Mg2SiO4-SiC复相材料的常压烧结及性能研究

Mg2SiO4-SiC复相材料的常压烧结及性能研究
杜磊;李晓云;丘泰;陆鑫翔
【期刊名称】《电子元件与材料》
【年(卷),期】2011(30)2
【摘要】在1 500～1 600℃氢气气氛下常压保温1 h制备了Mg2SiO4-SiC复相材料,研究了烧结助剂[Al2O3+Y2O3](r(Al2O3:Y2O3)=5:3)添加量对该复相材料烧结性能的影响.结果表明:Mg2SiO4-SiC复相材料的相组成为Mg2SiO4,6H-SiC、Y3Al5O12,最佳烧结温度为1 550℃,当[Al2O3+Y2O3]质量分数从0到7%逐渐增加时,该复相材料的显气孔率明显减小并趋于平稳;w(Al2O3+Y2O3)=5%时显气孔率最低达到0.36%.%Mg2SiO4-SiC composites were prepared by pressureless sintering method at 1 500～1 600 ℃ for I h in hydrogen atmosphere. The effect of the addition of sintering additives
[AI203+Y203][r(AI203: Y203)=5: 3] on the sintering properties of the composites was investigated. The results show that the composites consist of three phases, i.e,Mg2SiO4, 6H-SiC and Y3Al5O12. The optimum sintering temperature is I 550 ℃. With the increase ment of [Al203+Y203] content from 0 to 7％(mass fraction), the apparent porosity of the composites significantly decreases and then keep stable.Especially, the sample added with 5％ (mass fraction) of [AI203+Y203] show an apparent porosity of as Iow as 0.36％.
【总页数】3页(P8-10)
【作者】杜磊;李晓云;丘泰;陆鑫翔
【作者单位】南京工业大学,材料科学与工程学院,江苏,南京,210009;南京工业大学,材料科学与工程学院,江苏,南京,210009;南京工业大学,材料科学与工程学院,江苏,南京,210009;南京工业大学,材料科学与工程学院,江苏,南京,210009
【正文语种】中文
【中图分类】TM28
【相关文献】
1.常压烧结ZrB2-SiC复相材料的抗氧化行为研究 [J], 闫永杰;张辉;黄政仁;刘学建
2.SiC/mullite复相孔陶瓷的常压烧结与性能研究 [J], 杨金茹;陈玉强;李鹏
3.无压反应烧结MoSi_2-SiC_p复相材料的制备与性能 [J], 张小立;吕振林;金志浩
4.Y_2O_3-SiO_2助剂对常压烧结SiC-AlN复相材料烧结性能的影响 [J], 陈云;李晓云;王玉春;冯永宝;戴斌;丘泰;孙悦
5.常压烧结Mg_2SiO_4-SiC复相材料的微波衰减性能 [J], 杜磊;李晓云;丘泰
因版权原因，仅展示原文概要，查看原文内容请购买。