新型干式料的低温结合

新型干式料的低温结合

作者姓名靖相佳

专业无机非金属材料工程指导教师姓名赵萍

专业技术职务副教授

目录

摘要 (1)

第一章绪论 (3)

1.1 目的和意义 (3)

1.2 国内外研究现状 (3)

1.2.1 国内研究现状 (3)

1.2.2 国外研究现状 (4)

1.3中间包工作衬用耐火材料的发展 (5)

1.4中间包的功能 (6)

1.5干式振动料的特点 (7)

1.6 课题研究内容 (8)

第二章实验部分 (8)

2.1主要仪器及原料 (8)

2.1.1主要仪器 (8)

2.1.2主要原料 (8)

2.2颗粒级配 (9)

2.3自硬材料制备....................... 错误！未定义书签。

2.3.1自硬剂选择依据 ................... 错误！未定义书签。

2.3.2试样制备......................... 错误！未定义书签。

2.3.3测试方法......................... 错误！未定义书签。

2.3.4结果与分析.................................. - 12 -

2.4微观结构分析.................................. - 11 - 2.4.1 试样制备 ................................... - 12 - 2.4.2扫描分析.................................... - 12 - 2.5 结论 (16)

参考文献 (17)

致谢 (18)

摘要

干式振动料作为中间包工作衬具有施工方便、烘包时间短、保温性能好、易于翻包等优点，已被迅速推广使用。目前中间包干式振动料主要以酚醛树脂为结合剂，以镁砂和镁钙砂为主要原料。然而酚醛树脂不但价格昂贵，而且对环境和工人健康有很大危害,使这类材料在实际应用中受到一定限制。

本文首先进行颗粒级配的测试，以获得高致密性的材料。结果表明：镁质干式料的最佳粒度组成为：3～1mm39％，1～0.1mm 35％，<0.088mm 26％，q=0.4此时的堆积密度最大2.301g/cm3。通过对结合剂进行选择，确定了无毒、无害，无污染的环保型结合剂。研究发现乙酸乙酯和含水硅酸钠复合结合剂是一种较为理想的中间包干式振动料结合剂,能够在常温下自行硬化，从而达到无烘烤脱模的效果。以烧结镁砂为主要原料，采用乙酸乙酯和含水硅酸钠复合结合剂制备了镁质中间包干式振动料。结果表明：乙酸乙酯和含水硅酸钠加入量对镁质干式振动料性能影响显著。

关键词：中间包干式振动料结合剂耐火材料

ABSTRACT

Dry vibratable materials has unique merits. Because of its easy installation, fast speed of temperature rise, long life and easy separation from tundish etc. So dry vibratable materials has been developed and applied quickly. Nowadays, phenolic resin is used as the most popular binder and sintered magnesia and limestone as main strting materials. Simultaneously there is also fatal disadvantages. For instance, phenolic resin is high in price. So the dry vibratable materials be limited in practical application.

The paper has do some test on particle to get high density of the material. The result show that: the best particle size of dry vibratable materials is: 3～1mm39％,1～0mm 35％,<0.088mm 26％,q=0.4, at this time the biggest accumulation density is 2.301g/cm3 According to the choice of binder, make sure the binder is innocently harmless and non-pollution. The research shows that ethyl acetate-sodium metasilicate pentahydrate as composite binde is a comparatively ideal for dry

vibratable materials. It can become harden at normal temperature to achieve the effect of stripping without baking. Using sintered magnesia as main starting materials, ethyl acetate -sodium metasilicate pentahydrate as composite binder the basic dry vibration refractory was prepared. The result shows that effect of ethyl acetate-sodium metasilicate pentahydrate binder is very clear to dry vibratable materials.

Key W ords: Tundish; Dry Vibratable Materials; Binder; Refractory

声明

本人郑重声明我所呈交的论文是我个人在导师指导下进行的研究工作及取得的研究成果。尽我所知，除了文中特别加以标注和致谢的地方外，论文中不包含其他人已经发表或撰写过的研究成果，也不包含本人或其他人在其它单位已申请学位或为其它用途使用过的成果。与我一同工作的同志对本研究所做的所有贡献均已在论文中作了明确的说明并表示了致谢申请学位论文与资料若有不实之处，本人承担一切相关责任。