相思木EMCC硫酸盐浆氧脱木质素前后酶处理的影响研究

相思木EMCC硫酸盐浆氧脱木质素前后酶处理的影响研究王玉秀;童国林;尤纪雪
【期刊名称】《林产化学与工业》
【年(卷),期】2012(032)004
【摘要】研究了酶处理对相思木EMCC(延伸改良连续蒸煮)硫酸盐浆(KP浆)氧脱木质素效果的影响.结果表明,由白腐菌直接合成的漆酶/木聚糖酶体系(LXS)预处理相思木EMCC硫酸盐浆的的适宜酶用量为7 IU/g;LXS预处理后浆料氧脱木质素的适宜反应时间、最高反应温度及用碱量分别为60 min、100 ℃和2.5％;利用LXS 进行氧脱木质素后处理的适宜反应时间及酶用量分别为2h和5 IU/g.SEM观察到经过酶处理后纤维表面及横切面出现大量的裂隙及孔隙,其中以酶后处理最为明显,为后续漂白中化学药品的渗透和漂白降解产物的溶出创造条件.%The effect of enzyme treatment on oxygen delignification of Acacia EMCC kraft pulp was investigated. The results indicated that the optimum dosage of laccase/xylanase system ( LXS) , which produced by white-rot fungus, was 7 IU/g in the pre-treatment process. For LXS pretrealed pulp, high quality pulp was obtained when fibers were treated by 2.5 alkali dosage for 60 min at 100℃ in oxygen del ignification. The optimum treatment time and enzyme dosage was 2 h and 5 IU/g when LXS was used for pulp posttreatment after oxygen delignification. The SEM indicated that the fibers with rough surface and many tiny holes and cracks in the cross section of the cell wall were obtained after enzyme treatment. It clearly
showed that LXS could be used as posttreatment following oxygen delignification.
【总页数】6页(P77-82)
【作者】王玉秀;童国林;尤纪雪
【作者单位】南京林业大学,江苏省制浆造纸科学与技术重点实验室,江苏南京210037;山东亚太森博浆纸有限公司,山东日照216837;南京林业大学,江苏省制浆造纸科学与技术重点实验室,江苏南京210037;南京林业大学,江苏省制浆造纸科学与技术重点实验室,江苏南京210037
【正文语种】中文
【中图分类】TQ35
【相关文献】
1.溶解木质素对氧脱木质素以及二氧化氯脱木质素工序的影响 [J], 管敏
2.马尾松硫酸盐浆两段氧脱木质素最佳工艺条件的研究 [J], 马邕文;万金全;陈中豪;李新平;宋彬章
3.马尾松硫酸盐浆单段氧脱木质素最佳工艺条件的研究 [J], 马邕文;陈昌华;陈中豪;李新平;宋彬章
4.针叶木硫酸盐浆酶处理漂白效果 [J], 薛国新;Hsie.,JS
5.采用钨硅酸钒杂多阳离子作为桉木硫酸盐浆氧脱木质素催化剂 [J],
因版权原因，仅展示原文概要，查看原文内容请购买。