .8

宜昌某高磷赤铁矿反浮选提铁降磷试验研究

宜昌某高磷赤铁矿反浮选提铁降磷试验研究

宜昌某高磷赤铁矿反浮选提铁降磷
试验研究
宜昌某高磷赤铁矿反浮选提铁降磷试验研究
随着资源的消耗和环境污染的不断加剧,矿业行业面临越来越大的压力。

为了实现资源的高效利用和环境的保护,各个矿山企业纷纷加强技术创新,提高资源利用率和绿色发展水平。

本次试验研究的宜昌某高磷赤铁矿反浮选提铁降磷技术,就是一个很好的实践案例。

该矿床的磷含量较高,铁含量中等,为难选矿床。

传统的工艺流程,常使用浮选的方法来实现铁的提取,但浮选法对于高磷铁矿处理效果不佳,不能实现全程选矿。

另外,由于高磷赤铁矿磷元素和铁元素缺乏差异,传统的选矿方式无法有效地降低磷的含量,对于矿石磷含量的降低,增加了较大的难度。

此次实验研究,通过反浮选和选择性氧化焙烧工艺相结合的方式,成功地实现了高磷赤铁矿提铁降磷的目的。

具体操作步骤如下:
1.矿浆先进入反浮选弱磁选系统,利用反浮选的原理,将
磁性物质吸附到磁铁筒上,达到提铁的目的。

2.反浮选后的尾矿进入焙烧窑,经过选择性氧化焙烧的过程,使得其中的磷元素被氧化为氧化物,不能被水处理,磷含量大幅降低,达到降磷的目的。

3.焙烧后的矿渣进入湿选回路,脱除矿渣中的磁性物质。

实验研究结果表明,反浮选提铁降磷技术可以显著提高铁的回收率,同时降低磷的含量。

经过实验室的分析和现场试验的验证,该技术的使用,有效地提高了磁选环节铁回收率,提高了高磷赤铁矿的选别指数。

同时,降低了磷含量,使得矿石的利用率得到了显著的提高。

总的来说,本次试验研究的宜昌某高磷赤铁矿反浮选提铁降磷技术,是一项成功的创新实践,为矿业工业的可持续发展做出了积极的贡献。

在今后的工业生产中,必将起到重要的作用。

宜昌某高磷赤铁矿反浮选提铁降磷试验

宜昌某高磷赤铁矿反浮选提铁降磷试验

试验方法与步骤
原料准备
将原矿破碎至一定粒度,用球磨机磨 细至所需细度。
02
药剂制备
按照试验要求配制石灰、抑制剂和捕 收剂等药剂。
01
产品收集与检测
收集各段浮选产品,进行铁和磷含量 的检测,分析提铁降磷效果。
05
03
调浆
将磨细的原矿与石灰、抑制剂和捕收 剂等药剂混合,搅拌均匀,调节pH值 至合适范围。
总结词
该文献介绍了反浮选提铁降磷的基本原理和技术,包括药剂选择、工艺 流程和操作参数等。
THANKS
谢谢您的观看
国内外研究现状
国内研究现状
国内对于高磷赤铁矿的选矿研究 主要集中在选矿工艺和药剂研究 方面,取得了一定的成果,但仍 存在一定的技术难度和挑战。
国外研究现状
国外对于高磷赤铁矿的选矿研究 相对较早,一些技术和工艺已经 较为成熟,但同样面临一些技术 挑战和问题。
02
试验材料与方法
试验原料
宜昌某高磷赤铁矿
加强人才培养
为了更好地进行反浮选工艺研究和应 用,建议加强相关专业人才的培养和 引进。
05
参考文献
参考文献
01
总结词

该文献提供了宜昌某高磷赤铁矿的基本特征和性质,包括矿物组成、化
学成分和物理性质等。
02 03
详细描述
该文献详细描述了宜昌某高磷赤铁矿的矿物组成,主要包括赤铁矿、石 英、白云石等,并对其化学成分和物理性质进行了分析。这些数据为后 续的反浮选提铁降磷试验提供了重要的基础信息。
04
结论与建议
结论
铁品位提高
通过反浮选工艺,铁品位提高了10%以 上,达到了62%以上,满足了工业生产
的要求。

高磷、砷铁矿降磷、砷试验研究

高磷、砷铁矿降磷、砷试验研究

高磷、砷铁矿降磷、砷试验研究随着我国钢铁工业的迅速发展,2005年我国的钢产量已超过3亿吨,已经成为世界第一的钢铁大国,但是我国的铁矿石资源供需矛盾日益突出,2005年进口铁矿石达2.75亿t,进口铁矿石的数量已占我国钢铁厂需求总量的一半以上,已经超过日本成为世界上最大的铁矿石进口国。

对铁矿石进口依赖度的提高,使我国丧失了国际矿价的话语权,已成为我国钢铁工业经济安全的重大隐患。

因此,迫切需要依靠技术进步来最大限度地合理开发利用国内现有铁矿资源,尤其是受目前选矿技术限制而不能开发利用的复杂难选铁矿石,增储增效,充分挖掘现有铁矿山的生产潜力,提高铁矿石的自给率,缓解进口铁矿石的压力,维持稳定、足量、优质的铁矿原料供给,以保障钢铁工业持续稳定的发展。

目前我国有占总储量14.68%,总量达74.5亿吨的高磷铁矿石因技术问题而没有开发利用,所以研究高磷铁矿石降磷的工艺对保障我国钢铁工业原料的供给具有十分重要的理论意义和现实意义。

本课题以云南某高磷、砷褐铁矿提质降杂为研究对象,该矿Fe品位为54.09%,P含量为0.48%,As含量为1.054‰,从工艺矿物学研究出发,进行了一系列试验研究。

查清了矿石中的铁主要以褐铁矿的形式存在,磷主要以胶磷矿的形式存在,砷主要以砷黄铁矿的形式存在。

通过一系列探索性试验,进行对比研究,得出氧化焙烧—酸浸和加剂还原焙烧—磁选的效果较好。

本课题通过对氧化焙烧—酸浸工艺和加剂还原焙烧—磁选工艺进行条件试验,找出最佳试验条件,得出氧化焙烧—酸浸工艺能够达到精矿Fe品位为63.14%,P含量为0.146%,As含量为0.525‰,回收率约为100%的指标;加剂还原焙烧—磁选工艺能够达到精矿Fe品位为67.18%,P含量为0.156%,As含量为0.306‰,回收率为86.12%的指标。

综合考虑,加剂还原焙烧—磁选工艺要优于氧化焙烧—酸浸工艺。

通过对试验过程的理论分析,得出胶磷矿在氧化焙烧过程中将解胶分解,从而便于酸浸;胶磷矿在还原焙烧过程中将与除磷药剂反应生成独立的产物,从而便于磁选分离。

高磷铁矿石提质除磷的研究

高磷铁矿石提质除磷的研究

高磷铁矿石提质除磷的研究
比较了摇床重选、磁选和浮选的提质效果,最后选择摇床重选作为第一步提质选别方法。

研究了焙烧过程的相关机理和影响因素,铁矿石中的主要含磷矿物菱磷铝锶矾在煅烧到500℃后会逐渐分解成易溶于酸的磷酸铝而导致焙烧后的
铁矿石除磷效果远远大于未焙烧时的除磷效果,当焙烧温度超过1025℃时磷酸
铝会发生晶型转变而变成更难溶于酸的立方型磷酸铝,最佳的焙烧温度为800℃。

浸出过程的相关机理和影响因素也进行了研究,当反应时间小于1h时,浸出过程主要受化学反应的速度控制;大于1h时,浸出过程主要受内扩散控制。

在反应初期,增加酸的浓度和提高酸浸温度都有助于提高磷的浸出率,随着酸浸时间
的延长,磷的浸出率与酸浸时间的平方根成正比,搅拌速度对磷的浸出影响不大。

鄂西某高磷铁矿石浸出脱磷试验研究

鄂西某高磷铁矿石浸出脱磷试验研究

鄂西某高磷铁矿石浸出脱磷试验研究皮科武;龚文琪;李育彪【摘要】分别采用酸浸、生物浸出方法,对鄂西某高磷铁矿石(铁品位43.50%,磷含量0.85%)进行湿法浸出脱磷实验研究.试验结果表明:当矿浆浓度为2%时,100ml 单一的0.1mol/L草酸(C2H2O4)、柠檬酸(C6H8O7)、H2SO4、HNO3、HCl中,无机酸提铁降磷效果优于有机酸.其中,H2SO4的提铁除磷效果最佳,处理后矿石铁品位为49.08%,铁回收率为99.57%,除磷率为93.91%;草酸与柠檬酸的混合酸浸矿中,在混合比例介于100:0~20:80之间时,提铁除磷效果较好;当矿浆浓度低于5%时,单一硫酸浸出后矿石中的磷含量为0.18%;采用At.f菌和黑曲霉菌进行微生物浸矿除磷,浸出后固体中磷含最分别为0.25%、0.22%.【期刊名称】《中国矿业》【年(卷),期】2010(019)009【总页数】4页(P78-81)【关键词】高磷铁矿石;酸浸;生物浸出;除磷【作者】皮科武;龚文琪;李育彪【作者单位】武汉理工大学资源与环境工程学院,湖北武汉430070;湖北工业大学化学与环境学院,湖北武汉430068;武汉理工大学资源与环境工程学院,湖北武汉430070;武汉理工大学资源与环境工程学院,湖北武汉430070【正文语种】中文【中图分类】TD951随着钢铁工业的发展,可利用的铁矿资源日益趋向于贫、细、杂[1]。

我国高磷铁矿石储量占总储量的14.86%,达74.5亿t[2,3]。

目前,因含磷较高而无法得到充分利用[4-6]。

鄂西高磷铁矿石中,主要矿物——赤铁矿的嵌布粒度一般极细,且常与其他矿物共生、胶结或互相包裹,目前被国内外公认为最难选的铁矿石类型[7]。

因此,研究铁矿石除磷技术具有非常重要的意义[8]。

近年来,国内外针对不同的矿石性质,进行了较为深入的铁矿石除磷工艺研究[9],而酸浸及微生物浸出方法,对该类铁矿石进行浸矿除磷实验研究,被认为是行之有效的方法[10,11]。

某高磷铁矿悬浮焙烧—磁选—浸出提铁降磷实验研究

某高磷铁矿悬浮焙烧—磁选—浸出提铁降磷实验研究

某高磷铁矿悬浮焙烧—磁选—浸出提铁降磷实验研究
王绍兴;宁国栋;刘应志;李艳军
【期刊名称】《矿产保护与利用》
【年(卷),期】2024(44)1
【摘要】针对高磷铁矿因铁矿物与磷矿物共生关系复杂、常规选矿方法难以高效
利用的特点,提出了焙烧—浸出的提铁降磷技术。

对阿尔及利亚TFe品位为
60.81%、FeO含量为14.92%、P含量为0.71%的某高磷铁矿,采用悬浮焙烧(氧化焙烧—磁化焙烧)—磁选—浸出工艺开展了提铁脱磷实验研究,在氧化温度1 050℃、还原温度520℃、还原时间25 min、H2体积浓度50%的磁化焙烧工艺条件下,获得了TFe品位65.50%、TFe回收率96.31%、P含量0.16%的铁精矿指标,磷脱除率77.46%。

实验研究结果可为高磷铁矿提铁降磷提供指导。

【总页数】7页(P82-88)
【作者】王绍兴;宁国栋;刘应志;李艳军
【作者单位】上海逢石科技有限公司;东北大学资源与土木工程学院;难采选铁矿资
源高效开发利用技术国家地方联合工程研究中心
【正文语种】中文
【中图分类】TD952.1;TD924
【相关文献】
1.高磷鲕状赤铁矿转底炉直接还原提铁降磷研究
2.某高磷鲕状铁矿石气基直接还原⁃磁选提铁降磷研究
3.高磷鲕状铁矿氧化球气基还原-磁选提铁降磷研究
4.高磷鲕
状铁矿直接还原-磁选提铁降磷扩大试验研究5.探讨现代企业经济管理模式的规范化策略
因版权原因,仅展示原文概要,查看原文内容请购买。

高磷赤铁矿酸浸降磷及浸出液综合利用的研究的开题报告

高磷赤铁矿酸浸降磷及浸出液综合利用的研究的开题报告

高磷赤铁矿酸浸降磷及浸出液综合利用的研究的开题报告一、研究背景和意义高磷赤铁矿是一种重要的铁矿资源,其磷含量通常超过0.1%,是我国常规铁矿中磷含量较高的一种。

高磷含量的赤铁矿开采和综合利用是当前我国铁矿资源开发和利用的难点之一。

磷元素是钢铁生产中的重要污染物,高磷含量的铁矿进入钢铁行业会引起破坏冶金坩埚和提高炉渣粘度等问题,影响生产效益和环境污染。

传统的高磷赤铁矿处理方法是采用浸出法脱除磷,在钢铁生产中大多采用烧结-烧结-磁选的工艺路线,但这种方法存在铁资源浪费严重、环境污染较大等问题。

因此,如何实现高磷赤铁矿磷元素的综合利用是当前重要的研究方向之一。

本课题旨在研究高磷赤铁矿酸浸降磷及浸出液综合利用的工艺技术,实现高磷赤铁矿中磷元素的资源化利用,减少环境污染和铁资源浪费,具有重要的理论和实际意义。

二、研究内容和方法本课题的研究内容主要包括:1.高磷赤铁矿酸浸降磷技术研究:选择合适的酸性介质和浸出条件,研究高磷赤铁矿的浸出率和磷元素的降解率。

2.浸出液中磷元素的回收与综合利用:采用化学沉淀、离子交换、反渗透等技术将浸出液中的磷元素回收并转化为有用的化学品或者肥料。

3.高磷赤铁矿资源化利用的实验研究:通过实验研究,探究高磷赤铁矿中磷元素在其他用途方面的应用,如水泥生产、废水处理等方面。

本课题的研究方法主要包括文献调研、实验研究、数据分析等。

三、预期目标和创新点本课题的预期目标是:1.研究出高效、可行的高磷赤铁矿酸浸降磷技术,实现高磷赤铁矿中磷元素的高效降解和回收。

2.实现高磷赤铁矿浸出液中磷元素的资源化利用,开发出可行的技术路线,将浸出液中的磷元素转化为有用的化学品或者肥料。

3.在水泥生产、废水处理等方面探究高磷赤铁矿中磷元素在其他用途方面的应用。

本课题的创新点在于:1.研究高磷赤铁矿酸浸降磷技术并将其应用于实际生产,实现高磷赤铁矿中磷元素的高效降解和回收。

2.实现高磷赤铁矿浸出液中磷元素的资源化利用,开发出可行的技术路线,将浸出液中的磷元素转化为有用的化学品或者肥料。

  1. 1、下载文档前请自行甄别文档内容的完整性,平台不提供额外的编辑、内容补充、找答案等附加服务。
  2. 2、"仅部分预览"的文档,不可在线预览部分如存在完整性等问题,可反馈申请退款(可完整预览的文档不适用该条件!)。
  3. 3、如文档侵犯您的权益,请联系客服反馈,我们会尽快为您处理(人工客服工作时间:9:00-18:30)。

KEY O RDS : io r ;s akig tbe;lw itn i g n tc ih itniyma n tc d p o p oi t n W rn oe h c n a l o ne st ma ei ;hg ne st g ei; e h s h rz i y ao
Su y o p 0p 0 iain P o es o n Or f g h s h r td nDe h s h r t rc s ra eo h P op o z 0 f Hi
HE Ja g y ,Z in - i HOU P n ,Z ig HU ANG u— h n , G z a g DU Jn - o g, ig h n ZHANG J n,L U Yu bn ,YANG Z i h i u I e— ig h — u
表1 ,铁化 学物 相 分 析 见 表 2 ,主要 矿 物 组 成见 表

提 出铁 精矿 含磷 应 低 于 0 0 4 ,我 国钢 铁企 业 则 .2 %
收稿 1期 :20 _4 3 3 07 0 _O
A BS TRA CT :I hsp p r h mp ra c fd p 0 p 0iainp o esi rame to ihp o p ou rnoe i a aye .Th nti a e ,te i o n eo e h s h rzt rc s n t t n fhg h sh rsi r s n lz d t 0 e o e
2 铁 矿 石 工 艺 矿 物 学 特 征
2 1 原矿 化学 成分 与矿 物特 征 .
我 国高磷铁 矿石 储量 占总储 量 的 1 . 6 ,达 7 . 48% 45
亿t 。 进入 2 0世 纪 9 0年代 以后 ,Ceead CisIc lvl lf n n f
试 验 样 品取 自云南 某铁 矿 ,原矿 多元 素分 析见
艺势 在必 行 。
重要 战 略资源 。世 界铁 矿 资源较 为 丰富 ,分 布也极 为广 泛 。但是 随着 现代 工业 的高 速发 展 ,地球 上有 限的富铁 矿和 易选 铁矿 资源将 逐 步枯 竭 ,对微 细粒
极高 杂 ( 含磷 、硫 )铁 矿 石 的分 选 显 得 十分 重 要 。
( aut o a dR suc n ier g K n n nvr t o F c l f n eoreE g e n , u migU ie i f y L n i sy
S i c n e h o g ,K n ig Y n a 5 0 3 hn ) c n ea dT c n l y u m n , u n n6 0 9 ,C ia e o
何姜毅 ,周 平 ,庄故章 ,杜景红 ,张 军 ,刘 阅兵 ,杨 志惠
( 昆明理 工 大学 国土 资源学 院 ,云南 昆 明

609 ) 503
要 :分 析 了高 磷 铁 矿 石 降 磷 的 重 要 性 ,并 且 叙 述 了 某 高磷 铁 矿 石 的 主要 工 艺 矿 物 学 特 征 、磷 赋 存 状 态 及
嵌布特征。通过 工艺研究 ,最后选择弱磁一强磁一摇床精选的工艺流程 ,加强 矿物的细磨 ,是铁矿 降磷 和提 高精
矿 指 标 的 重 要措 施 。
关 键 词 :铁 矿石 ;摇 床 ;弱 磁 ;强 磁 ;降 磷 中 图 分 类 号 :T 9 文献 标 识 码 :A 文 章 编 号 :10 - 38 ( 0 7 0 -0 7 5 D2 0 6 0 0 20 ) 6 0 1 - 0
mi e a o y c a a trsi so n i n o e a d te o c re c n se n t n c a a t rsis o h s h r u r e c b d n r lg h rc e t fa r r n h c u r n e a d dis mia i h r ce tc fp o p o o s a e d s r e .T r u h t e r - i c o o i i h o g h e sac e r h,t e d p o p o ii g prc s f o ne st g e i h e h s h r n o e so w i t n i ma n t z l y c—h g n e st g e i i h i t n i ma n tc—s a k n a l e a ai n wa ee t d y h c i g t b e s p r t s s l ce ・F n r n - o ieg d i i g i n i o t n l a u e f r p o p o u e v n . n s a mp r tne s r o h s h r s r mo i g a
维普资讯 http://www.cqviБайду номын сангаас.com
20 07年 1 2月
云 南 冶 金
YUNNAN MET AL URGY L
De . 2 0 e 0 7
第3 6卷第 6期 ( 总第 27期 ) 0
V 13 .N . ( u 0 ) o 6 . o6 S m 2 7
某 高 磷铁 矿 降磷 技 术 研 究
1 引 言
铁矿 石作 为钢 铁工业 的主要 原料 是一 个 国家 的
要求 铁 精 矿 含 磷 必 须 低 于 0 2 ~0 3 ,然 而 我 .% .% 国一 些 铁 矿 山精 矿 含 磷 超 过 0 3 有 的甚 至 高 达 .%
0 6 。为 了能 够 很 好 的 利 用 这 些 高 磷 铁 矿 资 源 , .% 增加 这 些矿 山的 服务 年限 ,研究 铁 矿石 高效脱 磷 工
相关文档