程序升温表面反应技术研究氧化铈上H2S的吸附和转化

程序升温表面反应技术研究氧化铈上H2S的吸附和转化
刘冰;徐恒泳;张泽会
【期刊名称】《催化学报》
【年(卷),期】2012(33)10
【摘要】H2S adsorption and reaction on CeO2,TiO2,and γ-Al2O3 were studied by temperature programmed surface reaction (TPSR).Ceria had the best desulfidation ability.The pretreatment atmosphere affected H2S adsorption and reaction on ceria,and desulfidation efficiency increased in the order of inert atmosphere,reducing atmosphere,oxidizing atmosphere.H2S was first adsorbed on pretreated ceria at room temperature.On increasing the temperature in an Ar (99.99％) atmosphere,part of the H2S desorbed below 673 K,and another part reacted with the surface oxygen on ceria to produce sulfur and water below 473 K,and SO2 between 473 and 673 K,which further reacted with lattice oxygen and was transformed into sulfate above 673 K.The sulfate decomposed into SO2 again at 873 K.To avoid the complex regeneration,it is advisable to carry out desulfidation below 673 K when using ceria as adsorbent.%采用程序升温表面反应技术研究了H2S在CeO2,TiO2和Al2O3三种载体上的吸附和反应行为.结果表明,CeO2具有最强的脱硫能力.系统研究了预处理气氛对H2S在CeO2上吸附和反应行为.发现CeO2的脱硫能力在惰性气氛、还原性气氛、氧化性气氛中依次增强.H2S首先吸附在经预处理的CeO2表面,进一步在Ar氛围下升温脱附时,一部分H2S在673 K以下脱附,部分则与CeO2表面氧反
应,在473 K下产生硫和水,而在473～673 K温度范围内,生成SO2.在673 K以上,所生成的SO2进一步与晶格氧反应,转化成硫酸盐.后者在873 K再次分解为SO2.因此,CeO2表面脱硫过程应控制在673 K以下,可避免复杂的再生过程.
【总页数】5页(P1631-1635)
【作者】刘冰;徐恒泳;张泽会
【作者单位】中南民族大学催化材料教育部-国家民委共建重点实验室,湖北武汉430074;中国科学院大连化学物理研究所,辽宁大连116023;中国科学院大连化学物理研究所,辽宁大连116023;中南民族大学催化材料教育部-国家民委共建重点实验室,湖北武汉430074
【正文语种】中文
【中图分类】O643
【相关文献】
1.甲烷作为化工原料直接转化生成芳烃和乙烯新催化过程的研究——Ⅰ.甲烷在Mo/HZSM-5催化剂上的程序升温表面反应 [J], 王林胜;崔巍
2.程序升温表面反应技术在固体催化剂上的应用(上) [J], 满毅;黄文氢;陈松
3.程序升温表面反应技术在固体催化剂上的应用(下) [J], 满毅;黄文氢;陈松
4.Co2C上CO的程序升温脱附和程序升温表面反应研究 [J], 裴彦鹏;丁云杰;臧娟;宋宪根;董文达;朱何俊;王涛;陈维苗
5.氮化钼催化剂上丁二烯吸附物种的程序升温表面反应 [J], 郝志显;吴自力;魏昭彬;李灿;辛勤;闵恩泽
因版权原因，仅展示原文概要，查看原文内容请购买。