活化工艺对煤基活性炭结构及电容性能的影响

活化工艺对煤基活性炭结构及电容性能的影响
杨森;韩洋;李阳;董伟;刘智慧
【期刊名称】《煤炭转化》
【年(卷),期】2018(41)2
【摘要】The activated carbon was prepared by KOH activation process,and the optimum technological parameters were obtained by orthogonal experiment:the lignite particle size is 0.075 0 mm-0.150 0 mm (100 mesh-200 mesh),the mass ratio of KOH and activated carbon is 3 ∶ 1,the activation temperature is 600 ℃C,and the activation time is 1 h.The optimum specific surface area through the optimum process is 504.7
m2/g,and the degree of graphitization is low.The specific capacitance is 107.7 F/g,the specific capacitance retention was 96.6％ at 2 times the current and 93.8 ％ at 5 times the current,the attenuation is small and the magnification performance is good.%利用KOH活化工艺制备活性炭,通过正交实验得到最优工艺参数:褐煤粒度为0.075 0 mm～0.150 0 mm(过100目～200目筛),KOH与活性炭质量比为3∶1,活化温度为600℃,活化时间为1h.最佳工艺时样品的比表面积最大,为504.7m2/g,石墨化程度低,比电容达107.7F/g,在2倍电流下比电容保持率达96.6％,在5倍电流下比电容保持率达93.8％,衰减较小,倍率性能良好.
【总页数】10页(P57-66)
【作者】杨森;韩洋;李阳;董伟;刘智慧
【作者单位】辽宁工程技术大学矿业技术学院,125105辽宁葫芦岛;辽宁工程技术大学矿业技术学院,125105辽宁葫芦岛;辽宁工程技术大学矿业技术学院,125105辽宁葫芦岛;辽宁工程技术大学材料科学与工程学院,123000辽宁阜新;辽宁工程技术大学材料科学与工程学院,123000辽宁阜新
【正文语种】中文
【中图分类】TQ424.1;TQ15
【相关文献】
1.浸渍活化工艺对银催化剂性能及其微观结构的影响 [J], 张锋;林伟;李金兵
2.预炭化对KOH活化石油焦的结构及电容性能的影响 [J], 时志强;赵朔;陈明鸣;王妹先;王成扬
3.二次活化对活性炭孔结构和电容性能的影响 [J], 孟玲
4.基于碳化木材电极探究不同活化方式对其结构特征和电容性能的影响 [J], 辛福恩; 刘沛静
5.活化温度对无灰煤基活性炭结构及性能的影响 [J], 刘俊科; 孙章; 樊丽华
因版权原因，仅展示原文概要，查看原文内容请购买。