钢丝绳重量系数和最小破断拉力系数

钢丝绳重量系数和最小破断拉力系数

钢丝绳重量系数和最小破断拉力系数(表)

WIRE ROPE WEIGHT COEFFICIENT AND MBL COEFFICIENT (LIST 1)

类别Class 钢丝绳重量系数 K'Wire rope weight coefficient

最小破断拉力系数 K'

Minimum breaking load coefficient 天然纤维芯

钢丝绳NF

合成纤维

芯钢丝绳

SF

钢芯钢丝绳

IWR/IWS

K2/K1n K2/K1p

纤维芯钢

丝绳FC

钢芯钢丝绳

IWR/IWS

K'1/K'2 K1n K1p K2

K'1 K'2

kg/100m·mm2

1x7 - - 0.522 - - - 0.54 -

1 1x19 - - 0.507 - - - 0.53 - 1x37 - - 0.501 - - - 0.49 -

2 6x7 0.351 0.344 0.387 1.1 1.12 0.332 0.359 1.08

3 6x19(a)

0.38 0.371 0.418 1.1 1.13 0.33 0.356 1.08

4 6x37(a)

5 6x19(b) 0.351 0.344 0.4 1.14 1.1

6 0.30

7 0.332 1.08

6 6x37(b) 0.346 0.33

7 0.4 1.16 1.19 0.295 0.319 1.08

7 6x61 0.361 0.354 0.398 1.1 1.12 0.283 0.306 1.08

8 8x19

0.357 0.344 0.435 1.22 1.26 0.293 0.346 1.18

9 8x37

10 18x7

0.39 0.43 1.1 1.1 0.31 0.328 1.06

11 18x19

12 34x7 0.39 0.43 1.1 1.1 0.308 0.318 1.03

13 35Wx7 - 0.46 - - - 0.36 -

14 6Vx7 0.412 0.404 0.437 1.06 1.08 0.375 0.398 1.06

15 6Vx19

0.405 0.397 0.429 1.06 1.08 0.36 0.382 1.06

16 6Vx37

17 4Vx39 0.41 0.402 - - - 0.36 - -

18 6Qx19+6Vx21 0.41 0.402 - - - 0.36 - -

19 6x12 0.251 0.231 - - - 0.209 - -

20 6x24 0.318 0.304 - - - 0.28 - -

21 6x15 0.2 0.185 - - - 0.18 - -

22 4x19 0.41 - - - 0.36 - -

23 4x37 0.41 - - - 0.36 - - 注释:

1.在第3项、第5项、第8项钢丝绳中，当股内钢丝的数目为19或19根以下时，重量系数应比表中所列

的数小3%;

2.在第15项钢丝绳中,股含纤维芯6Vx21,6Vx24结构钢丝绳的重量系数和最小破断拉力系数应分别比表中

所列的数小8%;6Vx30结构钢丝绳的最小破断拉力系数应比表中所列的数小10%;在第16项钢丝绳中，股为

线接触结构6Vx37S钢丝绳的重量系数和最小破断拉力系数则应分别比表中所列的数大3%;

3.在第20项钢丝绳中，股为等捻距结构钢丝绳的重量系数和最小破断拉力系数应分别比表中所列的数大

4%。

4.K1p重量系数是对聚丙烯纤维芯钢丝绳而言。

Note:

1. For the wire ropes in 3, 5, or 8, when the number of wires in a strand is 19 or less, the weight coefficient should be 3% less than the figure in the table.

2. In 15, 6Vx21 and 6Vx24 have fiber cores inside strand. The wire rope weight coefficient and minimum breaking load coefficient should be 8% less than the figure in the table. The minimum breaking load for 6Vx30 should be 10% less than the figure in the table. While in 16, 6Vx37S is made with equal lay strands, the weight coefficient and minimum breaking load coefficient should be 3% larger than the figure in the table.

3.In 20, for the wire ropes with same lay pitch, the weight coefficient and minimum breaking load coefficient should be 4% larger than the figure in the table.

4. K1p weight coefficient is used for wire ropes with polypropylene fiber cores.

供电距离过长，必须允许一定的电压降。

供电电压为660伏，负荷400KW时的额定电流：

I＝P/1.732×U×cosφ＝400/1.732×0.66×0.8≈437(A)

距离：L＝1000米，铜芯电线电阻率：ρ＝0.0172，线路末端线与线(电压630V)允许电压降为30V，即单线压降：U＝15V

求单线阻：

R＝U/I＝15/437≈0.034(Ω)

求线截面：

S＝ρ×L/R＝0.0172×1000/0.034≈506(平方)

用线算图求取1千伏以下供电线路的电压损失

(苏)技术科学副博士 B．C．库兹涅佐夫蒋福强译编

众所周知，大部分用电设备对供电电压的变化是很敏感的。例如供电电压比额定值降低10％，感应电动机的旋转力矩就要减少19％，而电灯的光通量则要减少30—40％。

但供电电压超过用电设备的额定值(这种情况在用电低峰时可能出现)，也同样会影响用电设备的正常工作。例如白炽灯和日光灯的供电电压超过额定值