纳米氢氧化镁的超重力沉淀法制备及沉降性能

纳米氢氧化镁的超重力沉淀法制备及沉降性能
申红艳;刘有智
【期刊名称】《化工进展》
【年(卷),期】2016(35)10
【摘要】针对传统沉淀法存在的问题，提出采用一种新的液-液反应机制——撞击流-旋转填料床（IS-RPB）反应器制备纳米氢氧化镁，通过单因素实验和正交试验研究了镁离子初始浓度、镁离子和氢氧根离子摩尔浓度比、转速、液体流量及反应温度等因素对氢氧化镁浆料沉降性能的影响规律，确定了最佳工艺条件。

研究表明：在镁离子初始浓度为0.70mol/L、镁离子和氢氧根离子摩尔浓度比为1/2、转速为900r/min、液体流量为40L/h、反应温度为70℃的最佳工艺条件下，得到了粒径为60～80nm的六方片状氢氧化镁，其沉降性能良好。

%Aiming at solving the problems of liquid precipitation method,this paper proposed a novel impinging stream-rotating packed bed reactor(IS-RPB)to prepare magnesium hydroxide nanoparticles. The effects of various operating variables,including the initial Mg2+concentration,reactant concentration ratio,rotation speed,liquid flow rate,and reaction temperature,on the settlement property of magnesium hydroxide slurry were determined by means of single factor test method and multi-factor orthogonal test procedure and the optimum conditions were obtained. The obtained magnesium hydroxide nanoparticles were of 60~80nm in diameter,regular hexagonal plate in appearance,and with excellence settlement
property,when the initial Mg2+ concentration was 0.70mol/L,reactant
concentration ratio was 1/2,rotation speed was 900r/min,liquid flow rate was 40L/h,and reaction temperature was 70℃.
【总页数】7页(P3281-3287)
【作者】申红艳;刘有智
【作者单位】中北大学超重力化工过程山西省重点实验室，山西太原 030051;中北大学超重力化工过程山西省重点实验室，山西太原 030051
【正文语种】中文
【中图分类】TQ03.39
【相关文献】
1.超重力反应共沉淀法制备纳米尖晶石锰酸锂 [J], 黄新武;周继承;谢芝柏;廖晶晶;刘思维
2.超重力液相沉淀法制备纳米铁酸钴 [J], 祁贵生;武晓利;刘有智;郑奇;郭林雅
3.超重力反应器制备纳米氢氧化镁的实验研究 [J], 申红艳;刘有智;朱芝敏
4.超重力技术制备纳米氢氧化镁阻燃剂的应用研究 [J], 宋云华;陈建铭;刘立华;郭奋
5.超重力反应沉淀法制备纳米钛酸锶的性能表征 [J], 胡雄;丁一刚;吴元欣;戢峻;刘敏;丁晓娟
因版权原因，仅展示原文概要，查看原文内容请购买。