高固体厚膜型焦油环氧涂料简述

Storageand Handling 贮存与管理Storage 贮存 Store in cool and dry conditions 贮存于阴凉干燥处

Pack size 包装规格 A;20Kg in 20 liter container 甲:20公斤装于20公升容器中 B:4Kg in 4 liter container 乙:4公斤装于4公升容器中Flash Point 闪点 above 23℃(after mixture) 大于23℃（混合后）Specific Gravity 比重Approx 1.3Kg/L 大约1.3公斤/公升

Intended Uses

用途高度防护性煤焦环氧树脂漆，特别适用于全部或部分或间断浸于盐水的环境，以及浸于水中的打樁工种和地下埋设施。

High performance protective paint of tar epoxy resin type, especially suitable for condition of whole, partial or intermittent immersing in salt water, along with in water or laying underground.

Product Information 产品简介高固体，厚膜型焦油环氧树脂漆

High-solids, high-build tar epoxy resin paint

Application details 产品数据V olume Solids 固体份≥66%

Dry Flm Thickness干膜厚度

250 microns equivalent to 375 microns of wet film

250微米相当于375微米湿膜厚

Theoretical Coverage 理论涂布率

2.0 m2 /Kg at the stipulated volume aolids and 250microns of dry film

thickness

2.0平方米/公斤，以规定的体积固体份和250微米干膜厚计Practical Coverage 实际涂布率Allow appropriate loss 允许适量损耗

Storage and Handling 施工详述Mix Radio 混合比 A : B=5:1(by weight) 甲:乙=5:1(重量比)

Method of Application 施工方法

Airless Spray 无空气喷涂 Recommended 推荐采用

Brush or Roller 涂刷或辊涂 Not Recommended 不推荐采用

Conwentional Spray 传统喷涂 Not Recommended 不推荐采用

Thinner 稀释剂 Not necessary in normal, if needed use SC003

不推荐使用，如需要用C003

Cleaner 油漆设备清洗剂 SC003

Pot Life 使用期 5℃:8h (小时) 23℃:3h (小时) 35℃:1h (小时) Storage 贮存期 One year 一年

Drying time

干燥时间

Substrate

Temperature

底材温度

Touch Dry

表干

（h）

Hard Dry

硬干

(h）

Over coating Interval

覆涂间隔

Min最短Max最长

5℃

23℃

35℃

12

6

3

48

16

12

48 hours 小时

16 hours 小时

6 hours 小时

3days (天)

16 hours 小时

16 hours 小时

高固体厚膜型焦油环氧涂料简述

Specification and Surface preparation 技术要求及表面处Precoated primer surface:

A.This product is suitable for most precoated primer surface shops, If you have problem about specific shop

primer, get in touch with the company please.

B.Normall, remove rusty part with power disc. Blast rusty weld seams, and wash solutable salt with clean

water.

If there is serious rust on the surface, it must be completely sanded

Rusty steel

A.Seriously rusted surface or oxidized part should be blasted to Swedish Standard SIS055900 Sa2.5 or near

to witte metal according to SSPC-SP10 standard

B.Slight and average rust: (a) if under abominable environment, blast clean to Sa2.5, (b) If Under other

environments , and in the same site, abrade to Swedish Standard SIS055900 St2.

It is suited for steel immersed in water or buried underground with cathodic protection, This is an ideal painting material, but the surface to be coated should be blasted to Sa2.5 or precoated

With some primers

预涂底漆表面：

1.本产品适用于大部分工厂涂装预涂底漆表面，假如对特别的车间底漆的疑问，请联络本公司

2.一般处理是以动力工具转盘清除生锈部分，喷砂处理生锈的焊道，并有和清水清除可溶盐份，

如果生锈情况严重，则要全部扫砂。

生锈钢板

1.严重生锈或氧化，喷砂至瑞典标准SIS055900 St

2.，B、在非恶劣环境下，且持续处在相同状

况下、采用磨锈至St2.，对浸于水中或埋于地下，而且有阴极保护措施的钢材，

本产品是理想的装饰材料，但在涂装前，表面需经喷砂至Sa2.5或预涂某种底漆

Limitations

限制

This product can not fully cure below 5℃, The optimum curing effect is obtained above10℃