仿生法在AZ91D镁合金表面制备羟基生物涂层

仿生法在AZ91D镁合金表面制备羟基生物涂层
张伶玲;刘万辉;陆文娟;陈城
【期刊名称】《广州化工》
【年(卷),期】2016(044)016
【摘要】The preparation of hydroxyapatite on magnesium make samples have good mechanical properties of magnesium , corrosion resistance and biocompatibility of HA . HA was produced by biomimetic method . Activated magnesium alloy surface by acid washing , alkali washing and activation , the sample was placed in SBF solution after alkali heat treatment.The results showed that the amount of deposits became larger with the concentration of NaOH solution increased .After soaking in
15%NaOH the amount of hydroxyapatite deposited in SBF was the highest .After 3 days of deposition , biological coating with good uniformity can be product on the surface of magnesium alloy .%镁基表面制备羟基磷灰石可以使材料同时具备镁良好的力学性能以及羟基磷灰石的耐腐蚀性、生物相容性等特点。

本课题通过酸洗、碱洗、活化的处理活化镁合金表面，试样经碱热处理后置于SBF溶液中仿生生成羟基磷灰石。

结果表明：随浸泡的NaOH溶液浓度升高，试样表面沉积物质量增加，经15％NaOH浸泡后，试样在SBF中沉积得到的羟基磷灰石量最多。

沉积3天后，镁合金表面得到均匀性较好的生物涂层。

【总页数】3页(P106-107,124)
【作者】张伶玲;刘万辉;陆文娟;陈城
【作者单位】常熟理工学院化学与材料工程学院，江苏苏州 215500;常熟理工学院化学与材料工程学院，江苏苏州 215500;常熟理工学院化学与材料工程学院，江苏苏州 215500;常熟理工学院化学与材料工程学院，江苏苏州 215500
【正文语种】中文
【中图分类】TQ63
【相关文献】
1.AZ91D镁合金表面羟基磷灰石涂层的构建及其腐蚀行为 [J], 赵丹丹;孙瑞雪
2.通过仿生法在纯镁表面制备羟基磷灰石涂层的研究 [J], 龚沛; 王欣宇; 郭洁
3.磁场诱导对AZ91D镁合金表面仿生矿化法制备羟基磷灰石涂层性能的影响 [J], 许晨阳; 吉妍; 兰昊天; 薄祥
4.仿生法在镁合金表面制备珍珠质涂层的性能研究 [J], 周锟广; 何美凤
5.仿生法在镁合金表面制备珍珠质涂层的性能研究 [J], 周锟广; 何美凤
因版权原因，仅展示原文概要，查看原文内容请购买。