搪瓷反应釜外型尺寸及其参数表
搪瓷反应釜外型尺寸及其参数表： 系列F系列搪瓷反应釜 型号F3000F5000F6300F8000F10000F12500F16000F20000F30000公称容积(L)30005000630080001000012500160002000030000计算容积(L)31005050686690601167013651174462179033500换热面积(m2)8.6113.1616.1018.3821.3524.8929.4834.0445.36 主要尺寸（mm）D1160017501750200022002200240026003000 D2175019001900220024002400260028003200 D31964215221522507270827082912--D4-------20002300 H1195195195210210210210210210 H2221528603244331035334053434646415340 H31050120012001200130013001400--H4132613261475154218801880188018802200 H385045005020522057806300659068907900 H0-------73268500 传动装置型号BLD-3BLD-4BLD-4BLD-4BLD-5BLD-5BLD-6BLD-6BLD-7 搅拌转速(转/分)浆式130130130130130130130130130叶轮 式 130130130130130130130130130 搪瓷管口 a300×400300×400300×400300×400300×400300×400300×400450450 b125125125200200200200250250 c100125125200200200200200200 d100125125150150150150150150 e125/灯125/灯125/灯125/灯125/灯125/灯125/灯125/灯125/灯f125150150150150150150150150 g100125125150150150150150150 h125150150150150150150150150 k----200200200200200 m---125125125125125125放料 口 125125125125150150150150150 夹套管口进出 口 3-653-653-653-654-804-804-1004-1004-100喷嘴 口 2-653-653-653-653-803-803-1003-1003-100 可修改
解析搪瓷修补剂在搪瓷反应釜破损的修补方法
大家都知道搪瓷反应釜是化工行业不可缺少的防腐设备，在使用中机械碰撞、温度急变等因素经常引起脱瓷、裂纹、气泡、气孔和面釉的其他损伤，这些缺陷在搪瓷设备中是决不允许的，一旦发生这种现象，必须进行修补，今天翌坤小陆给大家解析搪瓷反应釜破损的修补方法，方便处理搪瓷反应釜破损的修补难题。 因为一个搪瓷釜价值几万元，由于局部爆瓷而报废十分可惜。所以这时候就要及时采取适当修补，对破损的地方用翌坤搪瓷反应釜修补剂进行修补，这样设备仍能使用，不仅降低成本，而且还具有很好的实际意义和可观的经济效益。好了，废话不多说，知道了前奏，下面我们就主要来讲讲搪瓷反应釜破损的修补方法吧： 翌坤搪瓷反应釜修补剂具有较高的化学稳定性和良好的物理机械性能。高分子复合材料依靠自身更为细密的高分子结构，使得材料自身具有更强的粘接力和优异的耐腐蚀、抗腐蚀性能，高分子甚至能够渗透到金属里面，形成更为紧密的高分子复合材料保护层，所以搪瓷反应釜
脱瓷怎么修补这一问题，找翌坤就对了，采用翌坤搪瓷反应釜修补剂现场处理搪瓷脱落、基体防腐保护。用翌坤搪瓷反应釜破损的修补方法修复后不但具有优异的耐高温抗腐蚀等综合性能，延长设备使用寿命，而且以为企业节省拆卸更换所带来的时间和费用上的损失，并确保了企业的安全连续生产。采用搪瓷修补剂现场快速修搪瓷釜，简便、快速、有效，经济效益凸显。 翌坤搪瓷反应釜修补剂已成功应用于搪瓷反应釜修补、水泵叶轮修复、换热器渗漏及防腐、机械设备主轴、键槽、导轨等磨损修复、化工设备管道堵漏及防腐、船舶设备防腐等几百家企业，帮助企业减少了停工时间、节约了维修成本，贏得了业界良好声誉。 【以下产品为您排忧解难】 耐腐蚀修补剂品名耐腐蚀修 补剂修补 剂使用温 度 耐腐蚀修补剂特点及应用 耐腐蚀修补剂YK-8406 -60～160 YK-8406耐腐蚀修补剂是以陶瓷粉末为骨材的高性能高密度的防腐材 料，双组份，低粘度，可刷涂，耐强酸、强碱。用于修复受腐蚀的泵、 阀、管道、热交换器端板、贮槽、油槽,搪瓷反应釜交换器的修复， 等，并可做大面积预保护涂层。 耐腐蚀修 补剂YK-8416 -60～160 Yk-8416耐腐蚀修补剂是以陶瓷粉末为骨材的高性能高密度的防腐材 料，双组份，胶泥状，立面不流淌，耐强酸、强碱。用于修复受腐蚀 的泵、阀、管道、热交换器端板、贮槽、油槽等，并可做大面积预保 护涂层。 耐腐蚀修 补剂YK-8436 -60～160 YK-8436耐酸修补剂是以陶瓷粉末为骨材的高性能高密度的防腐材 料，双组份，在化学介质中具有优异的热稳定性、机械性能和耐腐蚀 性。适用于烟气脱硫系统、电解槽、化工设备、污水处理系统、石油 储罐等设备的修复及预保护涂层的制备。 耐腐蚀修补剂YK-8402 -60～150 高温搪瓷反应釜修补剂是由精细碳化硅填料与改性增韧耐热树脂进行 复合得到的高性能耐磨抗蚀聚合材料。专用于搪瓷反应釜衬里破损的 修补和防护，可有效抵御酸（含氢氟酸）、碱及物料的侵蚀和冲刷磨损。 产品是选用改性增韧耐热树脂复合得到的耐温抗蚀聚合材料。完全固 化后的耐磨防腐涂层可有效抵御以下介质侵蚀：碳酸、10%氢溴酸、 20%亚硝酸、20%的硝酸、30%硫酸、15%磷酸、30%氨水、石灰水、 氢氧化钾、氢氧化钙、、丙醇、丁醇、乙二醇你、二乙醇胺、甲胺、碳 酸氢盐、矿物油、无机盐等；与金属搪瓷热膨胀系数一致，固化后收 缩率低，不超过0.02%，按ASTM E228测试热膨胀率为28.3ppm/℃ 衬胶修补剂YK-937 -60～150 YK-937衬胶修补剂由各类高性能耐磨、抗蚀材料（如陶瓷、碳化硅、 金刚砂、钛合金）与改性增韧耐热树脂进行复合得到的高性能耐磨抗 蚀聚合陶瓷材料。双组分，膏状，立面不流淌，可用刮刀或舌板涂布 施工，适合垂直表面及顶面的施工，固化后形成表面光滑平顺、耐腐 蚀、抗磨损的保护涂层；修补各类遭受高温腐蚀的泵、阀、管路、热 交换器端板、叶片、反应釜。尤其对罐体内衬、管道内衬、化学储罐 内衬的破损、脱落的修补，效果好。适用于烟气脱硫系统、电解槽、 化工设备、污水处理系统、石油储罐等设备的修复及预保护涂层.用于
搪瓷反应釜安全操作规程
搪瓷反应釜安全操作规程 一、性能用途:抗酸腐蚀性能优良,一般用作反应器或贮罐,在绝大部分有机酸与有机酸得介质条件下使用,但不适用于碱性介质、氢氟酸等。 二、安全操作条件: 1、允许最大操作压力:罐夹套内6kg/cm2,罐内 2、5kg/cm2,或按设备铭牌规定使用。 2、检查与反应釜有关得管道与阀门,在确保符合受料条件得情况下,方可投料。 3、检查搅拌电机、减速机、机封等就是否正常,减速机油位就是否适当,机封冷却水就是否供给正常。 4、在确保无异常情况下,启动搅拌,按规定量投入物料。 5、10m3以上反应釜或搅拌有底轴承得反应釜严禁空运转,确保底轴承浸在液面下时,方可开启搅拌。 6、严格执行工艺操作规程,密切注意反应釜内温度与压力以及反应釜夹套压力,严禁超温与超压。 7、反应过程中,应做到巡回检查,发现问题,应及时处理。 8、若发生超温现象,立即用水降温。降温后得温度应符合工艺要求。 9、若发生超压现象,应立即打开放空阀。紧急泄压。 10、停车;若停电造成停车,应停止投料;投料途中停电,应停止投料,打开放空阀,给水降温。长期停车应将釜内残液清洗干净,关闭底阀、进料阀、进汽阀、放料阀等。 三、允许操作温度:-30～250℃。 四、适用酸碱度:PH≤10 。 五、安全使用与维护事项: 1.罐内外表面不宜敲打、碰撞,以防止搪玻璃脱落; 2.不准在罐内与搪玻璃壁上动用电焊与气焊。在外层夹套进行焊割时,必须在罐内部冲水后方可使用; 3.反应器得充填系数为75%,贮罐不超过90%; 4.敞口放置时,防止硬物掉入,以免损坏搪玻璃; 5.罐卡有松动或掉落时,应及时紧固; 6.对安全阀、压力表、温度计等要求应灵敏、准确、经常检查,如发现损坏及时更换; 7.基础完整、紧固,各部连接螺栓应齐全、紧固; 8.主体整洁、油漆完好,无跑、冒、滴、漏现象; 9.室外最低气温在0℃以下时必须放尽存水; 10.安全防护装置完好; 11.内容物温度在110℃需冷却时,应先开冷却水,待内容物冷却到50℃以下时,才可改用冰盐水。不得直接用冰盐水冷却,以免温差过大,引起搪玻璃开裂。 压滤机安全操作规程 1、操作前得准备工作 1、1机器经安装、调整、确认无误后方可投入使用。 1、2检查滤布状况,滤布不得折叠与破损。 1、3检查各关口接头有否接错,法兰螺栓有否均匀旋紧,垫片有否垫好。 2、操作过程 2、1操作按下列程序进行。 压紧滤板→开泵进料→关闭进料泵→拉开滤板卸料→清洗检查滤布→准备进入下一循环。 2、2操作方法
搪瓷反应釜标准操作及维护保养规程 .
目的：建立搪瓷反应釜标准操作规程，使操作规范化、标准化，保证安全生产，延长设备使用寿命。 范围：本程序适用于搪瓷反应釜的操作和日常维护保养。 职责：质量管理部、生产部 1操作前状态确认 1.1检查釜内外表面是否清洁。 1.2检查减速机的润滑油是否充足，搅拌桨的旋转方向是否正确。 1.3检查底阀、密封是否有泄漏，各接管是否连接完好。 1.4检查各仪表是否指示正常。 1.5检查冷冻水、蒸汽和电供给是否正常。 2生产操作： 2.1投料 将液体物料加到反应釜后，再投入固体物料。加料数量和顺序严格按照工艺要求。 2.2加热 2.2.1加热前封闭反应釜盖，确保搅拌开启。确保冷凝器中循环水开启。 2.2.2缓慢开启疏水阀（或回汽阀）和进汽阀，使之对夹套预热，逐步升压，夹套内压力不准超过0.25MPa。待温度快升高到规定值时适当关小进汽阀，缓慢升温到规定温度。 2.3保温 待温度到规定值，关闭回汽阀和进汽阀，在保温过程中若温度示数降到规定值以下，再进行适度通汽加热。 2.4降温
开启回水阀和进水阀，进行降温。降至规定温度，关闭进回水阀。 2.5停机 2.5.1停机检查水电汽是否关闭，检查所有物料阀门是否关闭 2.5.2停机及时填写设备运行记录。 3清洁 按照《搪瓷反应釜标准清洁规程》进行清洁。 4操作注意事项 4.1根据生产操作要求，严格控制各阀门的启闭。 4.2生产时，注意物料的反应特点。 4.3查看釜内情况使用防爆灯，查看结束立即关闭，避免浪费。 5、维护保养 5.1设备运行时听减速机和电机声音是否正常，摸减速机、电机、机座轴承等各部位的开车温度不过烫。 5.2设备运行时检查减速机有无漏油现象，轴封是否完好，检查减速箱内油位和油质变化情况，釜用机封油盒内是否缺油，必要时补加或更新相应的机油。 5.3检查安全阀、压力表、温度计等安全装置是否准确灵敏好用。 5.4运行时倾听反应釜内有无异常的振动和响声。 5.5保持搅拌轴清洁见光，对圆螺母连接的轴，检查搅拌轴转动方向是否按顺时针方向旋转，严禁反转。 5.6检查反应釜所有进出口阀是否完好可用，若有问题必须及时处理。 5.7检查反应釜的法兰和机座等有无螺栓松动，安全护罩是否完好可靠。 5.8检查反应釜本体有无裂纹、变形、鼓包、穿孔、掉瓷、泄漏等现象，油漆等是不是完整，有无脱落、烧焦情况。 5.9做好设备卫生，保证无油污、设备见本色。
搪瓷反应釜修复时要注意哪些细节
搪玻璃反应釜修复时如何安全操作？搪玻璃反应釜在日常使用中出现破损是常见的，然而当搪玻璃反应釜出现破损是，我们应及时的维修，切不可拖拖拉拉，其中的很多安全操作事项大家要谨记心中。 1、金属基体腐蚀洞穿需要补焊时，应尽量全焊透，且应不连续焊接，感到焊接部位周围搪玻璃层温度超过200℃时，应停止焊接，采取降温措施，待温度冷却后再焊。否则，周围的搪玻璃层会大面积灼伤爆瓷。焊接后要做内筒体或夹套水压试验，合格后再进行修复。补焊后搪玻璃反应釜最好静置2～3天后再进行表面处理，用砂轮机清理干净焊缝周围烘伤的搪玻璃层，并打磨出新鲜的金属表面。修复表面一定要清洗干净。总之，正确的材料选择和合理的施工工艺是成功修复的保证。 2、修复时必须两人，一人在罐内，一人在罐外安全监护。 3、人员进入搪玻璃反应釜时，必须切断搅拌器电机电源，关死介质进口阀门，并一定要有人值守。 4、对罐内的易燃、易爆、毒性介质严格检测，不达到安全指标，决不进人。 5、釜内打磨或施焊时，必须要有防护面具（防毒、防飞渣损伤脸部、眼睛）。 6、罐内必须安有通风装置。 7、特别注意管口、垫片等角落残留的介质，由于罐内温度升高（例如罐内施焊，焊渣飞溅）而挥发，燃烧或毒害施工人员。 8、一定要等修复剂完全固化后再投料。 【以下产品为您排忧解难】 耐腐蚀修补剂品名耐腐蚀修 补剂修补 剂使用温 度 耐腐蚀修补剂特点及应用 搪瓷反应釜修补剂YK-8406 -60～160 YK-8406耐腐蚀修补剂是以陶瓷粉末为骨材的高性能高密度的防腐 材料，双组份，低粘度，可刷涂，耐强酸、强碱。用于修复受腐蚀的 泵、阀、管道、热交换器端板、贮槽、油槽,搪瓷反应釜交换器的修 复，等，并可做大面积预保护涂层。 耐腐蚀修补剂YK-8416 -60～160 Yk-8416耐腐蚀修补剂是以陶瓷粉末为骨材的高性能高密度的防腐材 料，双组份，胶泥状，立面不流淌，耐强酸、强碱。用于修复受腐蚀 的泵、阀、管道、热交换器端板、贮槽、油槽等，并可做大面积预 保护涂层。 耐腐蚀修补剂YK-8436 -60～160 YK-8436耐酸修补剂是以陶瓷粉末为骨材的高性能高密度的防腐材 料，双组份，在化学介质中具有优异的热稳定性、机械性能和耐腐蚀 性。适用于烟气脱硫系统、电解槽、化工设备、污水处理系统、石油 储罐等设备的修复及预保护涂层的制备。 搪瓷修补剂-60～150 高温搪瓷反应釜修补剂是由精细碳化硅填料与改性增韧耐热树脂进
汽车钣金刮伤铝质修补剂
汽车钣金刮伤铝质修补剂 麻城翌坤胶业有限公司一家专业的铝质修补剂生产厂家，我司可以根据客户的不同需求和耐温要求定做从-60度到300度的铝质修补剂。现如今汽车的钣金大部分是选择铝质材质的，在汽车组装的时候由于铝件较软，很容易被刮伤，铝板刮伤的对着钣金喷点装饰的美观度不好操作。福建某汽车配件有限公司就碰到这样一个难题，他们在组装的时候不小心把铝板刮伤，有几条很深的痕迹，做油漆会出现下陷的现象，极度的不美观。该公司的工程人员也找了很多家的铝质修补剂，但是效果都不好，附着力不好，胶水在涂上去之后会脱落，没什么效果，后来仔细我们工程，工程推荐一款铝质修补剂3313，客户那边订购一组测试后，效果不错，可以进行机械加工，附着力也不错，现在他们只要碰到这样的问题就会联系我司。以下是这款铝质修补剂的参数，仅供参考： 【适用范围】 ◆铝质修补剂3313广泛应用于各种铝及铝合金铸件、零件及设备的缺陷、磨损、划伤、腐蚀、断裂的修复，修复后颜色一致，典型应用于空调系统零件及设备的冷焊修复。 铝质修补剂YK-3313固化前 产品型号颜 色 密度 (g/c m3) 抗压 强度 (Mpa ) 拉伸 强度 (Mpa) 剪切 强度 (Mpa) 弯曲 强度 (Mp a) 硬度 (Shore D) 工作 温度 (℃)
YK-3 313 铝 1.74 96.5 30.4 17.9 54.3 79 —60～168 铝质修补剂YK-3313固化后 产品型号配比(A:B) 操作 时间 (min) 投入 运行 前需 最短 时间 （h) 机加工. 轻负荷 前需 最短固 化时间 （h) 满负荷或热 负荷需 固化时间（h) 浸泡化 学物前 需 固化时 间（h) 重 量体积 YK-3 313 6比 1 4.5 比1 40～ 60 8 12 24 72 麻城翌坤胶业有限公司长期供应高温胶，工业修补剂，发动机缸体修补剂，搪瓷反应釜修补剂，高温修补剂，导电金属修补剂，电镀胶，电泳修补剂，耐磨修补剂，耐腐蚀修补剂，高温密封胶，衬胶修补剂，高温导电胶，液压缸修补剂，导轨磨损修补剂，环氧树脂胶水胶粘剂品!
搪瓷储罐哪家好
搪瓷储罐作为容量大，耐腐蚀的储存容器，生产厂家的工艺成熟与否直接决定了搪瓷储罐质量的好坏。所以，在购入搪瓷储罐之前，了解其的基本情况和注意事项是至关重要的。淄博华星化工设备厂作为搪瓷储罐的老牌生产厂家，其工艺和技术都相当的成熟。 说到工业消费消费范畴中的搪瓷搅拌设备，固然它的耐腐蚀性与耐磨性都非常突出，但是这类设备异常却也会呈现透露状况，异常也会呈现磨损状况。遇到这类成果需求做的就是做好及时的应急处置。那麼，关于搪玻璃反应罐设备来讲，究竟该如何无效处置这种设备的透露状况呢？ 900℃高温焙烧，冷却后搪瓷与钢板粘结在一同。由于搪瓷的线收缩系数和延伸率小于钢板，因而冷却后搪玻璃的变形量小于钢板的变形量，搪瓷遭到钢板的约束产生压应力。搪瓷釜制成后，其搪玻璃
即存在预紧缩应力，而钢板则存在预拉伸应力。由于预应力与线收缩系数和延伸率相关，线收缩系数和延伸率与温度又亲密相关，因而搪瓷釜的工作温度对搪瓷釜的运用影响很大。假如因温度变化大而使搪瓷产生的应力超越其运用应力，搪瓷将被毁坏。因而搪瓷釜搪瓷层遇冷、热急变，极瓷。因而搪瓷釜有耐温。 如有平衡罐按要求定在机架上，接通密封液进出口与机械密封的管路，连接氮气瓶、减压器与平衡罐的管路，试静压符合要求后接通水夹套，通冷却水待整机试车。54、安装固定机械密封底座及固定环，并调整搅拌轴上固定环内六角紧定螺钉，使机械密封的弹簧均匀受力，机械密封的动、静环端面紧密结合待总装完工试车。 1）水压试验时，设备出现明显变形，或者残余变形超过规定值时；（（搪瓷反应釜兼具玻璃的稳定性和金属强度等优点，是一种使用寿命长久的耐腐蚀设备，因为多用于酸碱溶液中，在运行到一定年限后，
育儿知识：陶瓷面盆有划痕怎么办
陶瓷面盆有划痕怎么办 在我们的卫浴产品中，面盆是我们每天都会使用到的产品。我们在面盆里洗漱、洗手，非常的方便。大多数家庭的面盆都是陶瓷的，而陶瓷面盆很容易会出现划痕情况。那么，陶瓷面盆有划痕怎么办呢？我们一起来看看吧。 1、陶瓷金属修补剂 陶瓷金属搪玻璃修补剂搪瓷反应釜修补剂（劲素成）JS916是一种高分子合金修补剂，主要用于搪玻璃设备及其零部件表面衬层局部损坏的修复。搪瓷反应釜修补剂修补剂的特点不仅在于其耐磨蚀和耐腐蚀性能高，还在于搪瓷反应釜修补剂快速修复能力。搪瓷反应釜修补剂几乎可以在生产流水线不停状况下对损坏设备进行现场常温快速修复。该搪瓷反应釜修补剂有磁性但不导申，搪瓷反应釜修补剂的最高使用温度可达230 ℃。 2、陶瓷金属修补技术 （1）表面处理清除蚀损部位的积附物，用角向或直柄砂轮机打磨待修补部位，原则是“越毛糙越好”，最后用丙酮或酒精清洗脱脂（不允许再用手、物触摸）。 （2）配料将基料和固化剂按其配比倒出在工作板上，充分混合均匀成为深色胶料。 （3）将配好的胶料用胶料刮刀均匀涂敷在修补部位表面，刮实赶尽气泡，确保表面与修补剂密实接触，20 - 30 ℃固化2 小时。 （4）固化在20 一30 ℃条件下，3 ~ 5 小时可进行机械加工，完全固化需24小时以上。涂层厚温度高则固化时间可缩短。 （5）处理可利用辨听敲打声音来检查固化效果。使用过的工具应即时用清洁剂清洗。 以上就是妈网百科介绍有关陶瓷面盆有划痕怎么办的相关内容了。总而言之，陶瓷金属修补剂在反应釜、塔节等设备上的使用，效果很好，其简便实用性能不仅为贵公司节约了大量人力物力，也带来了可观的经济效益。希望本文可以帮助到大家。 怀孕8周孕囊小怎么办 怀孕8周的时候，已经到了孕两个月的时候。这个时候的孕囊已经发育得比较大了，可以在b超中看到孕囊了。但是有的时候怀孕8周孕囊会出现偏小的情况。这种情况到底应该怎么办呢？怀孕8周孕囊到底多大算是正常的呢？ 孕囊偏小怎么办？ 首先，由于情绪紧张等原因导致孕妇月经推迟、排卵期错后、受孕时间晚，从而出现孕囊较实际停经天数小。 例如，停经50天，但检查中却发现孕囊仅有40天左右大小。这种孕囊偏小属正常情况，只要经一周动态检查显示绒毛膜促性腺激素及孕酮值正在逐渐增多，孕囊在继续生长，并且逐渐出现了胎芽和胎心，即说明孕囊偏小是由于排卵期错后、受孕时间晚等生理性原因所致，可继续妊娠。 其次，由于精子、卵子发育不良，孕妇在孕期感染支原体、衣原体、风疹病毒或孕妇在怀孕期间接触到有毒有害物质等原因，导致孕囊发育不良，小于正常月份。出现以上情况的孕妇在妊娠期随着时间的推移孕囊会继续长大，但见不到胎芽和胎心，这种情况下的孕囊是不健康的，最终会导致孕妇流产。 怀孕八周孕囊多大正常？ 1、7周：胎儿长到1.33厘米，胚胎已具有人雏形，体节已全部分化，四肢分出，各系统进一步发育。B超清楚看到胎芽及胎心跳，胎囊约占宫腔的l/3。 2、8周：胎儿长到1.66厘米，胎形已定，可分出胎头、体及四肢，胎头大于躯干。B超可见胎囊约占官腔1/2，胎儿形态及胎动清楚可见，并可看见卵黄囊。
F系列搪瓷反应釜
F系列搪瓷反应釜 部件名称 罐内 夹套填料密封机械密封 设计压力 (Mpa)0.20.40.6设计温度( °C )200200200工作温度( °C )0 - 180 高电压实验 (KV)20 瓷层厚度 (mm)0.8 - 2.0 耐温差急变性( °C )冷冲击110 热冲击120
闭式搪瓷反应釜外型尺寸及其参数表： 系列F系列搪瓷反应釜 型号F3000 F5000 F6300 F8000 F10000 F12500 F16000 F20000 F30000 公称容积(L) 3000 5000 6300 8000 10000 12500 16000 20000 30000 计算容积(L) 3100 5050 6866 9060 11670 13651 17446 21790 33500 换热面积(m2) 8.61 13.16 16.10 18.38 21.35 24.89 29.48 34.04 45.36 主要尺寸（mm）D1 1600 1750 1750 2000 2200 2200 2400 2600 3000 D2 1750 1900 1900 2200 2400 2400 2600 2800 3200 D3 1964 2152 2152 2507 2708 2708 2912 - - D4 - - - - - - - 2000 2300 H1 195 195 195 210 210 210 210 210 210 H2 2215 2860 3244 3310 3533 4053 4346 4641 5340 H3 1050 1200 1200 1200 1300 1300 1400 - - H4 1326 1326 1475 1542 1880 1880 1880 1880 2200 H 3850 4500 5020 5220 5780 6300 6590 6890 7900 H0 - - - - - - - 7326 8500 传动装置型号BLD-3 BLD-4 BLD-4 BLD-4 BLD-5 BLD-5 BLD-6 BLD-6 BLD-7 搅拌转速(转/分) 浆式130 130 130 130 130 130 130 130 130 叶轮式130 130 130 130 130 130 130 130 130 搪瓷管口 a 300×400300×400300×400300×400300×400300×400300×400450 450 b 125 125 125 200 200 200 200 250 250 c 100 125 125 200 200 200 200 200 200 d 100 125 125 150 150 150 150 150 150 e 125/灯125/灯125/灯125/灯125/灯125/灯125/灯125/灯125/灯 f 125 150 150 150 150 150 150 150 150 g 100 125 125 150 150 150 150 150 150 h 125 150 150 150 150 150 150 150 150 k - - - - 200 200 200 200 200 m - - - 125 125 125 125 125 125 放料口125 125 125 125 150 150 150 150 150 夹套管口 进出口3-65 3-65 3-65 3-65 4-80 4-80 4-100 4-100 4-100 喷嘴口2-65 3-65 3-65 3-65 3-80 3-80 3-100 3-100 3-100 参考重量 kg 3500 4950 5400 7600 8800 10300 13800 14700 22200 注意：以上参数符合HG5-251-79标准 K系列搪瓷反应釜
搪瓷反应釜破损了自己来修补!
搪瓷反应釜局部损坏现场修补 搪瓷釜的破损原因： 搪瓷釜是将含硅量高的瓷釉喷涂到低碳钢胎表面，经900℃左右的高温焙烧，使瓷釉密着于金属钢胎表面而形成，由于这两种材料的机械性能和物理性能各不相同，因此搪瓷釜的破损原因也多样，一般有以下主要原因： 1)机械损坏 搪瓷表面硬而脆，机械强度很低，表面硬度比较大，抗冲击力非常差，任何金属、硬物对其进行撞击均会导致搪瓷破损。 2)热应力损坏 热应力损坏主要是由于瓷层和金属坯体的热膨胀系数存在巨大的差异而引起的。因金属坯体的热膨胀系数大于瓷层的热膨胀系数，这就意味着在常温下瓷层总是存在着残余的应力。因此搪瓷釜的工作温度对搪瓷釜的使用影响很大，受生产工艺中的冷热变化大影响，而使搪瓷产生的应力超过其使用应力，搪瓷将被破坏，极易爆瓷。 3)加工应力损坏 在釜体加工过程中，由于卷筒、冲压、焊接产生大量的内应力。这些应力在搪瓷前如消除不彻底，会导致搪瓷爆瓷。这一现象往往也会出现在设备运输、安装的过程中。 4)静电穿刺 搪瓷釜内搅拌带有悬浮物的液体时会产生强烈的磨擦，同时悬浮物自身也产生磨擦，这样就产生大量的静电荷，对搪瓷产生强烈的穿刺作用，从而导致搪瓷点蚀。 5)基体材料不合格 为了降低成本，个别生产企业降低金属胎体材质，直接导致钢材中的碳、硫在搪烧过程气化，使搪瓷层与基体间、搪瓷层内部形成大量气泡，导致搪瓷结合强度降低。 6)搪烧质量欠佳 有的搪瓷釜生产厂家生产环境简陋、除锈防尘达不到标准，致使底釉与基体结合不好。 有的减少搪烧遍数，增加每层厚度，使内应力过大，影响搪瓷釜使用寿命。 搪瓷釜修复工艺及控制 1)材料的选择： 搪瓷设备修复需根据腐蚀部位尺寸、介质、温度来选择适合的高分子复合材料，并选
衬胶修补剂在电厂凝汽器水室衬胶修复
设备问题：凝汽器水室衬胶随着使用时间的延长，出现局部衬胶鼓包、破裂、破损。 问题危害：如不及时修补，海水渗入粘接面腐蚀金属基体，使衬胶脱层，加大了海水与金属面的接触，使金属基体腐蚀加大的恶性循环，造成泄漏。 解决方案：现场快速修补修复，不动火施工，达到好的修复效果。 应用材料： 1、翌坤胶业衬胶修补剂YK-937是一种专门设计的高性能衬胶修复材料，对金属及原衬胶基体有着极强的结合性，固化后具有优异的抗腐蚀、抗磨蚀、抗冲刷性能。 2翌坤胶业衬胶修补剂YK-937，是一种专门设计的高性能内衬涂层材料，用于重建被介质腐蚀损坏的金属防护系统。对各种金属及非金属材料有着极强的粘接力，固化后有着优异的抗磨蚀、抗腐蚀性能。 施工方案： 1、挖掉鼓包、破裂部位的衬胶，与金属面脱离的衬胶须全部铲除； 2、基体表面处理； 3、翌坤胶业衬胶修补剂YK-937做底涂，浸润基体表面； 4、翌坤胶业衬胶修补剂YK-937做修补，重建缺失部位的衬胶； 5、表面再涂覆一道翌坤胶业衬胶YK-937（内衬涂层材料），以形成光滑致密的表面； 6、养护固化。 修复效果： 方案特点：现场不动火，修复快捷，成本低廉，工艺简单，效果优异。 技术咨询：如有任何疑问，欢迎来电咨询。 【以下产品为您排忧解难】 耐腐蚀修补剂品名耐腐蚀修 补剂修补 剂使用温 度 耐腐蚀修补剂特点及应用 耐腐蚀修补剂YK-8406 -60～160 YK-8406耐腐蚀修补剂是以陶瓷粉末为骨材的高性能高密度的防腐材 料，双组份，低粘度，可刷涂，耐强酸、强碱。用于修复受腐蚀的泵、 阀、管道、热交换器端板、贮槽、油槽,搪瓷反应釜交换器的修复， 等，并可做大面积预保护涂层。 耐腐蚀修 补剂YK-8416 -60～160 Yk-8416耐腐蚀修补剂是以陶瓷粉末为骨材的高性能高密度的防腐材 料，双组份，胶泥状，立面不流淌，耐强酸、强碱。用于修复受腐蚀 的泵、阀、管道、热交换器端板、贮槽、油槽等，并可做大面积预保 护涂层。 耐腐蚀修 补剂YK-8436 -60～160 YK-8436耐酸修补剂是以陶瓷粉末为骨材的高性能高密度的防腐材 料，双组份，在化学介质中具有优异的热稳定性、机械性能和耐腐蚀 性。适用于烟气脱硫系统、电解槽、化工设备、污水处理系统、石油 储罐等设备的修复及预保护涂层的制备。 耐腐蚀修补剂YK-8402 -60～150 高温搪瓷反应釜修补剂是由精细碳化硅填料与改性增韧耐热树脂进行 复合得到的高性能耐磨抗蚀聚合材料。专用于搪瓷反应釜衬里破损的 修补和防护，可有效抵御酸（含氢氟酸）、碱及物料的侵蚀和冲刷磨损。 产品是选用改性增韧耐热树脂复合得到的耐温抗蚀聚合材料。完全固 化后的耐磨防腐涂层可有效抵御以下介质侵蚀：碳酸、10%氢溴酸、 20%亚硝酸、20%的硝酸、30%硫酸、15%磷酸、30%氨水、石灰水、
搪瓷反应釜厂家
搪瓷反应釜是将含高二氧化硅的玻璃，衬在钢制容器的内表面，经高温灼烧而牢固地密着于金属表面上成为复合材料制品。所以，它具有玻璃的稳定性和金属强度的双重优点，是一种优良的耐腐蚀设备。 搪瓷反应釜，分开式和闭式两种结构，开式为体盖分离，中间用垫子和卡子连接起来，一般是容积在5000L以下；闭式为体盖一体，一般容积在5000L以上。这两种结构各有优势，开式拆卸比较方便，如果罐盖上的管口出现问题，则易于拆下单独修理，而闭式则密封性能要好。一般来说，开式结构还有平焊对接式法兰连接和平盖式两种。 搪瓷反应釜经900℃高温焙烧，冷却后搪瓷与钢板粘结在一起。由于搪瓷的线膨胀系数和延伸率小于钢板，因此冷却后搪玻璃的变形量小于钢板的变形量，搪瓷受到钢板的约束产生压应力。搪瓷釜制成后，其搪玻璃即存在预压缩应力，而钢板则存在预拉伸应力。由于预应力与线膨胀系数和延伸率相关，线膨胀系数和延伸率与温度又密切
相关，因此搪瓷釜的工作温度对搪瓷釜的使用影响很大。如果因温度变化大而使搪瓷产生的应力超过其使用应力，搪瓷将被破坏。 因此搪瓷釜搪瓷层遇冷、热急变，极易爆瓷。因此搪瓷釜有耐温限制温度200℃，耐温急变冷冲击<11O~C，热冲击<120℃。投料时物料温度与釜体温差太大以及升温时蒸汽过猛、降温太急也能导致爆瓷。因此搪瓷釜在使用中升、降温要缓慢、均匀，分级冷却。 搪瓷设备的质量除了与瓷釉的好坏有关系外，还与搪瓷设备所选用喷涂技术有重要的关系。简单来说，冷喷是搪瓷设备的毛坯在冷却常温状态下进行的喷粉作业，热喷则是搪瓷设备毛坯在未完全冷却即达到可工作状态下进行的喷粉作业。冷喷便于工人对钢坯及瓷粉的一次次的修磨及精细化作业，且瓷粉中水份自然干燥，此技术作业下的
搪瓷反应釜清洁规程
目 的：建立生产车间搪瓷反应釜清洁标准操作规程，清洗周期及使用周期， 规范搪瓷反应釜清洁操作，确保防止物料在生产过程中造成交叉污 染或物料损失。 适用范围：生产车间搪瓷反应釜使用工序 责 任 人：搪瓷反应釜操作人员、车间班组长 程 序： 清洗程序： 1、 先用饮用水对反应釜进行冲洗，若发现反应釜有无法冲掉的物料，应采 用人工机械清理，如用毛刷刷洗。 2、 向反应釜饮用水至反应釜变口垫，加氢氧化钠（或盐酸）至溶液浓度为 0.02mol （3000L 反应釜加氢氧化钠2400g 、加盐酸6L ；2000L 反应 釜加氢氧化钠1600g 、加盐酸4L ，1000L 反应釜加氢氧化钠1600g 、 加盐酸2L ，500L 反应釜加氢氧化钠800g ，加盐酸1L 。）升温至80℃ 左右，保温搅拌30分钟后，打开下料阀，经物料循环泵，清洗物料 管道15--20分钟。 .3、 用300L 左右饮用水淋洗反应釜壁至淋洗液为中性。 .4、 将反应釜进料阀、出料阀撤下后反复用饮用水冲洗洁净。 .5、 清洗检查：用1000ml 烧杯取清洗水目测有无杂质，和用试纸测清 洗水是否为中性；同时用白绸布或棉签擦拭反应釜底部下料口凹处、 边口垫，釜盖法兰凹处及搅拌交叉处，看是否有异物，否则要重新 清洗，直到检查合格。 6、当一个生产批次的产品完成后，在车间清场的同时应按照清洗程序对 反应釜进行清洗，如果反应釜清洗后超过24小时未使用，在使用前 应用饮用水进行冲洗并检查合格后使用。 文 件 名 搪瓷反应釜清洁程序 制 定 人 年 月 日 文件编号 BSX ／SOP-SC -14-2014 审 核 人 年 月 日 版 本 号 00 批 准 人 年 月 日 生效日期 年 月 日 办 公 室□ 质检部□ 生产部□ 库 房□ 技术开发部□ 销售部□ 财务部□ 供应部□
高分子复合材料修复木糖车间搪瓷釜破损(图文)
高分子复合材料修复木糖车间) 图文(搪瓷釜破损 高分子复合材料修复木糖车间搪瓷釜破损对磨损源和现场修【摘要】采用新型高分子复合材料对搪瓷釜破损进行现场修复； 复的优势进行了分析，并提出了预防设备故障的改进措施。现场修复高分子复合材料【关键词】搪瓷釜破损设备简介1. 经高温灼烧而牢固搪瓷反应釜是将含高二氧化硅的玻璃，衬在钢制容器的内表面，它具有玻璃的稳定性和金属强度的双重地密着于金属表面上成为复合材料
制品。所以，优点，是一种优良的耐腐蚀设备。中间用垫子和卡子连接起开式为体盖分离，搪瓷反应釜，分开式和闭式两种结构，以上。这两种结 5000L5000L来，一般是容积在以下；闭式为体盖一体，一般容积在构各有优势，开式拆卸比较方便，如果罐盖上的管口出现问题，则易于拆下单独修理，而闭式则密封性能要好。一般来说，开式结构还有平焊对接式法兰连接和平盖式两种。搪玻璃反应釜广泛地应用于化工、石油、医药、农药、食品等工业。为了保证搪玻 璃设备正常使用，现将其主要性能和安设备问题与原因分析2.使瓷℃左右的高温焙烧，经900搪瓷釜是将含硅量高的瓷釉喷涂到低碳钢胎表面，因此由于这两种材料的机械性能和物理性能各不相同，釉密着于金属钢胎表面而形成，2）。(搪瓷釜的破损原因也多样见图由于搪瓷（搪玻璃）表面硬而脆，机械强度很低，表面硬度比较大，受到冲击力的 作用即行破碎、再加上化学液体的腐蚀导致罐体受损。设备在运输、安装的过程中，常常导致搪瓷表面出现脱瓷现象，造成罐体腐蚀甚至穿孔，无法使用。页 8 共页 2 第 一般有以下几种原因：1、机械损坏.搪瓷抗冲击力非常差，任何金属、硬物对其进行撞击均会导致搪瓷破损。在安装 因此搪瓷釜使用过程直接敲击搪瓷釜釜体，拆卸搪瓷釜附属设备时，会导致搪瓷破损。中严防任何金属、硬物掉进釜内，如遇堵料，必须用塑料棒疏通，检修时盖好锅盖，严防焊渣熔化瓷面出现小坑或爆瓷。、工作温度影响2由于搪瓷 的线膨胀900℃高温焙烧，冷却后搪瓷与钢板粘结在一起。搪瓷反应釜经搪瓷受到钢板系数和延伸率小于钢板，因此冷却后搪玻璃的变形量小于钢板的变形
搪瓷反应釜破损原因及如何快速修补
几种原因： （一）机械损坏 或爆瓷。 （二）热应力损坏 搪瓷釜经900 耐温限制：温度200 （三）加工应力损坏
理能防止爆瓷。 （四）静电穿刺 搪瓷釜内搅拌带有悬浮物的液体，悬浮物与搪瓷强烈的磨擦，同时悬浮物自身也产生磨擦，这样就产生大量的静电荷，高的静电荷对搪瓷产生强烈的穿刺作用，从而导致搪瓷点蚀，因此搅拌转速不宜太快。（五）析氢腐蚀 搪瓷釜的夹套在使用一段时间后会结垢和生锈，如果使用酸性除垢剂清除污垢或夹套中的冷却液偏酸性，都会导致金属发生析氢腐蚀(Fe+2HCI=FeC12+H2O一部分H原子扩散到金属内空穴，结合成}b，这些H：由于搪瓷的致密性而不能再向外扩散，因此当Hz聚积到一定的程度，形成定的动力时，搪瓷就会发生破裂。 因此清洗结垢采用酸洗时，必须加缓冲剂，如果搪瓷釜的价值较高或者不容易更换甚至出现腐蚀性穿孔的话，必须采用腐蚀率低的高品质清洗剂，避免清洗操作不当带来的严重后果，比如“福世泰克”清洗剂等就可以实现极低腐蚀下的水垢清洗。 （六）基体材料不合格 为了降低成本，有些厂家胚体采用Q235钢代用，直接导致钢材中的碳、硫在搪烧过程气化，使搪瓷层与基体间、搪瓷层内部形成大量气泡，导致搪瓷结合强度降低。搪瓷层遇冷热急变，极易爆瓷。所以搪瓷釜选用含碳、硫低的钢材做胚体能防止爆瓷。 （七）搪烧质量欠佳 有些搪瓷釜生产厂家生产环境简陋、除锈防尘达不到标准，致使底釉与基体结合不好。有的减少搪烧遍数，增加每层厚度，使内因力过大，影响搪瓷釜使用寿命。因此严格按制造规程制造才能保证搪瓷釜的质量。 三．搪瓷釜的修复 搪瓷釜大面积搪瓷损坏，需将设备送制造厂重新搪瓷，费用约是新购置的1／4。损坏面积不大的可在现场进行局部修补。采用现场快速修复，不用拆设备，只需打开人孔即可修复，修复后24小时即可投入使 用。现场修补剂有环氧树脂、聚四氟乙烯树脂、高性能搪瓷修补剂等。下面介绍的是福世蓝高分子复合材料搪瓷修补剂修复搪瓷釜的方法。 （一）高性能搪瓷现场修补剂 福世蓝高分子复合材料搪瓷现场修补剂是由高分子聚合物、合金钢粉末或耐磨陶瓷粉末为基材并配以固化剂的双组份复合材料。与普通树脂型的修补剂相比，高分子复合材料依靠自身更为细密的高分子结构，使得材料自身具有更强的粘接力和优异的耐腐蚀、抗腐蚀性能，高分子甚至能够渗透到金属里面，形成更
搪玻璃反应釜介绍
搪玻璃反应釜介绍 搪玻璃反应釜作为化工行业里常用的设备，具有非常好的耐用性和抗腐蚀性，但要想使其能够正常发挥功效，就要先确保其配件能够正常使用，不然一旦有一个配件无法使用都会导致反应釜无法正常运转。那么话说回来，该反应釜都有哪些配件呢？ 搪玻璃反应釜的构成是由反应容器、搅拌器及传动系统、冷却装置、安全装置、加热炉等组成。 1、釜体、釜盖采用不锈钢加工制成，釜体通过螺纹与法兰联接，釜盖为正体平板盖，两者由周向均布的主螺栓、螺母紧固联接。 2、高压釜主密封口采用A型的双线密封，其余密封点均采用圆弧面与平面、圆弧面与圆弧面的线接触的密封形式，依靠接触面的高精度和光洁度，达到良好的密封效果。 3、搪玻璃反应釜的釜体外装有桶型碳化硅炉芯，电炉丝穿于炉芯中，其端头由炉壳侧下部穿出，通过接线螺柱，橡套电缆与控制器相连。 4、釜盖上装有压力表，膜安全装置，汽液相阀，温度传感器等，便于随时了解釜内的反应情况，调节釜内的介质比例，并确保安全运行。 5、联轴器主要由具有很强磁力的一对内、外磁环组成，中间有承压的隔套。搅拌器由伺服电机通过联轴器驱动。控制伺服电机的转速，便可达到控制搅拌转速的目的。 6、隔套上部装有测速线圈，连成一体的搅拌器与内磁环旋转时，测速线圈便产生感应电动势，该电势与搅拌转速相应，该电势传递到转速表上，便可显示出搅拌转速。 7、搪玻璃反应釜的磁联轴器与釜盖间装有冷却水套，当操作温度较高时应通冷却水，以及磁钢温度太高而退磁。 8、轴承采用不锈钢轴承或高强电化石墨，耐摩损，维修周期长。 所以通过上文相信大家可以了解到搪玻璃反应釜的组成配件都有什么，从而不管是在安装、使用还是检修的时候都可以帮助自己很好的进行工作。并且大家要明白，要想更好的操控使用反应釜设备，就要多方面的去了解该设备哦。
搪瓷
搪瓷反应釜基础知识 搪瓷反应釜是将含高二氧化硅的玻璃，衬在钢制容器的内表面，经高温灼烧而牢固地密着于金属表面 搪瓷反应釜上成为复合材料制品。它具有玻璃的稳定性和金属强度的双重优点，是一种优良的耐腐蚀设备。 搪瓷反应釜，分开式和闭式两种结构，开式为体盖分离，中间用垫子和卡子连接起来，一般是容积在5000L以下;闭式为体盖一体，一般容积在5000L以上。 搪玻璃反应釜广泛地应用于化工、石油、医药、农药、食品等工业。为了保证搪玻璃设备正常使用，现将其主要性能和安装、使用注意事项说明如下： 1、使用压力：0.2---0.4Mpa 2、耐酸性：对各种有机酸、无机酸、有机溶剂均有较好的抗蚀性。如将我厂生产的搪玻璃试样置于20%HCI溶液中煮沸48h，腐蚀速率为0.9g/m2.d(优等品指标为1.0g/m2.d)。 3、耐碱性：搪玻璃对碱性溶液抗蚀性较酸溶液差。但将我厂搪玻璃试样置于1N氢氧化钠溶液腐蚀，试验温度80℃时间48h。腐蚀速率为6.76g/m2.d(优等品指标为7.0g/m2.d)。 4、操作温度：搪玻璃设备加热和冷却时，应缓慢进行。我厂制造的搪玻璃设备使用温度为0-200℃，耐温急变性≥200℃。 5、瓷层厚度：玻璃设备的瓷层厚度0.8-2.0mm，搪玻璃设备附件的瓷层厚度 0.6-1.8mm。 6、耐压电：搪玻璃具有良好的绝缘性，当搪玻璃在规定厚度内用20KV高频电火花检查瓷层时，高频电火花不能击穿瓷层。 7、耐冲击性：玻璃层的内应力越小，弹性越好，硬度越大，抗弯抗压强度越高，则耐冲击就越好。玻璃层在规定厚度内，用直径30mm，重量112g钢球冲击时，其冲击功为282×10-3J(优等品指标为260×10-3J)。 反应釜是化工、医药等行业关键设备之一。在高温、浓酸腐蚀工况下，釜体内部通常采用搪瓷工艺保护基体。 含高二氧化硅的玻璃，衬在钢制。由于这两种材料的机械性能和物理性能各不相同，因此搪瓷釜的破损原因也多样，一般有以下几种原因： （一）机械损坏
金属铸件金属修补剂在工业方面的应用案例
金属铸件金属修补剂在工业方面的应用案例 金属铸件在铸造成型的时候由于模具，设备，人为因素等原因而造成砂眼，气孔，缩松，夹碴，裂纹等缺陷，严重影响铸件质量，造成浪费。但是基于金属材料流动性较差、热胀冷缩以及铸造工艺的局限性，铸造缺陷很难避免。耀日康金属修补系列产品是以金属及合金为骨材的聚合金属复合型修补材料，在铸造业的广泛使用，为众多客户挽救了大量不合格品，真正实现铸造零缺陷。 铸造缺陷修补剂： 图一YK-3301铸件缺陷修补剂修补及缺陷大于2mm的铸件 图二YK-3302铸件缺陷修补剂修补及缺陷小于2mm的铸件 铁质修补剂，钢质修补剂，铝质修补剂，铜质修补剂： 可针对不同的铸件选择相应的修补剂进行修补,与金属结合强度高,可以进行机加工,颜色可保持与被修基体一致。 图四：使用YK-3311铸铁修补剂对发动机液力变矩器壳体的铸造缺陷进行修补。 图五：使用YK-3312钢质修补剂对发动机缸体的铸造缺陷进行修补。 图六：使用YK-3313铝质修补剂及YK-3315聚合铝对发动机缸体的铸造缺陷进行修补。图七：使用YK-3314铜质修补剂对镏金的工艺品进行修补。 以上我我公司的金属修补剂在金属铸件，有缺陷的金属零件修补剂的一些案例，金属修补剂的好坏直接影响到缺陷的金属铸件等美观和质量，目前市场上金属修补剂层次不齐，客户在挑选的时候一定要谨慎。 以上信息来源于翌坤胶业官网，如需了解更多可登陆或者联系我司工程 麻城翌坤胶业有限公司长期供应高温胶，工业修补剂，发动机缸体修补剂，搪瓷反应釜修补剂，高温修补剂，导电金属修补剂，电镀胶，电泳修补剂，耐磨修补剂，耐腐蚀修补剂，高温密封胶，衬胶修补剂，高温导电胶，液压缸修补剂，导轨磨损修补剂，环氧树脂胶水胶粘剂品!