钕铁硼磁铁性能一览表
钕铁硼磁铁性能参数牌号表
钕铁硼磁铁性能参数牌号表
牌号Br Hcb Hcj (BH)max TW 剩磁矫顽力内禀矫顽力最大磁能积最高工作
温度T KGS KA/m KOe KA/m KOe KJ/m3 MGOe ℃
N35 1.17-1.21 11.7-12.1 876-899 11.0-11.3 ≥955≥12263-279 33-25 ≤80
N38 1.22-1.26 12.2-12.6 876-923 11.0-11.6 ≥955≥12287-303 36-38 ≤80
N40 1.26-1.29 12.6-12.9 876-923 11.0-11.6 ≥955≥12303-318 38-40 ≤80
N42 1.30-1.33 13.0-13.3 876-926 11.0-11.6 ≥955≥12318-334 40-42 ≤80
N45 1.33-1.37 13.3-13.7 876-926 11.0-11.6 ≥955≥12342-358 43-45 ≤80
N48 1.36-1.42 13.6-14.2 876-926 11.0-11.6 ≥955≥12358-382 45-48 ≤80
N50 1.41-1.45 14.1-14.5 828-907 10.4-11.4 ≥876≥11382-398 48-50 ≤70
N52 1.44-1.48 14.4-14.8 828-907 10.4-11.4 ≥876≥11394-414 49.5-52 ≤70
N35M 1.17-1.21 11.7-12.1 892-915 11.2-11.5 ≥1114≥14263-279 33-35 ≤100
强力磁铁特性表
磁铁特性表
内算矩顽力 KOe >= 12 >= 12 >= 12 >= 12 >= 12 >= 12 >= 12 >= 12 >= 14 >= 14 >= 14 >= 14 >= 14 >= 14 >= 14 >= 14 >= 17 >= 17 >= 17 >= 17 >= 17 >= 32 >= 20 >= 20 >= 20 >= 20 >= 25 >= 25 >= 25 >= 25 >= 25 >= 25 >= 30 >= 30 >= 30 >= 30 >= 30 >= 35 >= 35 >= 35 >= 35 KA/m >= 955 >= 955 >= 955 >= 955 >= 955 >= 955 >= 955 >= 955 >= 1114 >= 1114 >= 1114 >= 1114 >= 1114 >= 1114 >= 1114 >= 1114 >= 1353 >= 1353 >= 1353 >= 1353 >= 1353 >= 2547 >= 1595 >= 1595 >= 1595 >= 1595 >= 1990 >= 1990 >= 1990 >= 1990 >= 1990 >= 1990 >= 2388 >= 2388 >= 2388 >= 2388 >= 2388 >= 2785 >= 2785 >= 2785 >= 2785 最大磁能积 MGOe KJ/m3 标准值 最小值 标准值 最小值 30 28 239 223 33 31 263 247 35 33 279 263 38 36 303 287 40 38 318 303 42 40 342 326 45 43 358 342 48 46 383 367 30 28 239 223 33 31 263 247 35 33 279 263 38 36 303 257 40 38 318 303 42 40 342 326 45 43 358 342 48 46 383 367 33 31 263 247 35 33 279 263 40 38 318 303 42 40 342 326 45 43 358 342 34 31 271 247 35 33 279 263 38 36 303 287 40 38 318 303 42 40 342 326 28 26 223 207 30 28 239 223 33 31 263 247 35 33 279 263 38 35 303 279 40 38 319 303 26 24 207 191 28 26 223 207 30 28 239 223 33 30 263 239 36 33 287 263 28 26 223 207 30 28 239 223 33 31 263 247 34 31 271 247 工作温度 ° C <= 80 <= 80 <= 80 <= 80 <= 80 <= 80 <= 80 <= 80 <= 100 <= 100 <= 100 <= 100 <= 100 <= 100 <= 100 <= 100 <= 120 <= 120 <= 120 <= 120 <= 120 <= 240 <= 150 <= 150 <= 150 <= 150 <= 180 <= 180 <= 180 <= 180 <= 180 <= 180 <= 200 <= 200 <= 200 <= 200 <= 200 <= 240 <= 240 <= 240 <= 240
钕铁硼磁铁性能参数牌号表
钕铁硼磁铁性能参数牌号表
牌号Br
剩磁Hcb
矫顽力
Hcj
内禀矫顽力
(BH)max
最大磁能积
TW
最高工作
温度
°C
T KGS KA/m KOe KA/m KOe KJ/m3 MGOe
N35 1.17-1.21 11.7-12.1 876-899 11.0-11.3 羽55 >2 263-279 33-25 宅0 N38 1.22-1.26 12.2-12.6 876-923 11.0-11.6 羽55 >2 287-303 36-38 宅0 N40 1.26-1.29 12.6-12.9 876-923 11.0-11.6 羽55 >2 303-318 38-40 宅0 N42 1.30-1.33 13.0-13.3 876-926 11.0-11.6 羽55 >2 318-334 40-42 宅0 N45 1.33-1.37 13.3-13.7 876-926 11.0-11.6 羽55 >2 342-358 43-45 宅0 N48 1.36-1.42 13.6-14.2 876-926 11.0-11.6 羽55 >2 358-382 45-48 宅0 N50 1.41-1.45 14.1-14.5 828-907 10.4-11.4 為76 >1 382-398 48-50 <70 N52 1.44-1.48 14.4-14.8 828-907 10.4-11.4 為76 >1 394-414 49.5-52 <70 N35M 1.17-1.21 11.7-12.1 892-915 11.2-11.5 >1114 >4 263-279 33-35 <00 N38M 1.22-1.26 12.2-12.6 907-931 11.4-11.7 >1114 >4 287-303 36-38 <00 N40M 1.26-1.29 12.6-12.9 907-947 11.4-11.9 >1114 >4 303-318 38-40 <00 N42M 1.30-1.33 13.0-13.3 907-947 11.4-11.9 >1114 >4 318-334 40-42 <00 N45M 1.33-1.37 13.3-13.7 907-955 11.4-12.0 >1114 >4 334-358 42-45 <00 N48M 1.36-1.42 13.6-14.2 907-955 11.4-12.0 >1114 >4 358-382 45-48 <00 N33H 1.14-1.17 11.4-11.7 820-876 10.3-11.0 >1353 >7 247-263 31-33 <20 N35H 1.17-1.21 11.7-12.1 860-907 10.8-11.4 >1353 >7 263-279 33-35 <20 N38H 1.22-1.26 12.2-12.6 907-947 11.4-11.9 >1353 >7 287-303 36-38 <20 N40H 1.26-1.29 12.6-12.9 907-947 11.4-11.9 >1353 >7 303-318 38-40 <20 N42H 1.30-1.33 13.0-13.3 907-947 11.4-11.9 >1353 >7 318-334 40-42 <20 N44H 1.33-1.36 13.3-13.6 907-947 11.4-11.9 >1274 >6 334-350 42-44 <10 N30SH 1.08-1.12 10.8-11.2 804-844 10.1-10.6 >1592 >0 223-239 28-30 <50 N33SH 1.14-1.17 11.4-11.7 820-876 10.3-11.0 >1592 >0 247-263 31-33 <50 N35SH 1.17-1.21 11.7-12.1 860-907 10.8-11.4 >1592 >0 263-279 33-35 <50 N38SH 1.22-1.26 12.2-12.6 907-947 11.4-11.9 >1592 >0 287-303 36-38 <50 N40SH 1.26-1.29 12.6-12.9 907-947 11.4-11.9 >1592 >0 303-318 38-40 <50 N42SH 1.30-1.33 13.0-13.3 907-947 11.4-11.9 >1512 >9 318-334 40-42 <40 N28UH 1.04-1.08 10.4-10.8 780-812 9.8-10.2 >1990 >5 207-223 26-28 <80 N30UH 1.08-1.12 10.8-11.2 804-844 10.1-10.6 >1990 >5 223-239 28-30 <80 N33UH 1.14-1.17 11.4-11.7 820-876 10.3-11.0 >1990 >5 247-263 31-33 <80 N35UH 1.17-1.21 11.7-12.1 860-907 10.8-11.4 >1990 >5 263-279 33-35 <80 N38UH 1.22-1.26 12.2-12.6 860-907 10.8-11.4 >1990 >5 287-303 36-38 <80
钕铁硼磁铁性能参数牌号表之欧阳科创编
钕铁硼磁铁性能参数牌号
表
牌号
Hcb Hcj(BH)max TW
剩磁矫顽力内禀矫顽
力
最大磁能积
最高工
作
温度
T KGS KA/m KOe KA/m KOe KJ/m3MGOe℃
N351.17-
1.21
11.7-
12.1
876-
899
11.0-
11.3
≥955≥12
263-
279
33-25≤80
N381.22-
1.26
12.2-
12.6
876-
923
11.0-
11.6
≥955≥12
287-
303
36-38≤80
N401.26-
1.29
12.6-
12.9
876-
923
11.0-
11.6
≥955≥12
303-
318
38-40≤80
N421.30-
1.33
13.0-
13.3
876-
926
11.0-
11.6
≥955≥12
318-
334
40-42≤80
N451.33-
1.37
13.3-
13.7
876-
926
11.0-
11.6
≥955≥12
342-
358
43-45≤80
N481.36-
1.42
13.6-
14.2
876-
926
11.0-
11.6
≥955≥12
358-
382
45-48≤80
N501.41-
1.45
14.1-
14.5
828-
907
10.4-
11.4
≥876≥11
382-
398
48-50≤70
N521.44-
1.48
14.4-
14.8
828-
907
10.4-
11.4
≥876≥11
394-
414
49.5-52≤70
N35M 1.17-
1.21
11.7-
12.1
892-
915
11.2-
11.5
≥1114≥14
263-
279
33-35≤100
N38M 1.22-
1.26
12.2-
12.6
907-
931
钕铁硼磁铁性能参数牌表
钕铁硼磁铁性能参数牌号表
牌号Br Hcb Hcj (BH)max TW 剩磁矫顽力内禀矫顽力最大磁能积最高工作
温度T KGS KA/m KOe KA/m KOe KJ/m3 MGOe ℃
N35 1.17-1.21 11.7-12.1 876-899 11.0-11.3 ≥955≥12263-279 33-25 ≤80
N38 1.22-1.26 12.2-12.6 876-923 11.0-11.6 ≥955≥12287-303 36-38 ≤80
N40 1.26-1.29 12.6-12.9 876-923 11.0-11.6 ≥955≥12303-318 38-40 ≤80
N42 1.30-1.33 13.0-13.3 876-926 11.0-11.6 ≥955≥12318-334 40-42 ≤80
N45 1.33-1.37 13.3-13.7 876-926 11.0-11.6 ≥955≥12342-358 43-45 ≤80
N48 1.36-1.42 13.6-14.2 876-926 11.0-11.6 ≥955≥12358-382 45-48 ≤80
N50 1.41-1.45 14.1-14.5 828-907 10.4-11.4 ≥876≥11382-398 48-50 ≤70
N52 1.44-1.48 14.4-14.8 828-907 10.4-11.4 ≥876≥11394-414 49.5-52 ≤70
N35M 1.17-1.21 11.7-12.1 892-915 11.2-11.5 ≥1114≥14263-279 33-35 ≤100
钕铁硼磁铁性能参数表
沈阳中北通磁科技股份有限公司磁性能指标内控标准 版次：A/0
页次：1/2
Grade Br bHc iHc (BH)max Temperature Density 规格剩磁矫顽力内禀矫顽力最大磁能积工作温度密度kGs T kOe KA/m kOe kA/m MGOe kJ/m3℃/(L/D=0.7) g/cm3 N52 14.9~14.2 1.49~1.42 ≥10.5≥835 ≥11≥876 53~49 422~390 ≤80≥7.45 N50 14.5~14.0 1.45~1.40 ≥10.5≥835 ≥11≥876 51~47 406~374 ≤80≥7.45 N48 14.1~13.6 1.41~1.36 ≥10.5≥835 ≥11≥876 49~45 390~358 ≤80≥7.45 N45 13.8~13.2 1.38~1.32 ≥10.5≥835 ≥11≥876 46~42 366~334 ≤80≥7.45 N42 13.3~12.8 1.33~1.28 ≥10.5≥835 ≥11≥876 43~40 342~318 ≤80≥7.45 N40 13.1~12.5 1.31~1.25 ≥10.5≥835 ≥11≥876 41~38 326~303 ≤80≥7.45 N38 12.7~12.3 1.27~1.23 ≥10.5≥835 ≥11≥876 39~36 311~287 ≤80≥7.45 N50M 14.5~14.0 1.45~1.40 ≥13.0≥1035 ≥14≥1115 51~47 406~374 ≤100≥7.45 N48M 14.1~13.6 1.41~1.36 ≥12.8≥1019 ≥14≥1115 49~45 390~358 ≤100≥7.45 N45M 13.8~13.2 1.38~1.32 ≥12.4≥987 ≥14≥1115 46~43 366~342 ≤100≥7.45 N42M 13.3~12.8 1.33~1.28 ≥12.1≥963 ≥14≥1115 43~40 342~318 ≤100≥7.45 N40M 13.1~12.5 1.31~1.25 ≥12.0≥955 ≥14≥1115 41~38 326~303 ≤100≥7.45 N38M 12.7~12.3 1.27~1.23 ≥11.8≥939 ≥14≥1115 39~36 311~287 ≤100≥7.45 N50H 14.5~14.0 1.45~1.40 ≥13.0≥1035 ≥16≥1274 51~47 406~374 ≤120≥7.45 N48H 14.1~13.6 1.41~1.36 ≥12.8≥1019≥16≥1274 49~45 390~358 ≤120≥7.45 N46H 13.9~13.2 1.39~1.32 ≥12.5≥995 ≥17≥1354 47~44 374~350 ≤120≥7.45 N45H 13.8~13.2 1.38~1.32 ≥12.4≥987 ≥17≥1354 46~42 366~334 ≤120≥7.45 N44H 13.7~13.1 1.37~1.31 ≥12.3≥979 ≥17≥1354 45~42 358~334 ≤120≥7.45 N42H 13.3~12.8 1.33~1.28 ≥12.1≥963 ≥17≥1354 43~40 342~318 ≤120≥7.45 N40H 13.1~12.5 1.31~1.25 ≥12.0≥955 ≥17≥1354 41~38 326~303 ≤120≥7.45 N38H 12.7~12.3 1.27~1.23 ≥11.5≥916 ≥17≥1354 39~35 311~279 ≤120≥7.45
钕铁硼性能表
Q/DDX 安徽大地熊新材料股份有限公司企业标准
Q/DDX001-2009
代替Q/AHXF001-2005
烧结钕铁硼磁体
2009-2-10 发布2009-3-1实施安徽大地熊新材料股份有限公司发布
Q/AHDDX001-2009 目次
前言 (Ⅱ)
1 范围 (1)
2 规范性引用文件 (1)
3 定义和术语 (1)
4材料分类与牌号 (1)
5技术要求 (1)
6 试验方法 (1)
7 检验规则 (2)
8．标志、包装、运输 (2)
前言
本标准起草单位：安徽大地熊新材料股份有限公司
本标准主要起草人：陈新、周志国、吴真元
烧结钕铁硼磁体
1．范围
本标准规定了烧结钕铁硼磁体的分类、技术要求、试验方法、检验规则、标志、包装、运输、贮存。
本标准适用于粉末冶金工艺生产的烧结钕铁硼磁体。
2．规范性引用文件
下列文件中的条款通过本标准的引用而成为本标准的条款。凡是注日期的引用文件，其随后所有的修改单（不包括勘误的内容）或修订版均不适用于本标准，然而，鼓励根据本标准达成协议的各方研究是否可使用这些文件的最新版本。凡是不注日期的引用文件，其最新版本适用于本标准。
GB/T 2828 逐批检查计数抽样程序及抽样表（适用于连续批的检查）
GB/T 3217 永磁（硬磁）材料磁性试验方法
GB/T 9637 磁学基本术语和定义
GB/T 13560 烧结钕铁硼磁体
XB/T 903 烧结钕铁硼磁体表面镀覆层
3．术语与定义
本标准采用下列定义：
3.1 主要磁性能：包括永磁材料的剩磁（Br）、磁极化强度矫顽力（内禀矫顽力）（HcJ）、磁感应
强度矫顽力（矫顽力）（HcB）、最大磁能积（（BH）max）
钕铁硼磁铁性能一览表
钕铁硼磁铁性能一览表
1. 磁能积（BHmax）：磁能积是衡量磁体的磁性能的重要指标，表示
单位磁体体积中所包含的能量。钕铁硼磁铁具有非常高的磁能积，通常在
最高的级别达到400-600 kJ/m³。这使它成为目前最强大的可用磁体之一
2. 矫顽力（Hcj）：矫顽力是材料抵抗磁化反转的能力，即磁场强度
增加到一定程度时磁铁发生磁化反转的临界点。钕铁硼磁铁具有非常高的
矫顽力，通常高达1000-2000 kA/m。这使得它能够在高温和高磁场环境
下保持较稳定的磁性能。
3.剩磁（Br）：剩磁是材料磁化后去除磁场后剩余的磁感应强度。钕
铁硼磁铁通常具有非常高的剩磁，通常在1.1-1.4T的范围内。这使得它
具有非常强的吸附和保持力，可以广泛应用于各种工业和消费产品。
4.温度系数（α）：温度系数是衡量材料磁性能随温度变化的能力。
钕铁硼磁铁具有较高的温度系数，通常在0.1-0.13%/°C之间。这意味着
在高温下，钕铁硼磁铁的磁性能会有一定的衰减。因此，在高温环境下使
用钕铁硼磁铁时需要注意温度影响。
5.耐蚀性：由于钕铁硼磁铁中含有大量的铁元素，它对环境中的湿气
和酸性物质敏感，容易生锈和腐蚀。因此，钕铁硼磁铁通常需要通过电镀
或涂层等方式进行保护，以延长其使用寿命。
6.尺寸和形状：钕铁硼磁铁可以制成各种尺寸和形状，如片状、环状、棒状和复杂形状等。这使得它具有广泛的应用领域，可以满足不同的设计
要求。
7.成本：由于钕铁硼磁铁是一种稀有土矿石，以及制备和加工的复杂性，导致其价格较高。因此，在使用钕铁硼磁铁时需要权衡其性能和成本，选择合适的型号和规格。
钕铁硼磁铁材料表
钕铁硼磁铁材料表
钕铁硼磁铁是一种高性能永磁材料，具有高磁能积、高剩磁、高矫顽力等优异性能，广泛应用于电机、电器、电子、机械等领域。以下是一些常见钕铁硼磁铁材料的性能参数表：
| 品牌/型号 | 磁能积(MGOe) | 相对磁导率 | 硬度(HV) | 矫顽力(KOe) | 矫顽力(kA/m) | 密度(g/cm) |
| --------- | ------------ | ---------- | --------- | ------------ | ------------ | ----------- |
| N35 | 33-36 | 1.12-1.17 | 606-653 | 10.9-12.1 | 868-967 | 7.5 |
| N38 | 36-38 | 1.17-1.22 | 606-653 | 11.6-12.9 | 923-1027 | 7.5 |
| N40 | 38-41 | 1.22-1.26 | 606-653 | 12.0-13.3 | 955-1060 | 7.5 |
| N42 | 40-43 | 1.26-1.30 | 606-653 | 12.5-14.0 | 995-1114 | 7.5 |
| N45 | 43-46 | 1.30-1.33 | 606-653 | 12.8-14.5 | 1019-1152 | 7.5 |
| N48 | 46-49 | 1.33-1.38 | 606-653 | 13.5-14.8 | 1071-1180 | 7.5 |
(整理)钕铁硼磁铁介绍及性能表
钕铁硼磁铁介绍及性能表
第三代稀土永磁钕铁硼是当代磁铁中性能最强的永磁铁。它的BHmax值是铁氧体磁铁的
5-12倍，是铝镍钴磁铁的3-10倍；它的矫顽力相当于铁氧体磁铁的5-10倍，铝镍钴磁铁的5-15倍，其潜在的磁性能极高，能吸起相当于自身重量640倍的重物。
由于钕铁硼磁铁的主要原料铁非常便宜，稀土钕的储藏量较钐多10-16倍，故其价格也较钐钴磁铁低很多。
钕铁硼磁铁的机械性能比钐钴磁铁和铝镍钴磁铁都好，更易于切割和钻孔及复杂形状加工。
钕铁硼磁铁的不足之处是其温度性能不佳，在高温下使用磁损失较大，最高工作温度较低。一般为80摄氏度左右，在经过特殊处理的磁铁，其最高工作温度可达200摄氏度。由于材料中含有大量的钕和铁，故容易锈蚀也是它的一大弱点。所以钕铁硼磁铁必须进行表面涂层处理。可电镀镍(Ni), 锌(Zn), 金(Au), 铬(Cr), 环氧树脂(Epoxy)等。
钕铁硼磁铁目前广泛应用于工业航空航天，电子，机电，仪器仪表，医疗等领域。而且非技术领域使用也越来越广泛，如吸附磁铁，玩具，首饰等。
生产流程：
配料---->熔炼---->制粉---->成型---->烧结---->测试---->机械加工---->电镀---->磁化---->检验---->包装
钕铁硼磁铁磁性能Magnetic Properties of NdFeB Magnets
注：工作温度是指该温度下的开路磁通不可逆损失小于或等于5%，测试温度为20°C±2°C
Note: Working temperature is tested under 20°C±2°C, the inevitable loss of magnetic force is no more than 5%.
(整理)钕铁硼磁铁介绍及性能表
钕铁硼磁铁介绍及性能表
第三代稀土永磁钕铁硼是当代磁铁中性能最强的永磁铁。它的BHmax 值是铁氧体磁铁的
5-12 倍，是铝镍钴磁铁的 3-10 倍；它的矫顽力相当于铁氧体磁铁的 5-10 倍，铝镍钴磁铁的5-15 倍，其潜在的磁性能极高，能吸起相当于自身重量 640 倍的重物。
由于钕铁硼磁铁的主要原料铁非常便宜，稀土钕的储藏量较钐多 10-16 倍，故其价格也较钐钴磁铁低很多。
钕铁硼磁铁的机械性能比钐钴磁铁和铝镍钴磁铁都好，更易于切割和钻孔及复杂形状加工。
钕铁硼磁铁的不足之处是其温度性能不佳，在高温下使用磁损失较大，最高工作温度较低。一般为80 摄氏度左右，在经过特殊处理的磁铁，其最高工作温度可达 200 摄氏度。由于材料中含有大量的钕和铁，故容易锈蚀也是它的一大弱点。所以钕铁硼磁铁必须进行表面涂层处理。可电镀镍(Ni), 锌(Zn), 金(Au), 铬(Cr), 环氧树脂(Epoxy)等。
钕铁硼磁铁目前广泛应用于工业航空航天，电子，机电，仪器仪表，医疗等领域。而且非技术领域使用也越来越广泛，如吸附磁铁，玩具，首饰等。
生产流程：
配料---->熔炼---->制粉---->成型---->烧结---->测试---->机械加工---->电镀---->磁化---->检验---->包装
钕铁硼磁铁磁性能Magnetic Properties of NdFeB Magnets
矫顽力Hcb
材料
牌号
T N35
N38
N40
N42
KOe KOe 11.0-11.3 ≥955≥12 11.0-11.6 ≥955≥12 11.0-11.6 ≥955≥12 11.0-11.6 ≥955≥12
钕铁硼磁铁性能参数牌号表
钕铁硼磁铁性能参数牌号表
牌号Br Hcb Hcj (BH)max TW 剩磁矫顽力内禀矫顽力最大磁能积最高工作
温度T KGS KA/m KOe KA/m KOe KJ/m3 MGOe ℃
N35 1.17-1.21 11.7-12.1 876-899 11.0-11.3 ≥955 ≥12 263-279 33-25 ≤80
N38 1.22-1.26 12.2-12.6 876-923 11.0-11.6 ≥955 ≥12 287-303 36-38 ≤80
N40 1.26-1.29 12.6-12.9 876-923 11.0-11.6 ≥955 ≥12 303-318 38-40 ≤80
N42 1.30-1.33 13.0-13.3 876-926 11.0-11.6 ≥955 ≥12 318-334 40-42 ≤80
N45 1.33-1.37 13.3-13.7 876-926 11.0-11.6 ≥955 ≥12 342-358 43-45 ≤80
N48 1.36-1.42 13.6-14.2 876-926 11.0-11.6 ≥955 ≥12 358-382 45-48 ≤80
N50 1.41-1.45 14.1-14.5 828-907 10.4-11.4 ≥876 ≥11 382-398 48-50 ≤70
N52 1.44-1.48 14.4-14.8 828-907 10.4-11.4 ≥876 ≥11 394-414 49.5-52 ≤70
N35M 1.17-1.21 11.7-12.1 892-915 11.2-11.5 ≥1114 ≥14 263-279 33-35 ≤100
磁铁性能表
等级 N30 N33 N35 N38 N40 N42 N45 N48 N30M N33M N35M N38M N40M N42M N45M N48M N30H N33H N35H N40H N42H N45H 剩磁/T 1.12 1.17 1.21 1.26 1.29 1.32 1.37 1.41 1.12 1.17 1.21 1.26 1.26 1.32 1.37 1.41 1.12 1.17 1.21 1.29 1.32 1.37 矫顽力/（kA/m) 内禀矫顽力/（kA/m) 最大磁能积/（kJ/m3) 836 ≥955 239 876 ≥955 263 915 ≥955 279 915 ≥955 303 876 ≥955 318 876 ≥955 342 876 ≥955 358 876 ≥955 383 836 ≥1114 239 876 ≥1114 263 915 ≥1114 279 915 ≥1114 303 915 ≥1114 318 876 ≥1114 342 976 ≥1114 358 876 ≥1114 383 836 ≥1353 239 876 ≥1353 263 915 ≥1353 279 955 ≥1353 318 876 ≥1353 342 876 ≥1353 358
工作温度/℃ ≤80 ≤80 ≤80 ≤80 ≤80 ≤80 ≤80 ≤80 ≤100 ≤100 ≤100 ≤100 ≤100 ≤100 ≤100 ≤100 ≤120 ≤120 ≤120 ≤120 ≤120 ≤120
钕铁硼磁铁常用型号
钕铁硼磁铁常用型号
1、N35：是一种极强的磁性硬体材料，有良好的温度稳定性和高温耐
久性，磁性能强度可达10.5-11.5kOe；
2、N38：具有良好的磁性和高温耐久性，磁性能强度可达11.5-
12kOe，也是科研实验中最常用的磁性材料之一；
3、N40：具有优异的磁性和高温耐久性，磁性能强度可达12-
12.5kOe，改变温度对磁性不敏感；
4、N42：具有极强的磁性和抗高温性，磁性能强度可达12.5-
13.2kOe，温度变化影响较小；
5、N45：具有极高的磁性和抗高温性，磁性能强度可达13.2-
13.7kOe，温度变化影响小；
6、N48：具有超高的磁性和抗高温性，磁性能强度可达13.7-
14.2kOe，温度变化对磁性影响较小；
7、N50：是一种超强的磁性材料，具有良好的抗高温性和耐腐蚀性，
磁性能强度可达14.2-15kOe；
8、N52：是一种极强的磁性材料，具有良好的抗高温性和耐腐蚀性，
磁性能强度可达14.8-15.5kOe；
9、N35H：具有极强的磁性和抗高温性，磁性能强度可达11-12kOe，
温度变化影响小；
10、N38H：具有超高的磁性和抗高温性，磁性能强度可达12-13kOe，温度变化对磁性影响较小；
11、N40H：具有极高的磁性和抗高温性，磁性能强度可达13-14kOe，温度变化影。