CO脱除催化剂简介

一氧化碳脱除剂CO Removal Catalyst

1. 工作原理及流程Operation and Process

一氧化碳脱除催化剂可用于脱除石油气、惰性气体、氧气等气体中少量一氧化碳，还可用于烤炉、壁炉等设备用于催化燃烧未完全燃烧的CO，净化效果极其优良。

在温度150~200℃，空速（0.3〜1）×104h−1条件下，经其净化后的气体，一氧化碳含量可降至0.5ppm以下；催化剂吸氧容量可达50ml/g，可催化一氧化碳和氧反应成为二氧化碳，催化剂可以再生使用。

HHGS03 catalyst works efficiently to remove CO from petro gas, inert gas, oxygen and etc, also could be used in various furnace like oven, chimney place, incinerator to treat not burst CO.

This catalyst could make CO content less than 0.5ppm under temperature 150~200℃and space velocity at (0.3~1.0)×104 h-1; oxygen capacity of this catalyst could be 50ml/g, and catalyze reaction CO and O2 to be CO2.

Reaction formula: CO+O2 CO2

2. 工艺特点Operation Properties

一氧化碳脱除催化剂使用前需要配氮气加热至180-200℃活化（烤炉、壁炉等本身是高温源尾气的则可用新鲜空气加热活化），然后再通入待处理气体，温度在200℃时操作最佳，在1.5~3.0×103h-1的反应条件下将CO气体中的CO消除至0.5ppm以下，最高耐热温度为750℃（若可燃性气体浓度高还需配冷却系统，防止催化剂烧结），机械强度好，使用寿命可达3年以上。

Before using, CO removal catalyst should be heated up to 180~200℃by nitrogen (fresh air is also available for high temperature exhaust gas in oven and fireplace), in order to active its performance. The optimal operating temperature is 200℃, and removal CO until 0.5ppm left under operation space velocity (0.3~1.0)×104 h-1; Max temperature is 750℃(cooling system is required if flammable gas is in high concentration).

3. 技术指标Technology Properties

序列号No 测试项目Test item 技术参数Technology parameter 载体：各种规格堇青石与复合氧化铝

Carrier: cordierite and composite alumina with various specs

1 空速Space velocity ≥3×103h-1

2 起燃温度Initial ignition temperature 100℃-150℃

3 最佳操作温度Optimal service temperature 180℃-200℃

4 CO脱除率CO remova ratio

Service life ≥98﹪

≥2 years

5 寿命Service life ≥2 years

5 CO出口浓度CO outlet content ＜5ppm

6 堆积比重Bulk density 0.68±0.05g/mL

7 抗压强度Crushing strength ≥14 MPa

8 涂层负载Coating component ≥10.0%

9 活性成份负载Activity component 0.1%-0.2% (also depends on your demand)

10 脱落率Expulsion ratio ＜1%

11 外观Appearance Usually is light yellow (would be grey after pre-reduction)

12 包装Packing Moisture-proof

13 Suggested loading height/diameter Honeycomb type 4:1, particle 2:1