钢材抗拉强度与硬度的对照表

抗拉强度与硬度对照表

抗拉强度Rm N/mm2维氏硬度HV布氏硬度HB 洛氏硬度HRC 抗拉强度Rm N/mm2维氏硬度HV 布氏硬度HB 洛氏硬度HRC 2508076112535033335.52708580.7111536034236.62859085.2119037035237.73059590.2122038036138.832010095125539037139.833510599.8129040038040.8350110105132041039041.8370115109135042039942.7380120114138543040943.6400125119142044041844.5415130124145545042845.3430135128148546043746.1450140133152047044746.9465145138155548045647480150143159549046648.4490155147163050047549.1510160152166551048549.8530165156170052049450.5545170162174053050451.1560175166177554051351.7575180171181055052352.3595185176184556053253610190181188057054253.6625195185192058055154.1640200190195559056154.7660205195199560057055.2675210199203061058055.7690215204207062058956.3705220209210563059956.8720225214214564060857.374023021921806506185775523522366058.377024022820.367058.878524523321.368059.280025023822.269059.782025524223.170060.1835260247247206185026525224.874061.886527025725.676062.5根据德国标准DIN50150,以下是常用范围的钢材抗拉强度与维氏硬度、布氏硬度、洛氏硬度的对照表88027526126.478063.3 90028026627.180064 91528527127.882064.7 93029027628.584065.3 95029528029.286065.9 96530028529.888066.4 9953102953190067 103032030432.292067.5 106033031433.394068 109534032334.4* HRB St12=65St13=55St14=50硬度试验是机械性能试验中最简单易行的一种试验方法。

(完整版)硬度与抗拉强度的关系对照表

一、硬度与抗拉强度的关系
当钢的硬度在500HB以下时，其抗拉强度与硬度成正比，kg/m㎡（óB）=1/3 X HB=3.2 X HRC=2.1 X HS,但上述关系式也并非在什么场合都成立，从热处理方面说，回火温度低时，kg/m㎡与HRC时的相关关系便可能被破坏，钢的回火温度，硬度和抗拉强度的关系如图所示。

由此图可见硬度随回火温度的升高而下降，但在淬火状态以及300℃以下低温回火时，硬度与抗拉强度的关系难以成立。

当回火温度在300℃左右时，kg/m ㎡与HRC具有相关关系，即硬度高，抗拉强度就高；硬度低，抗拉强度就低。

在低温回火状态欲求出kg/m㎡值是很困难的，因为此时抗拉强度值分布很离散。

由于低温回火件的kg/m㎡不稳定而不能确定，故在日本工业标准（JIS）中也是通试验来测定400℃以上温度回火件的拉伸特性（也有300℃回火工件）。

换言之是只对调质件（淬火+400℃回火）进行拉伸试验。

在工业上只是在要求抗旋转弯曲疲劳和抗磨损时才使用低温回火件。

高频淬火和渗碳淬火即为此适用例。

受拉应力的零件不采用低温回火。

不过在低碳钢中，但淬火M能发生自回火(故Ms点高)时，亦有在淬火状态下使用者。

低碳钢的板条马氏体组织结构自回火，正可在工业上应用，但此时必须考虑淬透性和质量效应（必要时应添加B、Cr、Mn等金属元素）。

二、钢材抗拉强度与维氏硬度、布氏硬度、洛氏硬度的对照表
如果您要查的抗拉强度>1000N/mm2，或者维氏硬度>310HV，或者布氏硬度>300HB，或者洛氏硬度>32HRC，请查本表。

钢材抗拉强度与硬度的对照表

根据德国标准DIN50150,以下是常用范围的钢材抗拉强度与维氏硬度、布氏硬度、洛氏硬度的对照表。

HB有两种一种是ＨＢＳ（钢球）另一种是ＨＢＷ（硬质合金球）
用一定直径的钢球或硬质合金球，以规定的试验力（F）压入式样表面，经规定保持时间后卸除试验力，测量试样表面的压痕直径（L）。

布氏硬度值是以试验力除以压痕球形表面积所得的商。

以HBS（钢球）表示，
单位为N/mm2(MPa)。

其计算公式为：
式中：F--压入金属试样表面的试验力，N；
D--试验用钢球直径，mm；
d--压痕平均直径，mm。

测定布氏硬度较准确可靠，但一般HBS只适用于450N/mm2（MPa）以下的金属材料，对于较硬的钢或较薄的板材不适用。

在钢管标准中，布氏硬度用途最广，往往以压痕直径d来表示该材料的硬度，既直观，又方便。

布氏硬度试验还可用于有色金属和软钢，采用小直径球压头可以测量小尺寸和较薄材料。

布氏硬度计多用于原材料和半成品的检测，由于压痕较大，一般不用于成品检测。

举例：120HBS10/1000/30：表示用直径10mm钢球在1000Kgf（9.807KN）试验力作用下，保持30s（秒）
测得的布氏硬度值为120N/ mm2（MPa）。

HBS是布氏硬度的一种,现在已经不在采用,测试标准已经更改,HBS是钢球头,而现在均采用HBW即HB,硬质合金钢球,橡胶邵氏硬度为HA或HD,HA为软橡胶,HD为硬橡胶。

抗拉强度与硬度对照表图文

抗拉强度与硬度公司专营宝钢产品:冷板、热板、镀锌板. ：021-******** 宝钢资源抗拉强度与硬度对照表抗拉强度N/mm2 维氏硬度布氏硬度洛氏硬度抗拉强度N/mm2维氏硬度布氏硬度洛氏硬度Rm HV HB HRB Rm HV HB HRB 250 80 76 1125 350 333 35.5 270 85 80.7 1115 360 342 36.6 285 90 85.2 1190 370 352 37.7 305 95 90.2 1220 380 361 38.8 320 100 95 1255 390 371 39.8 335 105 99.8 1290 400 380 40.8 350 110 105 1320 410 390 41.8 370 115 109 1350 420 399 42.7 380 120 114 1385 430 409 43.6 400 125 119 1420 440 418 44.5415 130 124 1455 450 428 45.3 430 135 128 1485 460 437 46.1 450 140 133 1520 470 447 46.9 465 145 138 1555 480 456 47 480 150 143 1595 490 466 48.4 490 155 147 1630 500 475 49.1 510 160 152 1665 510 485 49.8 530 165 156 1700 520 494 50.5 545 170 162 1740 530 504 51.1 560 175 166 1775 540 513 51.7 575 180 171 1810 550 523 52.3 595 185 176 1845 560 532 53 610 190 181 1880 570 542 53.6 625 195 185 1920 580 551 54.1 640 200 190 1955 590 561 54.7 660 205 195 1995 600 570 55.2675 210 199 2030 610 580 55.7 690 215 204 2070 620 589 56.3 705 220 209 2105 630 599 56.8 720 225 214 2145 640 608 57.3 740 230 219 2180 650 618 57.8 755 235 223 660 58.3 770 240 228 20.3 670 58.8 785 245 233 21.3 680 59.2 800 250 238 22.2 690 59.7 820 255 242 23.1 700 60.1 835 260 247 24 720 61 850 265 252 24.8 740 61.8 865 270 257 25.6 760 62.5 880 275 261 26.4 780 63.3 900 280 266 27.1 800 64 915 285 271 27.8 820 64.7930 290 276 28.5 840 65.3950 295 280 29.2 860 65.9965 300 285 29.8 880 66.4995 310 295 31 900 671030 320 304 32.2 920 67.51060 330 314 33.3 940 681095 340 323 34.4* HRB St12=65 St13=55 St14=50硬度试验是机械性能试验中最简单易行的一种试验方法。

硬度与抗拉强度的关系对照表

一、硬度与抗拉强度的关系
当钢的硬度在500HB以下时，其抗拉强度与硬度成正比，kg/m㎡（óB）=1/3 X HB= X HRC= X HS,但上述关系式也并非在什么场合都成立，从热处理方面说，回火温度低时，kg/m㎡与HRC时的相关关系便可能被破坏，钢的回火温度，硬度和抗拉强度的关系如图所示。

由此图可见硬度随回火温度的升高而下降，但在淬火状态以及300℃以下低温回火时，硬度与抗拉强度的关系难以成立。

当回火温度在300℃左右时，kg/m ㎡与HRC具有相关关系，即硬度高，抗拉强度就高；硬度低，抗拉强度就低。

在低温回火状态欲求出kg/m㎡值是很困难的，因为此时抗拉强度值分布很离散。

由于低温回火件的kg/m㎡不稳定而不能确定，故在日本工业标准（JIS）中也是通试验来测定400℃以上温度回火件的拉伸特性（也有300℃回火工件）。

换言之是只对调质件（淬火+400℃回火）进行拉伸试验。

在工业上只是在要求抗旋转弯曲疲劳和抗磨损时才使用低温回火件。

高频淬火和渗碳淬火即为此适用例。

受拉应力的零件不采用低温回火。

不过在低碳钢中，但淬火M能发生自回火(故Ms点高)时，亦有在淬火状态下使用者。

低碳钢的板条马氏体组织结构自回火，正可在工业上应用，但此时必须考虑淬透性和质量效应（必要时应添
加B、Cr、Mn等金属元素）。

二、钢材抗拉强度与维氏硬度、布氏硬度、洛氏硬度的对照表
如果您要查的抗拉强度>1000N/mm2，或者维氏硬度>310HV，或者布氏硬度>300HB，或者洛氏硬度>32HRC，请查本表。

硬度与抗拉强度的关系对照表

一、硬度与抗拉强度的关系
当钢的硬度在500HB以下时，其抗拉强度与硬度成正比，kg/m㎡（óB）=1/3 X HB= X HRC= X HS,但上述关系式也并非在什么场合都成立，从热处理方面说，回火温度低时，kg/m㎡与HRC时的相关关系便可能被破坏，钢的回火温度，硬度和抗拉强度的关系如图所示。

由此图可见硬度随回火温度的升高而下降，但在淬火状态以及300℃以下低温回火时，硬度与抗拉强度的关系难以成立。

当回火温度在300℃左右时，kg/m ㎡与HRC具有相关关系，即硬度高，抗拉强度就高；硬度低，抗拉强度就低。

在低温回火状态欲求出kg/m㎡值是很困难的，因为此时抗拉强度值分布很离散。

由于低温回火件的kg/m㎡不稳定而不能确定，故在日本工业标准（JIS）中也是通试验来测定400℃以上温度回火件的拉伸特性（也有300℃回火工件）。

换言之是只对调质件（淬火+400℃回火）进行拉伸试验。

在工业上只是在要求抗旋转弯曲疲劳和抗磨损时才使用低温回火件。

高频淬火和渗碳淬火即为此适用例。

受拉应力的零件不采用低温回火。

不过在低碳钢中，但淬火M能发生自回火(故Ms点高)时，亦有在淬火状态下使用者。

低碳钢的板条马氏体组织结构自回火，正可在工业上应用，但此时必须考虑淬透性和质量效应（必要时应添加B、Cr、Mn等金属元素）。

二、钢材抗拉强度与维氏硬度、布氏硬度、洛氏硬度的对照表
如果您要查的抗拉强度>1000N/mm2，或者维氏硬度>310HV，或者布氏硬度>300HB，或者洛氏硬度>32HRC，请查本表。

硬度和抗拉强度的关系对照表

一、硬度与抗拉强度的关系
当钢的硬度在500HB以下时，其抗拉强度与硬度成正比，kg/m㎡（óB）=1/3 X HB=3.2 X HRC=2.1 X HS,但上述关系式也并非在什么场合都成立，从热处理方面说，回火温度低时，kg/m㎡与HRC时的相关关系便可能被破坏，钢的回火温度，硬度和抗拉强度的关系如图所示。

由此图可见硬度随回火温度的升高而下降，但在淬火状态以及300℃以下低温回火时，硬度与抗拉强度的关系难以成立。

当回火温度在300℃左右时，kg/m ㎡与HRC具有相关关系，即硬度高，抗拉强度就高；硬度低，抗拉强度就低。

在低温回火状态欲求出kg/m㎡值是很困难的，因为此时抗拉强度值分布很离散。

由于低温回火件的kg/m㎡不稳定而不能确定，故在日本工业标准（JIS）中也是通试验来测定400℃以上温度回火件的拉伸特性（也有300℃回火工件）。

换言之是只对调质件（淬火+400℃回火）进行拉伸试验。

在工业上只是在要求抗旋转弯曲疲劳和抗磨损时才使用低温回火件。

高频淬火和渗碳淬火即为此适用例。

受拉应力的零件不采用低温回火。

不过在低碳钢中，但淬火M能发生自回火(故Ms点高)时，亦有在淬火状态下使用者。

低碳钢的板条马氏体组织结构自回火，正可在工业上应用，但此时必须考虑淬透性和质量效应（必要时应添
加B、Cr、Mn等金属元素）。

二、钢材抗拉强度与维氏硬度、布氏硬度、洛氏硬度的对照表
如果您要查的抗拉强度>1000N/mm2，或者维氏硬度>310HV，或者布氏硬度>300HB，或者洛氏硬度>32HRC，请查本表。

硬度与抗拉强度的关系对照表

一、硬度与抗拉强度的关系当钢的硬度在500HB以下时，其抗拉强度与硬度成正比，kg/m㎡（óB）=1/3 X HB=3.2 X HRC=2.1 X HS,但上述关系式也并非在什么场合都成立，从热处理方面说，回火温度低时，kg/m㎡与HRC时的相关关系便可能被破坏，钢的回火温度，硬度和抗拉强度的关系如图所示。

由此图可见硬度随回火温度的升高而下降，但在淬火状态以及300℃以下低温回火时，硬度与抗拉强度的关系难以成立。

当回火温度在300℃左右时，kg/m ㎡与HRC具有相关关系，即硬度高，抗拉强度就高；硬度低，抗拉强度就低。

在低温回火状态欲求出kg/m㎡值是很困难的，因为此时抗拉强度值分布很离散。

由于低温回火件的kg/m㎡不稳定而不能确定，故在日本工业标准（JIS）中也是通试验来测定400℃以上温度回火件的拉伸特性（也有300℃回火工件）。

换言之是只对调质件（淬火+400℃回火）进行拉伸试验。

在工业上只是在要求抗旋转弯曲疲劳和抗磨损时才使用低温回火件。

高频淬火和渗碳淬火即为此适用例。

受拉应力的零件不采用低温回火。

不过在低碳钢中，但淬火M能发生自回火(故Ms点高)时，亦有在淬火状态下使用者。

低碳钢的板条马氏体组织结构自回火，正可在工业上应用，但此时必须考虑淬透性和质量效应（必要时应添加B、Cr、Mn等金属元素）。

二、钢材抗拉强度与维氏硬度、布氏硬度、洛氏硬度的对照表维氏布氏克罗普洛氏标尺肖氏拉伸强度HV HB HK HRA HRB HRC HS Kg/m㎡528 496 558 76.3 51 67.6 264 513 481 542 75.9 50 66.2 255 498 469 526 75.2 49 64.7 246 484 455 510 74.7 48 63.4 238 471 443 495 74.1 47 62.1 229 458 432 480 73.6 46 60.8 221 446 421 466 73.1 45 59.6 215 434 409 452 72.5 44 58.4 208 423 400 438 72.0 43 57.2 201 412 390 426 71.5 42 56.1 194 402 381 414 70.9 41 55.0 188 392 371 402 70.4 40 53.9 182 382 362 391 69.9 39 52.9 177 372 353 380 69.4 38 51.8 171 363 344 370 68.9 37 50.7 166 354 336 360 68.4 36 49.7 161 345 327 351 67.9 35 48.7 156 336 319 342 67.4 34 47.7 152 327 311 334 66.8 33 46.6 149 318 301 326 66.3 32 45.6 146 310 294 318 65.8 31 44.6 141 302 286 311 65.3 30 43.6 138 294 279 304 64.6 29 42.7 135 286 271 297 64.3 28 41.7 131 279 264 290 63.8 27 40.8 128 272 258 284 63.3 26 39.9 125 266 253 278 62.8 25 39.2 123 260 247 272 62.4 24 38.4 119254 243 266 62.0 100 23 37.7 117 248 237 261 61.5 99.0 22 36.9 115 243 231 256 61.0 98.5 21 36.3 112 238 226 251 60.5 97.8 20 35.6 110 230 219 243 60.2 96.7 34.6 109 222 212 236 59.5 96.3 33.5 104 213 203 229 58.9 96.0 32.3 102 204 194 220 58.3 95.0 31.1 100 196 187 212 57.6 94.0 30.0 98 188 179 204 57.0 93.0 94 180 171 196 56.4 92 92 173 165 189 55.8 91 90 如果您要查的抗拉强度>1000N/mm2，或者维氏硬度>310HV，或者布氏硬度>300HB，或者洛氏硬度>32HRC，请查本表抗拉强度RmN/mm2维氏硬度HV 布氏硬度HB 洛氏硬度HRC 250 80 76.0 -270 85 80.7 -285 90 85.2 -305 95 90.2 -320 100 95.0 -335 105 99.8 -350 110 105 -370 115 109 -380 120 114 -400 125 119 -415 130 124 -430 135 128 -450 140 133 -465 145 138 -480 150 143 -490 155 147 -510 160 152 - 530 165 156 - 545 170 162 - 560 175 166 - 575 180 171 - 595 185 176 - 610 190 181 - 625 195 185 - 640 200 190 - 660 205 195 - 675 210 199 - 690 215 204 - 705 220 209 - 720 225 214 - 740 230 219 - 755 235 223 - 770 240 228 20.3 785 245 233 21.3 800 250 238 22.2 820 255 242 23.1 835 260 247 24.0 850 265 252 24.8 865 270 257 25.6 880 275 261 26.4 900 280 266 27.1 915 285 271 27.8 930 290 276 28.5 950 295 280 29.2 965 300 285 29.8 995 310 295 31.0 1030 320 304 32.21060 330 314 33.3 1095 340 323 34.4 1125 350 333 35.5 1115 360 342 36.6 1190 370 352 37.7 1220 380 361 38.8 1255 390 371 39.8 1290 400 380 40.8 1320 410 390 41.8 1350 420 399 42.7 1385 430 409 43.6 1420 440 418 44.5 1455 450 428 45.3 1485 460 437 46.1 1520 470 447 46.9 1555 480 (456) 47.7 1595 490 (466) 48.4 1630 500 (475) 49.1 1665 510 (485) 49.8 1700 520 (494) 50.5 1740 530 (504) 51.1 1775 540 (513) 51.7 1810 550 (523) 52.3 1845 560 (532) 53.0 1880 570 (542) 53.61920 580 (551) 54.1 1955 590 (561) 54.7 1995 600 (570) 55.2 2030 610 (580) 55.7 2070 620 (589) 56.3 2105 630 (599) 56.8 2145 640 (608) 57.3 2180 650 (618) 57.8660 58.3670 58.8680 59.2690 59.7700 60.1720 61.0740 61.8760 62.5780 63.3800 64.0820 64.7840 65.3860 65.9880 66.4900 67.0920 67.5940 68.0。

钢材抗拉强度与硬度的对照表

.根据德国标准DIN50150,以下是常用范围的钢材抗拉强度与维氏硬度、布氏硬度、洛氏硬度的对照表。

抗拉强度维氏硬度布氏硬度洛氏硬度HRC HV HB Rm2N/mm - 80 76.0 250- 80.7 270 85- 285 85.2 90- 90.2 95 305- 95.0 100 320335 - 99.8 105105 110 350 -- 109 115 370114 120 - 380400 125 - 119- 415 124 130128 430 - 135- 133 140 450145 - 138 465143 150 480 -490 - 147 155- 510 152 160-530 156 165162 170 545 -175 166 560 -180 - 171 575185 - 176 595190-181610-195185625200-190640205-195660210199675-215204690-220209705--214720225219740230-223755235-77024022820.378524523321.3..22.2 238 250 80023.1 242 820 25524.0 260 247 835 850 265 24.8 252 257 865 25.6 270 275 880 26.4 261 266 900 27.1 280 271 285 915 27.8 930 290 276 28.5 950 29.2 280 295 300 285 965 29.8 31.0 995 310 295 1030 320 304 32.2 330 33.3 1060 31434.4 340 323 109535.5 333 1125 350 360 1115 342 36.6 370 352 1190 37.7 361 380 38.8 12201255 39.8 371 390 1290 400 380 40.8 410 1320 390 41.8420 399 1350 42.7 43.6 409 430 1385 418 1420 440 44.5 1455 428 450 45.3 1485 460 437 46.1 470 1520 447 46.9480 1555 (456) 47.7 4901595(466)48.4500(475)163049.1510(485)49.81665 (494)170052050.5 (504)174053051.1 (513)177554051.7 5501810(523)52.3 1845560(532)53.0 5701880(542)53.6 5801920(551)54.1 (561)195559054.7..55.2 (570) 600 199555.7 2030 610 (580)(589) 620 56.3 207056.8 630 2105 (599)2145 57.3 (608) 64057.8 (618) 650 218058.3 660670 58.859.2 68059.7 690700 60.161.0 720740 61.8760 62.563.3 78064.0 80064.7 82065.3 84065.9 860880 66.4900 67.067.5 92068.0940HB有两种一种是ＨＢＳ（钢球）另一种是ＨＢＷ（硬质合金球））压入式样表面，经规定保持时间后卸除试验力，测F用一定直径的钢球或硬质合金球，以规定的试验力（（钢球）表示，HBSL）。

硬度与抗拉强度的关系对照表

一、硬度与抗拉强度的关系
当钢的硬度在500HB以下时，其抗拉强度与硬度成正比，kg/m㎡（óB）=1/3 X HB=3.2 X HRC=2.1 X HS,但上述关系式也并非在什么场合都成立，从热处理方面说，回火温度低时，kg/m㎡与HRC时的相关关系便可能被破坏，钢的回火温度，硬度和抗拉强度的关系如图所示。

由此图可见硬度随回火温度的升高而下降，但在淬火状态以及300℃以下低温回火时，硬度与抗拉强度的关系难以成立。

当回火温度在300℃左右时，kg/m ㎡与HRC具有相关关系，即硬度高，抗拉强度就高；硬度低，抗拉强度就低。

在低温回火状态欲求出kg/m㎡值是很困难的，因为此时抗拉强度值分布很离散。

由于低温回火件的kg/m㎡不稳定而不能确定，故在日本工业标准（JIS）中也是通试验来测定400℃以上温度回火件的拉伸特性（也有300℃回火工件）。

换言之是只对调质件（淬火+400℃回火）进行拉伸试验。

在工业上只是在要求抗旋转弯曲疲劳和抗磨损时才使用低温回火件。

高频淬火和渗碳淬火即为此适用例。

受拉应力的零件不采用低温回火。

不过在低碳钢中，但淬火M能发生自回火(故Ms点高)时，亦有在淬火状态下使用者。

低碳钢的板条马氏体组织结构自回火，正可在工业上应用，但此时必须考虑淬透性和质量效应（必要时应添加B、Cr、Mn等金属元素）。

二、钢材抗拉强度与维氏硬度、布氏硬度、洛氏硬度的对照表
如果您要查的抗拉强度>1000N/mm2，或者维氏硬度>310HV，或者布氏硬度>300HB，或者洛氏硬度>32HRC，请查本表。

硬度与抗拉强度的关系对照表

一、硬度与抗拉强度的关系
当钢的硬度在500HB以下时，其抗拉强度与硬度成正比，kg/m m2（ d B）
= 1/3 X HB=3.2 X HRC=2.1 X HS,但上述关系式也并非在什么场合都成立，从热
处理方面说，回火温度低时，kg/m m与HRC时的相关关系便可能被破坏，钢的
回火温度，硬度和抗拉强度的关系如图所示
由此图可见硬度随回火温度的升高而下降，但在淬火状态以及300 C以下低温回火时，硬度与抗拉强度的关系难以成立。

当回火温度在300C左右时，kg/m
m与HRC具有相关关系，即硬度高，抗拉强度就高；硬度低，抗拉强度就低。

在低温回火状态欲求出kg/m m?值是很困难的，因为此时抗拉强度值分布很离散。

由于低温回火件的kg/m m?不稳定而不能确定，故在日本工业标准（JIS）中也是通试验来测定400C以上温度回火件的拉伸特性（也有300C回火工件）。

换言之是只对调质件（淬火+400C回火）进行拉伸试验。

在工业上只是在要求抗旋转弯曲疲劳和抗磨损时才使用低温回火件。

高频淬火和渗碳淬火即为此适用例。

受拉应力的零件不采用低温回火。

不过在低碳钢中，但淬火M能发生自回火（故Ms点高）时，亦有在淬火状态下使用者。

低碳钢的板条马氏体组织结构自回火，正可在工业上应用，但此时必须考虑淬透性和质量效应（必要时应添加B、Cr、Mn等金属元素）。

、钢材抗拉强度与维氏硬度、布氏硬度、洛氏硬度的对照表
如果您要查的抗拉强度＞1000N/mm，或者维氏硬度＞310HV, 或者布氏硬度＞300HB，或者洛氏硬度＞32HRC，请查本表。

抗拉强度和硬度对照表图文

抗拉强度与硬度上海国华公司专营宝钢产品:冷板、热板、镀锌板、电话:02１-５678９９9９宝钢资源抗拉强度与硬度对照表抗拉强度N/mm2维氏硬度布氏硬度洛氏硬度抗拉强度N/mm2维氏硬度布氏硬度洛氏硬度Rm HV HB HRB Rm HV HB HRB 250 80 76 1125 350 333 35、5 270 85 80、7 1115 360 342 36、6 285 90 85、2 1190 370 352 37、7 305 95 90、2 1220 380 361 38、8 320 100 95 1255 390 371 39、8 335 105 99、8 1290 400 380 40、8 350 110 105 1320 410 390 41、8 370 115 109 1350 420 399 42、7 380 120 114 1385 430 409 43、6400 125 119 1420 440 418 44、5 415 130 124 1455 450 428 45、3 430 135 128 1485 460 437 46、1 450 140 133 1520 470 447 46、9 465 145 138 1555 480 456 47 480 150 143 1595 490 466 48、4 490 155 147 1630 500 475 49、1 510 160 152 1665 510 485 49、8 530 165 156 1700 520 494 50、5 545 170 162 1740 530 504 51、1 560 175 166 1775 540 513 51、7 575 180 171 1810 550 523 52、3 595 185 176 1845 560 532 53 610 190 181 1880 570 542 53、6 625 195 185 1920 580 551 54、1640 200 190 1955 590 561 54、7 660 205 195 1995 600 570 55、2 675 210 199 2030 610 580 55、7 690 215 204 2070 620 589 56、3 705 220 209 2105 630 599 56、8 720 225 214 2145 640 608 57、3 740 230 219 2180 650 618 57、8 755 235 223 660 58、3 770 240 228 20、3 670 58、8 785 245 233 21、3 680 59、2 800 250 238 22、2 690 59、7 820 255 242 23、1 700 60、1 835 260 247 24 720 61 850 265 252 24、8 740 61、8 865 270 257 25、6 760 62、5880 275 261 26、4 780 63、3900 280 266 27、1 800 64915 285 271 27、8 820 64、7930 290 276 28、5 840 65、3950 295 280 29、2 860 65、9965 300 285 29、8 880 66、4995 310 295 31 900 671030 320 304 32、2 920 67、51060 330 314 33、3 940 681095 340 323 34、4* HRB St12=65 St13=55 St14=50硬度试验就是机械性能试验中最简单易行得一种试验方法。

常用钢材抗拉强度与硬度换算对照表

根据德国标准DIN50150,以下是常用范围的钢材抗拉强度与维氏硬度、布氏硬度、洛氏硬度的对照表。

抗拉强度<=1000N/mm2，或者维氏硬度<=310HV，或者布氏硬度<=300HB，或者洛氏硬度<=32HRC抗拉强度RmN/mm2维氏硬度HV布氏硬度HB洛氏硬度HRC250 80 76.0 - 270 85 80.7 - 285 90 85.2 - 305 95 90.2 - 320 100 95.0 - 335 105 99.8 - 350 110 105 - 370 115 109 - 380 120 114 - 400 125 119 - 415 130 124 - 430 135 128 - 450 140 133 - 465 145 138 - 480 150 143 - 490 155 147 - 510 160 152 - 530 165 156 - 545 170 162 - 560 175 166 - 575 180 171 - 595 185 176 - 610 190 181 - 625 195 185 - 640 200 190 - 660 205 195 - 675 210 199 - 690 215 204 - 705 220 209 - 720 225 214 - 740 230 219 - 755 235 223 - 770 240 228 20.3 785 245 233 21.3800 250 238 22.2820 255 242 23.1835 260 247 24.0850 265 252 24.8865 270 257 25.6880 275 261 26.4900 280 266 27.1915 285 271 27.8930 290 276 28.5950 295 280 29.2965 300 285 29.8995 310 295 31.0抗拉强度>1000N/mm2，或者维氏硬度>310HV，或者布氏硬度>300HB，或者洛氏硬度>32HRC抗拉强度Rm N/mm2维氏硬度HV布氏硬度HB洛氏硬度HRC103032030432.2 106033031433.3 109534032334.4 112535033335.5 111536034236.6 119037035237.7 122038036138.8 125539037139.8 129040038040.8 132041039041.8 135042039942.7 138543040943.6 142044041844.5 145545042845.3 148546043746.1 152047044746.9 1555480(456)47.7 1595490(466)48.4 1630500(475)49.1 1665510(485)49.8 1700520(494)50.5 1740530(504)51.1 1775540(513)51.71810550(523)52.31845560(532)53.01880570(542)53.61920580(551)54.11955590(561)54.71995600(570)55.22030610(580)55.72070620(589)56.32105630(599)56.82145640(608)57.32180650(618)57.866058.367058.868059.269059.770060.172061.074061.876062.578063.380064.082064.784065.386065.988066.490067.092067.594068.0 硬度试验是机械性能试验中最简单易行的一种试验方法。

硬度与抗拉强度的关系对照表

一、硬度与抗拉强度的关系当钢的硬度在500HB以下时，其抗拉强度与硬度成正比，kg/m㎡（óB）=1/3 X HB=3.2 X HRC=2.1 X HS,但上述关系式也并非在什么场合都成立，从热处理方面说，回火温度低时，kg/m㎡与HRC时的相关关系便可能被破坏，钢的回火温度，硬度和抗拉强度的关系如图所示。

由此图可见硬度随回火温度的升高而下降，但在淬火状态以及300℃以下低温回火时，硬度与抗拉强度的关系难以成立。

当回火温度在300℃左右时，kg/m ㎡与HRC具有相关关系，即硬度高，抗拉强度就高；硬度低，抗拉强度就低。

在低温回火状态欲求出kg/m㎡值是很困难的，因为此时抗拉强度值分布很离散。

由于低温回火件的kg/m㎡不稳定而不能确定，故在日本工业标准（JIS）中也是通试验来测定400℃以上温度回火件的拉伸特性（也有300℃回火工件）。

换言之是只对调质件（淬火+400℃回火）进行拉伸试验。

在工业上只是在要求抗旋转弯曲疲劳和抗磨损时才使用低温回火件。

高频淬火和渗碳淬火即为此适用例。

受拉应力的零件不采用低温回火。

不过在低碳钢中，但淬火M 能发生自回火(故Ms点高)时，亦有在淬火状态下使用者。

低碳钢的板条马氏体组织结构自回火，正可在工业上应用，但此时必须考虑淬透性和质量效应（必要时应添加B、Cr、Mn等金属元素）。

二、钢材抗拉强度与维氏硬度、布氏硬度、洛氏硬度的对照表如果您要查的抗拉强度>1000N/mm2，或者维氏硬度>310HV，或者布氏硬度>300HB，或者洛氏硬度>32HRC，请查本表（注：专业文档是经验性极强的领域，无法思考和涵盖全面，素材和资料部分来自网络，供参考。

可复制、编制，期待你的好评与关注）。