(新)中德材料牌号对照表

中德金属材料对照表_2007

Comparison of German and Chinese material designations, Basic SN359 No guarantee in respect of completeness and substitution of materials!ATE2 Standardisiation department kuwe@https://www.360docs.net/doc/ff18484016.html, Material designation Basis SN359Material No. Former designation Standard Remark Material designation Standard Title Remark Matching of properties: E295 1. 0050St 50-2DIN EN 10025-2 -Q275 Z GB 700-88Unalloyed engineering steels C content 0.28 to 0.38%, only limited weldability, Z = Fully killed steel only is permissible,identical E335 1. 0060St 60-2DIN EN 10025-2 -Q 345 A GB T 1591-94High strength low alloy structural steels Fully killed steel is permissible identical E360 1. 0070St 70-2DIN EN 10025-2 -Q 390 A GB T 1591-94High strength low alloy structural steels Fully killed steel is permissible identical S235JR 1. 0038St 37-2 R St 37-2 S235JRG2DIN EN 10025-2KV at room temperature, unkilled not permitted Q 235 B GB 700-88 Unalloyed engineering steels Fully killed steel is permissible identical S235J0 1. 0114R St 37-3 S235J0G2DIN EN 10025-2KV at 0°C, unkilled not permitted Q 235 C GB 700-88Unalloyed engineering steels Fully killed steel only permissible, KV at 0°C ,similar S235J2 1. 0117Q St 37-3N S235J2G3DIN EN 10025-2KV at -20°C, unkilled not permitted Q 235 D GB 700-88Unalloyed engineering steels Fully killed or double-killed steel is permissible, KV at -20°C ,similar S275JR 1. 0044St 44-2 S275JRG2 S275JRC DIN EN 10025-2KV at room temperature, unkilled not permitted Q 275 Z GB 700-88Unalloyed engineering steels C content must be limited to 0.22%, otherwise only limited weldability, notch impact energy not guaranteed.similar Q 275 GB 700-88Unalloyed engineering steels C content must be limited to 0.22%, notch impact energy not guaranteed.do not use Q 345 C GB T 1591-94High strength low alloy structural steels Fully killed steel is permissible, KV at 0°C, similar Q 275GB 700-88Unalloyed engineering steels C content must be limited to 0.22%, notch impact energy not guaranteed. do not use Q 345 D GB T 1591-94High strength low alloy structural steels Fully killed steel is permissible, KV at -20°C., identical S355JR 1. 0045 -DIN EN 10025-2KV at room temperature, unkilled not permitted Q 345 B GB T 1591-94High strength low alloy structural steels Fully killed steel is permissible, identical S355J0 1. 0553S355J0G2DIN EN 10025-2KV at 0°C, unkilled not permitted Q 345 C GB T 1591-94High strength low alloy structural steels Fully killed steel is permissible, KV at room 0°C,identical S355J2 1. 0569S355J2G3DIN EN 10025-2KV at -20°C, unkilled not permitted Q 345 D GB T 1591-94High strength low alloy structural steels Fully killed steel is permissible, KV at -20°C.,identical S355N 1. 0545StE 355DIN EN 10025-3normalised, KV at -20°C,Q 345 D GB T 1591-94High strength low alloy structural steels KV at -20°C similar S355NL 1. 0546TStE 355DIN EN 10025-3normalised KV at -50°C,Q 345 E GB T 1591-94High strength low alloy structural steels KV at -40°C !similar S420N 1. 8902StE 420DIN EN 10025-3normalised KV at -20°C,Q 420 D GB T 1591-94High strength low alloy structural steels KV at -20°C !similar S420NL 1. 8912TStE 420DIN EN 10025-3normalised KV at -50°C,Q 420 E GB T 1591-94High strength low alloy structural steels KV at -40°C !similar S460N 1. 8901StE 460DIN EN 10025-3normalised KV at -20°C,Q 460 D GB T 1591-94High strength low alloy structural steels KV at -20°C !similar S460NL 1. 8903TStE 460DIN EN 10025-3normalised KV at -50°C,Q 460 E GB T 1591-94High strength low alloy structural steels KV at -40°C !similar German Chinese Engineering steels Fine-grained engineering steels, weldable DIN EN 10025-2Status: 01.05.2007 in progress KV at 0°C, unkilled not permitted S275J2 1. 0145St 44-3N S275J2G3 S275J2G3C S275J2G4DIN EN 10025-2KV at -20°C, unkilled not permitted S275J0 1. 0143St 44-3

中德材料对照表1

中德常用金属材料对照表Comparison List For Standard Material 一、普通碳素结构钢Carbon structure steel Page 1 of 15 *Remark:20MnMo will be used for forged material

一、碳素结构钢Carbon structure steel Page 2 of 15 （a）V：调质处理quenching and tempering； （b）①为调质处理时参数parameter after quenching and tempering。

一、碳素结构钢Carbon structure steel Page 3 of 15 注：N：正火。 Note:N-normalizing

二、合金结构钢Alloy structure steel Page 4 of 15 Note： ① For section ≤100,QT；② When section≤ 120，QT；③When section is 15，QT；④ When section is 25，QT；⑤ When section is 30，QT。* If the bill of material(b.o.m) will not request the “V”(quench and temper) the material will be converted without the +QT by CMMP If the material “+QT” will not be available, CMMP will do the quenching and tempering to reach the requested material properties.

钢材表-中德对照表

摘要:钢材表-中德对照表 优质碳素结构钢 中国德国材料分组 Y15 10S20(1.0721) 抗拉强度〈700MPa Y20 22S20(1.0724) 抗拉强度〈700MPa Y30 35S20(1.0726) 抗拉强度〈700MPa 优质碳素结构钢 中国德国材料分组 10 CK10(1.1121) 抗拉强度〈700MPa 15 C15(1.0401),CK15(1.1141),Cm15(1.1140) 抗拉强度〈700MPa 35 C35(1.0501),CK35(1.1181),Cm35(1.1180) 抗拉强度〈700MPa 45 C45(1.0503),CK45(1.1191),Cm45(1.1201) 抗拉强度700MPa~1000MPa 55 C55(1.0535),CK55(1.1181),Cm55(1.1209) 抗拉强度700MPa~1000MPa 60 C60(1.0601),CK60(1.1221),Cm60(1.1223) 抗拉强度700MPa~1000MPa 15Mn 17Mn4(1.8044) 抗拉强度〈700MPa 40Mn 40Mn4(1.5038) 抗拉强度700MPa~1000MPa 合金结构钢 中国德国材料分组 30Mn2 28Mn6(1.5065),30Mn5(1.5066) 抗拉强度〈700MPa 35Mn2 36Mn5(1.5067) 抗拉强度〈700MPa 35SiMn 37MnSi5(1.5122) 42SiMn 46MnSi4(1.5121) 15MnV 15MnV5(1.5213) 42Mn2V 42MnVT(1.5223) 35Cr 34Cr4(1.7033),37Cr4(1.7034) 抗拉强度700MPa~1000MPa 40Cr 41Cr4(1.7035) 抗拉强度1000MPa~1300MPa 15CrMn 20MnCr4(1.7147) 抗拉强度700MPa~1000MPa 20CrV 22CrV4(1.7513) 40CrV 42CrV6(1.7561) 50CrV 50CrV4(1.8159) 抗拉强度1000MPa~1300MPa 16Mo 15Mo3(1.5415) 抗拉强度〈700MPa 12CrMo 13CrMo44(1.7335) 抗拉强度〈700MPa 15CrMo 16CrMo44(1.7337) 抗拉强度700MPa~1000MPa 20CrMo 25CrMo4(1.7218) 抗拉强度700MPa~1000MPa 30CrMo 34CrMo4(1.7220) 抗拉强度1000MPa~1300MPa 35CrMo 34CrMo4(1.7220) 抗拉强度1000MPa~1300MPa 42CrMo 42CrMo4(1.7225) 抗拉强度1000MPa~1300MPa 38CrMoAl 34CrAlMo5(1.8507) 抗拉强度700MPa~1000MPa 15CrMnMo 15CrMo5(1.7262) 抗拉强度700MPa~1000MPa 20CrMnMo 20CrMo5(1.7264) 抗拉强度700MPa~1000MPa 24CrMoV 24CrMoV55(1.7733) 12CrNi3A 14NiCr10(1.5732) 抗拉强度〈700MPa

中德钢材牌号对照

机械加工中德钢材牌号对照 https://www.360docs.net/doc/ff18484016.html, CNC数控机械加工,瑞典三坐标测量机自动测量,零件出口德国瑞士,提供可靠的信赖协作德国牌号中国牌号德国牌号中国牌号 1.0035Q195 1.0517C46D2 1.0038Q235C48D2 1.0038Q235qC 1.0518C56D2 1.0044Q275 1.052830/Mn 1.0045Q345qC 1.053555 1.0114Q235 1.054150 1.0117Q235/qD C42D2 1.0143Q275 1.0546Q345/qE 1.0145Q275 1.0553Q345 1.0213ML08Al 1.0577Q345/qD 1.021410 1.0586C50D2 ML10Al 1.0588C52D2 ML10 1.0596Q345 1.023415 1.060160/Mn ML15Al 1.0609C58D2 ML15 1.0611C62D2 1.0303ML04Al 1.0612C66D2/B 1.0304C8D265 1.031C10D2 1.0613C68D2 1.0311C12D2 1.061475 1.031205F C76D2 1.0319S210（1类） 1.0615C70D2 1.034708*70 1.040220/Mn 1.061685 1.040625C86D2 1.041120 1.0617C72D2 ML20Al 1.0618C92D2 ML20 1.0622 80 1.0413C15D2C80D2 1.0414C20D2 1.0626C82D2 1.041525Mn 1.0628C88D2 C26D2 1.0715Y15 1.0416C18D2 1.0718T15Pb 1.0434ML18 1.0722Y12Pb 1.0438HRB500 1.0725Y20 1.0459S245（1类）/（2类） 1.0726Y12/30/35 1.0466HRB500 1.1147ML18Mn 1.047320Mn2/A/E ML22Mn 1.0483S290（1类）/（2类） 1.1152ML25 1.0499S360（1类）/（2类） 1.1172ML35/Mn 1.050135/Mn 1.119145H 1.050345/Mn 1.1192ML45 1.051140/Mn 1.120145H 1.0516C36D2 1.40020Cr13Al C38D2 德国牌号中国牌号德国牌号中国牌号 1.40061Cr12/13 1.48282Cr21Ni2N 1Cr12Mo1Cr20Ni14Si2 1.4016ML1Cr17 1.4833 2Cr23Ni13 1Cr170Cr23Ni13 1.40212Cr13 1.48412Cr25Ni20 1.40241Cr13Mo 1.48451Cr25Ni20Si2 1.40283Cr13 1.48641Cr16Ni35 1.40314Cr13 1.48715Cr21Mn9Ni4N 1.40571Cr17Ni2 1.48780Cr18Ni10Ti 1.4105Y1Cr17 1.502655Si2Mn 1.41097Cr17 1.5502ML20B 1.41131Cr17Mo 1.5514ML35B 1.412511Cr17 1.551540B/A/E 9Cr18Mo 1.5525ML20MnB

中德钢材对照表

No guarantee in respect of completeness and substitution of materials!ATL2 Standardisation

No guarantee in respect of completeness and substitution of materials!ATL2 Standardisation

No guarantee in respect of completeness and substitution of materials!ATL2 Standardisation German Chinese Basis: SN 359 Material designation Mat. No. Former designat.Standard Remark Material designation Standard Title Remark Matching of properties: Qenched and tempered steels, unalloyed Quenched and tempered steels, unalloyed C22 +N 1. 0402 C 22 N DIN EN 10083-2normalised20GB 699-88Plain carbon quality steel identical C35 +N 1. 0501 C 35 N DIN EN 10083-2normalised35GB 699-88Plain carbon quality steel identical C35 +QT 1. 0501 C 35 V quenched & tempered35GB 699-88Plain carbon quality steel Agreement required for QT instead of normalising.similar C35E +QT 1. 1181Ck 35 V DIN EN 10083-1quenched & tempered35GB 699-88Plain carbon quality steel Agreement required for QT instead of normalising. Yield point similar at small nom. thickness differs from European material. C45 +N 1. 0503 C 45 N DIN EN 10083-2normalised45GB 699-88Plain carbon quality steel identical C45 +QT 1. 0503 C 45 V quenched & tempered45GB 699-88Plain carbon quality steel Agreement required for QT instead of normalising.similar C45E +QT 1. 1191Ck 45 V DIN EN 10083-1quenched & tempered45GB 699-88Plain carbon quality steel Agreement required for QT instead of normalising. Yield point similar at small nom. thickness differs from European material. C55 +QT 1. 0535 C 55 V DIN EN 10083-2quenched & tempered55GB 699-88Plain carbon quality steel Agreement required for QT instead of normalising.similar similar C55E +QT 1. 1203Ck 55 V DIN EN 10083-1quenched & tempered55GB 699-88Plain carbon quality steel Agreement required for QT instead of normalising. Yield point at small nom. thickness differs from European material. C60 +N 1. 0601 C 60 N DIN EN 10083-2normalised60GB 699-88Plain carbon quality steel identical Flame hardening steels Flame hardening steels Cf 35 V 1. 1183.05Cf 35 V DIN 17212quenched & tempered35GB 699-88Plain carbon quality steel Agreement required for QT instead of normalising.similar Cf 45 V 1. 1193.05Cf 45 V DIN 17212quenched & tempered45GB 699-88Plain carbon quality steel Agreement required for QT instead of normalising.similar Cf 55 V 1. 1213.05Cf 55 V DIN 17212quenched & tempered55GB 699-88Plain carbon quality steel Agreement required for QT instead of normalising.similar Quenched and tempered steels, alloyed Quenched and tempered steels, alloyed 25CrMo4+QT 1.721825 CrMo 4 V DIN EN 10083-1quenched & tempered30CrMo GB 3077-88Alloyed structural steels Heat treatment strength to be agreed upon similar 42CrMo4+QT 1.722542 CrMo 4 V DIN EN 10083-1quenched & tempered42CrMo GB 3077-88Alloyed structural steels Heat treatment strength to be agreed upon similar 50CrMo4+QT 1.722850 CrMo 4 V DIN EN 10083-1quenched & tempered50CrMo EZB 1184-93(Title not known) 34CrNiMo6+QT 1.658234 CrNiMo 6 V DIN EN 10083-1quenched & tempered34CrNi3Mo EZB 1184-93(Title not known) 30CrNiMo8+QT 1.658030 CrNiMo 8 V DIN EN 10083-1quenched & tempered30Cr2Ni2Mo EZB 1184-93(Title not known) Case hardening steels Case hardening steels 16MnCr5+TH 1.713116 MnCr 5 BF DIN EN 1008420CrMnTi GB 3077-88Alloyed structural steels 16MnCr JB T 6396-92Large forged piece of alloyed structural steel 20MnCr5+TH 1.714720 MnCr 5 BF DIN EN 1008420CrMnTi GB 3077-88Alloyed structural steels 20MnCr JB T 6396-92Large forged piece of alloyed structural steel 18CrNiMo7-6+TH 1.658717 CrNiMo 6 BF DIN EN 10084Not known Not known