压力容器用钢板通用技术条件ASTM A20
ASTM标准号A
英文 Standard Specification for Carbon Steel Tee Rails Standard Specification for Carbon Steel Girder Rails of Plain, Grooved, and Guard Types Standard Specification for Steel Joint Bars, Low, Medium, and High Carbon (Non-Heat-Treated) Standard Specification for General Requirements for Rolled Structural Steel Bars, Plates, Shapes, and Sheet Piling Standard Specification for General Requirements for Steel Plates for Pressure Vessels Standard Specification for Steel Castings, Carbon, for General Application Standard Specification for Steel Bars, Carbon and Alloy, Hot-Wrought, General Requirements for Standard Specification for Steel Rivets and Bars for Rivets, Pressure Vessels Standard Practice for Sampling and Procurement Testing of Magnetic Materials Standard Specification for Carbon Structural Steel Standard Specification for Ferritic Malleable Iron Castings Standard Specification for Gray Iron Castings Standard Specification for Heat-Treated Carbon Steel Joint Bars, Microalloyed Joint Bars, and Forged Carbon Steel Compromise Joint Bars Standard Specification for Pipe, Steel, Black and Hot-Dipped, Zinc-Coated, Welded and Seamless Standard Specification for Steel Track Spikes Standard Specification for Steel Screw Spikes Standard Specification for Steel Tie Plates, Low-Carbon and High-Carbon Hot-Worked Standard Specification for Cast Iron Soil Pipe and Fittings Standard Specification for Steel Wire, Plain, for Concrete Reinforcement Standard Test Method for Weight [Mass] of Coating on Iron and Steel Articles with Zinc or Zinc-Alloy Coatings Standard Specification for Ferromanganese Standard Specification for Ferrosilicon Standard Specification for Ferrochromium Standard Specification for Ferrovanadium Standard Specification for Carbon Steel Forgings for Piping Applications Standard Specification for Seamless Carbon Steel Pipe for High-Temperature Service
A20及A6标准介绍
5
二、适用范围及代表性牌号
• 1. ASTM A6/A6M（ASME SA6/SA6M） 适用于由ASTM(ASME)发行的结构用轧制棒材、 钢板、型钢和钢桩的一般要求。
注：包括化学成分范围、波动，表面质量，附加要求，厚度平偏差，标识 及质保书等（独立要求，除相关牌号性能，成分外的要求） 。
我公司代表性牌号：ASTM A36,A283Gr.C/D, A 572 Gr.50/65, A709 Gr.50等。
7
三、与国标对比特点
分类 厚度附加 力学性能 冲击方向 标识 附加性能 美标 无厚度附加值概念 均默认无冲击要求 均默认纵向 名称写法很多 附加项极多 国标 分N,A,B,C四类偏差 根据牌号不同要求不同 结构、桥梁等钢种为纵 向，容器为横向 唯一 附加项很少
8
四、具体要求
1. 化学成分：默认检验元素C、Si、Mn、P、S、 Ni 、 Cr 、 Cu 、 Mo 、 V 、 Nb。 2. 热处理：附加冲击性能要求，往往需要正火状 态交货。 3. 力学性能：默认屈服强度以Rp0.2为主；拉伸试 验标记为50mm或200mm，不采用比例标距。
9
四、具体要求
4.冲击试验：默认不进行冲击试验；如检验，所有 冲击试验均为纵向，冲击温度由A6/A20附加要 求选择。 5. 牌号名称：牌号名称写法往往很多，例如A 516 Gr.70又可以写成A 516 Gr.485。 6. 热处理标记：热处理后，需要增加-N-MT等标识。
10
五、认证许可
11
1
ASTM A6/A6M及ASTM A20/A20M 标准介绍
2
目录
• • • • • 一、定义 二、适用范围及代表性牌号 三、与国标对比特点 四、具体要求 五、认证许可
ASTM A标准(中文)
AA1000-99 弹簧专用碳钢和合金钢钢丝规范A1001-99 大型材高强度钢铸件规范A1002-99 镍铝类合金铸件规范A100-93(2000) 硅铁A101-93(2000) 铬铁A102-93(2000) 钒铁合金A105/A105M-01 管系部件用碳素钢锻件A106-999e1 高温用无缝碳素钢管A108-99 优质冷加工碳素钢棒材技术规范A109/A109M-00e1 冷轧碳素钢带技术规范A111-99a 电话和电报线路用镀锌"铁"丝规格A116-00 镀锌钢丝编织栏栅网A121-99 镀锌刺钢丝A123/A123M-00 钢铁产品的锌镀层（热浸镀锌）技术规范A125-96 热处理螺旋形钢弹簧A126-95(2001) 阀门、法兰和管配件用灰铁铸件A128/A128M-93(1998) 钢铸件,奥氏体锰A131/A131M-94 海船用结构钢A132-89(2000) 钼铁合金A134-96 电熔(电弧)焊钢管(NPS为16英寸和16英寸以上)A135-01 电阻焊钢管A139-00 电熔(电弧)焊钢管(4英寸以上的)A143-74(1999) 热浸镀锌结构钢制品防脆裂措施和探测脆裂的程序A146-64(2000) 氧化钼制品A148/A148M-01 结构用高强度钢铸件A153/A153M-00 钢铁制金属构件上镀锌层(热浸)A159-83(2001) 汽车用灰铁铸件A167-99 不锈钢和耐热铬镍钢板、薄板及带材A176-99 不锈钢和耐热铬钢板、薄板及带材A178/A178M-95(2000) 电阻焊接碳素钢钢管及碳锰钢锅炉和过热器管的技术规范A179/A179M-90a(1996)e1 热交换器和冷凝器用无缝冷拉低碳钢管A181/A181M-01 普通锻制碳素钢管的规格A182/A182M-01 高温设备用锻制或轧制的合金钢管法兰、锻制管件、阀门及零件A183-98 钢轨用碳素钢螺栓和螺母A184/A184M-01 混凝土加筋用变形钢筋编织网A185-97 钢筋混凝土用焊接钢丝结构A1-00 碳素钢丁字轨A192/A192M-91(1996)e1 高压用无缝碳素钢锅炉管A193/A193M-01 高温设备用合金钢和不锈钢螺栓材料A194/A194M-01 高温和高压设备用碳素钢与合金钢螺栓和螺母的规格A197/A197M-00 化铁炉用可锻铸铁A20/A20M-01 压力容器用钢板材通用要求A202/A202M-93(1999) 压力容器用铬锰硅合金钢板A203/A203M-97 压力容器用镍合金钢板A204/A204M-93(1999) 压力容器用钼合金钢板A209/A209M-98 锅炉和过热器用无缝碳钼合金钢管A210/A210M-96 锅炉和过热器用无缝中碳素管A213/A213M-01 无缝铁素体和奥氏体合金钢锅炉、过热器和换热器管A214/A214M-96 热交换器与冷凝器用电阻焊接碳素钢管A216/A216M-93(1998) 高温下使用的适合于熔焊的碳素钢铸件规格A217/A217M-01 适合高温受压零件用合金钢和马氏体不锈钢铸件A21-94(1999) 铁路用未经热处理和经热处理的碳素钢轴A220/A220M-99 珠光体可锻铁A225/A225M-93(1999) 压力容器用锰矾镍合金钢板A227/A227M-99 机械弹簧用冷拉钢丝A228/A228M-00 乐器用优质弹簧钢丝A229/A229M-99 机械弹簧用油回火的钢丝A230/A230M-99 阀门用油回火优质碳素钢弹簧丝A231/A231M-96 铬钒合金钢弹簧丝A232/A232M-99 阀门用优质铬钒合金钢弹簧丝A234/A234M-00a 中温与高温下使用的锻制碳素钢及合金钢管配件A239-95(1999) 用普力斯试验法(硫酸铜浸蚀)确定铁或钢制品上镀锌层最薄点的测试方法A240/A240M-01 压力容器用耐热铬及铬镍不锈钢板、薄板及带材A242/A242M-00a 高强度低合金结构钢A247-67(1998) 铁铸件中石墨显微结构评定试验方法A249/A249M-01 锅炉、过热器、换热器和冷凝器用焊接奥氏体钢管A250/A250M-95(2001) 锅炉和过热器用电阻焊铁素体合金钢管A252-98e1 焊接钢和无缝钢管桩A254-97 铜焊钢管规格A255-99 测定钢淬透性用末端淬火试验的标准试验方法A262-98 奥氏体不锈钢晶间浸蚀敏感性的检测A263-94a(1999) 耐腐蚀铬钢包覆板材,薄板材及带材技术规范A264-94a(1999) 包覆的不锈铬镍钢板,薄板及带材规格A265-94a(1999) 镍和镍基合金包覆钢板规格A266/A266M-99 压力容器部件用碳素钢锻件规格A268/A268M-01 一般设备用无缝和焊接铁素体与马氏体不锈钢管A269-01 一般设备用无缝和焊接奥氏体不锈钢管A27/A27M-95(2000) 通用碳素钢铸件A270-01 卫生设施用无缝钢和焊接奥氏体不锈钢管A275/A275M-98 钢锻件的磁粉检查试验方法A276-00a 不锈钢棒材和型材A278-93 适用于650F容压部件用灰铸铁件的技术规范A283/A283M-00 低和中等抗拉强度碳素钢板A285/A285M-90(2001) 压力容器用低和中等抗拉强度的碳素钢板A288-91(1998) 涡轮发电机磁性定位环用碳素钢和合金钢锻件A289/A289M-97 发电机非磁性定位环用合金钢锻件的技术规范A29/A29M-99e1 热锻及冷加工碳素钢和合金钢棒A2-90(1997) 普通型,带槽和防护型碳素工字钢轨A290-95(1999) 减速器环用碳素钢和合金钢锻件A291-95(1999) 减速器小齿轮、齿轮和心轴用碳素钢和合金钢锻件A295-98 高碳耐磨轴承钢技术规范A297/A297M-97(1998) 一般用耐热铬铁与镍铬铁合金钢铸件规格A299/A299M-97e1 压力容器用锰硅碳钢板A302/A302M-97e1 压力容器用锰钼和锰钼镍合金钢板A304-96 有末端淬火淬透性要求的合金钢棒材的技术规范A307-00 抗拉强度为60000psi的碳素钢螺栓和螺柱的技术规范A308-99 经热浸处理镀有铅锡合金的薄板材的技术规范A309-94a(1999) 用三点试验法测定长镀锌薄钢板镀层的重量成分的试验方法A311/A311M-95(2000) 有机械性能要求的消除应力的冷拉碳素钢棒A312/A312M-00c 无缝和焊接奥氏体不锈钢管A313/A313M-98 不锈钢弹簧丝技术规范A314-97 锻造用不锈及耐热钢坯及钢棒规格A31-00 钢铆钉及铆钉和压力容器用棒材A319-71(2001) 高温无压部件用灰铁铸件A320/A320M-01 低温用合金钢螺栓材料规格A321-90(1995)e1 经淬火和回火的碳素钢棒A322-91(1996) 合金钢棒材.级别A323-93(2000) 硼铁规格A324-73(2000) 钛铁合金A325-00 经热处理最小抗拉强度为120/105ksi的钢结构螺栓A325M-00 结构钢连接件用高强度螺栓(米制)A327-91(1997) 铸铁冲击试验方法A327M-91(1997) 铸铁冲击试验方法(米制)A328/A328M-00 薄钢板桩A331-95(2000) 冷加工合金钢棒A333/A333M-99 低温用无缝与焊接钢管规格A334/A334M-99 低温设备用无缝与焊接碳素和合金钢管A335/A335M-01 高温用无缝铁素体合金钢管A336/A336M-99e1 压力与高温部件用合金钢锻件规格A338-84(1998) 铁路,船舶和其他重型装备在温度达到650华氏度(345摄氏度)时使用的可锻铸铁法兰,管件和阀门零件A34/A34M-96 磁性材料的抽样和采购试验的标准惯例A340-99a 有关磁性试验用符号和定义的术语A341/A341M-00 用直流磁导计和冲击试验法测定材料的直流磁性能的试验方法A342/A342M-99 磁铁材料导磁率的试验方法A343-97 在电力频率下用瓦特计-安培计-伏特计法(100-1000赫兹)和25 厘米艾普斯亭(EPSTEIN) 机架测定材料的交流电磁性能的试验方法A345-98 磁设备用平轧电炉钢A348/A348M-00 用瓦特计--安培计--伏特计法(100-10000赫兹)和25厘米艾普斯亭框测定材料的交流磁性能的试验方法A350/A350M-00c 要求进行缺口韧性试验的管道部件用碳素钢与低合金钢锻件技术规范A351/A351M-00 容压零件用奥氏体及奥氏体铁素体铸铁的技术规范A352/A352M-93(1998) 低温受压零件用铁素体和马氏体钢铸件规格A353/A353M-93(1999) 压力容器用经二次正火及回火处理的含9％镍的合金钢板A354-01 淬火与回火合金钢螺栓,双头螺栓及其他外螺纹紧固件规格A355-89(2000) 渗氮用合金钢棒A356/A356M-98e1 蒸汽轮机用厚壁碳素钢、低合金钢和不锈钢铸件A358/A358M-01 高温用电熔焊奥氏体铬镍合金钢管A36/A36M-00a 碳素结构钢技术规范A363-98 地面架空线用镀锌钢丝绳A367-60(1999) 铸铁的激冷试验方法A368-95a(2000) 不锈钢和耐热钢丝绳的标准A369/A369M-01 高温用锻制和镗孔碳素钢管和铁素体合金钢管A370-97a 钢制品机械测试的标准试验方法和定义A372/A372M-99 薄壁压力容器用碳素钢及合金钢锻件A376/A376M-01 高温中心站用无缝奥氏钢管A377-99 球墨铸铁压力管规范索引A380-99e1 不锈钢零件、设备和系统的清洗和除垢A381-96 高压输送用金属弧焊钢管A384-76(1996) 防止钢组件热浸镀锌时翘曲和扭曲用安全保护A385-00 提供高质量镀锌覆层(热浸)A3-01 低、中、高碳素钢鱼尾（连接）板A387/A387M-99e1 压力容器用铬钼合金钢板A388/A388M-95(2000)e1 重型钢锻件超声波检测A389/A389M-93(1998) 适合高温受压部件用经特殊热处理的合金钢铸件规格A390-95(2001) 饲养家禽用镀锌钢丝栏栅网(六角形和直线形)A391/A391M-98 80号合金钢链条A392-96 镀锌钢丝链环栏栅网A394-00 传动塔架用镀锌和裸露钢螺栓A395/A395M-99 高温用铁素体球墨铸铁受压铸件A400-69(2000) 钢棒的成分及机械性能选择指南A401/A401M-98 铬硅合金钢丝A403/A403M-00b 锻制奥氏体不锈钢管配件A407-93(1998) 盘簧用冷拉钢丝A409/A409M-01 腐蚀场所或高温下使用的焊接大口径奥氏体钢管A411-98 镀锌低碳钢铠装线A413/A413M-00 碳素钢链A414/A414M-00 压力容器用碳素薄钢板A416/A416M-99 预应力混凝土用无涂层七股钢铰线A417-93(1998) 之字型、方型和正弦型装垫弹簧元件用冷拉钢丝A418-99 涡轮机及发电机钢转子锻件的超声波检查方法A420/A420M-00b 低温下用锻制碳素钢和合金钢管配件A421/A421M-98a 预应力混凝土用无涂层消除应力钢丝的技术规范A423/A423M-95(2000) 无缝和电焊低合金钢管A424-00 搪瓷用钢薄板A426-92(1997) 高温用离心铸造的铁素体合金钢管A427-74(1996)e1 冷轧和热轧用锻制合金钢辊A428/A428M-01 钢铁制品上铝覆层重量的测试方法A434-90a(2000) 热轧与冷精轧经回火及淬火的合金钢棒A435/A435M-90(2001) 钢板的直射束纵向超声波检验A436-84(1997)e1 奥氏体灰口铁铸件A437/A437M-01 高温用经特殊处理的涡轮型合金钢螺栓材料A438-80(1997) 灰铸铁横向弯曲试验A439-83(1999) 奥氏体可锻铸铁铸件A447/A447M-93(1998) 高温用镍铬铁合金钢铸件(25-12级)A449-00 经淬火和回火的钢螺栓和螺柱A450/A450M-96a 碳素钢管、铁素体合金钢管及奥氏体合金钢管A451-93(1997) 高温用离心铸造的奥氏体钢管A453/A453M-00 具有同奥氏体钢相类似的膨胀系数、屈服强度为50-120Ksi(345-827MPa)的耐高温螺栓材料A455/A455M-90(2001) 压力容器用高强度碳锰钢板A456/A456M-99 大型曲轴锻件的磁粉检查A459-97 镀锌平轧扁钢铠装带A460-94(1999) 包铜钢丝绳标准A463/A463M-00 热浸镀铝薄钢板A466/A466M-98 非焊接碳素钢链A467/A467M-98 机器链和盘旋链A469-94a(1999) 用于发电机转子的真空处理钢锻件A470-01 涡轮机转子和轴用经真空处理的碳素钢和合金锻件A471-94(1999) 涡轮转子转盘和转轮用真空处理合金钢锻件技术规范A472-98 蒸汽涡轮机轴及转子锻件的热稳定性的试验方法A473-01 不锈和耐热钢锻件A474-98 包铝钢丝绳标准A475-98 镀锌钢丝绳A476/A476M-00 造纸厂干燥辊用球墨可锻铸铁件A478-97 铬镍不锈钢和耐热钢制编织钢丝A479/A479M-00 锅炉及压力容器用不锈钢和耐热钢棒与型材A47/A47M-99 铁素体可锻铁铸件A480/A480M-01 扁平轧制耐热不锈钢厚板材、薄板材和带材通用要求A481-94(2000) 金属铬A482-93(2000) 铬铁硅A483-64(2000) 硅锰合金A484/A484M-00 不锈及耐热锻钢棒,钢坯及锻件的规格A485-00 高淬透性耐磨轴承钢的技术规范A487/A487M-93(1998) 受压钢铸件A488/A488M-01 钢铸件焊接规程和工作人员的合格鉴定A48-94ae1 灰铁铸件A489-00 碳素钢吊耳A490-00 最小拉伸强度为150千磅/平方英寸热处理钢结构螺栓A491-96 镀铝钢链环栏栅结构A492-95(2000) 耐热不锈钢丝绳A493-95(2000) 冷镦和冷锻不锈钢和耐热钢丝A494/A494M-00 镍和镍合金铸件A495-94(2000) 硅钙合金钢技术规范A496-97ae1 钢筋混凝土用变形钢丝A497-99e1 钢筋混凝土用焊接变形钢丝网A498-98 无缝与焊接碳素钢,铁素体钢与奥氏体钢制有整体散热片的换热器钢管A49-01 经热处理的碳素钢鱼尾（连接）板，微合金鱼尾板及锻制碳素钢异型鱼尾板A499-89(1997)e1 轧制丁字钢轨用的碳素钢棒材及型材的技术规范A500-01 圆形与异型焊接与无缝碳素钢结构管A501-01 热成型焊接与无缝碳素钢结构管A503/A503M-01 锻制大型曲轴的超声波检验A504-93(1999) 锻制碳素钢轮A505-00 热轧和冷轧合金钢薄板和带材A506-00 正规质量及优质结构的热轧和冷轧合金钢薄板与带材A507-00 优质拉拔,热轧和冷轧合金钢薄板与带材A508/A508M-95(1999) 压力容器用经回火和淬火真空处理的碳素钢与合金钢锻件A510-00 碳素钢盘条和粗圆钢丝通用要求A510M-00 碳素钢盘条和粗圆钢丝(米制)A511-96 无缝不锈钢机械管A512-96 冷拉对缝焊碳素钢机械管A513-00 电阻焊碳素钢与合金钢机械钢管A514/A514M-00a 焊接用经回火与淬火的高屈服强度合金钢板A515/A515M-92(1997) 中温及高温压力容器用碳素钢板A516/A516M-90(2001) 中温及低温压力容器用碳素钢板A517/A517M-93(1999) 压力容器用经回火与淬火的高强度合金钢板A518/A518M-99 耐蚀高硅铁铸件A519-96 无缝碳素钢与合金钢机械管A521-96 一般工业用闭式模钢锻件A522/A522M-95b(2000) 低温用锻制或轧制含镍8%和9%的合金钢法兰,配件,阀门和零件规格A523-96 高压管型电缆线路用平端无缝与电阻焊钢管A524-96 常温和低温用无缝碳素钢管A529/A529M-00 高强度碳锰结构钢质量A530/A530M-99e1 特种碳素钢和合金钢管A531/A531M-91(1996) 涡轮发电机钢定位环的超声波检验A532/A532M-93a(1999)e1 耐磨铸铁A533/A533M-93(1999) 压力容器用经回火和淬火的锰钼及锰钼镍合金钢板A534-94 用于耐摩擦轴承的渗碳钢A536-84(1999)e1 球墨铸铁件A537/A537M-95(2000) 压力容器用经热处理的碳锰硅钢板A53/A53M-01 无镀层热浸的、镀锌的、焊接的及无缝钢管的技术规范A539-99 天然气和燃料油管线用电阻焊钢盘管A540/A540M-00 特殊用途的合金钢螺栓材料A541/A541M-95(1999) 压力容器部件用经淬火和回火的碳素钢及合金钢锻件A542/A542M-99e1 压力容器用经回火和淬火的铬钼、铬钼钒及铬钼钒钛硼合金钢板A543/A543M-93(1999) 压力容器用经回火和淬火的镍铬钼合金钢板A550-78(2000) 铌铁合金A551-94(1999) 钢轮箍A553/A553M-95(2000) 压力容器用经回火和淬火的含8%及9%镍的合金钢板A554-98e1 焊接的无缝钢机械管A555/A555M-97 耐热不锈钢丝和盘条的通用要求A556/A556M-96 无缝冷拉碳素钢给水加热器管A560/A560M-93(1998) 铬镍合金铸件A561-71(1999) 工具钢棒的宏观刻蚀试验A562/A562M-90(2001) 搪玻璃或扩散金属镀层的压力容器用锰钛合金碳素钢板A563-00 碳合金钢螺母A563M-00 碳素钢及合金钢螺母技术规范（米制）A564/A564M-01 热轧及冷精轧时效硬化处理过的不锈钢棒材和型材技术规范A565-97 高温用马氏体不锈钢棒,锻件和锻制坯规格A568/A568M-00b 热轧及冷轧高强度低合金碳素钢薄板A571-84(1997) 适用于低温压力容器零件的奥氏体球墨铸铁件A571M-84(1997) 适用于低温压力容器零件的奥氏体球墨铸铁件(米制)A572/A572M-00a 高强度低合金钴钒结构钢技术规范A573/A573M-00a 增强韧性的结构碳素钢板A574-00 合金钢内六角螺钉A574M-00 合金钢内六角螺钉(米制)A575-96 商品级碳素钢棒(M级)A576-90b(2000) 特级热轧碳素钢棒A577/A577M-90(2001) 钢板的超声角波束检验A578/A578M-96(2001) 特殊设备用的普通钢板和包覆钢板的直波束超声探伤检验A579-99 超高强度合金钢锻件A580/A580M-98 耐热不锈钢丝A581/A581M-95b(2000) 高速切削用耐热不锈钢丝和盘条A582/A582M-95b(2000) 热轧或冷精轧的高速切削不锈及耐热钢棒A583-93(1999) 铁路用铸钢轮A584-97 镀铝钢丝编织栅栏网A585-97 镀铝刺钢丝A586-98 镀锌平行和螺旋形钢丝绳A587-96 化学工业用电阻焊低碳钢管A588/A588M-00a 高强度低合金结构钢4英寸(100mm)厚屈服点最小为50ksi(345MPa) A589-96 水井用无缝和焊接碳素钢管A591/A591M-98 薄镀层电解镀锌薄钢板A592/A592M-89(1999) 压力容器用经回火和淬火的高强度低合金钢锻制附件和零件A595-98 结构用圆锥形低碳钢管A596/A596M-95(1999) 用环形试验法和冲击法测定材料的直流磁性能的试验方法A597-87(1999) 铸造工具钢A598-92(1997) 磁放大器磁芯的磁性能测试法A599/A599M-99 锡制品，电解镀锡的冷滚轧薄板规范A6/A6M-01 轧制结构钢板材、型材和薄板桩通用技术要求A600-92a(1999) 高速工具钢A601-96(2000) 电解金属锰A602-94(1998) 汽车用可锻铸铁件A603-98 镀锌结构钢丝绳A604-93(1998) 自耗电极再溶化钢棒与钢坯的宏观腐蚀试验方法A606-98 改进防大气腐蚀性的热轧和冷轧高强度低合金钢薄板和带材A608-91a(1998) 高温受压离心铸造的铁铬镍高合金钢管A609/A609M-91(1997) 碳素钢,低合金钢和马氏体不锈钢铸件的超声波检测A610-79(2000) 尺寸测量用铁合金的取样和试验A611-00 冷轧优质碳素结构钢薄板A612/A612M-00 中温和低温压力容器用高强度碳素钢板A615/A615M-01a 钢筋混凝土配筋用变形和光面坯钢筋A618-01 热成型焊接与无缝高强度低合金结构钢管系A623-00 锡轧制产品A623M-00 镀锡薄钢板轧制品通用要求(米制)A624/A624M-98 锡辊轧制品.单压延电解马口铁A625/625M-98 一次轧制原钢板（未镀）和镀锡薄钢板轧制产品技术规范A626/A626M-98 二次压延电解镀锡厚钢板轧制品技术规范A626/A626M-98 锡轧制品.二次压延的电解镀锡板(米制)A627-95 安全设备用均质不易加工的钢棒A629-88(1994)e1 安全设备用不易加工的扁钢棒和型材A630-98 热浸电解镀锡板镀锡层重量测定的方法A632-01 通用无缝和焊接奥氏体不锈钢管(小直径)A633/A633M-00a 正火的高强度低合金结构钢A635/A635M-00 热轧碳素钢薄板,带材和重型粗盘条规格A636-76(2000) 氧化镍烧结块A638/A638M-00 高温用沉积硬化铁基超级合金棒,锻件及锻坯料A640-97 8字型缆吊架用镀锌钢丝绳A641/A641M-98 镀锌（电镀）碳素钢丝技术规范A644-98 铁铸件的相关术语A645/A645M-99a 压力容器用经特殊热处理的5%镍合金钢板A646-95(1999) 飞机及航空器锻件用优质合金钢大方坯及坯段A648-95(2000) 预应力混凝土管用冷拉钢丝A649/A649M-99 波纹纸机械用锻制钢辊规格A650/A650M-98 二次压延的锡轧黑板材A653/A653M-00 热浸处理的镀锌铁合金或镀锌合金薄钢板的标准规范A656/A656M-00a 具有改良可模锻性的高强度低合金热轧结构钢板A657/A657M-98a 一次和二次压延电解镀铬黑钢板轧制品技术规范A65-01 钢轨道钉A659/A659M-97 商业级热轧碳素钢薄板和带材(最大含碳量为0.16%-0.25%) A660-96 高温用离心铸造碳素钢管A662/A662M-99 中温和低温压力容器用锰碳钢板规格A663/A663M-89(2000) 商品级碳素钢棒的机械特性A664-99 在ASTM规范中对电工钢和层压钢级别的识别A666-00 退火或冷加工的奥氏体不锈钢薄板、带材、中厚板和扁棒A667/A667M-87(1998) 离心铸造的双金属(灰口及白口铸铁)圆柱体A668/A668M-96e1 一般工业用碳素钢和合金钢锻件A66-01 钢质螺旋道钉A671-96 常温和较低温用电熔焊钢管A672-96 中温高压用电熔焊钢管A673/A673M-95 结构钢冲击试验的取样程序A674-00 水或其它液体用球墨铸铁管的聚乙烯包装A675/A675M-90a(2000) 专用热轧碳素钢棒的机械特性A677/A677M-99 全处理型无取向电工钢A678/A678M-00a 结构用经回火和淬火的高强度低合金碳素钢板规格A679/A679M-00 硬(冷)拉高抗拉强度钢丝A67-00 热加工低碳钢和高碳钢垫板技术规范A681-94(1999) 合金工具钢A682/A682M-00 弹簧用冷轧高碳钢带材A683/A683M-99 半处理型无取向电工钢A684/A684M-99 冷轧高碳钢带材A686-92(1999) 碳素工具钢A688/A688M-01 焊接的奥氏体不锈钢给水加热器管A689-97 弹簧用碳素钢及合金钢棒A690/A690M-00a 在海洋环境中使用的高强度低合金工字形钢桩和薄板桩规格A691-98 高温下高压装置用电熔焊碳素钢和合金钢管A693-93(1999) 沉淀硬化耐热不锈钢板、薄板和带材A694/A694M-00 高压传输设备用碳素钢及合金钢管法兰、配件、阀门及零件用锻件A695-90b(1995)e1 流体动力设备专用热锻碳素钢棒A696-90a(2000) 压力管道部件专用热锻或冷精轧碳素钢棒A697-98 用伏特计、安培计和瓦特计法测定迭层铁芯样品的交流磁特性的试验方法A698/A698M-92(1997)e1 在弱交流磁场中磁屏蔽效率的试验方法A700-99e1 钢制品国内装运的包装、标记和装载方法A701-96(2000) 硅锰铁A702-89(2000) 热锻钢栅栏柱和组件A703/A703M-01 受压部件用钢铸件A704/A704M-96 混凝土加筋用焊接普通钢棒或杆的光面钢筋或钢筋网A705/A705M-95(2000) 时效硬化的不锈和耐热钢锻件A706/A706M-01 混凝土配筋用变形低合金光面无节钢筋A707/A707M-00a 低温设备用锻制碳素钢和合金钢法兰A709/A709M-01 桥梁用结构钢A710/A710M-00 低碳时效硬化的镍铜铬钼铌合金钢A711-92(1996)e1 钢锻件坯料A712-97 软磁性合金电阻率的测试方法A713-93(1998) 热处理部件用高碳弹簧钢丝A714-99 高强度低合金焊接钢管和无缝钢管A716-99 球墨铸铁涵洞管A717/A717M-95 单片样品表面绝缘电阻率的试验方法A719-97 磁性材料的叠装系数的试验方法A720-97 无取向电工钢延展性的试验方法A721-97 取向的电工钢的延展性试验方法A722/A722M-98 预应力混凝土用无涂覆的高强度钢筋A723/A723M-94(1999) 高强度压力元件用合金钢锻件A724/A724M-99 叠层焊接的压力容器用经淬火及回火的碳素钢压力容器板A726-00 半成品型冷轧磁性迭片级钢A727/A727M-00 具有固定切口韧性的管道部件用碳素钢锻件A729-93(1999) 货物运输及电气铁路用热处理合金钢轴A730-93(1999) 铁路用碳素钢及合金钢锻件A732/A732M-98 一般设备用熔模铸造碳素低合金钢及高强度加温钴合金钢铸件A733-99 焊接及无缝碳素钢和奥氏体不锈钢管接头A734/A734M-87a(1997) 经淬火和回火的合金钢与高强度低合金钢压力容器板A735/A735M-99 中温和低温用低碳锰钼钶合金钢压力容器板A736/A736M-88(2000) 低碳时效硬化的镍铜铬钼铌和镍铜锰钼铌合金钢压力容器板A737/A737M-99 高强度低合金钢压力容器板A738/A738M-00 中温和低温设备用经热处理的碳锰硅钢压力容器板A739-90a(2000) 升温或/和加压部件用热轧合金钢棒A740-98 钢丝网(编织或焊接电镀钢丝网)A741-98 公路护栏用镀锌钢丝绳和配件A742/A742M-98 波纹钢管用预涂聚合物和金属涂覆钢薄板A743/A743M-98ae1 一般用耐腐蚀铬铁及镍铬铁合金铸件A744/A744M-00 严酷条件下使用的耐腐蚀镍铬铁合金铸件A745/A745M-94(1999) 奥氏体钢锻件的超声波检验A746-99 排污管用球墨铸铁A747/A747M-99 沉淀硬化不锈钢铸件A748/A748M-87(1998) 压力容器用静态铸造的激冷白口铁-灰口铁双金属轧辊A749/A749M-97 热轧碳素钢和高强度低合金钢带材通用要求A74-98 铸铁污水管及配件的技术规范A750-77(1994)e1 阻挡区域用钢制通风格栅A751-96 钢制品化学分析的实验方法、操作和术语A752-93(1998) 合金钢条和粗圆钢丝A752M-93(1998) 合金钢条和粗圆钢丝(米制)A753-97 镍铁软磁合金A754/A754M-96(2000) X射线荧光涂层厚度的试验方法A755/A755M-99 外露建筑材料用热浸涂覆和用卷涂工艺预涂的钢薄板A756-94(2001) 耐磨不锈轴承钢A757/A757M-00 低温下承压设备及其它设备用铁素体和马氏体钢铸件A758/A758M-00 具有改进的切口韧性的对缝焊锻制碳素钢管配件A759-00 起重机用碳钢轨条A760/A760M-01 下水道和排水沟用金属涂覆的波纹钢管A761/A761M-98 现场栓接管、管拱和拱用波纹镀锌结构钢板A762/A762M-00 下水道和排水沟用预涂聚合物波纹钢管A763-93(1999)e1 铁素体不锈钢晶间腐蚀敏感性检测A764-95(2001) 机械弹簧用冷拉镀锌和按成品尺寸镀锌的碳素钢丝A765/A765M-98a 具有强制性韧性要求的碳素钢及低合金钢压力容器部件锻件A767/A767M-00b 钢筋混凝土用镀锌钢筋A768-95 涡轮机转子及轴用经真空处理的含铬12%的合金钢锻件A769/A769M-00 电阻焊钢结构型材A770/A770M-86(2001) 专用钢板通过厚度测量进行的抗拉试验A771/A771M-95(2001) 增殖反应堆堆芯部件用奥氏体不锈钢管A772/A772M-00 正弦电流用材料的交流磁导率的试验方法A773/A773M-96 用带直流电子的磁滞曲线记录仪的（B－H）回路法测量材料的磁性能的标准试验方法A774/A774M-00 低温和中温一般腐蚀情况下用的焊接锻制奥氏体不锈钢配件A775/A775M-01 涂环氧树脂的钢筋钢棒A778-01 焊接未退火的奥氏体不锈钢管形制品A779/A779M-00 预应力混凝土用应力消除未涂覆的密实七股钢丝绞绳A780-01 热浸镀锌层的损坏及无覆层区域的检修A781/A781M-00 一般工业用一般要求的钢和合金铸件A782/A782M-90(2001) 经淬火和回火的锰铬钼硅锆合金钢压力容器板A786/A786M-00b 轧制钢楼板A787-01 电阻焊金属涂覆碳素钢机械配管A788-98a 钢锻件A789/A789M-01 普通设备用无缝与焊接铁素体/奥氏体不锈钢管A790/A790M-01 无缝与焊接铁素体/奥氏体不锈钢管A792/A792M-99 热浸工艺法处理的55%铝-锌合金涂覆钢板A793-96 不锈钢轧制楼板A794-97 商品级冷轧碳素钢薄板(最高含碳量为0.16%-0.25%)A795-00 防火用黑色及热浸镀锌的焊接和无缝钢管A796/A796M-00 雨水管和卫生污水管及其它地下埋设管道用波纹钢管、管托架及拱形架结构设计惯例A798/A798M-01 下水道及其它类似用途用工厂制波纹钢管的安装A799/A799M-92(1997) 估算不锈钢铸件铁素体含量用仪表的校准A800/A800M-01 奥氏体合金钢铸件中铁素体含量的估算A801/A801M-99 铁钴高磁性饱和合金A802/A802M-95(2001) 钢铸件外观检验的表面验收标准A803/A803M-01 焊接铁素体不锈钢给水加热器管A804/A804M-99 在电力频率下用薄钢板型试样对材料交流磁特性的测试方法A805-93(1998) 冷轧碳素钢扁平线A807/A807M-97 下水道及其它类似用途用波纹结构钢涂覆管的安装A808/A808M-00a 具有改进的切口韧性的结构级高强度低合金碳钢、锰钢、铌钢和钒钢A809-98 镀铝碳素钢丝A810-00 镀锌钢管用绕网A811-97 粉末冶金技术制造的软磁铁零件A813/A813M-01 单或双焊接奥氏体不锈钢管A814/A814M-01 冷加工焊接奥氏体不锈钢管A815/A815M-01 锻制铁素体、铁素体/奥氏体和马氏体不锈钢管配件A817-00 链接栅栏网用金属涂覆钢丝A818-91(2001) 镀铜碳素钢丝A820-96 纤维增强混凝土用钢纤维A821/A821M-99 预应力混凝土容器用经回火的冷拉钢丝A822-90(2000) 液压系统设备用冷拉碳素无缝钢管A823-99 静铸永久铸模灰铸件A824-01 链接栅栏用Marcelled拉力金属涂覆钢丝A826/A826M-95(2001) 增殖反应堆堆芯部件用奥氏体和铁素体不锈钢管A827/A827M-93a(1998) 锻造及类似用途用的碳素钢板技术规范A829/A829M-00 结构性合金钢板A82-97ae1 钢筋混凝土用无节钢丝A830/A830M-00 按照化学成分要求提供的优质碳素钢板技术规范A831/A831M-95(2000) 核心部件用不锈耐热钢棒,坯段及锻件规格A832/A832M-99e1 压力容器板用铬钼钒及铬钼钒钛硼合金钢A833-84(1996) 用比较硬度测试仪测量金属材料的压痕硬性A834-95(2001) 一般工业用铁铸件的一般要求A835-84(2000) 铁合金与合金添加剂的筛分粒度A836/A836M-95b(2001) 搪瓷管和压力容器设备用钛稳定碳素体钢锻件A837-91(1996)e1 渗碳用合金钢锻件A838/A838M-97 继电器用易切削铁素体不锈软磁合金技术规范A839/A839M-96 软磁用途的磷铁粉末冶金制造的零件技术规范A840/A840M-00 全处理的磁性夹层钢A841/A841M-01 压力容器用温度机械控制工艺加工的钢板A842-85(1997) 高密度石墨铸铁A844/A844M-93(1999) 压力容器用直接淬火加工的含镍9%的合金钢板A845-85(2000) 用于脱氧与合金钢的钛碎片A846-85(2000) 用于脱氧与合金钢的铝碎片A847-99a 具有增强耐大气腐蚀性能的冷成型焊接与无缝高强度低合金结构管A848/A848M-96 低碳磁铁A849-00 波纹钢排水管和污水管用后涂覆铺面和衬里材料A851-96 高频感应焊接的未退火奥氏体钢冷凝器管A852/A852M-00a 最小屈服强度为70Ksi(485MPa),厚度为4英寸(100mm)的经淬火和回火的低合金结构钢板A853-93(1998) 普通碳素钢丝A854/A854M-98 镀锌高强度钢栅栏和格架用光滑金属线A855/A855M-98 锌-5%铝-铈合金涂覆的钢丝绳A856/A856M-98 锌-5%铝-铈合金涂覆的碳素钢丝A857/A857M-00a 冷成形轻型薄钢板桩A858/A858M-00 低温和腐蚀情况下用热处理碳素钢配件A859/A859M-95(1999) 压力容器部件用时效硬化镍铜铬钼钶低碳合金钢锻件A860/A860M-00 锻制高强度低合金钢的高强度对缝焊接配件A861-94e1 高硅铁管和配件A862/A862M-98 波纹钢污水管和排水管沥清(柏油)涂层的应用A865-97 钢管连接用黑色或镀锌焊接或无缝钢螺纹接头A866-94 耐磨中碳轴承钢A867/A867M-94(1998)e1 继电器用铁硅钢。
ASTM标准号A B C
ASTM标准号A B CASTM A/B/C/D/E/F/G 2006年标准，只为索引无下载A3-01(2006) 低、中、高碳素钢鱼尾（连接）板A20/A20M-06 压力容器用钢板材通用要求A34/A34M-06 磁性材料的抽样和采购试验的标准惯例A49-01(2006) 经热处理的碳素钢鱼尾（连接）板，微合金鱼尾板及锻制碳素钢异型鱼尾板A53/A53M-06 无镀层热浸的、镀锌的、焊接的及无缝钢管的技术规范A74-06 铸铁污水管及配件的技术规范A106/A106M-06a 高温用无缝碳素钢管A135/A135M-06 电阻焊钢管A159-83(2006) 汽车用灰铁铸件A181/A181M-06 普通锻制碳素钢管的规格A182/A182M-06 高温设备用锻制或轧制的合金钢管法兰、锻制管件、阀门及零件A184/A184M-06 混凝土加筋用变形钢筋编织网A185-06e1 钢筋混凝土用焊接钢丝结构A193/A193M-06a 高温设备用合金钢和不锈钢螺栓材料A194/A194M-06a 高温和高压设备用碳素钢与合金钢螺栓和螺母的规格A197/A197M-00(2006) 化铁炉用可锻铸铁A213/A213M-06ae1 无缝铁素体和奥氏体合金钢锅炉、过热器和换热器管A227/A227M-06 机械弹簧用冷拉钢丝A234/A234M-06 中温与高温下使用的锻制碳素钢及合金钢管配件A240/A240M-06c 压力容器用耐热铬及铬镍不锈钢板、薄板及带材A275/A275M-06 钢锻件的磁粉检查试验方法A276-06 不锈钢棒材和型材A278/A278M-01(2006) 适用于650F容压部件用灰铸铁件的技术规范A312/A312M-06 无缝和焊接奥氏体不锈钢管A319-71(2006) 高温无压部件用灰铁铸件A322-06 合金钢棒材.级别A325-06 经热处理最小抗拉强度为120/105ksi的热处理钢结构螺栓A327-91(2006) 铸铁冲击试验方法A327M-91(2006) 铸铁冲击试验方法(米制)A335/A335M-06 高温用无缝铁素体合金钢管A336/A336M-06 压力与高温部件用合金钢锻件规格A351/A351M-06 容压零件用奥氏体及奥氏体铁素体铸铁的技术规范A352/A352M-06 低温受压零件用铁素体和马氏体钢铸件规格A355-89(2006) 渗氮用合金钢棒A369/A369M-06 高温用锻制和镗孔碳素钢管和铁素体合金钢管A370-06 钢制品机械测试的标准试验方法和定义A376/A376M-06 高温中心站用无缝奥氏钢管A380-06 不锈钢零件、设备和系统的清洗和除垢A387/A387M-06 压力容器用铬钼合金钢板A390-06 饲养家禽用镀锌钢丝栏栅网(六角形和直线形)A400-69(2006) 钢棒的成分及机械性能选择指南A403/A403M-06 锻制奥氏体不锈钢管配件A414/A414M-06 压力容器用碳素薄钢板A416/A416M-06 预应力混凝土用无涂层七股钢铰线A420/A420M-06 低温下用锻制碳素钢和合金钢管配件A424-06 搪瓷用钢薄板A434-06 热轧与冷精轧经回火及淬火的合金钢棒A436-84(2006) 奥氏体灰口铁铸件A437/A437M-06 高温用经特殊处理的涡轮型合金钢螺栓材料A451/A451M-06 高温用离心铸造的奥氏体钢管A466/A466M-01 非焊接碳素钢链A467/A467M-01(2006) 机器链和盘旋链A469/A469M-06 用于发电机转子的真空处理钢锻件A471-06 涡轮转子转盘和转轮用真空处理合金钢锻件技术规范A479/A479M-06a 锅炉及压力容器用不锈钢和耐热钢棒与型材A480/A480M-06a 扁平轧制耐热不锈钢厚板材、薄板材和带材通用要求A484/A484M-06a 不锈及耐热锻钢棒,钢坯及锻件的规格A488/A488M-06 钢铸件焊接规程和工作人员的合格鉴定A490-06 最小拉伸强度为150千磅/平方英寸热处理钢结构螺栓A495-06 硅钙合金钢技术规范A497/A497M-06e1 钢筋混凝土用焊接变形钢丝网A498-06 无缝与焊接碳素钢,铁素体钢与奥氏体钢制有整体散热片的换热器钢管A503/A503M-01(2006)e1 锻制大型曲轴的超声波检验A507-06 优质拉拔,热轧和冷轧合金钢薄板与带材A510-06 碳素钢盘条和粗圆钢丝通用要求A510M-06 碳素钢盘条和粗圆钢丝通用要求A512-06 冷拉对缝焊碳素钢机械管A513-06a 电阻焊碳素钢与合金钢机械钢管A516/A516M-06 中温及低温压力容器用碳素钢板A519-06 无缝碳素钢与合金钢机械管A522/A522M-06 低温用锻制或轧制含镍8%和9%的合金钢法兰,配件,阀门和零件规格A531/A531M-91(2006) 涡轮发电机钢定位环的超声波检验A537/A537M-06 压力容器用经热处理的碳锰硅钢板A540/A540M-06 特殊用途的合金钢螺栓材料A550-06 铌铁合金A553/A553M-06 压力容器用经回火和淬火的含8%及9%镍的合金钢板A562/A562M-06 搪玻璃或扩散金属镀层的压力容器用锰钛合金碳素钢板A563M-06 碳素钢及合金钢螺母技术规范（米制）A568/A568M-06a 热轧及冷轧高强度低合金碳素钢薄板A571/A571M-01(2006) 适用于低温压力容器零件的奥氏体球墨铸铁件A572/A572M-06 高强度低合金钴钒结构钢技术规范A576-90b(2006) 特级热轧碳素钢棒A580/A580M-06 耐热不锈钢丝A595/A595M-06 结构用圆锥形低碳钢管A608/A608M-06 高温受压离心铸造的铁铬镍高合金钢管A615/A615M-06a 钢筋混凝土配筋用变形和光面坯钢筋A623-06a 锡轧制产品A623M-06a 镀锡薄钢板轧制品通用要求(米制)A633/A633M-01(2006) 正火的高强度低合金结构钢A635/A635M-06a 热轧碳素钢薄板,带材和重型粗盘条规格A653/A653M-06 热浸处理的镀锌铁合金或镀锌合金薄钢板的标准规范A659/A659M-06 商业级热轧碳素钢薄板和带材(最大含碳量为0.16%-0.25%)A663/A663M-89(2006) 商品级碳素钢棒的机械特性A664-06 在ASTM规范中对电工钢和层压钢级别的识别A671-06 常温和较低温用电熔焊钢管A672-06 中温高压用电熔焊钢管A679/A679M-06 硬(冷)拉高抗拉强度钢丝A684/A684M-06 冷轧高碳钢带材A693-06 沉淀硬化耐热不锈钢板、薄板和带材A696-90a(2006) 压力管道部件专用热锻或冷精轧碳素钢棒A702-89(2006) 热锻钢栅栏柱和组件A703/A703M-06 受压部件用钢铸件A704/A704M-06 混凝土加筋用焊接普通钢棒或杆的光面钢筋或钢筋网A706/A706M-06a 混凝土配筋用变形低合金光面无节钢筋A709/A709M-06 桥梁用结构钢A717/A717M-06 单片样品表面绝缘电阻率的试验方法A722/A722M-06 预应力混凝土用无涂覆的高强度钢筋A729/A729M-06 货物运输及电气铁路用热处理合金钢轴A739-90a(2006) 升温或/和加压部件用热轧合金钢棒A743/A743M-06 一般用耐腐蚀铬铁及镍铬铁合金铸件A744/A744M-06 严酷条件下使用的耐腐蚀镍铬铁合金铸件A751-01(2006) 钢制品化学分析的实验方法、操作和术语A754/A754M-06 X射线荧光涂层厚度的试验方法A760/A760M-06 下水道和排水沟用金属涂覆的波纹钢管A774/A774M-06 低温和中温一般腐蚀情况下用的焊接锻制奥氏体不锈钢配件A775/A775M-06 涂环氧树脂的钢筋钢棒A781/A781M-06 一般工业用一般要求的钢和合金铸件A782/A782M-06 经淬火和回火的锰铬钼硅锆合金钢压力容器板A788/A788M-06 钢锻件A792/A792M-06 热浸工艺法处理的55%铝-锌合金涂覆钢板A796/A796M-06 雨水管和卫生污水管及其它地下埋设管道用波纹钢管、管托架及拱形架结构设计惯例A800/A800M-01(2006) 奥氏体合金钢铸件中铁素体含量的估算A802/A802M-95(2006) 钢铸件外观检验的表面验收标准A818-06 镀铜碳素钢丝A820/A820M-06 纤维增强混凝土用钢纤维A829/A829M-06 结构性合金钢板A830/A830M-06 按照化学成分要求提供的优质碳素钢板技术规范A832/A832M-06 压力容器板用铬钼钒及铬钼钒钛硼合金钢A834-95(2006) 一般工业用铁铸件的一般要求A837/A837M-06 渗碳用合金钢锻件A840/A840M-00(2006) 全处理的磁性夹层钢A848-01(2006) 低碳磁铁A858/A858M-06 低温和腐蚀情况下用热处理碳素钢配件A865-06 钢管连接用黑色或镀锌焊接或无缝钢螺纹接头A879/A879M-06 每面镀层质量应予标明的电解镀锌薄钢板A897/A897M-06 等温淬火球墨铸铁A900/A900M-01(2006) 非晶磁性带材叠装系数的测试方法A902-06 与金属涂覆的钢制品有关的标准技术术语A917-06a 要求每一面标识有镀层质量用的电解工艺涂层的薄钢板材标准规范A918-06 要求在每一面标识有涂层质量用电解工艺镀锌镍合金的薄钢板技术规范A923-06 检测锻制双重奥氏体/铁素体不锈钢中有害金属间相的标准试验方法A924/A924M-06 用热浸镀法对薄钢板金属涂层的一般要求的标准规范A932/A932M-01(2006) 用瓦特计-安培计-伏特计和薄钢板样品测试在电源频率下非晶体材料交流磁性能的标准试验方法A937/A937M-06 使用临界试验面测定绝缘涂层层间阻力的标准测试方法A939-96(2006) 圆柱体锻件镗孔表面反射超声检测的标准试验方法A940-06 涡轮转子用的差温热处理真空处理钢锻件,合金钢锻件的标准规范A941-06a 钢,不锈钢,有关合金和铁合金术语A945/A945M-06e1 为改良可焊接性、可加工性及粘接性用低碳限硫的高强度低合金结构钢板的标准规范A951/A951M-06 砌体接缝配筋的技术规范A955/A955M-06a 混凝土增强的变形的和无节钢筋技术规范A956-06 钢制品依阔提皮(Equotip)硬度测试方法A957/A957M-06 一般工业用普通要求熔模铸造的钢及合金钢熔模铸件技术规范A958-00(2006) 拉伸要求及化学要求类似于标准铸造等级的碳钢和合金钢铸件的技术规范A960/A960M-06 普通要求的锻制钢管管件的标准规范A962/A962M-06 预定用于从低温至蠕变范围内任何温度的钢紧固件或其材料的通用要求A965/A965M-06a 压力和高温零件用奥氏体钢锻件的技术规范A966/A966M-96(2006) 用交流电和磁粉探伤检验钢锻件的标准试验方法A970/A970M-06 混凝土配筋用焊接或锻制镦头的棒材技术规范A983/A983M-06 中速柴油发动机用连续晶粒流向锻制的碳素钢及合金钢曲轴技术规范A986/A986M-01(2006) 连续晶粒流向曲轴锻件的磁粉探伤检查技术规范A990-06 耐腐用保压零件用特殊控制阀的铁铬镍和铬合金铸件技术规范A992/A992M-06a 建筑框架中使用的结构成型件钢规范A996/A996M-06a 混凝土用条钢和车轴钢变形钢棒规范A1001-01(2006) 大型材高强度钢铸件规范A1008/A1008M-06a 高强度低合金和改性高强度低合金冷轧结构碳钢板材规范A1011/A1011M-06b 高强度低合金和改型高强度低合金热轧结构碳钢板材和带材规范A1014/A1014M-06 高温下使用的沉淀硬化螺栓连接材料规范(UNS N07718)A1017/A1017M-06 压力容器铬-钼-钨合金钢板规范A1018/A1018M-06c 含铌或钒的高强度低合金和改性高强度低合金热轧厚镀锡卷板结构碳钢板材和带材规范A1022/A1022M-06 用于混凝土加固的变形和未变形的不锈钢钢筋和焊接钢筋规范A1035/A1035M-06 用于混凝土加固的变形和未变形的低碳含铬棒材规范A1040-06 Standard Guide for Specifying Harmonized Standard Grade Compositions f or Wrought Carbon, Low-Alloy, and Alloy SteelsA1046/A1046M-06 Standard Specification for Steel Sheet, Zinc-Aluminum-Magnesium Alloy-Coated by the Hot-Dip ProcessA1048/A1048M-06 Standard Specification for Pressure Vessel Forgings, Alloy Steel, High er Strength Chromium-Molybdenum-Tungsten for Elevated Temperature ServiceA1049/A1049M-06 Standard Specification for Stainless Steel Forgings, Ferritic/Austenitic(Duplex), for Pressure Vessels and Related ComponentsA1053/A1053M-06 Standard Specification for Welded Ferritic-Martensitic Stainless Steel PipeC10-06 Standard Specification for Natural CementC11-06 石膏及相关建材和系统相关术语C12-06 陶化粘土管线的安装C24-01(2006) 耐火和高矾土耐溶材料的溶锥当量测试法C25-06 石灰石,生石灰和熟石灰的化学分析方法C31/C31M-06 现场混凝土试样的制备和养护C43-06 结构用粘土制品的术语C51-06 与石灰及石灰石相关的(工业用)名词术语C59/C59M-00(2006) 石膏铸件和模型用灰泥C61/C61M-00(2006) 基恩(Keene)石膏水泥C67-06 砖及结构粘土瓦的取样和试验的试验方法C70-06 细集料表面湿度的测试方法C90-06a 承重混凝土空心砌块C94/C94M-06 搅拌好的混凝土规范C99-87(2006) 规格石料断裂模数的试验方法C110-06 生石灰,熟石灰和石灰石的物理试验方法C119-06 与规格石料相关的术语C120-06e1 石板的弯曲试验方法(弯曲模数和弹性模数)C121-06 石板吸水性的试验方法C125-06a 与混凝土和混凝土集料相关术语C131-06 用洛杉机磨耗试验机测定小规格粗集料的抗磨性与抗冲击性的试验方法C136-06 细集料及粗集料筛分试验方法C148-00(2006) 玻璃容器偏振检验的试验方法C157/C157M-06 硬化水泥灰浆和混凝土长度变化的试验方法C159-06 釉面陶瓷过滤块C170-06 天然建筑石料抗压强度的试验方法C174/C174M-06 混凝土钻心测量长度的试验方法C192/C192M-06 实验室中制造和养护混凝土的试验样品C207-06 砌筑用熟石灰C212-00(2006) 建筑用饰面瓷砖C216-06 饰面砖(粘土或页岩制实心砌块)C230/C230M-03 水硬性水泥试验用流动台C260-06 混凝土用加气混合物C265-06 水化硅酸盐水泥灰浆中的硫酸钙的试验方法C267-01(2006) 灰浆,薄浆和整块铺面石料耐化学侵蚀性的试验方法C270-06 砌块用的灰浆C273/C273M-06 夹层结构或夹层芯材的平直剪切性能的试验方法C305-06 塑性稠度的水硬性水泥泥浆和灰浆机械搅拌C309-06 养护混凝土用液态成膜化合物C315-06 粘土烟道衬砌料C323-56(2006) 卫生陶瓷粘土的化学分析的试验方法C329-88(2006) 焙烧卫生陶瓷材料比重的试验方法C341/C341M-06 水泥灰浆或混凝土的钻取试样和锯取试样长度变化的试验方法C359-06 硅酸盐水泥早硬的试验方法(灰浆法)C368-88(2006) 陶瓷器具抗冲击性的试验方法C370-88(2006) 焙烧卫生陶瓷制品受潮膨胀的试验方法C373-88(2006) 焙烧卫生陶瓷制品的吸水率、松密度、表观多孔性与表观比重的试验方法C375-58(2006) 搪瓷研磨用水的分类C387/C387M-06a 灰浆和混凝土用包装、烘干和复合材料C393/C393M-06 平夹层结构的挠曲试验方法C395-01(2006) 耐化学腐蚀的树脂灰浆C400-98(2006) 中和废酸用生石灰和熟石灰的试验方法C404-06 砌筑用灰浆集料C406-06 屋面石板瓦C408-88(2006) 卫生陶瓷制品传热性的试验方法C413-01(2006) 耐化学侵蚀的灰浆,薄浆和整块铺面石料吸收性的试验方法C424-93(2006) 用热压处理法测定焙烧卫生釉瓷抗破裂性的试验方法C428-05(2006) 石棉水泥无压污水管C448-88(2006) 工业瓷器茨漆的耐磨蚀的试验方法C452-06 暴露在硫酸盐中的硅酸盐水泥灰浆潜在膨胀性的试验方法C457-06 硬化混凝土中孔隙度和孔隙系统参数的显微测定的试验方法C458-98(2006) 石棉水泥制品中有机纤维含量的试验方法C459-97(2006) 石棉水泥板制品的试验方法C473-06 石膏板制品和石膏板条的物理测试标准试验方法C478-06b 预制钢筋混凝土检查井构件C478M-06b 预制钢筋混凝土检查井构件(米制)C500-98(2006) 石棉水泥管的试验方法C509-06 多孔弹性预成型垫片和密封材料C539-84(2006) 用干扰法测定搪瓷、釉瓷和白色陶瓷材料线性热膨胀的试验方法C541-98(2006) 石棉水泥管道的衬料C547-06 预制矿物纤维管形绝热材料C549-06 珠光岩疏松填充隔热材料C554-93(2006) 用热冲击法测定焙烧上釉卫生陶瓷器抗裂开的试验C578-06 刚性,蜂窝状聚苯乙烯的隔热C584-81(2006) 卫生陶瓷器具和有关制品的透光光泽度的试验方法C595-06 混合水硬性水泥C602-06 农用石灰处理材料C632-88(2006) 搪瓷用薄钢板的再煮倾向的试验方法C636/C636M-06 吸音瓦及铺设顶棚镶板用金属悬吊装置的安装C642-06 硬化混凝土的比重、吸收性及空隙度的试验方法C645-06 石膏板上无荷载(轴向)承载钢柱,滑槽(道)和硬性槽钢用的螺钉C661-06 用硬度计测量弹性密封件的压痕硬度的试验方法C665-06 木框架和轻型建筑物用矿质纤维毡绝热材料C674-88(2006) 卫生陶瓷材料的挠曲特性的试验方法C692-06 评定奥氏体钢热绝缘材料对外部应力腐蚀开裂趋势的影响的试验方法C694-90a(2006) 薄钢板在硫酸溶液浸渍过程中重量损失(质量损失)的试验方法C703-72(2006) 铝制搪瓷涂层的抗脱落试验方法C715-90(2006) 用光度计分析法测定搪瓷用钢表面沉积镍量的试验方法C716-06 安装锁条衬垫和固定上光材料C717-06 建筑用密封剂和密封料的术语C731-00(2006) 包装老化后胶乳密封料的可挤压性试验方法C732-06 人工风蚀对胶乳密封料老化效果的试验方法C734-06 胶乳密封料受人工气候影响后的低温柔韧性的试验方法C738-94(2006) 从上釉陶瓷表面提取铅和镉的试验方法C756-87(2006) 表面精整的清洁性试验方法C757-06 核纯级可烧结的二氧化钚粉末的规格C764-06 矿物纤维疏松填充热绝缘C773-88(2006) 预制封缝带泛油或增塑剂泛出的试验方法C774-88(2006) 焙烧的白色陶瓷材料抗压(压碎)强度的试验方法C778-06 玻璃上陶瓷装璜耐硫化物作用的试验方法C780-06 混凝土表面水平方向抗磨力的测试方法C787-06 浓缩用六氟化铀C794-06 弹性封缝料的抗撕裂粘附力的试验方法C810-90(2006) 用X射线光谱测定法测定搪瓷用钢制品表面镍沉积量的试验方法C822-06 混凝土管及其有关制品的术语C825-06 预制混凝土栅栏C830-00(2006) 用真空压力法测定耐火砖和异型砖的表观多孔性、吸水性、表观比重和体密度的试验方法C835-01(2006) 20-1400℃表面整个半球辐射热的测试方法C836-06 分层磨损层用的高固体含量冷却液体用弹性防水薄膜C840-06 石膏板的加工和应用C843-99(2006) 石膏砌面粉饰的应用C848-88(2006) 用共振法测定卫生陶瓷的弹性模量、切变模量和泊松比的试验方法C849-88(2006) 卫生陶瓷努氏压痕硬度的试验方法C864-05 致密弹性压缩密封垫片，调整垫块和定位块技术规范C866-77(2006) 卫生陶瓷粘土的过滤速率的测试方法C869-91(2006) 泡沫混凝土用生产预制泡沫材料用发泡剂C880-06 天然建筑石料弯曲强度的试验方法C889-06 核纯级的氧化钆(Gd2O3)粉末规格C890-06 整体或分段预制混凝土贮水及废水建筑物的最低结构设计负载的推荐规程C902-06 行人及交通不繁忙的道路用铺面砖C904-01(2006) 耐化学腐蚀的非金属材料的术语C905-01(2006) 耐化学的灰浆、薄胶泥和整体面层的表观密度的试验方法C908-00(2006) 预制密封带的屈服强度的试验方法C910-06 单一成份弹性溶剂释放型密封料的粘结力及粘聚力的试验方法C926-06 硅酸盐水泥基灰浆的应用C932-06 室外粉刷表面用粘结剂C933-05 焊丝板条C953-06 在实验室内测定预置集料混凝土的灌浆料凝固时间的试验方法C955-06 螺钉安装石膏板及金属灰泥基板用承载(横向及轴向)钢墙骨、导板、系杆或隔栅撑C957-06 与整体磨损层一同使用的冷却液用含大量固体物质的弹性防水薄膜C961-06 热用密封材料的搭接剪切强度的试验方法C968-06 烧结氧化钆及二氧化铀丸粒的分析方法C970-87(2006) 多个容器堆中专用核材料取样C972-00(2006) 密封带的压缩恢复的试验方法C989-06 混凝土和灰浆用研磨成颗粒状的高炉碎渣的技术规范C990-06 使用预制接缝密封胶粘结的混凝土管道、检查孔和预制箱型型件C990M-06 使用预制接缝密封胶粘结混凝土管道、检查孔和预制箱形件C992-06 核废燃料存放架用系列硼基中子吸收材料设备C1009-06 核工业化学分析实验室制订质量保证大纲C1015-06 纤维素和矿物纤维松充填热绝缘装置C1028-06 用水平功率拉力计法估价瓷砖及其它相同表面的磨擦电系数的试验方法C1032-06 钢丝网抹灰底层C1043-06 使用护热板装置中线电源加热器时稳态热传导特性测量用的加热板温度的测定C1072-06 砌块抗弯粘结强度的测定C1077-06 建筑用混凝土和混凝土集料的实验室测试标准惯例和实验室评定准则C1083-06 弹性泡沫垫圈和密封材料吸水性的试验方法C1088-06 粘土或泥板岩制薄陶面砖C1089-06 离心铸造的预应力混凝土C1093-06 砌块试验方法的鉴定C1094-01(2006) 可移动的挠性绝热覆盖物C1097-06 沥青混凝土混合物用熟石灰C1104/C1104M-00(2006) 测定未覆面矿物纤维绝缘材料蒸汽的吸收率的试验方法C1108-99(2006) 控制电势库仑法测定钚的试验方法C1114-00(2006) 薄加热设备稳态热传导特性的试验方法C1115-06 密实弹性体硅橡胶衬垫和附件C1120-98(2006) 石棉清洗试验方法C1136-06 热绝缘材料用柔性、低渗透蒸汽阻化剂C1141-06 喷浆混凝土用添加剂C1145-06 高级陶瓷术语C1154-06 石棉水泥和纤维水泥术语C1166-06 致密及多孔弹性体衬垫和附件火焰蔓延的试验方法C1170-06 使用振动台测定滚动压实混凝土的稠度和密度的试验方法C1173-06 地下管道系统用挠性过渡管联接件C1177/C1177M-06 用于遮敝的玻璃衬垫石膏基层C1210-06 制定核工业分析化学实验室用测量系统质量控制大纲C1215-92(2006) 核工业用试验方法标准中精密度与及偏倚报告的编写和表达C1217-00(2006) 处理核材料及放射性材料用设备的设计C1222-06 实验室试验水硬水泥的评定C1226-93(2006) 石棉中可溶氯化物的试验方法C1239-06a 报告单轴强度数据和评估高级陶瓷维泊尔分布参数C1245/C1245M-06 测定路碾水硬性压缩混凝土与其它水硬性水泥混合物结合强度的标准试验方法-点负荷试验C1248-06 用连接密封层时多孔衬底染色的标准试验方法C1249-06a 结构件密封剂上光泽用的密封隔热玻璃装置二次密封指南C1257-06 溶剂释放型密封剂加速老化的标准试验方法C1267-06 近距预演金属探测器操作灵敏度设置调整的标准规程C1271-99(2006) 石灰和石灰岩X射线光谱分析标准试验方法C1274-00(2006) 用物理吸收法对高级陶瓷比表面积的标准试验方法C1277-06 防护联接器连接无毂铸铁污水管和配件标准规范C1278/C1278M-06 增强纤维石膏镶板标准规范C1282-00(2006) 用离心光电沉淀法测定高级陶瓷粒径分布的标准试验方法C1283-06 安装粘土烟道衬块的标准操作规范C1289-06 贴面硬质泡沫聚异氰尿酸酯隔热板的标准规范C1290-06 外部隔热HVAC导管用的软玻璃纤维地毯隔热材料的标准规范C1293-06 用测定碱-硅石反应引起的混凝土长度变化对混凝土集料的标准试验方法C1305-06 液体外加防水薄膜的裂缝挖补能力的标准测定方法C1315-06 固化混凝土和密封混凝土液膜性化合物特种性能的标准规范C1341-06 连续纤维增强高级陶瓷合成物弯曲特性的标准试验方法C1355/C1355M-96(2006) 玻璃纤维增强的石膏组合件的技术规范C1364-06 建筑铸石的标准规范C1367-06 最大承载剪切下热应用密封剂的标准试验方法C1368-06 在环境温度下加恒定应力弯曲试验测定整体高级陶瓷裂纹缓慢增长参数的标准试验方法C1384-06a 砌筑用砂浆改性剂技术规范C1393-00a(2006) 管道和罐绝热用的垂直导向矿物质纤维包裹物和覆盖物规范C1396/C1396M-06 石膏灰泥屋顶板规范C1433M-06 涵洞，雨水排放管道和污水管道用的预浇筑加强混凝土箱型制件规范（米制）C1433-06 涵洞，雨水排放管道和污水管道用的预浇筑加强混凝土箱型制件规范C1435/C1435M-06 用震动锤在桶型模具中模压制作滚轮压缩的混凝土标准惯例C1442-06 用人工风化仪器对密封剂进行试验标准惯例C1452-00(2006) 高压加气增强混凝土构件规范C1453-00(2006) 用核级二氧化铀粉末和颗粒点火及氧铀(O/U)原子比法测定铀的试验方法C1461-06 地下和地上用接合排水、废物、通风、污水、卫生及暴雨排放系统用带热塑弹性垫圈的机械连接器的规范C1464-06 弯曲玻璃规范C1465-00(2006) 高温下用恒定应力速度挠曲试验测定高级陶瓷的慢裂增长系数的标准试验方法C1467/C1467M-00(2006) 模制玻璃纤维增强石膏部件安装规范C1468-06 室温下连续纤维增强高级陶瓷过渡厚度抗拉强度试验方法C1470-06 高级陶瓷热性能测试指南C1472-06 确定密封材料接缝宽度时计算运动和其它影响因素的标准指南C1474-00(2006)e1 四极感应耦合等离子质谱法分析核纯级燃料中铀的同位素组分的试验方法C1476-06 感应耦合等离子质谱法分析尿液中锝99试验方法C1477-06 多收集器感应耦合等离子质谱法分析六氟化铀同位素丰度的标准试验方法C1478-06 钢筋混凝土雨水排水结构、管道和支管之间的雨管水道弹性连接件规范C1478M-03(2006) 钢筋混凝土雨水排水结构、管道和支管之间的雨管水道弹性连接件规范(米制）C1481-00(2006) 外部绝缘和精整系统用密接剂使用的标准指南C1485-06 用电辐射热能量源测量露天阁楼地板绝缘材料临界辐射通量的测试方法C1495-06 表面研磨对高级陶瓷抗弯强度影响试验方法C1507-01(2006) 土壤中锶-90放射化学测定的试验方法C1508-01(2006) 用X射线荧光光谱法测定UF-6和硝酸铀酰中溴和氯的含量的标准试验方法C1529-06 生石灰、熟石灰和石灰石的环境用途规范C1532-06 从现有建筑选择，移动，装运石工装配样品指南C1577-06 Standard Specification for Precast Reinforced Concrete Box Sections fo r Culverts, Storm Drains, and Sewers Designed According to AASHTO LRFDC1579-06 Standard Test Method for Evaluating Plastic Shrinkage Cracking of Res trained Fiber Reinforced Concrete (Using a Steel Form Insert)C1587-06 Standard Practice for Preparation of Field Removed Manufactured Masonr y Units and Masonry Specimens for Compressive Strength TestingC1601-06 Standard Test Method for Field Determination of Water Penetration ofMasonry Wall SurfacesC1602/C1602M-06 Standard Specification for Mixing Water Used in the Production of Hy draulic Cement ConcreteC1607-06 Standard Test Method for Determination of "Microwave Safe for Reheati ng" for CeramicwareC1608-06 Standard Test Method for Chemical Shrinkage of Hydraulic Cement Paste C1610/C1610M-06 Standard Test Method for Static Segregation of Self-Consolidating Concrete Using Column TechniqueC1621/C1621M-06 Standard Test Method for Passing Ability of Self-Consolidating Concrete by J-RingC1630-06 Standard Guide for Development of Coverage Charts for Loose-Fill Thermal Building InsulationsC1635-06 Standard Test Method to Evaluate Adhesion/Cohesion Properties of a Se alant at Fixed ExtensionC1636-06a Standard Guide for the Determination of Uranium-232 in Uranium HexafluorideC1637-06 Standard Test Method for the Determination of Impurities in PlutoniumMetal: Acid Digestion and Inductively Coupled Plasma-Mass Spectroscopy (ICP-MS) AnalysisC1638-06 Standard Guide for the Determination of Iodine-129 In Uranium OxideC1644-06 Standard Specification for Resilient Connectors Between Reinforced Conc rete On-Site Wastewater Tanks and PipesC1645-06 Standard Test Method for Freeze-thaw and De-icing Salt Durability of Solid Concrete Interlocking Paving UnitsC1647-06 Standard Practice for Removal of Uranium or Plutonium, or both, forImpurity Assay in Uranium or Plutonium Materials特别声明：1：资料来源于互联网，版权归属原作者2：资料内容属于网络意见，与本账号立场无关3：如有侵权，请告知，立即删除。
ASTMA20中文版
压力容器用钢板通用要求SA-20/SA-20M(与ASTM标准A20/A20M-04完全等同)1 适用围1.1 本标准包括一组通用要求，除专用材料标准中另有规定外，这些要求应适用于下列各项ASTM压力容器用轧制钢板标准：1.1.1 本标准还包括一组补充要求，适用于上列若干个标准中本身已指明的场合。
这些补充要求仅当买方在订货单中要求附加试验或检验并作了单独规定时采用。
1.2 附录X1叙述了制造压力容器钢板用卷材的生产及一些特性。
1.3 附录X2提供了关于压力容器用钢板拉伸性能变化性的资料。
1.4 附录X3提供了关于压力容器用钢板夏比V型缺口冲击试验性能变化的材料。
1.5 附录X4提供了包括冷弯时建议的最小弯曲半径在的有关钢板冷弯的资料。
1.6 这些材料仅适于熔焊，熔焊时应采用适合于该钢种级别及使用条件的焊接工艺。
1.7 如本标准与专用材料标准的要求不一致，则以专用材料标准的要求为准。
1.8 买方可以规定不否定本标准或专用材料标准任何条款的附加要求。
这些附加要求必须纳入采购订货单说明中，并取得供方同意。
1.9 为了确定供应材料是否与标准及材料标准的规定极限值相一致，各数值右面的有效位数应按E29推荐的圆整方法进行圆整。
1.10 以英寸-磅单位或SI单位表示的数值均可作为标准值。
本文中SI单位表示于括号。
由于各单位制所表示的数值不能与另一种单位制进行精确换算，因此，每一种单位制必须独立使用。
1.11 本标准及所引用的材料标准均采用英寸-磅和SI两种单位，但除非订货单中规定采用“M”标志（SI单位），材料将以英寸-磅单位供货。
2 引用标准3 术语3.1 本标准专用术语说明：3.1.1 封顶钢---因受早期压盖过程而使沸腾作用受到限制的沸腾钢。
压盖可用机械方法，在瓶口式锭模顶部采用一个重的金属槽，也可用化学方法对敝口式锭模中钢水的顶部加铝或硅铁。
3.1.2 卷板—以卷材形式加工为成品钢板的热轧钢。
3.1.3 除外—当应用与围有关时，例如尺寸允许偏差表中厚度的围，本术语表示不包括围中的较大值。
ASTM美国标准
1013A1013-00 Standard Test Method for High-Frequency (10 kHz-1 MHz) Core Loss 1014A1014-02 Standard Specification for Precipitation-Hardening Bolting Materi 1015A1015-01 Standard Guide for Videoborescoping of Tubular Products for Sanit 1016A1016/A1016M-02a Standard Specification for General Requirements for Ferritic Allo 1017A1017/A1017M-01 Standard Specification for Pressure Vessel Plates, Alloy Steel, C 1018A1018/A1018M-01a Standard Specification for Steel, Sheet and Strip, Heavy Thicknes 1019A1019/A1019M-01 Standard Specification for Closed Rib Steel Pipe with Diameter of 1020A1020/A1020M-02 Standard Specification for Steel Tubes, Carbon and Carbon Mangane 1021A1021-01 Standard Specification for Martensitic Stainless Steel Forgings a 1022A1022-01 Standard Specification for Deformed and Plain Stainless Steel Wir 1023A1023/A1023M-02 Standard Specification for Stranded Carbon Steel Wire Ropes for G 1024A1024/A1024M-02 Standard Specification for Steel Line Pipe, Black, Plain-End, Sea 1025A1025-02通用铁合金规范头的结果设计指南o the Minimum Expected Corrosion Characteristics of Metallic, Painted-Metallic, and Nonmetallic-Coated Steel Sheet Intend pe, Black, Plain End, Longitudinal and Helical Seam, Double Submerged-Arc Weldedpe, Black, Plain End, Laser Beam WeldedWire for Wire RopeCold-Rolled, Carbon, Structural, High-Strength Low-Alloy and High-Strength Low-Alloy with Improved MnZn Ferrite Core Materials for High Frequency (10 kHz-1 MHz) Power Transformer and Filter Inductor th Martensitic Stainless Steel Plate, Sheet , and Stripand Strip, Hot-Rolled, Carbon, Structural, High-Strength Low-Alloy and High-Strength Low-Alloy with Welded Ferritic, Austenitic and Duplex Alloy Steel Condenser and Heat Exchanger Tubes With Integral(10 kHz-1 MHz) Core Loss of Soft Magnetic Core Components at Controlled Temperatures Using the Voltm -Hardening Bolting Material (UNS N07718) for High Temperature Serviceubular Products for Sanitary Applicationsrements for Ferritic Alloy Steel, Austenitic Alloy Steel, and Stainless Steel Tubesel Plates, Alloy Steel, Chromium-Molybdenum-Tungstenand Strip, Heavy Thickness Coils, Hot Rolled, Carbon, Structural, High-Strength Low-Alloy, Columbium eel Pipe with Diameter of 36 in. [900 mm] or Less, Polymer Precoated for Sewers and DrainsCarbon and Carbon Manganese, Fusion Welded, for Boiler, Superheater, Heat Exchanger and Condenser Ap tainless Steel Forgings and Forging Stock for High-Temperature ServicePlain Stainless Steel Wire and Welded Wire for Concrete Reinforcementon Steel Wire Ropes for General Purposespe, Black, Plain-End, Seamless。
ASTM_A240-05中温压力容器用耐热铬及铬镍不锈钢板、薄板和带材的标准规范(中文版)
…
0.75 0.75
0.75
0.75
1.0-2.0 0.5-1.5 … … 1.00 … … … …
… … … … … … … … … … … … … … … … … 0.50 0.35 … … … … …
…
…
2.00
0.045
0.030
0.75
24.0-26.0
19.0-22.0
…
…
…
2.00
0.045
2.00 2.00 5.5-7.5 5.5-7.5 6.4-7.5 4.0-6.0 7.5-10.0 7.0-9.0 4.0-6.0
14.0-16.0 7.5-9.0 7.5-9.0 7.0-9.0 11.5-14.5 2.00 2.00 2.00 2.00 2.00 2.00 2.00 0.80 2.00 2.00 2.00 2.00 2.00 0.50-0.80 2.00 0.80 2.00 2.00 2.00
4 可 从 汽 车 工 程 协 会 （ SAE ） 获 得 。 该 协 会 位 于 400 Commonwealth Dr., Warrendale, PA 15096-0001。
* 修改的总结部分在本标准的结束部分。 ASTM International 的版权©，100 Barr Harbor Drive, 邮政信箱 C700, West Conshohocken,PA 19428-2959, 美国
12.0-16.0
19.0-22.0
6.0-7.0 …
…
…
4.0-5.0 6.0-7.0 … … … … … … 1.50-3.00
… 2.00-3.00 2.00-3.00 … … … … … … … … … … … … … … 0.20 0.20 … … … … …
A20及A6标准介绍
4
一、定义
2. ASTM 及ASME 区别 a. ASTM材料经ASME认可,可用于承压设备后就成为ASME 材料(ASME锅炉压力容器规范第Ⅱ卷)，ASME材料标准大部分 都是引用ASTM的，也有引用其他国际性规范； b. ASME标准中的材料编号以SA打头，而ASTM标准中的 材料编号以A打头。 c. 在ASME锅炉压力容器规范第Ⅱ卷各篇开篇部分有明 确说明是否与ASTM等同以及具体的不同点。 d. ASME材料用于承压设备，检验项目要比ASTM的多， 主要是一些材料增加了焊接、热处理、无损检测等要求。
分类美标国标厚度附加无厚度附加值概念分nabc四类偏差力学性能均默认无冲击要求根据牌号不同要求不同冲击方向均默认纵向结构桥梁等钢种为纵向容器为横向标识名称写法很多唯一附加性能附加项极多附加项很少四具体要求化学成分
1
ASTM A6/A6M及ASTM A20/A20M 标准介绍
2
目录
• • • • • 一、定义 二、适用范围及代表性牌号 三、与国标对比特点 四、具体要求 五、认证许可
3
一、定义
1. 标准概念 • ASTM A6/A6M（ASME SA6/SA6M）：结构用轧制棒材、钢板、 型钢和钢桩的一般要求。 • ASTM A20/A20M(ASME SA20/SA20M)：压力容器用钢板通用 要求。
• ASTM：美国材料与试验协会制定的标准。 • ASME：美国机械工程师协会的标准.
7
三、与国标对比特点
分类 厚度附加 力学性能 冲击方向 标识 附加性能 美标 无厚度附加值概念 均默认无冲击要求 均默认纵向 名称写法很多 附加项极多 国标 分N,A,B,C四类偏差 根据牌号不同要求不同 结构、桥梁等钢种为纵 向，容器为横向 唯一 附加项很少
ASTM A标准(中文)
AA1000-99 弹簧专用碳钢和合金钢钢丝规范A1001-99 大型材高强度钢铸件规范A1002-99 镍铝类合金铸件规范A100-93(2000) 硅铁A101-93(2000) 铬铁A102-93(2000) 钒铁合金A105/A105M-01 管系部件用碳素钢锻件A106-999e1 高温用无缝碳素钢管A108-99 优质冷加工碳素钢棒材技术规范A109/A109M-00e1 冷轧碳素钢带技术规范A111-99a 电话和电报线路用镀锌"铁"丝规格A116-00 镀锌钢丝编织栏栅网A121-99 镀锌刺钢丝A123/A123M-00 钢铁产品的锌镀层（热浸镀锌）技术规范A125-96 热处理螺旋形钢弹簧A126-95(2001) 阀门、法兰和管配件用灰铁铸件A128/A128M-93(1998) 钢铸件,奥氏体锰A131/A131M-94 海船用结构钢A132-89(2000) 钼铁合金A134-96 电熔(电弧)焊钢管(NPS为16英寸和16英寸以上)A135-01 电阻焊钢管A139-00 电熔(电弧)焊钢管(4英寸以上的)A143-74(1999) 热浸镀锌结构钢制品防脆裂措施和探测脆裂的程序A146-64(2000) 氧化钼制品A148/A148M-01 结构用高强度钢铸件A153/A153M-00 钢铁制金属构件上镀锌层(热浸)A159-83(2001) 汽车用灰铁铸件A167-99 不锈钢和耐热铬镍钢板、薄板及带材A176-99 不锈钢和耐热铬钢板、薄板及带材A178/A178M-95(2000) 电阻焊接碳素钢钢管及碳锰钢锅炉和过热器管的技术规范A179/A179M-90a(1996)e1 热交换器和冷凝器用无缝冷拉低碳钢管A181/A181M-01 普通锻制碳素钢管的规格A182/A182M-01 高温设备用锻制或轧制的合金钢管法兰、锻制管件、阀门及零件A183-98 钢轨用碳素钢螺栓和螺母A184/A184M-01 混凝土加筋用变形钢筋编织网A185-97 钢筋混凝土用焊接钢丝结构A1-00 碳素钢丁字轨A192/A192M-91(1996)e1 高压用无缝碳素钢锅炉管A193/A193M-01 高温设备用合金钢和不锈钢螺栓材料A194/A194M-01 高温和高压设备用碳素钢与合金钢螺栓和螺母的规格A197/A197M-00 化铁炉用可锻铸铁A20/A20M-01 压力容器用钢板材通用要求A202/A202M-93(1999) 压力容器用铬锰硅合金钢板A203/A203M-97 压力容器用镍合金钢板A204/A204M-93(1999) 压力容器用钼合金钢板A209/A209M-98 锅炉和过热器用无缝碳钼合金钢管A210/A210M-96 锅炉和过热器用无缝中碳素管A213/A213M-01 无缝铁素体和奥氏体合金钢锅炉、过热器和换热器管A214/A214M-96 热交换器与冷凝器用电阻焊接碳素钢管A216/A216M-93(1998) 高温下使用的适合于熔焊的碳素钢铸件规格A217/A217M-01 适合高温受压零件用合金钢和马氏体不锈钢铸件A21-94(1999) 铁路用未经热处理和经热处理的碳素钢轴A220/A220M-99 珠光体可锻铁A225/A225M-93(1999) 压力容器用锰矾镍合金钢板A227/A227M-99 机械弹簧用冷拉钢丝A228/A228M-00 乐器用优质弹簧钢丝A229/A229M-99 机械弹簧用油回火的钢丝A230/A230M-99 阀门用油回火优质碳素钢弹簧丝A231/A231M-96 铬钒合金钢弹簧丝A232/A232M-99 阀门用优质铬钒合金钢弹簧丝A234/A234M-00a 中温与高温下使用的锻制碳素钢及合金钢管配件A239-95(1999) 用普力斯试验法(硫酸铜浸蚀)确定铁或钢制品上镀锌层最薄点的测试方法A240/A240M-01 压力容器用耐热铬及铬镍不锈钢板、薄板及带材A242/A242M-00a 高强度低合金结构钢A247-67(1998) 铁铸件中石墨显微结构评定试验方法A249/A249M-01 锅炉、过热器、换热器和冷凝器用焊接奥氏体钢管A250/A250M-95(2001) 锅炉和过热器用电阻焊铁素体合金钢管A252-98e1 焊接钢和无缝钢管桩A254-97 铜焊钢管规格A255-99 测定钢淬透性用末端淬火试验的标准试验方法A262-98 奥氏体不锈钢晶间浸蚀敏感性的检测A263-94a(1999) 耐腐蚀铬钢包覆板材,薄板材及带材技术规范A264-94a(1999) 包覆的不锈铬镍钢板,薄板及带材规格A265-94a(1999) 镍和镍基合金包覆钢板规格A266/A266M-99 压力容器部件用碳素钢锻件规格A268/A268M-01 一般设备用无缝和焊接铁素体与马氏体不锈钢管A269-01 一般设备用无缝和焊接奥氏体不锈钢管A27/A27M-95(2000) 通用碳素钢铸件A270-01 卫生设施用无缝钢和焊接奥氏体不锈钢管A275/A275M-98 钢锻件的磁粉检查试验方法A276-00a 不锈钢棒材和型材A278-93 适用于650F容压部件用灰铸铁件的技术规范A283/A283M-00 低和中等抗拉强度碳素钢板A285/A285M-90(2001) 压力容器用低和中等抗拉强度的碳素钢板A288-91(1998) 涡轮发电机磁性定位环用碳素钢和合金钢锻件A289/A289M-97 发电机非磁性定位环用合金钢锻件的技术规范A29/A29M-99e1 热锻及冷加工碳素钢和合金钢棒A2-90(1997) 普通型,带槽和防护型碳素工字钢轨A290-95(1999) 减速器环用碳素钢和合金钢锻件A291-95(1999) 减速器小齿轮、齿轮和心轴用碳素钢和合金钢锻件A295-98 高碳耐磨轴承钢技术规范A297/A297M-97(1998) 一般用耐热铬铁与镍铬铁合金钢铸件规格A299/A299M-97e1 压力容器用锰硅碳钢板A302/A302M-97e1 压力容器用锰钼和锰钼镍合金钢板A304-96 有末端淬火淬透性要求的合金钢棒材的技术规范A307-00 抗拉强度为60000psi的碳素钢螺栓和螺柱的技术规范A308-99 经热浸处理镀有铅锡合金的薄板材的技术规范A309-94a(1999) 用三点试验法测定长镀锌薄钢板镀层的重量成分的试验方法A311/A311M-95(2000) 有机械性能要求的消除应力的冷拉碳素钢棒A312/A312M-00c 无缝和焊接奥氏体不锈钢管A313/A313M-98 不锈钢弹簧丝技术规范A314-97 锻造用不锈及耐热钢坯及钢棒规格A31-00 钢铆钉及铆钉和压力容器用棒材A319-71(2001) 高温无压部件用灰铁铸件A320/A320M-01 低温用合金钢螺栓材料规格A321-90(1995)e1 经淬火和回火的碳素钢棒A322-91(1996) 合金钢棒材.级别A323-93(2000) 硼铁规格A324-73(2000) 钛铁合金A325-00 经热处理最小抗拉强度为120/105ksi的钢结构螺栓A325M-00 结构钢连接件用高强度螺栓(米制)A327-91(1997) 铸铁冲击试验方法A327M-91(1997) 铸铁冲击试验方法(米制)A328/A328M-00 薄钢板桩A331-95(2000) 冷加工合金钢棒A333/A333M-99 低温用无缝与焊接钢管规格A334/A334M-99 低温设备用无缝与焊接碳素和合金钢管A335/A335M-01 高温用无缝铁素体合金钢管A336/A336M-99e1 压力与高温部件用合金钢锻件规格A338-84(1998) 铁路,船舶和其他重型装备在温度达到650华氏度(345摄氏度)时使用的可锻铸铁法兰,管件和阀门零件A34/A34M-96 磁性材料的抽样和采购试验的标准惯例A340-99a 有关磁性试验用符号和定义的术语A341/A341M-00 用直流磁导计和冲击试验法测定材料的直流磁性能的试验方法A342/A342M-99 磁铁材料导磁率的试验方法A343-97 在电力频率下用瓦特计-安培计-伏特计法(100-1000赫兹)和25 厘米艾普斯亭(EPSTEIN) 机架测定材料的交流电磁性能的试验方法A345-98 磁设备用平轧电炉钢A348/A348M-00 用瓦特计--安培计--伏特计法(100-10000赫兹)和25厘米艾普斯亭框测定材料的交流磁性能的试验方法A350/A350M-00c 要求进行缺口韧性试验的管道部件用碳素钢与低合金钢锻件技术规范A351/A351M-00 容压零件用奥氏体及奥氏体铁素体铸铁的技术规范A352/A352M-93(1998) 低温受压零件用铁素体和马氏体钢铸件规格A353/A353M-93(1999) 压力容器用经二次正火及回火处理的含9％镍的合金钢板A354-01 淬火与回火合金钢螺栓,双头螺栓及其他外螺纹紧固件规格A355-89(2000) 渗氮用合金钢棒A356/A356M-98e1 蒸汽轮机用厚壁碳素钢、低合金钢和不锈钢铸件A358/A358M-01 高温用电熔焊奥氏体铬镍合金钢管A36/A36M-00a 碳素结构钢技术规范A363-98 地面架空线用镀锌钢丝绳A367-60(1999) 铸铁的激冷试验方法A368-95a(2000) 不锈钢和耐热钢丝绳的标准A369/A369M-01 高温用锻制和镗孔碳素钢管和铁素体合金钢管A370-97a 钢制品机械测试的标准试验方法和定义A372/A372M-99 薄壁压力容器用碳素钢及合金钢锻件A376/A376M-01 高温中心站用无缝奥氏钢管A377-99 球墨铸铁压力管规范索引A380-99e1 不锈钢零件、设备和系统的清洗和除垢A381-96 高压输送用金属弧焊钢管A384-76(1996) 防止钢组件热浸镀锌时翘曲和扭曲用安全保护A385-00 提供高质量镀锌覆层(热浸)A3-01 低、中、高碳素钢鱼尾（连接）板A387/A387M-99e1 压力容器用铬钼合金钢板A388/A388M-95(2000)e1 重型钢锻件超声波检测A389/A389M-93(1998) 适合高温受压部件用经特殊热处理的合金钢铸件规格A390-95(2001) 饲养家禽用镀锌钢丝栏栅网(六角形和直线形)A391/A391M-98 80号合金钢链条A392-96 镀锌钢丝链环栏栅网A394-00 传动塔架用镀锌和裸露钢螺栓A395/A395M-99 高温用铁素体球墨铸铁受压铸件A400-69(2000) 钢棒的成分及机械性能选择指南A401/A401M-98 铬硅合金钢丝A403/A403M-00b 锻制奥氏体不锈钢管配件A407-93(1998) 盘簧用冷拉钢丝A409/A409M-01 腐蚀场所或高温下使用的焊接大口径奥氏体钢管A411-98 镀锌低碳钢铠装线A413/A413M-00 碳素钢链A414/A414M-00 压力容器用碳素薄钢板A416/A416M-99 预应力混凝土用无涂层七股钢铰线A417-93(1998) 之字型、方型和正弦型装垫弹簧元件用冷拉钢丝A418-99 涡轮机及发电机钢转子锻件的超声波检查方法A420/A420M-00b 低温下用锻制碳素钢和合金钢管配件A421/A421M-98a 预应力混凝土用无涂层消除应力钢丝的技术规范A423/A423M-95(2000) 无缝和电焊低合金钢管A424-00 搪瓷用钢薄板A426-92(1997) 高温用离心铸造的铁素体合金钢管A427-74(1996)e1 冷轧和热轧用锻制合金钢辊A428/A428M-01 钢铁制品上铝覆层重量的测试方法A434-90a(2000) 热轧与冷精轧经回火及淬火的合金钢棒A435/A435M-90(2001) 钢板的直射束纵向超声波检验A436-84(1997)e1 奥氏体灰口铁铸件A437/A437M-01 高温用经特殊处理的涡轮型合金钢螺栓材料A438-80(1997) 灰铸铁横向弯曲试验A439-83(1999) 奥氏体可锻铸铁铸件A447/A447M-93(1998) 高温用镍铬铁合金钢铸件(25-12级)A449-00 经淬火和回火的钢螺栓和螺柱A450/A450M-96a 碳素钢管、铁素体合金钢管及奥氏体合金钢管A451-93(1997) 高温用离心铸造的奥氏体钢管A453/A453M-00 具有同奥氏体钢相类似的膨胀系数、屈服强度为50-120Ksi(345-827MPa)的耐高温螺栓材料A455/A455M-90(2001) 压力容器用高强度碳锰钢板A456/A456M-99 大型曲轴锻件的磁粉检查A459-97 镀锌平轧扁钢铠装带A460-94(1999) 包铜钢丝绳标准A463/A463M-00 热浸镀铝薄钢板A466/A466M-98 非焊接碳素钢链A467/A467M-98 机器链和盘旋链A469-94a(1999) 用于发电机转子的真空处理钢锻件A470-01 涡轮机转子和轴用经真空处理的碳素钢和合金锻件A471-94(1999) 涡轮转子转盘和转轮用真空处理合金钢锻件技术规范A472-98 蒸汽涡轮机轴及转子锻件的热稳定性的试验方法A473-01 不锈和耐热钢锻件A474-98 包铝钢丝绳标准A475-98 镀锌钢丝绳A476/A476M-00 造纸厂干燥辊用球墨可锻铸铁件A478-97 铬镍不锈钢和耐热钢制编织钢丝A479/A479M-00 锅炉及压力容器用不锈钢和耐热钢棒与型材A47/A47M-99 铁素体可锻铁铸件A480/A480M-01 扁平轧制耐热不锈钢厚板材、薄板材和带材通用要求A481-94(2000) 金属铬A482-93(2000) 铬铁硅A483-64(2000) 硅锰合金A484/A484M-00 不锈及耐热锻钢棒,钢坯及锻件的规格A485-00 高淬透性耐磨轴承钢的技术规范A487/A487M-93(1998) 受压钢铸件A488/A488M-01 钢铸件焊接规程和工作人员的合格鉴定A48-94ae1 灰铁铸件A489-00 碳素钢吊耳A490-00 最小拉伸强度为150千磅/平方英寸热处理钢结构螺栓A491-96 镀铝钢链环栏栅结构A492-95(2000) 耐热不锈钢丝绳A493-95(2000) 冷镦和冷锻不锈钢和耐热钢丝A494/A494M-00 镍和镍合金铸件A495-94(2000) 硅钙合金钢技术规范A496-97ae1 钢筋混凝土用变形钢丝A497-99e1 钢筋混凝土用焊接变形钢丝网A498-98 无缝与焊接碳素钢,铁素体钢与奥氏体钢制有整体散热片的换热器钢管A49-01 经热处理的碳素钢鱼尾（连接）板，微合金鱼尾板及锻制碳素钢异型鱼尾板A499-89(1997)e1 轧制丁字钢轨用的碳素钢棒材及型材的技术规范A500-01 圆形与异型焊接与无缝碳素钢结构管A501-01 热成型焊接与无缝碳素钢结构管A503/A503M-01 锻制大型曲轴的超声波检验A504-93(1999) 锻制碳素钢轮A505-00 热轧和冷轧合金钢薄板和带材A506-00 正规质量及优质结构的热轧和冷轧合金钢薄板与带材A507-00 优质拉拔,热轧和冷轧合金钢薄板与带材A508/A508M-95(1999) 压力容器用经回火和淬火真空处理的碳素钢与合金钢锻件A510-00 碳素钢盘条和粗圆钢丝通用要求A510M-00 碳素钢盘条和粗圆钢丝(米制)A511-96 无缝不锈钢机械管A512-96 冷拉对缝焊碳素钢机械管A513-00 电阻焊碳素钢与合金钢机械钢管A514/A514M-00a 焊接用经回火与淬火的高屈服强度合金钢板A515/A515M-92(1997) 中温及高温压力容器用碳素钢板A516/A516M-90(2001) 中温及低温压力容器用碳素钢板A517/A517M-93(1999) 压力容器用经回火与淬火的高强度合金钢板A518/A518M-99 耐蚀高硅铁铸件A519-96 无缝碳素钢与合金钢机械管A521-96 一般工业用闭式模钢锻件A522/A522M-95b(2000) 低温用锻制或轧制含镍8%和9%的合金钢法兰,配件,阀门和零件规格A523-96 高压管型电缆线路用平端无缝与电阻焊钢管A524-96 常温和低温用无缝碳素钢管A529/A529M-00 高强度碳锰结构钢质量A530/A530M-99e1 特种碳素钢和合金钢管A531/A531M-91(1996) 涡轮发电机钢定位环的超声波检验A532/A532M-93a(1999)e1 耐磨铸铁A533/A533M-93(1999) 压力容器用经回火和淬火的锰钼及锰钼镍合金钢板A534-94 用于耐摩擦轴承的渗碳钢A536-84(1999)e1 球墨铸铁件A537/A537M-95(2000) 压力容器用经热处理的碳锰硅钢板A53/A53M-01 无镀层热浸的、镀锌的、焊接的及无缝钢管的技术规范A539-99 天然气和燃料油管线用电阻焊钢盘管A540/A540M-00 特殊用途的合金钢螺栓材料A541/A541M-95(1999) 压力容器部件用经淬火和回火的碳素钢及合金钢锻件A542/A542M-99e1 压力容器用经回火和淬火的铬钼、铬钼钒及铬钼钒钛硼合金钢板A543/A543M-93(1999) 压力容器用经回火和淬火的镍铬钼合金钢板A550-78(2000) 铌铁合金A551-94(1999) 钢轮箍A553/A553M-95(2000) 压力容器用经回火和淬火的含8%及9%镍的合金钢板A554-98e1 焊接的无缝钢机械管A555/A555M-97 耐热不锈钢丝和盘条的通用要求A556/A556M-96 无缝冷拉碳素钢给水加热器管A560/A560M-93(1998) 铬镍合金铸件A561-71(1999) 工具钢棒的宏观刻蚀试验A562/A562M-90(2001) 搪玻璃或扩散金属镀层的压力容器用锰钛合金碳素钢板A563-00 碳合金钢螺母A563M-00 碳素钢及合金钢螺母技术规范（米制）A564/A564M-01 热轧及冷精轧时效硬化处理过的不锈钢棒材和型材技术规范A565-97 高温用马氏体不锈钢棒,锻件和锻制坯规格A568/A568M-00b 热轧及冷轧高强度低合金碳素钢薄板A571-84(1997) 适用于低温压力容器零件的奥氏体球墨铸铁件A571M-84(1997) 适用于低温压力容器零件的奥氏体球墨铸铁件(米制)A572/A572M-00a 高强度低合金钴钒结构钢技术规范A573/A573M-00a 增强韧性的结构碳素钢板A574-00 合金钢内六角螺钉A574M-00 合金钢内六角螺钉(米制)A575-96 商品级碳素钢棒(M级)A576-90b(2000) 特级热轧碳素钢棒A577/A577M-90(2001) 钢板的超声角波束检验A578/A578M-96(2001) 特殊设备用的普通钢板和包覆钢板的直波束超声探伤检验A579-99 超高强度合金钢锻件A580/A580M-98 耐热不锈钢丝A581/A581M-95b(2000) 高速切削用耐热不锈钢丝和盘条A582/A582M-95b(2000) 热轧或冷精轧的高速切削不锈及耐热钢棒A583-93(1999) 铁路用铸钢轮A584-97 镀铝钢丝编织栅栏网A585-97 镀铝刺钢丝A586-98 镀锌平行和螺旋形钢丝绳A587-96 化学工业用电阻焊低碳钢管A588/A588M-00a 高强度低合金结构钢4英寸(100mm)厚屈服点最小为50ksi(345MPa) A589-96 水井用无缝和焊接碳素钢管A591/A591M-98 薄镀层电解镀锌薄钢板A592/A592M-89(1999) 压力容器用经回火和淬火的高强度低合金钢锻制附件和零件A595-98 结构用圆锥形低碳钢管A596/A596M-95(1999) 用环形试验法和冲击法测定材料的直流磁性能的试验方法A597-87(1999) 铸造工具钢A598-92(1997) 磁放大器磁芯的磁性能测试法A599/A599M-99 锡制品，电解镀锡的冷滚轧薄板规范A6/A6M-01 轧制结构钢板材、型材和薄板桩通用技术要求A600-92a(1999) 高速工具钢A601-96(2000) 电解金属锰A602-94(1998) 汽车用可锻铸铁件A603-98 镀锌结构钢丝绳A604-93(1998) 自耗电极再溶化钢棒与钢坯的宏观腐蚀试验方法A606-98 改进防大气腐蚀性的热轧和冷轧高强度低合金钢薄板和带材A608-91a(1998) 高温受压离心铸造的铁铬镍高合金钢管A609/A609M-91(1997) 碳素钢,低合金钢和马氏体不锈钢铸件的超声波检测A610-79(2000) 尺寸测量用铁合金的取样和试验A611-00 冷轧优质碳素结构钢薄板A612/A612M-00 中温和低温压力容器用高强度碳素钢板A615/A615M-01a 钢筋混凝土配筋用变形和光面坯钢筋A618-01 热成型焊接与无缝高强度低合金结构钢管系A623-00 锡轧制产品A623M-00 镀锡薄钢板轧制品通用要求(米制)A624/A624M-98 锡辊轧制品.单压延电解马口铁A625/625M-98 一次轧制原钢板（未镀）和镀锡薄钢板轧制产品技术规范A626/A626M-98 二次压延电解镀锡厚钢板轧制品技术规范A626/A626M-98 锡轧制品.二次压延的电解镀锡板(米制)A627-95 安全设备用均质不易加工的钢棒A629-88(1994)e1 安全设备用不易加工的扁钢棒和型材A630-98 热浸电解镀锡板镀锡层重量测定的方法A632-01 通用无缝和焊接奥氏体不锈钢管(小直径)A633/A633M-00a 正火的高强度低合金结构钢A635/A635M-00 热轧碳素钢薄板,带材和重型粗盘条规格A636-76(2000) 氧化镍烧结块A638/A638M-00 高温用沉积硬化铁基超级合金棒,锻件及锻坯料A640-97 8字型缆吊架用镀锌钢丝绳A641/A641M-98 镀锌（电镀）碳素钢丝技术规范A644-98 铁铸件的相关术语A645/A645M-99a 压力容器用经特殊热处理的5%镍合金钢板A646-95(1999) 飞机及航空器锻件用优质合金钢大方坯及坯段A648-95(2000) 预应力混凝土管用冷拉钢丝A649/A649M-99 波纹纸机械用锻制钢辊规格A650/A650M-98 二次压延的锡轧黑板材A653/A653M-00 热浸处理的镀锌铁合金或镀锌合金薄钢板的标准规范A656/A656M-00a 具有改良可模锻性的高强度低合金热轧结构钢板A657/A657M-98a 一次和二次压延电解镀铬黑钢板轧制品技术规范A65-01 钢轨道钉A659/A659M-97 商业级热轧碳素钢薄板和带材(最大含碳量为0.16%-0.25%) A660-96 高温用离心铸造碳素钢管A662/A662M-99 中温和低温压力容器用锰碳钢板规格A663/A663M-89(2000) 商品级碳素钢棒的机械特性A664-99 在ASTM规范中对电工钢和层压钢级别的识别A666-00 退火或冷加工的奥氏体不锈钢薄板、带材、中厚板和扁棒A667/A667M-87(1998) 离心铸造的双金属(灰口及白口铸铁)圆柱体A668/A668M-96e1 一般工业用碳素钢和合金钢锻件A66-01 钢质螺旋道钉A671-96 常温和较低温用电熔焊钢管A672-96 中温高压用电熔焊钢管A673/A673M-95 结构钢冲击试验的取样程序A674-00 水或其它液体用球墨铸铁管的聚乙烯包装A675/A675M-90a(2000) 专用热轧碳素钢棒的机械特性A677/A677M-99 全处理型无取向电工钢A678/A678M-00a 结构用经回火和淬火的高强度低合金碳素钢板规格A679/A679M-00 硬(冷)拉高抗拉强度钢丝A67-00 热加工低碳钢和高碳钢垫板技术规范A681-94(1999) 合金工具钢A682/A682M-00 弹簧用冷轧高碳钢带材A683/A683M-99 半处理型无取向电工钢A684/A684M-99 冷轧高碳钢带材A686-92(1999) 碳素工具钢A688/A688M-01 焊接的奥氏体不锈钢给水加热器管A689-97 弹簧用碳素钢及合金钢棒A690/A690M-00a 在海洋环境中使用的高强度低合金工字形钢桩和薄板桩规格A691-98 高温下高压装置用电熔焊碳素钢和合金钢管A693-93(1999) 沉淀硬化耐热不锈钢板、薄板和带材A694/A694M-00 高压传输设备用碳素钢及合金钢管法兰、配件、阀门及零件用锻件A695-90b(1995)e1 流体动力设备专用热锻碳素钢棒A696-90a(2000) 压力管道部件专用热锻或冷精轧碳素钢棒A697-98 用伏特计、安培计和瓦特计法测定迭层铁芯样品的交流磁特性的试验方法A698/A698M-92(1997)e1 在弱交流磁场中磁屏蔽效率的试验方法A700-99e1 钢制品国内装运的包装、标记和装载方法A701-96(2000) 硅锰铁A702-89(2000) 热锻钢栅栏柱和组件A703/A703M-01 受压部件用钢铸件A704/A704M-96 混凝土加筋用焊接普通钢棒或杆的光面钢筋或钢筋网A705/A705M-95(2000) 时效硬化的不锈和耐热钢锻件A706/A706M-01 混凝土配筋用变形低合金光面无节钢筋A707/A707M-00a 低温设备用锻制碳素钢和合金钢法兰A709/A709M-01 桥梁用结构钢A710/A710M-00 低碳时效硬化的镍铜铬钼铌合金钢A711-92(1996)e1 钢锻件坯料A712-97 软磁性合金电阻率的测试方法A713-93(1998) 热处理部件用高碳弹簧钢丝A714-99 高强度低合金焊接钢管和无缝钢管A716-99 球墨铸铁涵洞管A717/A717M-95 单片样品表面绝缘电阻率的试验方法A719-97 磁性材料的叠装系数的试验方法A720-97 无取向电工钢延展性的试验方法A721-97 取向的电工钢的延展性试验方法A722/A722M-98 预应力混凝土用无涂覆的高强度钢筋A723/A723M-94(1999) 高强度压力元件用合金钢锻件A724/A724M-99 叠层焊接的压力容器用经淬火及回火的碳素钢压力容器板A726-00 半成品型冷轧磁性迭片级钢A727/A727M-00 具有固定切口韧性的管道部件用碳素钢锻件A729-93(1999) 货物运输及电气铁路用热处理合金钢轴A730-93(1999) 铁路用碳素钢及合金钢锻件A732/A732M-98 一般设备用熔模铸造碳素低合金钢及高强度加温钴合金钢铸件A733-99 焊接及无缝碳素钢和奥氏体不锈钢管接头A734/A734M-87a(1997) 经淬火和回火的合金钢与高强度低合金钢压力容器板A735/A735M-99 中温和低温用低碳锰钼钶合金钢压力容器板A736/A736M-88(2000) 低碳时效硬化的镍铜铬钼铌和镍铜锰钼铌合金钢压力容器板A737/A737M-99 高强度低合金钢压力容器板A738/A738M-00 中温和低温设备用经热处理的碳锰硅钢压力容器板A739-90a(2000) 升温或/和加压部件用热轧合金钢棒A740-98 钢丝网(编织或焊接电镀钢丝网)A741-98 公路护栏用镀锌钢丝绳和配件A742/A742M-98 波纹钢管用预涂聚合物和金属涂覆钢薄板A743/A743M-98ae1 一般用耐腐蚀铬铁及镍铬铁合金铸件A744/A744M-00 严酷条件下使用的耐腐蚀镍铬铁合金铸件A745/A745M-94(1999) 奥氏体钢锻件的超声波检验A746-99 排污管用球墨铸铁A747/A747M-99 沉淀硬化不锈钢铸件A748/A748M-87(1998) 压力容器用静态铸造的激冷白口铁-灰口铁双金属轧辊A749/A749M-97 热轧碳素钢和高强度低合金钢带材通用要求A74-98 铸铁污水管及配件的技术规范A750-77(1994)e1 阻挡区域用钢制通风格栅A751-96 钢制品化学分析的实验方法、操作和术语A752-93(1998) 合金钢条和粗圆钢丝A752M-93(1998) 合金钢条和粗圆钢丝(米制)A753-97 镍铁软磁合金A754/A754M-96(2000) X射线荧光涂层厚度的试验方法A755/A755M-99 外露建筑材料用热浸涂覆和用卷涂工艺预涂的钢薄板A756-94(2001) 耐磨不锈轴承钢A757/A757M-00 低温下承压设备及其它设备用铁素体和马氏体钢铸件A758/A758M-00 具有改进的切口韧性的对缝焊锻制碳素钢管配件A759-00 起重机用碳钢轨条A760/A760M-01 下水道和排水沟用金属涂覆的波纹钢管A761/A761M-98 现场栓接管、管拱和拱用波纹镀锌结构钢板A762/A762M-00 下水道和排水沟用预涂聚合物波纹钢管A763-93(1999)e1 铁素体不锈钢晶间腐蚀敏感性检测A764-95(2001) 机械弹簧用冷拉镀锌和按成品尺寸镀锌的碳素钢丝A765/A765M-98a 具有强制性韧性要求的碳素钢及低合金钢压力容器部件锻件A767/A767M-00b 钢筋混凝土用镀锌钢筋A768-95 涡轮机转子及轴用经真空处理的含铬12%的合金钢锻件A769/A769M-00 电阻焊钢结构型材A770/A770M-86(2001) 专用钢板通过厚度测量进行的抗拉试验A771/A771M-95(2001) 增殖反应堆堆芯部件用奥氏体不锈钢管A772/A772M-00 正弦电流用材料的交流磁导率的试验方法A773/A773M-96 用带直流电子的磁滞曲线记录仪的（B－H）回路法测量材料的磁性能的标准试验方法A774/A774M-00 低温和中温一般腐蚀情况下用的焊接锻制奥氏体不锈钢配件A775/A775M-01 涂环氧树脂的钢筋钢棒A778-01 焊接未退火的奥氏体不锈钢管形制品A779/A779M-00 预应力混凝土用应力消除未涂覆的密实七股钢丝绞绳A780-01 热浸镀锌层的损坏及无覆层区域的检修A781/A781M-00 一般工业用一般要求的钢和合金铸件A782/A782M-90(2001) 经淬火和回火的锰铬钼硅锆合金钢压力容器板A786/A786M-00b 轧制钢楼板A787-01 电阻焊金属涂覆碳素钢机械配管A788-98a 钢锻件A789/A789M-01 普通设备用无缝与焊接铁素体/奥氏体不锈钢管A790/A790M-01 无缝与焊接铁素体/奥氏体不锈钢管A792/A792M-99 热浸工艺法处理的55%铝-锌合金涂覆钢板A793-96 不锈钢轧制楼板A794-97 商品级冷轧碳素钢薄板(最高含碳量为0.16%-0.25%)A795-00 防火用黑色及热浸镀锌的焊接和无缝钢管A796/A796M-00 雨水管和卫生污水管及其它地下埋设管道用波纹钢管、管托架及拱形架结构设计惯例A798/A798M-01 下水道及其它类似用途用工厂制波纹钢管的安装A799/A799M-92(1997) 估算不锈钢铸件铁素体含量用仪表的校准A800/A800M-01 奥氏体合金钢铸件中铁素体含量的估算A801/A801M-99 铁钴高磁性饱和合金A802/A802M-95(2001) 钢铸件外观检验的表面验收标准A803/A803M-01 焊接铁素体不锈钢给水加热器管A804/A804M-99 在电力频率下用薄钢板型试样对材料交流磁特性的测试方法A805-93(1998) 冷轧碳素钢扁平线A807/A807M-97 下水道及其它类似用途用波纹结构钢涂覆管的安装A808/A808M-00a 具有改进的切口韧性的结构级高强度低合金碳钢、锰钢、铌钢和钒钢A809-98 镀铝碳素钢丝A810-00 镀锌钢管用绕网A811-97 粉末冶金技术制造的软磁铁零件A813/A813M-01 单或双焊接奥氏体不锈钢管A814/A814M-01 冷加工焊接奥氏体不锈钢管A815/A815M-01 锻制铁素体、铁素体/奥氏体和马氏体不锈钢管配件A817-00 链接栅栏网用金属涂覆钢丝A818-91(2001) 镀铜碳素钢丝A820-96 纤维增强混凝土用钢纤维A821/A821M-99 预应力混凝土容器用经回火的冷拉钢丝A822-90(2000) 液压系统设备用冷拉碳素无缝钢管A823-99 静铸永久铸模灰铸件A824-01 链接栅栏用Marcelled拉力金属涂覆钢丝A826/A826M-95(2001) 增殖反应堆堆芯部件用奥氏体和铁素体不锈钢管A827/A827M-93a(1998) 锻造及类似用途用的碳素钢板技术规范A829/A829M-00 结构性合金钢板A82-97ae1 钢筋混凝土用无节钢丝A830/A830M-00 按照化学成分要求提供的优质碳素钢板技术规范A831/A831M-95(2000) 核心部件用不锈耐热钢棒,坯段及锻件规格A832/A832M-99e1 压力容器板用铬钼钒及铬钼钒钛硼合金钢A833-84(1996) 用比较硬度测试仪测量金属材料的压痕硬性A834-95(2001) 一般工业用铁铸件的一般要求A835-84(2000) 铁合金与合金添加剂的筛分粒度A836/A836M-95b(2001) 搪瓷管和压力容器设备用钛稳定碳素体钢锻件A837-91(1996)e1 渗碳用合金钢锻件A838/A838M-97 继电器用易切削铁素体不锈软磁合金技术规范A839/A839M-96 软磁用途的磷铁粉末冶金制造的零件技术规范A840/A840M-00 全处理的磁性夹层钢A841/A841M-01 压力容器用温度机械控制工艺加工的钢板A842-85(1997) 高密度石墨铸铁A844/A844M-93(1999) 压力容器用直接淬火加工的含镍9%的合金钢板A845-85(2000) 用于脱氧与合金钢的钛碎片A846-85(2000) 用于脱氧与合金钢的铝碎片A847-99a 具有增强耐大气腐蚀性能的冷成型焊接与无缝高强度低合金结构管A848/A848M-96 低碳磁铁A849-00 波纹钢排水管和污水管用后涂覆铺面和衬里材料A851-96 高频感应焊接的未退火奥氏体钢冷凝器管A852/A852M-00a 最小屈服强度为70Ksi(485MPa),厚度为4英寸(100mm)的经淬火和回火的低合金结构钢板A853-93(1998) 普通碳素钢丝A854/A854M-98 镀锌高强度钢栅栏和格架用光滑金属线A855/A855M-98 锌-5%铝-铈合金涂覆的钢丝绳A856/A856M-98 锌-5%铝-铈合金涂覆的碳素钢丝A857/A857M-00a 冷成形轻型薄钢板桩A858/A858M-00 低温和腐蚀情况下用热处理碳素钢配件A859/A859M-95(1999) 压力容器部件用时效硬化镍铜铬钼钶低碳合金钢锻件A860/A860M-00 锻制高强度低合金钢的高强度对缝焊接配件A861-94e1 高硅铁管和配件A862/A862M-98 波纹钢污水管和排水管沥清(柏油)涂层的应用A865-97 钢管连接用黑色或镀锌焊接或无缝钢螺纹接头A866-94 耐磨中碳轴承钢A867/A867M-94(1998)e1 继电器用铁硅钢A871/A871M-00a 抗空气腐蚀的高强度低合金结构钢板。
ASTMA20中文版
压力容器用钢板通用要求SA-20/SA-20M(与ASTM标准A20/A20M-04完全等同)1 适用范围1.1 本标准包括一组通用要求，除专用材料标准中另有规定外，这些要求应适用于下列各项ASTM压力容器用轧制钢板标准：1.1.1 本标准还包括一组补充要求，适用于上列若干个标准中本身已指明的场合。
这些补充要求仅当买方在订货单中要求附加试验或检验并作了单独规定时采用。
1.2 附录X1叙述了制造压力容器钢板用卷材的生产及一些特性。
1.3 附录X2提供了关于压力容器用钢板拉伸性能变化性的资料。
1.4 附录X3提供了关于压力容器用钢板夏比V型缺口冲击试验性能变化的材料。
1.5 附录X4提供了包括冷弯时建议的最小内弯曲半径在内的有关钢板冷弯的资料。
1.6 这些材料仅适于熔焊，熔焊时应采用适合于该钢种级别及使用条件的焊接工艺。
1.7 如本标准与专用材料标准的要求不一致，则以专用材料标准的要求为准。
1.8 买方可以规定不否定本标准或专用材料标准任何条款的附加要求。
这些附加要求必须纳入采购订货单说明中，并取得供方同意。
1.9 为了确定供应材料是否与标准及材料标准的规定极限值相一致，各数值右面的有效位数应按E29推荐的圆整方法进行圆整。
1.10 以英寸-磅单位或SI单位表示的数值均可作为标准值。
本文中SI单位表示于括号内。
由于各单位制所表示的数值不能与另一种单位制进行精确换算，因此，每一种单位制必须独立使用。
1.11 本标准及所引用的材料标准均采用英寸-磅和SI两种单位，但除非订货单中规定采用“M”标志（SI单位），材料将以英寸-磅单位供货。
2 引用标准3 术语3.1 本标准专用术语说明：3.1.1 封顶钢---因受早期压盖过程而使沸腾作用受到限制的沸腾钢。
压盖可用机械方法，在瓶口式锭模顶部采用一个重的金属槽，也可用化学方法对敝口式锭模中钢水的顶部加铝或硅铁。
3.1.2 卷板—以卷材形式加工为成品钢板的热轧钢。
压力容器用钢板通用要求标准规范
压力容器用钢板通用要求标准规范 1
A20/A 20M-07
本标准是基于 A20/A 20M 标准的基础上提出的；标号后面的数字表示初始
版本的年代，如有再版，则指最新再版的年代。括号中的数字表示最新批准通过
的年代。上标（ε）表示最新再版或重新批准后编排上的更改。
本标准已经被国防部批准使用。
常可以提供下列尺寸的钢板：
宽度 英寸[mm]
厚度英寸[mm]
＞8[200]
≥0.229[≥6.0mm]
＞48[1200]
≥0.179[≥4.6mm]
3.1.7.1 讨论——可以得到不同厚度、宽度和长度的钢板，这取决于不同生产方
和加工方设备与工艺能力。基于尺寸（厚度、宽度和长度）的钢板以前的限定不
考虑当前生产和工艺能力。要使钢板达到特定产品规范要求，则必须进行所有适
MIL-STD-163：准备用于海运和存贮的钢产品 6
2.4 美国联邦标准：
Fed.Std.No.123：海运标记（国内代理）6
2.5 汽车工业集团标准：
B1 Bar 代码标准 7
注：5、可以从美国机械工程师协会（ASME）获得，ASME 国际总部地址：Three Park
Ave., New York, NY 10016-5990, .
[1800mm]）。
3.1.3 热处理术语——见 3.1.8 及术语 A941。
3.1.4 热成形——在钢板被加热至使晶粒细化所要求的温度后执行永久变形的成
形操作。
3.1.5 生产方——是采用热轧方法直接控制钢锭、板坯轧制成热轧钢板或板卷；
而对轧制钢板来说，则是直接控制或负责与成品钢板有关的一个或多个操作的组
ASTM标准.A系列
A351/A351M-03 容压零件用奥氏体及奥氏体铁素体铸铁的技术规范
A352/A352M-03 A353/A353M93(1999)
A354-04
低温受压零件用铁素体和马氏体钢铸件规格
压力容器用经二次正火及回火处理的含9％镍的合金钢板 淬火与回火合金钢螺栓,双头螺栓及其他外螺纹紧固件规 格
氧化钼制品
A148/A148M-03 结构用高强度钢铸件
A153/A153M-04 钢铁制金属构件上镀锌层(热浸)
A159-83(2001) 汽车用灰铁铸件
A167-99
不锈钢和耐热铬镍钢板、薄板及带材
A176-99
A178/A178M-02 A179/A179M90a(2001)
不锈钢和耐热铬钢板、薄板及带材 电阻焊接碳素钢钢管及碳锰钢锅炉和过热器管的技术规 范
预应力混凝土用无涂层消除应力钢丝的技术规范 无缝和电焊低合金钢管
A424-00
搪瓷用钢薄板
A426/A426M-02 高温用离心铸造的铁素体合金钢管
A427-02
冷轧和热轧用锻制合金钢辊
A428/A428M-01 钢铁制品上铝覆层重量的测试方法
A434-04
A435/A435M90(2001)
热轧与冷精轧经回火及淬火的合金钢棒 钢板的直射束纵向超声波检验
磁在铁电材力料频导率磁下率用的瓦试特验计方-安法培计-伏特计法(100-1000赫 兹)和25 厘米艾普斯亭(EPSTEIN) 机架测定材料的交流 电磁性能的试验方法
A345-98 A348/A348M-00 A350/A350M-04
磁设备用平轧电炉钢
用瓦特计--安培计--伏特计法(100-10000赫兹)和25厘米 艾普斯亭框测定材料的交流磁性能的试验方法
ASTM-A20---中文版
压力容器用钢板通用要求SA-20/SA-20M(与ASTM标准A20/A20M-04完全等同)1 适用范围1.1 本标准包括一组通用要求，除专用材料标准中另有规定外，这些要求应适用于下列各项ASTM压力容器用轧制钢板标准：1.1.1 本标准还包括一组补充要求，适用于上列若干个标准中本身已指明的场合。
这些补充要求仅当买方在订货单中要求附加试验或检验并作了单独规定时采用。
1.2 附录X1叙述了制造压力容器钢板用卷材的生产及一些特性。
1.3 附录X2提供了关于压力容器用钢板拉伸性能变化性的资料。
1.4 附录X3提供了关于压力容器用钢板夏比V型缺口冲击试验性能变化的材料。
1.5 附录X4提供了包括冷弯时建议的最小内弯曲半径在内的有关钢板冷弯的资料。
1.6 这些材料仅适于熔焊，熔焊时应采用适合于该钢种级别及使用条件的焊接工艺。
1.7 如本标准与专用材料标准的要求不一致，则以专用材料标准的要求为准。
1.8 买方可以规定不否定本标准或专用材料标准任何条款的附加要求。
这些附加要求必须纳入采购订货单说明中，并取得供方同意。
1.9 为了确定供应材料是否与标准及材料标准的规定极限值相一致，各数值右面的有效位数应按E29推荐的圆整方法进行圆整。
1.10 以英寸-磅单位或SI单位表示的数值均可作为标准值。
本文中SI单位表示于括号内。
由于各单位制所表示的数值不能与另一种单位制进行精确换算，因此，每一种单位制必须独立使用。
1.11 本标准及所引用的材料标准均采用英寸-磅和SI两种单位，但除非订货单中规定采用“M”标志（SI 单位），材料将以英寸-磅单位供货。
2 引用标准3 术语3.1 本标准专用术语说明：3.1.1 封顶钢---因受早期压盖过程而使沸腾作用受到限制的沸腾钢。
压盖可用机械方法，在瓶口式锭模顶部采用一个重的金属槽，也可用化学方法对敝口式锭模中钢水的顶部加铝或硅铁。
3.1.2 卷板—以卷材形式加工为成品钢板的热轧钢。
压力容器专用钢板标准简介
钢号
07MnCrMoVR
07MnMoVR
厚 度 mm
12～60
10～60
Rm MPa
610～730
610～730
ReL MPa -20℃ KV2 J
≥490 ≥47
≥490 ≥80
2. 07MnNiVDR钢板 （1）钢号简介 （2）化学成分
标 准 GB19189-2003
钢 号 07MnNiMoVDR
S％
≤0.012
KV2 J
横向 -70℃， ≥34
13MnNi6-3 ≤80
0.30～0.85 ≤0.025 ≤0.015
横向 -60℃， ≥27
SA203Gr.A ≤50
2.10～2.50 ≤0.035 ≤0.035
纵向 -68℃， ≥18
三、GB19189-(2010)
《压力容器用调质高强度钢板》
标 准 GB/T20878-2007 GB/T4237-2007 GB24511-2009
代号或 牌号
S31782/ 015Cr21Ni26Mo5Cu2
015Cr21Ni26Mo5Cu2
S39042/ 015Cr21Ni26Mo5Cu2
C％
≤0.020
≤0.020
≤0.020
Cr ％ 19.00～23.00
标准
GB3531-1996 GB3531-2008
厚 度 mm
6～60
6～120
-70℃ KV2 J
≥27
≥34
（3）国内外标准对比
标 准 GB3531-2008 EN10028-4:2003 ASME(2007)
钢号
09MnNiDR
厚 度 mm
6～120
ASTM A20A20M-95
美国材料与试验协会标准ASTM A20/A20M-95压力容器用钢板通用技术条件(摘要)1适用范围1.1 本标准包括一组共同要求,除专用材料标准中另有规定外,这些要求应适用于下列各项ASTM压力容器用轧制钢板标准:1.1.1 本标准还包括一组补充要求,适用于上列若干个标准中本身已指明的场合。
这些补充要求仅当买方在订货单中要求附加试验或检验并作了单独规定时才采用。
1.5 这些材料仅适于熔焊,熔焊时应采用适合于该钢种级别及使用条件的焊接工艺。
1.6 如本标准与专用材料标准的要求不一致,则以专用材料标准的要求为准。
1.7 买方可以规定不否定本标准或专用材料标准条款的附加要求。
这些附加要求必须纳入订货单说明中,其验收条件应与供方协商(见4.1.8),并取得供方接受。
1.8 为了确定供应材料是否与本标准及1.1中所列各材料标准的规定极限值相一致,各数值右面的有效位数应按E29推荐的圆整方法进行圆整。
1.9 以英寸一磅单位或SI单位表示的数值均可作为标准值。
本文中SI单位表示于括号内。
由于各单位制所表示的数值不能与另一种单位制进行精确换算,因此,每一种单位制必须独立使用。
两个单位制的数值混合使用可能导致与本标准不一致的结果。
1.10 本标准及所引用的材料标准均采用英寸一磅和SI两种单位,但除非订货单中规定采用"M"标志(SI单位),否则材料将以英寸一磅单位供货。
3 本标准专用术语说明3.1 封顶钢-因受早期压盖过程而使沸腾作用受到限制的沸腾钢。
压盖可用机械方法,在瓶口式锭模顶部采用一个重的金属帽,也可用化学方法对敞口式锭模的钢水的顶部加铝或硅铁。
3.2 除外-当用于与范围有关时,例如尺寸允许偏差表中厚度的范围,本术语表示仅除去范围中的较大值。
例如在从60～72in.〈1500～180Omm〉除外的范围中,除外表示包括60in.(150Omm)但不包括72in.(180Omm)。
3.3 热处理术语一见3.7、3.10和E44定义。
ASTM A20&A20M-2004a 压力容器用钢板材通用要求
Designation:A20/A20M–04aStandard Specification forGeneral Requirements for Steel Plates for Pressure Vessels1This standard is issued under thefixed designation A20/A20M;the number immediately following the designation indicates the yearof original adoption or,in the case of revision,the year of last revision.A number in parentheses indicates the year of last reapproval.A superscript epsilon(e)indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the Department of Defense.1.Scope*1.1This general requirements specification2covers a groupof common requirements that,unless otherwise specified in theapplicable product specification,apply to rolled steel plates forpressure vessels covered by each of the following productspecifications issued by ASTM:Title of SpecificationASTM Designation3Pressure Vessel Plates,Alloy Steel,Chromium-ManganeseSiliconA202/A202MPressure Vessel Plates,Alloy Steel,Nickel A203/A203M Pressure Vessel Plates,Alloy Steel,Molybdenum A204/A204M Pressure Vessel Plates,Alloy Steel,Manganese-Vanadium A225/A225M Pressure Vessel Plates,Carbon Steel,Low-and Intermediate-Tensile StrengthA285/A285M Pressure Vessel Plates,Carbon Steel,Manganese-Silicon A299/A299M Pressure Vessel Plates,Alloy Steel,Manganese-Molybdenumand Manganese-Molybdenum-NickelA302/A302MPressure Vessel Plates,Alloy Steel,9Percent Nickel Double-Normalized and TemperedA353/A353M Pressure Vessel Plates,Alloy Steel,Chromium-Molybdenum A387/A387M Pressure Vessel Plates,Carbon Steel,High Strength Manga-neseA455/A455MPressure Vessel Plates,Carbon Steel,for Intermediate-andHigher-Temperature ServiceA515/A515MPressure Vessel Plates,Carbon Steel,Moderate-and Lower-Temperature ServiceA516/A516MPressure Vessel Plates,Alloy Steel,High-Strength,Quenchedand TemperedA517/A517MPressure Vessel Plates,Alloy Steel,Quenched and TemperedManganese-Molybdenum and Manganese-Molybdenum-NickelA533/A533MPressure Vessel Plates,Heat-Treated,Carbon-Manganese-Silicon SteelA537/A537MPressure Vessel Plates,Alloy Steel,Quenched and TemperedChromium-MolybdenumA542/A542MPressure Vessel Plates,Alloy Steel,Quenched and TemperedNickel-Chromium-MolybdenumA543/A543MPressure Vessel Plates,Alloy Steel,Quenched and Tempered8and9Percent NickelA553/A553MPressure Vessel Plates,Carbon Steel,Manganese-Titaniumfor Glass or Diffused Metallic CoatingsA562/A562MPressure Vessel Plates,Carbon Steel,High Strength,for Mod-erate and Lower Temperature Service A612/A612MPressure Vessel Plates,Five Percent Nickel Alloy Steel,Spe-cially Heat TreatedA645/A645MPressure Vessel Plates,Carbon-Manganese,for Moderate andLower Temperature ServiceA662/A662MPressure Vessel Plates,Carbon Steel,Quenched and Tem-pered,for Welded Layered Pressure VesselsA724/A724MPressure Vessel Plates,Alloy Steel and High-Strength Low-Alloy Steel,Quenched and TemperedA734/A734MPressure Vessel Plates,Low-Carbon Manganese-Molybdenum-Columbium Alloy Steel,for Moderate and LowerTemperature ServiceA735/A735MPressure Vessel Plates,Low-Carbon Age-Hardening Nickel-Copper-Chromium-Molybdenum-Columbium Alloy SteelA736/A736MPressure Vessel Plates,High-Strength Low-Alloy Steel A737/A737MPressure Vessel Plates,Heat-Treated,Carbon-Manganese-Silicon Steel,for Moderate and Lower Temperature ServiceA738/A738MPressure-Vessel Plates,Quenched and Tempered,Manganese-Chromium-Molybdenum-Silicon-ZirconiumAlloy SteelA782/A782MPressure Vessel Plates,Alloy Steel,Chromium-Molybdenum-VanadiumA832/A832MPressure Vessel Plates,Produced by the Thermo-MechanicalControl Process(TMCP)A841/A841MPressure Vessel Plates,9%Nickel Alloy,Produced by theDirect-Quenching ProcessA844/A844M1.1.1This general requirements specification also covers agroup of supplementary requirements that are applicable toseveral of the above product specifications as indicated therein.Such requirements are provided for use if additional testing oradditional restrictions are required by the purchaser,and applyonly if specified individually in the purchase order.1.2Appendix X1provides information on coil as a sourceof plates for pressure vessels.1.3Appendix X2provides information on the variability oftensile properties in plates for pressure vessels.1.4Appendix X3provides information on the variability ofCharpy-V-Notch impact test properties in plates for pressurevessels.1.5Appendix X4provides information on cold bending ofplates,including suggested minimum inside radii for coldbending.1.6These materials are intended to be suitable for fusionwelding.When the steel is to be welded,it is presupposed thata welding procedure suitable for the grade of steel and intendeduse or service will be utilized.1This specification is under the jurisdiction of ASTM Committee A01on Steel, Stainless Steel,and Related Alloys and is the direct responsibility of Subcommittee A01.11on Steel Plates for Boilers and Pressure Vessels.Current edition approved May1,2004.Published May2004.Originally approved st previous edition approved in2004as A20/A20M–04.2For ASME Boiler and Pressure Vessel Code applications,see related Specifi-cation SA-20/SA-20M in Section II of that Code.3These designations refer to the latest issue of the respective specification which appears in the Annual Book of ASTM Standards,V ol01.04.1*A Summary of Changes section appears at the end of this standard. Copyright©ASTM International,100Barr Harbor Drive,PO Box C700,West Conshohocken,PA19428-2959,United States.1.7In case of any conflict in requirements,the requirements of the applicable product specification prevail over those of this general requirements specification.1.8Additional requirements that are specified in the pur-chase order and accepted by the supplier are permitted,provided that such requirements do not negate any of the requirements of this general requirements specification or the applicable product specification.1.9For purposes of determining conformance with this general requirements specification and the applicable product specification,values are to be rounded to the nearest unit in the right-hand place of figures used in expressing the limiting values in accordance with the rounding method of Practice E 29.1.10The values stated in either inch-pound units or SI units are to be regarded as standard.Within the text,the SI units are shown in brackets.The values stated in each system are not exact equivalents.Therefore,each system is to be used independently of the other.1.11This general requirements specification and the appli-cable product specification are expressed in both inch-pound units and SI units;unless the order specifies the applicable “M”specification designation (SI units),the plates are to be furnished to inch-pound units.2.Referenced Documents42.1ASTM Standards:A 202/A202M Specification for Pressure Vessel Plates,Al-loy Steel,Chromium-Manganese-SiliconA 203/A203M Specification for Pressure Vessel Plates,Al-loy Steel,NickelA 204/A204M Specification for Pressure Vessel Plates,Al-loy Steel,MolybdenumA 225/A225M Specification for Pressure Vessel Plates,Al-loy Steel,Manganese-Vanadium-NickelA 285/A285M Specification for Pressure Vessel Plates,Car-bon Steel,Low-and Intermediate-Tensile StrengthA 299/A299M Specification for Pressure Vessel Plates,Car-bon Steel,Manganese-SiliconA 302/A302M Specification for Pressure Vessel Plates,Al-loy Steel,Manganese-Molybdenum and Manganese-Molybdenum-NickelA 353/A353M Specification for Pressure Vessel Plates,Al-loy Steel,9Percent Nickel,Double-Normalized and Tem-peredA 370Test Methods and Definitions for Mechanical Testing of Steel ProductsA 387/A387M Specification for Pressure Vessel Plates,Al-loy Steel,Chromium-MolybdenumA 435/A435M Specification for Straight-Beam Ultrasonic Examination of Steel PlatesA 455/A455M Specification for Pressure Vessel Plates,Car-bon Steel,High Strength ManganeseA 515/A515M Specification for Pressure Vessel Plates,Car-bon Steel,for Intermediate-and Higher-Temperature Ser-viceA 516/A516M Specification for Pressure Vessel Plates,Car-bon Steel,for Moderate-and Lower-Temperature Service A 517/A517M Specification for Pressure Vessel Plates,Al-loy Steel,High-Strength,Quenched and TemperedA 533/A533M Specification for Pressure Vessel Plates,Al-loy Steel,Quenched and Tempered Manganese-Molybdenum and Manganese-Molybdenum-NickelA 537/A537M Specification for Pressure Vessel Plates,Heat-Treated,Carbon-Manganese-Silicon SteelA 542/A542M Specification for Pressure Vessel Plates,Al-loy Steel,Quenched and Tempered,Chromium-Molybdenum,and Chromium-Molybdenum-Vanadium A 543/A543M Specification for Pressure Vessel Plates,Al-loy Steel,Quenched and Tempered Nickel-Chromium-MolybdenumA 553/A553M Specification for Pressure Vessel Plates,Al-loy Steel,Quenched and Tempered 8and 9Percent Nickel A 562/A562M Specification for Pressure Vessel Plates,Car-bon Steel,Manganese-Titanium for Glass or Diffused Metallic CoatingsA 577/A577M Specification for Ultrasonic Angle-Beam Examination of Steel PlatesA 578/A578M Specification for Straight-Beam Ultrasonic Examination of Plain and Clad Steel Plates for Special ApplicationsA 612/A612M Specification for Pressure Vessel Plates,Car-bon Steel,High Strength,for Moderate and Lower Tem-perature ServiceA 645/A645M Specification for Pressure Vessel Plates,Five Percent Nickel Alloy Steel,Specially Heat TreatedA 662/A662M Specification for Pressure Vessel Plates,Carbon-Manganese-Silicon Steel,for Moderate and Lower Temperature ServiceA 700Practices for Packaging,Marking,and Loading Methods for Steel Products for Domestic ShipmentA 724/A724M Specification for Pressure Vessel Plates,Carbon-Manganese-Silicon Steel,Quenched and Tem-pered,for Welded Layered Pressure VesselsA 734/A734M Specification for Pressure Vessel Plates,Al-loy Steel and High-Strength Low-Alloy Steel,Quenched and TemperedA 735/A735M Specification for Pressure Vessel Plates,Low-Carbon Manganese-Molybdenum-Columbium Alloy Steel,for Moderate and Lower Temperature ServiceA 736/A736M Specification for Pressure Vessel Plates,Low-Carbon Age-Hardening Nickel-Copper-Chromium-Molybdenum-Columbium and Nickel-Copper Manganese-Molybdenum-Columbium and Alloy SteelA 737/A737M Specification for Pressure Vessel Plates,High-Strength,Low-Alloy SteelA 738/A738M Specification for Pressure Vessel Plates,Heat-Treated,Carbon-Manganese-Silicon Steel,for Mod-erate and Lower Temperature Service4For referenced ASTM standards,visit the ASTM website,,or contact ASTM Customer Service at service@.For Annual Book of ASTM Standards volume information,refer to the standard’s Document Summary page on the ASTMwebsite.A 751Test Methods,Practices,and Terminology for Chemical Analysis of Steel ProductsA 770/A770M Specification for Through-Thickness Ten-sion Testing of Steel Plates for Special ApplicationsA 782/A782M Specification for Pressure-Vessel Plates,Quenched and Tempered,Manganese-Chromium-Molybdenum-Silicon-Zirconium Alloy SteelA 832/A832M Specification for Pressure Vessel Plates,Al-loy Steel,Chromium-Molybdenum-VanadiumA 841/A841M Specification for Steel Plates for Pressure Vessels,Produced by the Thermo-Mechanical Control Process (TMCP)A 844/A844M Specification for Steel Plates,9%Nickel Alloy,for Pressure Vessels,Produced by the Direct-Quenching Process 4A 941Terminology Relating to Steel,Stainless Steel,Re-lated Alloys,and FerroalloysE 21Test Methods for Elevated Temperature Tension Tests of Metallic MaterialsE 29Practice for Using Significant Digits in Test Data to Determine Conformance with SpecificationsE 112Test Methods for Determining Average Grain Size E 208Test Method for Conducting Drop-Weight Test to Determine Nil-Ductility Transition Temperature of Ferritic SteelsE 709Guide for Magnetic Particle Examination2.2American Society of Mechanical Engineers Code:ASME Boiler and Pressure Vessel Code,Section IX,Weld-ing Qualifications 5itary Standard:MIL-STD-163Steel Mill Products Preparation for Ship-ment and Storage 62.4U.S.Federal Standard:Fed.Std.No.123,Marking for Shipment (Civil Agencies)62.5Automotive Industry Action Group Standard:B 1Bar Code Symbology Standard 73.Terminology3.1Definitions of Terms Specific to This Standard:3.1.1capped steel —rimmed steel in which the rimming action is limited by an early capping operation.Capping may be carried out mechanically by using a heavy metal cap on a bottle-top mold or it may be carried out chemically by an addition of aluminum or ferrosilicon to the top of the molten steel in an open-top mold.3.1.2coil —hot-rolled steel in coil form for processing into finished plates.3.1.3exclusive —when used in relation to ranges,as for ranges of thicknesses in the tables of permissible variations in dimensions,the term is intended to exclude only the greater value of the range.Thus,a range from 60to 72in.[1500to1800mm]exclusive includes 60in.[1500mm],but does not include 72in.[1800mm].3.1.4heat treatment terms —see 3.1.8,3.1.12,and Termi-nology A 941.3.1.5hot forming —a forming operation producing perma-nent deformation,performed after the plate has been heated to the temperature required to produce grain refinement.3.1.6killed steel —steel deoxidized,either by addition of strong deoxidizing agents or by vacuum treatment,to reduce the oxygen content to such a level that no reaction occurs between carbon and oxygen during solidification.3.1.7manufacturer —the organization that directly controls the conversion of steel ingots or slabs,by hot rolling,into plate-as-rolled or into coil;and for plates produced from plate-as-rolled,the organization that directly controls,or is responsible for,one or more of the operations involved in finishing the plates.Such finishing operations include leveling,cutting to length,testing,inspection,conditioning,heat treat-ment (if applicable),packaging,marking,loading for shipment,and certification.3.1.7.1Discussion —The finishing operations need not be done by the organization that did the hot rolling of the plate.For plates produced from coil,see also 3.1.13.1.3.1.8normalizing —a heat treating process in which a steel plate is reheated to a uniform temperature above the upper critical temperature and then cooled in air to below the transformation range.3.1.9plate-as-rolled —the unit plate,as hot-rolled,prior to subdividing (if applicable)or any finishing operation.3.1.9.1Discussion —It does not refer to the surface condi-tion or heat treatment state of the plate.3.1.10plate identifier —the alpha,numeric,or alphanumeric designation used to identify the plate.3.1.11plates —flat hot-rolled steel,ordered to thickness or weight and typically to width and length,commonly available by size as follows:Width,in.[mm]Thickness,in.[mm]Over 8[200]Over 48[1200]over 0.229[6.0mm and over]over 0.179[4.6mm and over]3.1.11.1Discussion —Steel plates are available in various thickness,width,and length combinations dependent upon equipment and processing capabilities of various manufactur-ers and processors.Historic limitations of a plate based upon dimensions (thickness,width,and length)do not take into account current production and processing capabilities.To qualify any plate to a particular product specification requires that all appropriate and necessary tests be performed and that the results meet the limits prescribed in that product specifi-cation.If the necessary tests required by a product specification can not be conducted,the plate can not be qualified to that specification.This general requirements specification contains permitted variations for the commonly available sizes.Permit-ted variations for other sizes are subject to agreement between the purchaser and the manufacturer or processor,whichever is applicable.3.1.12precipitation heat treatment —a subcritical tempera-ture thermal treatment performed to cause precipitation of5Available from ASME,345E.47th St.,New York,NY 10017.6Available from the procuring activity or as directed by the contracting office or from Standardization Documents Order Desk,Bldg.4Section D,700Robbins Ave.,Philadelphia,PA 19111-5094,Attn:NPODS.7Available from Automotive Industry Action Group,26200Lahser Road,Suite 200,Southfield,MI48034.submicroscopic constituents,and so forth,to result in enhance-ment of some desirable property.3.1.13processor—the organization that directly controls, or is responsible for,operations involved in the processing of coil intofinished plates.Such processing operations include decoiling,leveling,cutting to length,testing,inspection,con-ditioning,heat treatment(if applicable),packaging,marking, loading for shipment,and certification.3.1.13.1Discussion—The processing operations need not be done by the organization that did the hot rolling of the coil. If only one organization is involved in the hot rolling and processing operations,that organization is termed the manu-facturer for the hot rolling operation and the processor for the processing operations.If more than one organization is in-volved in the hot rolling and processing operations,the organization that did the hot rolling is termed the manufacturer and the organization that does one or more processing opera-tions is termed a processor.3.1.14rimmed steel—steel containing sufficient oxygen to give a continuous evolution of carbon monoxide while the ingot is solidifying,resulting in a case or rim of metal virtually free of voids.3.1.15semikilled steel—incompletely deoxidized steel con-taining sufficient oxygen to form enough carbon monoxide during solidification to offset solidification shrinkage.4.Ordering Information4.1Orders should include the following information,as necessary,to adequately describe the desired product.4.1.1Quantity(weight[mass]or number of plates),4.1.2Dimensions,4.1.3Name of product(for example,plates,carbon steel; plates,alloy steel),4.1.4Specification designation(including type,class,and grade as applicable)and year-date,4.1.5Condition(as-rolled,normalized,quenched and tem-pered,etc.If heat treatment of plate is to be performed by the fabricator,this is to be stated.Also,if purchaser specifies a heat-treatment cycle,this is to be stated),4.1.6Impact test requirements,if any(see Section12).(For Charpy V-notch test,include test specimen orientation,testing temperature,and acceptance criteria.For drop-weight test,give testing temperature),4.1.7Exclusion of either plates produced from coil or plates produced from plate-as-rolled,if applicable.(See5.4and Appendix X1.)4.1.8Limits for grain refining elements other than alumi-num,if applicable(see8.2.4),4.1.9Paint marking(see13.2.1),4.1.10Supplementary requirements,if any(test specimen heat treatment,special impact test requirements,etc.),and4.1.11Additional requirements,if any.5.Materials and Manufacture5.1The steel shall be made in an open-hearth,basic-oxygen, or electric-arc furnace,possibly followed by additional refining in a ladle metallurgy furnace(LMF),or by another method;or secondary melting by vacuum-arc remelting(V AR),electro-slag remelting(ESR),or another method.5.2The steel may be strand cast or cast in stationary molds.5.2.1Strand Cast Slabs:5.2.1.1If heats of the same nominal chemical composition are consecutively strand cast at one time,the heat number assigned to the cast product(slab)may remain unchanged until all of the steel in the slab is from the following heat.5.2.1.2When two consecutively strand cast heats have different nominal chemical composition ranges,the manufac-turer shall remove the transition material by any established procedure that positively separates the grades.5.3The ratio of reduction of thickness from a strand-cast slab to plate shall be at least3.0:1,except that reduction ratios as low as2.0:1are permitted if all of the following limitations are met:5.3.1The purchaser agrees to the use of such reduction ratios.5.3.2The applicable product specification is A299/A299M, A515/A515M,A516/A516M,A537/A537M,A662/A 662M,or A737/A737M5.3.3The specified plate thickness is3.0in.[75mm]or more.5.3.4One or more of the following low hydrogen practices are used:vacuum degassing during steelmaking;controlled soaking of the slabs or plates;or controlled slow cooling of the slabs or plates.5.3.5The sulfur content is0.004%or less,based upon heat analysis.5.3.6One or more of the following practices are used: electromagnetic stirring during strand casting;soft reduction during strand casting;heavy pass reductions or other special practices during plate rolling;or combined forging and rolling during plate rolling.5.3.7The plates are ultrasonically examined in accordance with Specification A578/A578M,Level C based on continu-ous scanning over100%of the plate surface.5.3.8The plates are through-thickness tension tested in accordance with Specification A770/A770M.5.4Unless otherwise specified in the purchase order,plates shall be produced from plate-as-rolled or from coil.5.5Coils are excluded from qualification to the applicable product specification until they are decoiled,leveled,cut to length,and tested by the processor in accordance with the specified requirements(see Sections9,10,11,12,13,14,15, 16,and20.)5.5.1Plates produced from coil shall not contain splice welds,unless approved by the purchaser.6.Heat Treatment6.1If plates are required to be heat treated,the heat treatment shall be performed by the manufacturer,the proces-sor,or the fabricator,unless otherwise specified in the appli-cable product specification.6.2If the heat treatment required by the applicable product specification is to be performed by the purchaser or the purchaser’s agent,and the plates are to be supplied by the manufacturer or processor in a condition other than that required by the applicable product specification,the order shall sostate.6.2.1If plates are ordered without the heat treatment re-quired by the applicable product specification,heat treatment of the plates to conform to the requirements of the applicable product specification shall be the responsibility of the pur-chaser.6.3If heat treatment is to be performed,the plates shall be heat treated as specified in the applicable product specification. The purchaser may specify the heat treatment to be used, provided it is not in conflict with the requirements of the applicable product specification.6.4If normalizing is to be performed by the fabricator,the plates shall be either normalized or heated uniformly for hot forming,provided that the temperature to which the plates are heated for hot forming does not significantly exceed the normalizing temperature.6.5If no heat treatment is required,the manufacturer or processor shall have the option of heat treating the plates by normalizing,stress relieving,or normalizing and then stress relieving to meet the requirements of the applicable product specification.6.6If approved by the purchaser,cooling rates faster than those obtained by cooling in air are permissible to achieve specified mechanical properties,provided that the plates are subsequently tempered in the temperature range from1100to 1300°F[595to705°C].7.Chemical Composition7.1Heat Analysis7.1.1Sampling for chemical analysis and methods of analysis shall be in accordance with Test Methods,Practices, and Terminology A751.7.1.2For each heat,the heat analysis shall include determi-nation of the content of carbon,manganese,phosphorus,sulfur, silicon,nickel,chromium,molybdenum,copper,vanadium, columbium;any other element that is specified or restricted by the applicable product specification for the applicable grade, class,and type;aluminum,if the aluminum content is to be used in place of austenitic grain size testing of the heat(see 8.2.2.1);and any other austenitic grain refining element for which limits are specified in the purchase order(see8.2.4).7.1.3Heat analyses shall conform to the heat analysis requirements of the applicable product specification for the applicable grade,class,and type.In addition,for elements that are listed in Table1but are not specified or restricted in the applicable product specification for the applicable grade,class, and type,heat analyses shall conform to the applicable heat analysis limits given in Table1.7.2Product Analysis:7.2.1Sampling for chemical analysis and methods of analy-sis shall be in accordance with Test Methods,Practices,and Terminology A751.7.2.2For each plate-as-rolled,the purchaser shall have the option of chemically analyzing a broken tension test specimen or a sample taken from the same relative location as that from which the tension test specimen was obtained.7.2.3For elements that are specified or restricted by the applicable product specification for the applicable grade,class, and type,product analyses shall conform to the product analysis requirements of the applicable product specification for the applicable grade,class,and type.7.2.4For elements that are listed in Table1but are not specified or restricted by the applicable product specification for the applicable grade,class,and type,product analyses shall conform to the applicable product analysis limits given in Table1.7.3Referee Analysis—For referee purposes,Test Methods, Practices,and Terminology A751shall be used.8.Metallurgical Structure8.1If coarse austenitic grain size is specified,the steel shall have a carburized austenitic grain size number in the range from1to5,inclusive,as determined by the McQuaid-Ehn Test. Determinations shall be in accordance with Test Methods E112,Plate IV,by carburizing for8h at1700°F[925°C].At least70%of the grains in the area examined shall conform to the specified grain size requirement.One test per heat shall be made.8.2Fine Austenitic Grain Size:8.2.1Iffine austenitic grain size is specified,aluminum shall be used as the grain refining element,except as allowed by8.2.4.8.2.2Iffine austenitic grain size is specified,except as allowed by8.2.2.1,the steel shall have a carburized austenitic grain size number of5or higher(finer)as determined by the TABLE1Limits on Elements(see7.1.3and7.2.4)Copper,max%A Heat analysisProduct analysis0.400.43Nickel,max%A Heat analysisProduct analysis0.400.43Chromium,max%A,B Heat analysisProduct analysis0.300.34Molybdenum,max%A,B Heat analysisProduct analysis0.120.13Vanadium,max%C Heat analysisProduct analysis0.030.04Columbium,max%D Heat analysisProduct analysis0.020.03Titanium,max%E Heat analysisProduct analysis0.030.04A In addition for each heat,based upon the heat analysis,the sum of copper, nickel,chromium,and molybdenum shall not exceed1.00%,unless one or more of those elements are specified or restricted by the applicable product specification for the applicable grade,class,and type.B In addition for each heat,based upon the heat analysis,the sum of chromium and molybdenum shall not exceed0.32%,unless one or both of those elements are specified or restricted by the applicable product specification for the applicable grade,class,and type.C By agreement between the purchaser and the supplier,the heat analysis limit for vanadium is permitted to be increased to a value not higher than0.10%,and the product analysis limit for vanadium is permitted to be increased to a value not higher than0.11%.D By agreement between the purchaser and the supplier,the heat analysis limit for columbium is permitted to be increased to a value not higher that0.05%,and the product analysis limit for columbium is permitted to be increased to a value not higher than0.06%.E By agreement between the purchaser and the supplier,the heat analysis limit for titanium is permitted to be increased to a value not higher than0.04%,and the product analysis limit for titanium is permitted to be increased to a value not higher than0.05%.。
A20标准
3.1.7 钢板—— 指按厚度或重量订货的扁平热轧钢，以宽度和长度为特点，通常获得尺寸如下：
(1)宽度>8in.(200mm)和厚度>0.2290in.(6.0mm)。
(2)宽度>48in.(1200mm)和厚度>0.179in.(4.6mm)。
7.2.3 对于由适用产品标准对适用钢级、类别和类型规定或限制的元素，成品分析应符合适用产品标准对适用钢级、类别和类型的成品分析要求。
7.2.4 对于表 1 中列出、但由适用产品标准对适用钢级、类别和类型未规定或未限制的元素，成品分析应符合表 1 中适用的成品分析限制范围。
A204/A204M 压力容器用钼合金钢板
A225/A225M 压力容器用锰钒合金钢板
A285/A285M 压力容器用中、低强度碳钢板
A299/A299M 压力容器用碳锰硅钢钢板
A302/A302M 压力容器用锰钼和锰钼镍合金钢板
A353/A353M 压力容器用经二次正火加回火的9%镍合金钢板
3.1.8 沉淀热处理—— 一种亚临界温度的热处理，以产生亚微观组分的沉淀等从而提高某些所需性能。
3.1.9 加工厂—— 直接控制或负责从卷材生产钢板的组织。这些加工操作包括开卷、矫平、切割、试验、检验、精整、热处理（如适用）、包装、标志、装运和证书。
3.2 本标准使用的其它术语参见 A941 术语。
A612/A612M 中、低温压力容器用高强度碳钢板
A645/A645M 压力容器用 5%镍特殊热处理合金钢板
A662/A662M 中、低温压力容器用碳锰钢板
A724/A724M 多层焊接压力容器用淬火加回火碳钢板
A20-06
美国材料与试验协会标准压力容器用钢板一般要求(摘要)ASTM A20/A20M-06代替ASTM A20/A20M-031 适用范围1.1本标准包括一组通用的技术要求，除适用产品标准中另有规定外，这些要求适用于由ASTM颁布的下列压力容器用钢板标准：标准号标准名称A202/A202M 压力容器用铬—锰—硅合金钢板A203/A203M 压力容器用镍合金钢板A204/A204M 压力容器用钼合金钢板A225/A225M 压力容器用锰钒合金钢板A285/A285M 压力容器用中、低强度碳钢板A299/A299M 压力容器用碳锰硅钢钢板A302/A302M 压力容器用锰钼和锰钼镍合金钢板A353/A353M 压力容器用经二次正火加回火的9%镍合金钢板A387/A387M 压力容器用铬钼合金钢板A455/A455M 压力容器用高强度碳锰钢板A515/A515M 中、高温压力容器用碳钢板A516/A516M 中、低温压力容器用碳钢板A517/A517M 压力容器用高强度淬火加回火合金钢板A533/A533M 压力容器用锰钼、锰钼镍淬火加回火合金钢板A537/A537M 压力容器用碳锰硅热处理钢板A542/A542M 压力容器用铬钼淬火加回火合金钢板A543/A543M 压力容器用镍铬钼淬火加回火合金钢板A553/A553M 压力容器用8%和9%镍淬火加回火合金钢板A562/A562M 压力容器用搪玻璃或表面渗金属的碳锰钛钢板A612/A612M 中、低温压力容器用高强度碳钢板A645/A645M 压力容器用5%镍特殊热处理合金钢板A662/A662M 中、低温压力容器用碳锰钢板A724/A724M 多层焊接压力容器用淬火加回火碳钢板A734/A734M 压力容器用合金和高强度低合金淬火加回火钢板A735/A735M 中、低温压力容器用低碳锰钼铌合金钢板A736/A736M 压力容器用低碳镍铜铬钼铌时效硬化合金钢板A737/A737M 压力容器用低合金高强度钢板A738/A738M 中、低温压力容器用碳锰硅热处理钢板A782/A782M 压力容器用锰铬钼硅锆淬火加回火合金钢板A832/A832M 压力容器用铬钼钒合金钢板A841/A841M 压力容器用热机械控制工艺（TMCP）生产钢板A844/A844M 压力容器用直接淬火工艺生产的9%镍合金钢板A1017/A1017M 压力容器用铬钼钨合金钢板A1041/A1041M 压力容器用铬钼钨高强度合金钢板1.1.1 本标准还包括一组补充要求，适用于上列若干个标准中本身已指明的场合。
A387-2017压力容器用铬钼合金钢板标准
A387/A387M-2017A387/A387M 压力容器用铬-钼合金钢板标准 本标准以A387/A387M固定代号发布的，其后的数字表示原先采用版本的年号或者是当有修订时的最新修订版的年号。
圆括号中的数字为再次批准的年号。
上标符号（ε）表示因最新修订或再次批准发生的编辑性变化。
本标准已被批准供美国国防部的机构使用。
1.适用范围1.1.本标准适用于焊接锅炉和高温压力容器用铬-钼合金钢板。
1.2.本标准中的钢板按所含的合金元素分成以下几个等级：级别公称铬含量，% 公称钼含量，%2 0.50 0.5012 1.00 0.5011 1.25 0.5022，22L 2.25 1.0021，21L 3.00 1.005 5.00 0.509 9.00 1.0091 9.00 1.001.3.除21L、22L和91级外，每个级别的钢板均有如表2和表3所示的两个抗拉强度类别。
21L和22L级钢板仅适用于第1类钢，91级钢板仅适用于第2类钢。
注1—911级钢板以前在本标准内，现在由A1017/A1017M标准覆盖。
1.4.钢板的最大厚度仅受化学成分满足规定力学性能要求的能力限制。
1.5.以（SI）国际单位或英寸（-磅）表示的数值应认作为标准值。
在本标准文本中，国际（SI）单位用括号表示。
由于两种单位制的数值不能做到精确地相等，因此，必须分别地独立使用两种单位制。
如加以混用，将导致与本标准的不一致。
1.6.本国际标准是根据国际公认的标准化原则、由世界贸易组织技术贸易壁垒委员会发布的国际标准、指南和建议发展而来的。
2.引用标准2.1.ASTM标准：A20/A20M 压力容器用钢板通用标准A370 钢制品力学性能试验的试验方法和定义A435/A435M 钢板超声直射波检验标准A577/A577M钢板超声斜射波检验标准A578/A578M特殊用途的普通钢板与复合钢板的超声直射波检验标准A1017/ A1017M 压力容器用铬-钼-钨合金钢板标准2.2.AWS标准：A5.5/ A5.5M 保护金属电弧焊用低合金钢焊条规范A5.23/ A5.23M 埋弧焊用低合金钢焊条和焊剂规范A5.28/ A5.28M 气体保护电弧焊用低合金钢焊条和螺杆规范A5.29/ A5.29M 熔芯电弧焊用低合金钢焊条规范3.一般要求与订货须知3.1.按本标准供应的钢板应符合A20/A20M的要求。
压力容器用钢板通用技术条件ASTM A20
1.1.1 This specification also covers a group of supplementary requirements which are applicable to several of the above specifications as indicated therein. These are provided for use when additional testing or inspection is desired and apply only when specified individually by the purchaser in the order.1.2 Appendix X1 describes the production and s ome of the characteristics of coiled product from which pressure vessel plates may be produced.1.3 Appendix X2 provides information on the variability of tensile properties in plates for pressure vessels.1.4 Appendix X3 provides information on the variability of Charpy-V-Notch impact test properties in plates for pressure vessels.1.5 这些材料仅适于熔焊，熔焊时应采用适合于该钢种级别及使用条件的焊接工艺。
1.6 如本标准与专用材料标准的要求不一致，则以专用材料标准的要求为准。
1.7 买方可以规定不否定本标准或专用材料标准条款的附加要求。
这些附加要求必须纳入订货单说明中，其验收条件应与供方协商(见4.1.8)，并取得供方接受。
- 1、下载文档前请自行甄别文档内容的完整性，平台不提供额外的编辑、内容补充、找答案等附加服务。
- 2、"仅部分预览"的文档,不可在线预览部分如存在完整性等问题,可反馈申请退款(可完整预览的文档不适用该条件!)。
- 3、如文档侵犯您的权益，请联系客服反馈,我们会尽快为您处理(人工客服工作时间：9:00-18:30)。
1.1.1 This specification also covers a group of supplementary requirements which are applicable to several of the above specifications as indicated therein. These are provided for use when additional testing or inspection is desired and apply only when specified individually by the purchaser in the order.1.2 Appendix X1 describes the production and s ome of the characteristics of coiled product from which pressure vessel plates may be produced.1.3 Appendix X2 provides information on the variability of tensile properties in plates for pressure vessels.1.4 Appendix X3 provides information on the variability of Charpy-V-Notch impact test properties in plates for pressure vessels.1.5 这些材料仅适于熔焊，熔焊时应采用适合于该钢种级别及使用条件的焊接工艺。
1.6 如本标准与专用材料标准的要求不一致，则以专用材料标准的要求为准。
1.7 买方可以规定不否定本标准或专用材料标准条款的附加要求。
这些附加要求必须纳入订货单说明中，其验收条件应与供方协商(见4.1.8)，并取得供方接受。
1.8 为了确定供应材料是否与本标准及1.1中所列各材料标准的规定极限值相一致，各数值右面的有效位数应按E29推荐的圆整方法进行圆整。
1.9 以英寸一磅单位或SI单位表示的数值均可作为标准值。
本文中SI单位表示于括号内。
由于各单位制所表示的数值不能与另一种单位制进行精确换算，因此，每一种单位制必须独立使用。
两个单位制的数值混合使用可能导致与本标准不一致的结果。
1.10 本标准及所引用的材料标准均采用英寸一磅和SI两种单位，但除非订货单中规定采用"M"标志(SI单位)，否则材料将以英寸一磅单位供货。
2. 参考文献2.1 ASTM Standards:A 202/A202M Specification for Pressure Vessel Plates，Alloy Steel，Chromium-Manganese-SiIic~n~A 2031A203M Specification for Pressure Vessel Plates，Alloy Steel，Nickel4A 204/A204M Specification for Pressure Vessel Plates，Alloy Steel，Molybdenum4A 225iA225M Specification for Pressure Vessel Plates，Alloy Steel，Manganese-Vanadium-Nickel4A 285/A285M Specification for Pressure Vessel Plates，Carbon Steel，Low- and Intermediate-Tensile Strength4A 299/A299M Specification for Pressure Vessel Plates，Carbon Steel，Manganese-Silicon4A 30UA302M Specification for Pressure Vessel Plates，Alloy Steel，Manganese-Molybdenum andManganese-Molybdenum-Nickel4A 353iA353M Specification for Pressure Vessel Plates，Alloy Steel，9 Percent Nickel，Double-Normalized andTempered4A 370 Test Methods and Definitions for Mechanical Testing of Steel Products’A 3871A387M Specification for Pressure Vessel Plates，Alloy Steel，Chromium-Molybdenum4A 435iA435M Specification for Straight-Beam Ultrasonic Examination of Steel Plates4A 4551A455M Specification for Pressure Vessel Plates，Carbon Steel，High Strength Manganese4A 515iA515M Specification for Pressure Vessel Plates，Carbon Steel，for Intermediate- and Higher-TemperatureService4A 5161A5 16M Specification for Pressure Vessel Plates，Carbon Steel，for Moderate- and Lower-TemperatureService4A 517/A517M Specification for Pressure Vessel Plates，Alloy Steel，High-Strength，Quenched and Tempered4 A 5331A533M Specification for Pressure Vessel Plates，Alloy Steel，Quenched and TemperedManganese-Molybdenum and Manganese-Molybdenum-Nickel4A 5371A537M Specification for Pressure Vessel Plates，Heat-Treated，Carbon-Manganese-Silicon Steel4A 54UA542M Specification for Pressure Vessel Plates，Alloy Steel，Quenched and Tempered，Chromium-Molybdenum，and Chromium-Molybdenum-Vanadium4A 543lA543M Specification for Pressure Vessel Plates，Alloy Steel，Quenched and Tempered Nickel- Chromium-Molybdenum4A 5531A553M Specification for Pressure Vessel Plates，Alloy Steel，Quenched and Tempered 8 and 9 PercentNickel4A 562/A562M Specification for Pressure Vessel Plates，Carbon Steel，Manganese-Titanium for Glass or DiffusedMetallic Coatings4A 577/A577M Specification for Ultrasonic Angle-Beam Examination of Steel Plates4A 578iA578M Specification for Straight-Beam Ultrasonic Examination of Plain and Clad Steel Plates for SpecialApplications4A 61ZA612M Specification for Pressure Vessel Plates，Carbon Steel，High Strength，for Moderate and LowerTemperature Service4A 645lA645M Specification for Pressure Vessel Plates，Five Percent Nickel Alloy Steel，Specially Heat Treated4 A 6621A662M Specification for Pressure Vessel Plates，Carbon-Manganese，for Moderate and Lower TemperatureService4A 700 Practices for Packaging，Marking，and Loading Methods for Steel Products for Domestic Shipment6A 7241A724M Specification for Pressure Vessel Plates，Carbon Steel，Quenched and Tempered，for WeldedLayered Pressure Vessels4A 7341A734M Specification for Pressure Vessel Plates，Alloy Steel and High-Strength Low-Alloy Steel，Quenchedand Tempered4A 735/A735M Specification for Pressure Vessel Plates，Low-Carbon Manganese-Molybdenum-Columbium A lloySteel，for Moderate and Lower Temperature Service4A 7361A736M Specification for Pressure Vessel Plates，Low-Carbon Age-Hardening Nickel- Copper- Chromium-Molybdenum- Columbium and Nickel-Copper Manganese-Molybdenum-Columbium Alloy Steel4A 7371A737M Specification for Pressure Vessel Plates，High-Strength，Low-Alloy Steel4A 738lA738M Specification for Pressure Vessel Plates，Heat-Treated，Carbon-Manganese-Silicon Steel，forModerate and Lower Temperature Service4A 751 Test Methods，Practices，and Terminology for Chemical Analysis of Steel Products4Annual Book of ASTM Stanandords. Vol 01.05.Annual Book of ASTM Standards，Vol 01.04.Allnual Book ofASTM Standnrds，Vol 01.03.3 本标准专用术语说明3.1 封顶钢-因受早期压盖过程而使沸腾作用受到限制的沸腾钢。