聚酰胺酰亚胺与聚酯亚胺热固化机理的 TGA 法研究

聚酰胺酰亚胺与聚酯亚胺热固化机理的 TGA 法研究
张昌辉;周小丽;江勇;来水利
【期刊名称】《陕西科技大学学报（自然科学版）》
【年(卷),期】2015(033)003
【摘要】Material of polyamide-imide and polyester-imide have excellent mechanical proper-ties ,thermal properties ,corrosion resistance and electrical insulation properties ,thereby the demand increasing year by year .Using TG ,RH ,DMA ,DSC to characterize the the formation mechanism of polyamide-imide and polyester-imide varnish ,analysised the curing process . Results showed that :the film forming curing process of polyamide-imide and polyester-imide include two steps ,one is the physical curing reaction by solution evaporation ,the other is chemical curing reaction caused by the chain extension reaction ;chain extension reaction is the reverse of the capping reaction accompanied chain extension process ;cross-linking curing reaction does not occur in the film-forming curing process ,cured film formation process is only a linear chain extend process .%聚酰胺酰亚胺与聚酯亚胺材料拥有优异的机械性能、热性能、耐腐蚀性能及电绝缘性能 ,因而市场需求逐年增加 .采用 TG、RH、DMA、DSC等手段对聚酰胺酰亚胺与聚酯亚胺绝缘漆所成的膜进行表征 ,分析了其固化过程 ,结果表明:聚酰胺酰亚胺与聚酯亚胺的成膜固化过程是由溶液挥发的物理固化和扩链反应发生的化学固化两步反应构成 ;扩链反应是封端反应的逆过程并伴有扩链过程;成膜过程并没有发生交联固化反应 ,只是一种线性扩链固化成膜过程 .
【总页数】6页(P79-83,115)
【作者】张昌辉;周小丽;江勇;来水利
【作者单位】陕西科技大学教育部轻化工助剂化学与技术重点实验室 ,陕西西安710021;陕西科技大学教育部轻化工助剂化学与技术重点实验室 ,陕西西安710021;陕西科技大学教育部轻化工助剂化学与技术重点实验室 ,陕西西安710021;陕西科技大学教育部轻化工助剂化学与技术重点实验室 ,陕西西安710021
【正文语种】中文
【中图分类】O633
【相关文献】
1.红外光谱法研究共聚酰胺酸应变材料的热酰亚胺化 [J], 刘润山;邓美文;等
2.电喷雾质谱法研究聚酰胺、酰亚胺衍生物与HIV-1基因DNA的相互作用 [J], 李卉卉;韩德伟;袁谷
3.聚酯酰亚胺改性环氧树脂研究3聚酯酰亚胺用量的影响 [J], 罗炎;李善君
4.热致液晶共聚酯酰亚胺与聚酰胺的原位复合 [J], 陈培丰;童跃进;吴瑞宁;关怀民
5.制冷压缩机电机用聚酯亚胺/聚酰胺酰亚胺复合漆包线的工艺与质量 [J], 徐国维因版权原因，仅展示原文概要，查看原文内容请购买。