乏风瓦斯催化燃烧实验研究

乏风瓦斯催化燃烧实验研究
霍春秀;李强
【期刊名称】《矿业安全与环保》
【年(卷),期】2014(000)004
【摘要】A platinum, palladium and cordierite carrier catalyst with rare earth element coating was prepared, catalytic combustion experiment of this catalyst was carried out with low-concentration methane, and study was made on the conversion rate of methane under different reaction temperature, different volume fraction of methane and different reaction space velocity. The experimental results indicated that under the conditions of the reaction space velocity of 30 000 h-1 and reaction temperature of 450 ℃, the conversion rate of methane was about 68%, which reached the light-off temperature of the catalyst; the conversion rate methane reached 100% at 700 ℃. When the methane volume fraction was 0. 2% ~1. 5%, the conversion rate of methane was over 99%. This catalyst is suitable for catalytic combustion of ventilation air methane.%制备了含有稀土元素涂层的铂、钯贵金属堇青石载体催化剂，用低浓度甲烷对该催化剂进行催化燃烧实验，研究了不同反应温度、不同甲烷体积分数、不同反应空速下甲烷的转化率。

实验结果表明：在反应空速为30000 h-1条件下，温度为450益时，甲烷转化率为68%左右，达到催化剂的起燃温度；在700益时，甲烷转化率达到100%。

甲烷体积分数为0.2%~1.5%时，甲烷转化率都超过了99%，该催化剂适用于乏风瓦斯催化燃烧。

【总页数】3页(P1-3)
【作者】霍春秀;李强
【作者单位】瓦斯灾害监控与应急技术国家重点实验室，重庆400037; 中煤科工集团重庆研究院有限公司，重庆400037;瓦斯灾害监控与应急技术国家重点实验室，重庆400037; 中煤科工集团重庆研究院有限公司，重庆400037
【正文语种】中文
【中图分类】TD712+.67;TQ517.5
【相关文献】
1.适于煤矿乏风催化燃烧的高性能催化剂制备方法实验研究 [J], 康建东
2.煤矿乏风瓦斯燃烧用催化剂研究进展 [J], 张兆瑞; 党文龙; 耿丽
3.《改性CuO/ZrO_2催化剂催化乏风瓦斯燃烧性能研究》研究背景与意义 [J],
4.改性CuO/ZrO_2催化剂催化乏风瓦斯燃烧性能研究 [J], 李忠阳;刘昶;崔宝君;高宏亮;徐锋;朱丽华
5.低温等离子体改性CuO/ZrO_2催化剂上乏风瓦斯催化燃烧性能 [J], 朱丽华;徐锋;崔宝君;高宏亮
因版权原因，仅展示原文概要，查看原文内容请购买。