改性芳纶与环氧树脂复合体的制备及其防刺性能
合集下载
- 1、下载文档前请自行甄别文档内容的完整性，平台不提供额外的编辑、内容补充、找答案等附加服务。
- 2、"仅部分预览"的文档,不可在线预览部分如存在完整性等问题,可反馈申请退款(可完整预览的文档不适用该条件!)。
- 3、如文档侵犯您的权益，请联系客服反馈,我们会尽快为您处理(人工客服工作时间：9:00-18:30)。
more excellent stab resistance.
Keywords plasma treatment; modified aramid fiber; surface treatment; aramid epoxy composite; stab
resistant material
随着人们对生活品质要求的不断提高,对其自
能。 结果表明:采用氧等离子体处理,在处理功率为 600 W、处理 18 min 时,织物表面纤维刻蚀明显,含氧基团增
多,润湿性提高,但织物拉伸强度有所下降;当环氧树脂涂覆在等离子体改性后的芳纶织物上,树脂中环氧基团与
芳纶中含氧活性基团键合牢固,复合体黏结强度较好,拉伸强度较未经处理的芳纶织物增加了 7.89%,复合体防穿
when the epoxy resin is coated on the plasma-modified aramid fabric, the epoxy group in the resin is
firmly bonded with the oxygen-containing active group in the aramid fiber and the bond strength of the
complex is better. The tensile strength is increased by 7. 89% and the tested composite stab resistance is
significantly improved compared with the conventional aramid 1414 fabric, the multi-layered structure has
刺效果较普通芳纶 1414 织物提升显著,且多层组合结构的防刺效果更优异。
关键词 等离子体; 改性芳纶; 表面处理; 芳纶环氧复合体; 防刺材料
中图分类号:TS 156 文献标志码:A
Preparation of modified aramid fiber and epoxy resin
2. Suzhou Gao Jia Protection Technology Co., Ltd., Suzhou, Jiangsu 215000, China)
Abstract In order to improve the stab resistance of aramid fabrics, oxygen plasma modified aramid 1414
(1. 安徽农业大学 轻纺工程与艺术学院, 安徽 合肥 230036;
2. 苏州高甲防护科技有限公司, 江苏 苏州 215000)
摘 要 为提升芳纶织物的防穿刺效果,采用氧等离子体表面处理技术改性的芳纶 1414 织物与环氧树脂复合制
备环氧芳纶复合体。 分析了等离子体处理对织物功能改性的影响,研究了环氧树脂涂覆织物后复合体的防刺性
通信作者:杜兆芳(1967—) ,女,教授,博士。 主要研究方向为再生纤维综合利用和产业用纺织品。 E-mail:dzf@ 。
主要还是集中在军用、警用领域 [3] ,并且也有了一
足人们的多元需求,这就对纺织品的安全、防护性能
料的研究并不多见 [3-4] ,渔民、司机和某些特殊行业
身安全与健康也更加重视 [1] ,普通纺织品已无法满
提出了更高的要求,因此,具备防护功能织物的应用
领域越来越多 [2] 。 我国对于防刺材料的研究现在
些比较理想的成果。 而对应用于民用领域的防刺材
工作人员的人身防护经常被忽视 [4] 。 芳纶是高性
能个人防护织物中应用最广的纤维之一 [1] ,尤其是
收稿日期:2018-05-24 修回日期:2019-09-12
基金项目:安徽农业大学研究生创新基金项目(2019ysj-70)
第一作者:庄群(1995—) ,女,硕士生。 主要研究方向为产业用纺织品和纤维材料改性。
composites and stab resistance thereof
ZHUANG Qun 1 , ZHANG Fei 1 , DU Zhaofang 1 , JIANG Hua 2
(1. Textile Engineering and Academy of Art, Anhui Agricultural University, Hefei, Anhui 230036, China;
composites was further studied. The experiment results show that when the plasma treatment power is
600 W and the treatment time is 18 min, the fabric surface is etched obviously and the number of oxygencontaining groups increases, and the wettability is improved, but the fabric tensile strength decreases;
第 40 卷 第 12 期
纺 织 学 报
2019 年 12 月
Journal of Textile Research
Vol.40, No.12
Dec., 2019
D505806
改性芳纶与环氧树脂复合体的制备及其防刺性能
庄 群1 , 张 飞1 , 杜兆芳1 , 姜 华2
fabrics were combined with epoxy resin to prepare epoxy aramid composites. The influence of plasma
pretreatment on the functional modification of the fabric was investigated, and then stab resistance of the
Keywords plasma treatment; modified aramid fiber; surface treatment; aramid epoxy composite; stab
resistant material
随着人们对生活品质要求的不断提高,对其自
能。 结果表明:采用氧等离子体处理,在处理功率为 600 W、处理 18 min 时,织物表面纤维刻蚀明显,含氧基团增
多,润湿性提高,但织物拉伸强度有所下降;当环氧树脂涂覆在等离子体改性后的芳纶织物上,树脂中环氧基团与
芳纶中含氧活性基团键合牢固,复合体黏结强度较好,拉伸强度较未经处理的芳纶织物增加了 7.89%,复合体防穿
when the epoxy resin is coated on the plasma-modified aramid fabric, the epoxy group in the resin is
firmly bonded with the oxygen-containing active group in the aramid fiber and the bond strength of the
complex is better. The tensile strength is increased by 7. 89% and the tested composite stab resistance is
significantly improved compared with the conventional aramid 1414 fabric, the multi-layered structure has
刺效果较普通芳纶 1414 织物提升显著,且多层组合结构的防刺效果更优异。
关键词 等离子体; 改性芳纶; 表面处理; 芳纶环氧复合体; 防刺材料
中图分类号:TS 156 文献标志码:A
Preparation of modified aramid fiber and epoxy resin
2. Suzhou Gao Jia Protection Technology Co., Ltd., Suzhou, Jiangsu 215000, China)
Abstract In order to improve the stab resistance of aramid fabrics, oxygen plasma modified aramid 1414
(1. 安徽农业大学 轻纺工程与艺术学院, 安徽 合肥 230036;
2. 苏州高甲防护科技有限公司, 江苏 苏州 215000)
摘 要 为提升芳纶织物的防穿刺效果,采用氧等离子体表面处理技术改性的芳纶 1414 织物与环氧树脂复合制
备环氧芳纶复合体。 分析了等离子体处理对织物功能改性的影响,研究了环氧树脂涂覆织物后复合体的防刺性
通信作者:杜兆芳(1967—) ,女,教授,博士。 主要研究方向为再生纤维综合利用和产业用纺织品。 E-mail:dzf@ 。
主要还是集中在军用、警用领域 [3] ,并且也有了一
足人们的多元需求,这就对纺织品的安全、防护性能
料的研究并不多见 [3-4] ,渔民、司机和某些特殊行业
身安全与健康也更加重视 [1] ,普通纺织品已无法满
提出了更高的要求,因此,具备防护功能织物的应用
领域越来越多 [2] 。 我国对于防刺材料的研究现在
些比较理想的成果。 而对应用于民用领域的防刺材
工作人员的人身防护经常被忽视 [4] 。 芳纶是高性
能个人防护织物中应用最广的纤维之一 [1] ,尤其是
收稿日期:2018-05-24 修回日期:2019-09-12
基金项目:安徽农业大学研究生创新基金项目(2019ysj-70)
第一作者:庄群(1995—) ,女,硕士生。 主要研究方向为产业用纺织品和纤维材料改性。
composites and stab resistance thereof
ZHUANG Qun 1 , ZHANG Fei 1 , DU Zhaofang 1 , JIANG Hua 2
(1. Textile Engineering and Academy of Art, Anhui Agricultural University, Hefei, Anhui 230036, China;
composites was further studied. The experiment results show that when the plasma treatment power is
600 W and the treatment time is 18 min, the fabric surface is etched obviously and the number of oxygencontaining groups increases, and the wettability is improved, but the fabric tensile strength decreases;
第 40 卷 第 12 期
纺 织 学 报
2019 年 12 月
Journal of Textile Research
Vol.40, No.12
Dec., 2019
D505806
改性芳纶与环氧树脂复合体的制备及其防刺性能
庄 群1 , 张 飞1 , 杜兆芳1 , 姜 华2
fabrics were combined with epoxy resin to prepare epoxy aramid composites. The influence of plasma
pretreatment on the functional modification of the fabric was investigated, and then stab resistance of the