新型热敏变色储能材料的性能评价

新型热敏变色储能材料的性能评价
郑喜玲;马晓光;杜红恩;吴智磊;杨文芳;孟庆涛
【期刊名称】《纺织学报》
【年(卷),期】2013(034)008
【摘要】采用传统的涂层工艺,选取水性聚氨酯涂层剂将自制的热敏变色储能材料整理到织物上.对焙烘温度、焙烘时间、涂覆量等主要工艺参数进行研究,当焙烘温度为140℃,焙烘时间为3 min,涂覆量为50 g/m时,经热敏变色储能材料涂层整理后的织物变色性能和储能性能较好.扫描电镜结果显示,热敏变色储能微胶囊在织物上能够很好的黏附固着,保证了整理织物性能的耐久性.涂层整理后织物的DSC测试结果显示,涂层织物的储能性能良好,其起始相变温度为32.5℃,潜热值达到7.388 J/g,调热值达到l 137.752 J/m2.%The self-made thermo color-change and energy-storage materials were finished onto the fabric with waterborne polyurethane(PU) by conventional coating method.The main processing conditions such as curing temperature,curing time and coating weight were studied.When the curing temperature was 140 ℃,curing time was 3 min and coating weight was 50 g/m,the good discoloration performance and nice energy-storage property of the fabric treated with thermo color-change and energy-storage materials were obtained.Images of scanning electron microscopy (SEM) tests showed the thermo color-change and energy-storage materials were fixed firmly on the fabric,which ensured the durability of the performance of treated fabric.The DSC test of the treated fabric demonstrated obvious thermoregulatory performance,with the
initial phase change temperature 32.5 ℃,enthalpy up to 7.388 J/g,and thermoregulatory value up to 1 137.752 J/m2.
【总页数】5页(P95-99)
【作者】郑喜玲;马晓光;杜红恩;吴智磊;杨文芳;孟庆涛
【作者单位】天津工业大学纺织学院,天津300387;改性与功能纤维天津市重点实验室,天津300387;天津工业大学纺织学院,天津300387;改性与功能纤维天津市重点实验室,天津300387;天津工业大学纺织学院,天津300387;改性与功能纤维天津市重点实验室,天津300387;天津工业大学纺织学院,天津300387;改性与功能纤维天津市重点实验室,天津300387;天津工业大学纺织学院,天津300387;改性与功能纤维天津市重点实验室,天津300387;天津工业大学纺织学院,天津300387;改性与功能纤维天津市重点实验室,天津300387
【正文语种】中文
【中图分类】TS190.1
【相关文献】
1.新型热敏变色材料的微胶囊化研究 [J], 冯文昭;吴赞敏;葛婧媛
2.多元氯化物熔盐储能材料的制备及其热性能评价 [J], 徐贵钰;何廷鸿;殷海青;祝永强;王广乐
3.复合低温热敏变色储能材料的研制 [J], 吴智磊;马晓光;李青
4.热敏变色微胶囊的变色色谱拓展及其应用 [J], 王亮;马晓光;李俊君;杨州
5.热敏变色涂层厚度对织物变色性能的影响 [J], 陈安;刘茜
因版权原因，仅展示原文概要，查看原文内容请购买。