硅胶产品检验标准 The manuscript was revised on the evening of 2021硅胶产品检验标准一. 一般标准1.工作温度:-15℃—+80℃2.贮存温度:-30℃—+85℃3.贮存时间: A.产品在无挤压情况下平放:可长期保贮B.产品在挤压情况下存放:1个月4.工作相对湿度:45℅—95℅5.工作气压:86-106Kpa6.接触率:5MA在12VDC/秒/2*107次7.接触反弹:<12毫秒8.绝缘电阻:>1012欧姆/500VDC9.击穿电压:>25KV/mm二. 外观1. 颜色(1).标准:硫化装配后硅胶不外露,无较大差异(2).检测方法:在明亮的自然光或40W日光灯下,将标准样品或色卡与待校样品放在一起,经视力以上,无色盲的专业人员在肉眼与样品间距为30cm的情况下目检5秒钟.2. 偏心(1)标准: H厚–H薄弹性壁厚度≤0.1MM时,模具检测时X=20℅;≤X 弹性壁厚度≤0.2MM时,模具检测时X=15℅H厚+ H薄弹性壁厚度≤0.3MM时,模具检测时X=8%(2)检测方法:用厚度仪测试。

3. 溢料(1) 标准:从键面向下单色料高≥露出外壳高度+1.0MM,装外壳后看不见为宜.(2) 检测方法:用游标卡尺测量4. 毛边(1) 标准:产品边缘:≤0.5MM定位孔: ≤0.1MM5. 破裂(1) 标准:无影响装配与使用性能之处:≤1.0MM(2) 检测方法:用游标卡尺测量6. 色点凹凸点(1) 标准:客户装配后硅胶外露部分:无明显可见检测方法:在明亮的自然光或40瓦日光灯照射下,将样品放于距肉眼30CM左右处经视力以上人员目测5秒钟7.以上字符偏移(1) 标准:中心值±0.15MM(2) 检测方法:用工具显微镜测量三. 物理性能1.尺寸L<10 : L±0.05MM10≤L<20 : L±0.08MM20≤L<30 : L±0.10MM30≤L<50 : L±0.15MM50≤L<100 : L±℅LMM100≤L : L±℅LMM（2）检测方法:用投影仪测量 2.弹力(1) 标准:A.峰值P1标准值: 50±(5-10)g70±(10-15)g90±(15-20)g100±(15-20)g120±(20-25)g150±(20-25)g170±(25-30)g200-300g±35gb.最小回弹P3P1≤50G时: P3≥20G50G<P1≤120G时: P3≥25G120G<P1≤180G时: P3≥30G180G<P1≤250G时: P3≥40G250G<P1时: P3≥50Gc.感觉:20℅-80℅d.离散性P1中心值≤150g时,同片产品之同种键型:≤15℅不同片产品之同种键型:≤20℅P1中心值≥150g时,同片产品之同种键型:≤20℅不同片产品之同种键型:≤25℅(2) 测试方法:用AIKOH MODEL 1305弹力测量仪测出弹力随冲程的变化曲线图读取其峰值P1,接触弹力P2,最小回弹P3.计算其:感觉=(P1-P2)/P1*100℅离散性=((P1最大峰值)-P1(最小峰值))/P1(最大峰值)*100℅3.接触电阻(1) 标准:a.黑粒导电:≤100欧姆b.移印导电:≤250欧姆c.丝印导电:≤500欧姆(2) 测试方法:用压力为250g压力使产品键之导电基压在间隔为0.5MM的单缝半月形镀金板上.待万用表显示值基本稳定后,读取其显示值.5.寿命a.弹性壁寿命(1) 标准:≥50万次(2) 测试方法:在AIKOH硅胶寿命测试仪的打击速率为2-5次/秒的情况下,设置打击平台的打击接触行程为产品冲程+[经10万次打击后,弹性壁不得开裂破损,可回弹且提失≤30%,当客户无要求时均按50万次进行测试.b.印刷导电寿命(1) 标准:≥2,000,00次(2) 测试方法:在AIKOH硅胶寿命测试仪的打击速率为2-5次/秒的情况下,设置打击平台的打击接触行程为产品冲程+[经20万次打击后,导电物质不得从导电基上脱落且其接触电阻在规格内.c.印刷字体寿命(1) 标准:≥100圈(2) 测试方法:将字符单键安装于PK-3-4字体寿命仪上,使键高出-1.0MM,在加上500G的压力转动摩擦,字体不断开,当客户无明确要求时可采用目视厚度方法进行寿命控制.寿命⑴标准:≥RCA 50圈⑵测试方法:将测试KEY安装于RCA摩擦仪上露了高度-1mm,压力为175g情况下字体出现损伤时寿命即为PU寿命.客户无要求时,PU寿命按此标准.四.化学性能(只限录音电话机的硅胶按键)1.加热失重率(1) 标准: a.≤％(经200℃/4HRS加热失重后)b.≤％(经200℃/24HRS加热失重后)(2) 测试方法:将产品放于干燥箱内30分钟,然后取出,用分析天平称取测试前产品的片重,W1将产品放入温度为200+/-5℃的烘箱内烘烤4小时或24小时,然后将产品拿出放入干燥箱内放置30分钟后用分析天平称取其重量W2,计算(W1-W2)/W1*100℅之值.2.抽提失重率(1)标准:≤％(3) 测试方法:选取一些有代表性的键,剪取约0.5g样品,再将其剪成-0.01g的小粒,用分析天平称其准确总重为W1,将样品放抽提器内并加入异炳醇(IPA)进行提2小时,然后取出样品再放入温度为100℃的烘箱内烘烤半小时,取出后放入干燥箱内冷却半小时称其准确总重W2,计算(W1-W2)/W1*100℅之值.3.低分子含量(1) 标准: D3-D10≤300PPM测试方法:选取有代表性的键+/-0.002g样品,将其剪成约为2mm的小颗粒,放入小瓶内,再将20ML CCL4溶液注入小瓶中,加入20UL的内标物(CH3(CH2 9CH3)摇匀存放16-24HRS,用色谱分析仪测量其D3-D10的量.。

硅胶检测报告硅胶检测执行标准(二)

引言概述：硅胶检测是一项重要的质量控制措施，它广泛应用于各种工业和生活领域，如医疗器械、食品包装、电子产品等。

本文将介绍硅胶检测报告的编写流程和标准要求，以及硅胶材料的常见质量问题和解决方案。

正文：一、硅胶检测报告的编写流程1.收集相关样品信息在编写硅胶检测报告之前，首先需要收集相关样品的信息，包括样品来源、采样时间、采样地点等。

这些信息对于后续分析和解读结果至关重要。

2.进行实验检测硅胶检测通常通过实验室测试来完成。

常见的硅胶检测项目包括外观检查、物理性能测试和化学成分分析等。

在进行实验检测时，需要严格按照相关标准和方法进行操作，确保结果的准确性和可靠性。

3.分析和解读实验结果实验检测完成后，需要对实验结果进行详细的分析和解读。

对于不符合标准要求的结果，需要进一步寻找原因，提出改进建议，并与相关部门或供应商进行沟通和协商。

4.编写检测报告根据实验结果和分析，编写硅胶检测报告。

检测报告应包括测试样品的信息、检测方法和标准、实验结果、分析和解读、结论等内容。

同时，还应注明检测报告的有效期限和授权签字人。

5.审核和发布检测报告编写完成的检测报告需要经过审核，确保其内容的准确性和完整性。

审核通过后，检测报告可以正式发布，供相关方和利益相关者参考和使用。

二、硅胶检测的标准要求1.外观检查硅胶的外观检查主要包括观察样品是否有色差、气泡、杂质等缺陷。

一般情况下，硅胶的外观应为透明或半透明，无明显色差或污染。

2.物理性能测试硅胶的物理性能测试包括硬度、拉伸强度、断裂伸长率等方面。

硅胶的硬度对于其使用场景和要求有较大影响，一般要求硬度在一定范围内。

3.化学成分分析硅胶的化学成分分析主要包括有机物含量、无机物含量、重金属含量等。

硅胶中的有机物含量一般较低，应符合相关标准规定。

同时，无机物和重金属的含量也应在合理范围内。

4.生物相容性测试对于医疗器械等应用领域，硅胶的生物相容性也是重要的检测内容之一。

生物相容性测试主要检测硅胶对于细胞、组织和机体的影响，包括细胞毒性、刺激性、过敏反应等。

硅胶检验作业指导书

进料首件巡回自检全检出货1P MI 2P MI 3PMI 4P MI 5P MA 6P MA 7P MA 8P MA9P MA 10P MA荷重位移曲线测试按硅胶零件图纸要求，不可有荷重不良。

1.来料分区各取1PCS到FQC做荷重测试；2.依荷重-位移曲线测试仪操作规范作业,测试后必要时打印存档.荷重位移曲线测试仪编制核准审核检验图示修改记号修改内容修改依据签名及日期耐长按压测试用重量1000克砝码长按开关72H后测试开关不可有按压手感、性能、荷重不良。

利用按压寿命机重量1000克砝码长按开关72H。

寿命机/手感/荷重测试仪耐高温测试温度250±3℃,时间10±2分钟后测试开关不可有按压手感、荷重不良。

1.分区取样各5PCS，做高温试验后组装成品，继续做6、7、8、9项目分区各1PC；2.依烤箱操作规范作业,试验结束后在常温、常湿中放置1小时后测试.烤箱/手感/荷重测试仪环保确认符合公司内部环保标准 1.来料外包装贴环保标签;2.供应商SGS报告的核对确认；3.取样适量送测试中心测环保。

目视/ROHS仪尺寸依图纸尺寸公差检测，超出标准为不合格按每区抽检5PCS 投影仪外观 1.颜色比对承认样品是否相符;2.是否有杂质、缺胶、批峰、错位等现象目视样品/目视包装确认包装标签填写是否完整清晰(至少有供应商名称、产品料号、生产日期、区号)目视,注意每批来料供应商必须附一整模未切断的交工程经理保管。

目视允收标准C=0NO 检验项目判定标准检验方法检验工具检验工序严重度图纸编码制程巡回检验抽样标准/使用材质硅胶模穴数400类别厂商名称厂商品名产品系列产品名称硅胶颜色绿色低温特性测试温度-40±3℃,时间96±4H后低温下测试不可有手感、性能、荷重不良。

依恒温恒湿机操作规范作业,试验结束时在-40度低温下测试.恒温恒湿机/荷重测试仪耐热性测试温度85±3℃,时间96±4H;在常温/常湿中放置1.5H后测试不可有手感、性能、荷重不良。

硅胶制品质量检测报告【最新版】

硅胶制品质量检测报告【最新版】硅胶制品质量检测报告厨房电器检测范围:厨房电器(换气扇、电饭煲、电磁炉、豆浆机、电水壶、榨汁机、微波炉、电压力锅、面包机、咖啡机、电烤箱、打蛋器、酸奶机、电炖锅)CID艾达检测机构检测项目:标志和说明、对触电带电部件的防护、输入功率和电流、工作温度下的泄漏电流和电气强度、结构、电源连接和外部软线、接地措施、电气间隙爬电距离和固体绝缘、耐热和耐燃检测依据:GB 4706.1-2005、GB 4706.30-2008、GB 4706.19-2008、GB 4706.14-2008等检测范围:生活家电(挂烫机、电熨斗、干衣机、加湿器、抽湿机、室内加热器、空气净化器、电风扇、空调扇、缝纫机)检测项目:标志和说明、对触电带电部件的防护、输入功率和电流、工作温度下的泄漏电流和电气强度、稳定性和机械危险、结构、电源连接和外部软线、接地措施、电气间隙爬电距离和固体绝缘、耐热和耐燃CID艾达检测机构检测依据:GB 4706.1-2005、GB 4706.84-2007、GB 4706.27-2008、GB 4706.48-2009、GB 4706.45-2008、GB 4706.2-2008等检测范围:个人护理设备(电吹风、烫/卷发器、剃须刀、电动牙刷、剃/脱毛器、理发器、足浴盆)检测项目:标志和说明、对触电带电部件的防护、输入功率和电流、耐潮湿、泄漏电流和电气强度、机械强度、电源连接和外部软线、耐热和耐燃CID艾达检测机构检测依据:GB 4706.1-2005、GB 4706.9-2008、GB 4706.10-2008、GB 4706.59-2008、GB 4706.99-2009等暖手宝(电暖袋)检测范围:暖手宝、电暖袋检测项目:标志和说明、对触电带电部件的防护、输入功率和电流、结构、电源连接和外部软线。

检测依据:GB 4706.1-2005、GB 4706.99-2009检测范围:干鞋器检测项目:标志和说明、输入功率和电流、结构、对触电带电部件的防护、工作温度下的泄漏电流和电气强度、耐潮湿、电源连接和外部软线、耐热和耐燃。

硅胶检验报告

硅胶检验报告
检验对象：硅胶制品
检验目的：
1.检验硅胶制品的质量，确保符合相关标准和要求。

2.保障使用硅胶制品的安全性和稳定性。

检验方法：
采用国家标准《硅橡胶制品通则》（GB/T16560-2008）及《硅
胶制品品质检验规则》（QB/T2611-2003）的相关要求，进行检验。

检验内容：
1.外观检验：
（1）检查硅胶制品表面是否平整、无明显褶皱、气泡、棱角等缺陷。

（2）检查硅胶制品外部是否存在污渍、划痕、裂纹等缺陷。

2.尺寸检验：
（1）测量硅胶制品的尺寸是否符合制品图纸或规格书规定的要求。

（2）使用测量仪器对硅胶制品进行精度测量，确保产品的高精度性。

3.性能检验：
（1）硅胶制品的拉伸强度：
使用万能材料试验机对硅胶制品进行拉伸试验，测定其断裂强度，检验其耐拉伸强度是否符合规定的标准。

（2）硅胶制品的硬度：
使用杜氏硬度计对硅胶制品进行硬度测量，确保其硬度符合相关标准和要求。

（3）硅胶制品的耐热性：
将硅胶制品放置在烤箱中进行加热，检验其耐热性是否符合相关标准和要求。

检验结论：
经过全面、细致的检验，本次检验的硅胶制品符合相关标准和要求，可放心使用。

检验单位：XXX检验中心
检验人员：
XXX XXX XXX 日期：2021年xx月xx日。

硅胶检验标准

1.5~2.0MPA，
由供方提供检测报告
无
3
密封性
大于等于10mpa
由供方提供检测报告
4
介电常数
由供方提供检测报告，符合订货技术要求
无
5
体积电阻率
6
扯裂强度
7
肖氏硬度
8
延伸率
9ቤተ መጻሕፍቲ ባይዱ
固化时间
10
老化试验
85%湿度，85℃，2000小时，无明显黄便，部发脆。
高低温试验箱
备注：
1.原材料无需凭老化实验结果入库。
6
挤出性
0.3Mpa的气源压力下进行测定,记录挤出20g产品所用的时间,取出三次试验数据的平均值作为试验结果7-15(s/20g)
胶枪\秒表
B类标准：
序号
项目
检验内容、标准
检验方法（器具）
1
耐热性能
-45度~85度不脱胶。符合(IEC61215;IEC61730-2)
由供方提供检测报告
直尺
2
抗拉强度
硅胶：单批次抽检为1支，如为性能不合格，则退换货，如为外观不合格，进行二次抽检，抽检次数为2支次，如果未发现不合格项则同意放行，否则退换货
编写审核批准
硅胶检验标准文件编号
一、目的和用途：
本标准提出对硅胶送样检验的工艺过程、内容及标准。
二、适用范围：
适用于各种规格的硅胶。
三、工具和仪器设备：
秒表、胶枪、直尺，高低温试验箱，紫外箱
四、检验（项目）及标准：
A类标准：
序号
项目
检验内容、标准
检验方法（器具）
1
规格型号
检查规格型号是否与送检单一致，送检单是否与BOM单一致，检查供应商是否在合格供应商之例。

硅胶制品出厂检验报告

硅胶制品出厂检验报告硅胶制品出厂检验报告一、产品基本信息产品名称：硅胶制品产品型号：XXX生产厂商：XXX有限公司生产日期：XXX年XX月XX日二、检验项目及结果1. 外观检查：经目测，本批次硅胶制品外观整洁，无明显缺陷，无虫蚀、划痕及凹陷等问题。

2. 尺寸测量：测量本批次硅胶制品的尺寸，符合设计要求，误差在允许范围内。

3. 材质检测：通过材质测试，本批次硅胶制品主要成分为硅胶，不含有有害物质，符合相关标准要求。

4. 耐候性测试：将硅胶制品样品暴露在高温环境或低温环境下一定时间，经检测，硅胶制品无明显变形、脱色或断裂情况，能够良好适应各种气候环境。

5. 耐磨性测试：通过磨擦测试，本批次硅胶制品经过多次磨擦后，外观仍然保持完好，无明显磨损现象。

6. 耐温性测试：将硅胶制品样品置于高温环境中，经检测，硅胶制品能够耐受高温，不发生变形、脱落或爆裂等情况。

7. 强度测试：通过拉力测试，本批次硅胶制品的强度符合相关标准要求，能够承受一定的拉力而不易断裂。

8. 导电性测试：测试本批次硅胶制品的导电性，结果显示硅胶制品为绝缘材料，不存在导电问题。

三、检验结论经过上述检查项目的全面检验，本批次硅胶制品符合生产标准要求，全部合格。

四、检验结论本批次硅胶制品质量良好，通过检验并合格出厂，可正常投放市场销售。

五、其他注意事项作为厂家，我们将继续保持对产品质量的严格控制，确保产品在生产和制造过程中的合格率，并保证向用户提供优质的硅胶制品。

六、备注以上检验报告仅限于本批次硅胶制品，供参考使用。

若有问题，请及时与我公司联系，我们将积极解决并给予满意的答复。

联系人：XXX联系电话：XXXXXX联系邮箱：XXXXXXXXXX年XX月XX日。

硅胶检验报告

硅胶检验报告一、引言硅胶是一种广泛应用于工业和日常生活中的材料，具有优良的吸附性能和化学稳定性。

为了确保硅胶的质量和安全性，需要进行严格的检验和测试。

本文将对硅胶进行全面的检验报告，以确保其质量符合标准要求。

二、外观检验硅胶的外观检验是通过肉眼观察硅胶的颜色、透明度和表面是否光滑来判断其外观质量。

合格的硅胶应具有均匀的颜色，透明度高且表面平整光滑。

三、尺寸检验硅胶的尺寸检验是通过测量硅胶的长度、宽度和厚度来评估其尺寸精度。

合格的硅胶应具有符合规定的尺寸，并且各个部分之间的尺寸差异应在允许范围内。

四、吸附性能检验硅胶的吸附性能检验是评估硅胶对湿气和其他物质的吸附能力。

常用的测试方法是通过将硅胶暴露在特定湿度环境下，测量其吸湿量或吸附其他气体的能力。

合格的硅胶应具有较高的吸湿量和吸附能力。

五、化学性质检验硅胶的化学性质检验是评估硅胶的化学稳定性和安全性。

常用的测试方法包括酸碱度测试、重金属含量测试和有害物质释放测试等。

合格的硅胶应具有中性或弱酸性、低重金属含量和无有害物质释放的特点。

六、机械性能检验硅胶的机械性能检验是评估硅胶的物理强度和耐磨性能。

常用的测试方法包括拉伸强度测试、撕裂强度测试和耐磨性测试等。

合格的硅胶应具有较高的物理强度和耐磨性能。

七、热稳定性检验硅胶的热稳定性检验是评估硅胶在高温环境下的性能表现。

常用的测试方法包括热失重测试、热膨胀系数测试和热导率测试等。

合格的硅胶应具有较低的热失重率、较小的热膨胀系数和较低的热导率。

八、环境适应性检验硅胶的环境适应性检验是评估硅胶在不同环境条件下的性能表现。

常用的测试方法包括低温抗冻性测试、高温耐热性测试和耐候性测试等。

合格的硅胶应具有良好的环境适应性，能够在不同的温度和湿度条件下保持其性能稳定。

九、包装检验硅胶的包装检验是评估硅胶包装的完整性和防潮性能。

常用的测试方法包括包装密封性测试、防潮性能测试和包装标识检验等。

合格的硅胶包装应具有完好的密封性和防潮性能，并正确标识其产品信息。

道康宁JCR6101硅胶规格书

Product InformationLED MaterialsDow Corning®JCR 6101 UPTYPICAL PROPERTIESSpecification Writers: Please contact your local Dow Corning sales office or your GlobalDow Corning Connection before writing specifications on this product.Property UnitValue Viscosity cPmPa-secPa-sec194001940019.4Specific Gravity (Uncured) - 1.04Durometer Shore A (JIS) - 35Dielectric Strength volts/milkV/mm62524Volume Resistivity ohm*cm 2.9 E+15Shelf Life @ -5ºC months 6STORAGE AND SHELF LIFEShelf life is indicated by the “Use Before” date found on the product label. For best results, Dow Corning one-part products require cold storage at or below -5°C (23°F). Special precautions must be taken to prevent moisture from contacting these materials. Containers should be kept tightly closed with head space minimized. Partially filled containers should be purged with dry air or other gases, such as nitrogen. Check the product label for specific storage conditions.DESCRIPTIONDow Corning® brand silicone LED (light emitting diode) encapsulants are designed to meet the challenging needs of the LED market, including high adhesion, high purity, moisture resistance, thermal stability and optical transmittance. Silicone materials can absorb stresses caused by thermal cycling inside the package, protecting the chip and thebonding wires. And with theelectronics industry quickly movingtoward lead-free processing, siliconeencapsulants, with theirdemonstrated, excellent stability atreflow temperatures, are a natural fitfor LED applications.PREPARING SURFACESSurfaces should be clean and dry.Recommended cleaning methodsinclude Dow Corning® brand OSFluids, naphtha, mineral spirits,methyl ethyl ketone (MEK) or othersuitable solvent. Rougher surfacestend to promote adhesion of siliconesto other surfaces.PROCESSING/CURINGThese products are also compatiblewith commercially availableequipment and industry standardprocesses. These materials can bedispensed or molded depending onthe product and application. DowCorning OS Fluids are recommendedto clean cured or uncured siliconeresidue from application equipment.ADHESIONDow Corning LED materials arespecially designed for adhesion tocommonly used LED substrates.Surface treatments such as chemicaletching or plasma treatment mayprovide a reactive surface andimprove adhesion to these types ofsubstrates. In general, increasing thecure temperature and/or cure timewill improve the ultimate adhesion.USEFUL TEMPERATURERANGESFor most uses, silicone encapsulantsand resins should be operational overa temperature range of -45 to 200°C(-49 to 392°F) for long periods oftime. However, at both the low- andhigh-temperature ends of thespectrum, behavior of the materialsand performance in particularapplications can become moreDow Corning and Sylgard are registered trademarks of Dow Corning Corporation. All other trademarks or brand names are the property of their respective owners. ©2008 Dow Corning Corporation. All rights reserved. Printed in USA Form No. 11-1300A-01complex and require additionalconsiderations. For low-temperature performance, thermal cycling toconditions such as -55°C (-67°F) may be possible, but performance should be verified for your parts or assemblies. Factors that may influence performance areconfiguration and stress sensitivity of components, cooling rates and hold times, and prior temperature history. At the high-temperature end, the durability of the cured silicone encapsulants and resins is time and temperature dependent. As expected, the higher the temperature, the shorter the time the material will remain useable.COMPATIBILITYCertain materials, chemicals, curing agents and plasticizers can inhibit the cure of addition cure adhesives. Most notable of these include: Organotin and other organometallic compounds, Silicone rubber containing organotin catalyst, Sulfur, polysulfides, polysulfones or other sulfurcontaining materials, unsaturated hydrocarbon plasitcizers, and some solder flux residues. If a substrate or material is questionable with respect to potentially causing inhibition of cure, it is recommended that a small scale compatibility test be run to ascertain suitability in a givenapplication. The presence of liquid or uncured product at the interface between the questionable substrate and the cured gel indicatesincompatibility and inhibition of cure.HEALTH ANDENVIRONMENTAL INFORMATIONTo support customers in theirproduct safety needs, Dow Corning has an extensive Product Stewardship organization and a team of ProductSafety and Regulatory Compliance (PS&RC) specialists available in each area. For further information, please see our website,, or consult your local Dow Corning representative.LIMITATIONSThese products are neither tested nor represented as suitable for medical or pharmaceutical uses.LIMITED WARRANTY INFORMATION PLEASE READ CAREFULLYThe information contained herein is offered in good faith and is believed to be accurate. However, because conditions and methods of use of our products are beyond our control, this information should not be used in substitution for customer’s tests to ensure that Dow Corning’s products are safe, effective, and fullysatisfactory for the intended end use. Suggestions of use shall not be taken as inducements to infringe any patent. Dow Corning’s sole warranty is that the product will meet the DowCorning sales specifications in effect at the time of shipment. Yourexclusive remedy for breach of such warranty is limited to refund ofpurchase price or replacement of any product shown to be other than as warranted. DOW CORNINGSPECIFICALLY DISCLAIMS ANY OTHER EXPRESS OR IMPLIED WARRANTY OF FITNESS FOR A PARTICULAR PURPOSE OR MERCHANTABILITY. DOW CORNING DISCLAIMS LIABILITY FOR ANY INCIDENTAL ORCONSEQUENTIAL DAMAGES.SAFE HANDLING INFORMATIONPRODUCT SAFETYINFORMATION REQUIRED FOR SAFE USE IS NOT INCLUDED IN THIS DOCUMENT. BEFORE HANDLING, READ PRODUCT AND MATERIAL SAFETY DATA SHEETS AND CONTAINER LABELS FOR SAFE USE, PHYSICAL AND HEALTHHAZARD INFORMATION. THE MATERIAL SAFETY DATA SHEET IS AVAILABLE ON THE DOW CORNING WEBSITE AT , OR FROM YOUR DOW CORNING REPRESENTATIVE, ORDISTRIBUTOR, OR BY CALLING YOUR GLOBAL DOW CORNING CONNECTION.For More InformationTo learn more about these and other products available from Dow Corning, please visit the Dow Corning Electronics website at / electronics.。

硅胶检测报告(2024)

硅胶检测报告
引言：
硅胶是一种常用的吸湿剂，广泛应用于食品、药品、电子产品等行业中，其吸湿能力强、无毒无味、稳定性高等特点使其成为被广泛使用的产品。

为了确保产品的质量与安全性，需要对硅胶进行严格的检测。

本文将通过对硅胶的检测报告，详细介绍硅胶的检测方法、检测指标以及检测结果的分析。

概述：
本次硅胶检测是基于国际标准测试方法，通过多个方面的检测指标对硅胶样品进行全面分析。

通过对样品的性质、化学成分及其它重要指标进行检测，我们旨在提供客观准确的硅胶质量评估以及最终产品的安全性评价。

正文内容：
1.硅胶的外观与物理性质分析
硅胶样品的外观观察和比较
硅胶的质地分析、颜色分析、密度测试
2.硅胶的化学成分分析
硅胶中的主要成分分析：二氧化硅（SiO2）含量测试
其他成分分析：有机成分、金属离子、盐含量等
3.硅胶的吸湿性能分析
吸湿率测试：通过不同湿度条件下的吸湿性能测试
吸湿速率测试：通过时间与吸湿量的变化关系确定其吸湿速率循环吸放湿性能测试：检测硅胶在吸湿后的释放能力
4.硅胶的化学稳定性分析
酸度与碱度测试：检测硅胶样品的酸碱性
热分解性测试：检测硅胶在高温下的稳定性
氧化分析：检测硅胶样品的氧化程度
5.硅胶的可溶性与溶出物质分析
可溶性测试：检测硅胶在水或其他溶剂中的溶解性
溶出物分析：检测硅胶样品中的溶出物及其浓度
总结：
本次硅胶检测报告的主要目的是为了提供客观准确的硅胶质量评估以及最终产品的安全性评价。

通过对硅胶样品的全面分析，我们可以为客户提供参考，并通过改进和优化产品质量，进一步确保硅胶产品的稳定性和安全性，提供高质量的硅胶产品给予客户。

硅胶出货检验报告(2024)

引言：硅胶是一种常用于制造各种密封件、绝缘件和耐酸碱材料的特殊材料。

为了确保硅胶产品的质量和性能符合要求，出货前的检验是必不可少的环节。

本文是硅胶出货检验报告的第二部分，旨在详细介绍对于硅胶的出货检验流程和结果，帮助确保产品的合格率和客户满意度。

概述：硅胶是一种非常多功能的材料，具有优异的耐温、耐化学腐蚀和电绝缘性能。

出货前的检验对于确保产品的质量和性能至关重要。

本文将按照出货检验的流程和结果，从质量、物理性能、化学性能、外观和尺寸五个大点进行详细阐述，以确保产品的合格率和客户满意度。

正文内容：1.质量检验1.1主要检验项目及标准1.2检验方法和仪器1.3检验结果及合格率1.4异常情况分析和处理意见1.5检验报告和记录保存2.物理性能检验2.1引伸强度和断裂伸长率2.2硬度测试2.3导电性能检测2.4密度和温度稳定性2.5物性检验结果及合格率3.化学性能检验3.1化学成分分析3.2pH值检测3.3电离物含量检验3.4氧气透过率测定3.5化学性能检验结果及合格率4.外观检验4.1表面光泽度4.2含杂质检验4.3色差测试4.4裂纹和气泡检测4.5外观检验结果及合格率5.尺寸检验5.1尺寸测量工具和方法5.2尺寸检验要求5.3尺寸偏差和公差评定5.4尺寸测量结果及合格率5.5尺寸检验记录保存总结：硅胶出货检验是确保产品质量和性能符合要求的重要环节。

本文从质量、物理性能、化学性能、外观和尺寸五个大点进行了详细阐述，并对每个大点下的小点进行了探讨与分析。

通过严格的出货检验过程，可以做到将不合格产品排除在外，提高产品合格率和客户满意度。

同时，出货检验报告的记录和保存是进行质量追溯和质量改进的重要依据，为企业的可持续发展提供保障。

希望本文的内容能对硅胶出货检验的实施和相关人员提供有益的指导和参考。

硅胶出货检验报告引言概述：硅胶是一种常见的工业材料，具有优异的耐高温、耐腐蚀和绝缘性能。

在生产过程中，出货检验是确保所提供的硅胶产品质量可靠的重要步骤。

硅胶杯检测报告

引言概述:正文内容:一、外观检测1.1.外观缺陷检测\t通过对硅胶杯的外观进行仔细观察和检查，检测是否存在表面缺陷、污渍、色差等问题。

1.2.尺寸检测\t对硅胶杯的直径、高度等尺寸进行测量，确保其尺寸符合要求，并与产品说明书中的参数进行对比。

二、材料检测2.1.硅胶材料检测\t通过对硅胶杯材料的成分分析，确认其是否由纯硅胶制成，检测是否含有有害物质，如重金属、BPA等。

2.2.弹性测试\t对硅胶杯的弹性进行测试，评估其柔软性和是否具有足够的弹性，确保杯体不易变形和破裂。

三、使用安全性检测3.1.可溶性物质检测\t对硅胶杯进行可溶性物质检测，确保其在吸水、受潮等条件下不会释放出有害物质。

3.2.食品接触安全性检测\t通过模拟真实使用条件下的接触测试，评估硅胶杯与食品接触的安全性，确认其不会释放出有害物质对食品造成污染。

四、耐高温性检测4.1.热稳定性测试\t将硅胶杯置于高温环境中，测量其耐受高温的能力，确保其在高温环境下不会发生变形或破裂。

4.2.热传导性测试\t通过测试硅胶杯的热传导性能，评估其在高温环境下对用户手部的热传导情况，确保不会造成烫伤。

五、耐低温性检测5.1.低温稳定性测试\t将硅胶杯置于低温环境中，测试其耐受低温的能力，并观察其是否会发生变形或开裂。

5.2.冷热交替测试\t对硅胶杯进行冷热交替测试，模拟真实使用条件下的温度变化，评估其耐冷热交替的能力。

总结:通过对硅胶杯的外观检测、材料检测、使用安全性检测、耐高温性检测和耐低温性检测的全面评估，可以对该硅胶杯的质量进行客观的判断。

结果显示，该硅胶杯外观无明显缺陷，尺寸合适；材料成分纯净，无有害物质；使用安全，不会释放有害物质对食品造成污染；耐高温性和耐低温性较好，不易变形或开裂。

该硅胶杯经过检测，质量合格，可以安全使用于食品和饮料的包装和储存。

硅胶制品成品检验规范 (1)

核准：文件版本A/0 页码1/21、目的和范围本规范规定了硅胶按键的抽样、检验、判定和不合格的处置。

本规范适用于外协加工件硅胶按键的进货检验。

2、引用标准GB-2828-2003 逐批检查计数抽样及抽样表3、抽样序检验项目检查水平AQL1 外观检验一般检查水平Ⅱ 4.02 尺寸检验一般检查水平Ⅱ 1.53 电气性能检验S1 1.54 可靠性检验S1 1.55 包装检验一般检查水平Ⅱ 1.54、检验方法4.1 外观检验：在适当光照条件下，裸眼距离30CM检查进行直观检验；4.2 尺寸检验：使用测量精度应不小于0.02mm的游标卡尺或其它适用的长度测量器具进行其尺寸测量测量。

4.3 电气性能检验：使用数字万用表“200KΩ”档测量碳点的阻值。

4.4 可靠性检验：详见5.45、检验项目及标准5.1 外观检验项目和标准序检验项目检验描述及标准要求1 表面效果参照样本，其表面处理效果与样本一样；（比如是磨面还是光面）要求表面平整，不能凹凸不平等影响表面效果的缺陷，不能有脏污、划伤。

2 印刷参照图纸或样本，字符的内容、位置、颜色与图纸或样本一样。

要求字符不能有印花、少印、露底、断缺等不良的现象。

5.2 尺寸检验项目和标准序检验项目检验描述及标准要求1 外形尺寸要求外形尺寸公差在技术图纸允许的范围内或工程提供的样品一致。

核准：文件版本A/0 页码2/23 按键行程要求按键的行程与样品、技术图纸一致。

5.3 电气性能检验项目和标准序检验项目检验描述及标准要求1 碳点阻值根据邦定测试程序，要求工作电流不能大于程序规定的额定MAX值。

5.4 可靠性检验项目和标准序检验项目检验描述及标准要求1印油附着力用手轻括印字面，油墨不能被刮起，用“3M”透明胶布贴牢印字面后，快速拉起，印字面不脱漆，胶布上无印油块。

2 手感要求按键按下时时有明显的弹跳感，有客需特定参照客供样。

5.5 包装检验项目与标准5.5.1 产品内包装要求产品堆放规整，并有防潮保护。

硅胶检验规范

硅胶检验规范硅胶检验规范一. 目的:1.为明订硅胶产品的检验流程、项目、检验工具、检验方法、需实配检查料件、罗列需检附之文件作为对产品要求规范；为提升IQC新进人员、各工程师及主管的教育训练教材，使其能快速的了解本公司对硅胶产品之检验重点、检验项目、工具、方法、要求……等并提升进料检验水平与外验能力。

2.订立相关技术及检验文件的基础规范。

3.为未来新进人员教育训练教材。

4.二. 适用对象:键盘厂所有干部、品质工程师、工程部PE工程师、IQC….等。

壹﹒硅 ( 硅 ) 橡胶类料件的检验一﹒标准键盘按键类：1. 外观包装要求：1.1 供应商送货时需配送检查报告，内需含产品之抽测的曲线图。

1.2 产品需使用PE袋或夹炼袋密封套装，每袋最大包装数量为20000 pcs；1.3 供应我司之物料根据机种要求需要ROHS之标示。

2.目视检查项目：2.1 外观颜色。

2.2 检查料件外观是否有破损、缺胶、变形、异色…等不良现象。

2.3 以手指或手掌柔搓料件数次晃开约10秒后，检视料件外观部可以有变型之现象。

2.4 将料件拉伸约增长25%持续约2秒后放开，如此往覆3次后静置约10秒后检视料件外观不可有变型之情形。

2.5 如果是rubber sheet时应确认每一个下料孔均被正确的冲开。

2.6 检查切断线是否有残留的过大之毛边。

2.7 检查导通柱是否有成型不良或缺胶的现象、导电橡胶是否有附着不良或印刷不良的现象。

3. 实配检查：3.1 需与配合之中板、上盖、铁板、铝板…等配合件作动作实配动态检查，配合件载记于封面上4. 重点注记：弹力寿命、模穴数，此部分各检查人员需了解。

5. 破坏性测试：5.1 寿命测试—量测工具为寿命测试机，目前公司无此设备，暂时不做此项检查。

6. 尺寸检验项目：3.1 rubber dome的自由高度，公差值设定范围为 +/- 0.15 mm 或依设计图纸之规范—量测工具为卡尺或工具显微镜。

3.2 rubber dome的外围直径尺寸，公差值设定范围为 +/- 0.15 mm或依设计图纸之规范—量测工具为卡尺或工具显微镜。

硅胶进料检验规范

硅胶类
抽样计划(sampling plan )：C=0
编号
检验项目
检验依据
检验方法
检验设备
等级区分
CR
MA
MI
1
尺寸
工程图面
依工程图面要求测量其重点尺寸；
卡尺精度：0.01MM
V
2
外观及性能要求
工程图面
样品
液体硅胶：
目视
V
1）在明亮环境下，将产品挤成细条状进行目测，产品应为细腻﹑均匀膏状物或粘稠液体无结块﹑凝胶﹑气泡；
目视
V
2）各批之间颜色不应有明显差异,一般硅胶为白色或黑色,不许有塌糊或固化现象；
目视卡尺
V
3）无沉淀物溶出，无变色,无异味,符合RoHS要求；
目视
V
4）液体硅胶干胶时间，如表干、全干时长
应符合规定范围的要求(验证方式参照附件：SZI制程化学品（硅橡胶）检验)；
针筒
计时器
V
5）液体硅胶粘稠度、流动性应符合规定范围的要求(验证方式参照附件：SZI制程化学品（硅橡胶）检验)；
蔡恩杯（3号、44ml）、50ml针筒、秒表
V
6）要标明生产日期及有效期,如来料遇到来料将过有效期需要RMB评审；
目视
V
固体硅胶：
V
1）表面无明显裂纹、划伤、变形、披锋、头发丝及修边不良；
目视
V
2）表面无明显杂色、斑点、脏污及渗杂异物、填充不足、变色等不良；
目视
V
3）边缘允许有轻微夹合线,目视距离30CM不明显(IQC正常来料检验灯光),可允收；
目视
V
4）杂点、黑点、异色点.面积≦0.3mm；
目视
V
5）材质核对样品；

硅胶件通用检验标准

GB/2828.1计数抽样检验程序第一部分:按接收质量限(AQL)检索的逐批检验抽样计划
ISTA/A2国际安全运输协会标准
ROHS（2002/95/EC）限制使用）报废电子电器设备指令
REACHRegistrationEvaluationAuthorization and Restriction of Chemicals
5.3.2.2.1正常煲一个循环的纯净水后，立即打开壶盖或水箱盖，立即由至少5个评价员通过嗅觉感受样品容器，根据自己的感受来判定异味级别。
5.3.2.2.2 嗅觉测试完成后，用保鲜膜将样品(含水溶液)密封，放置冷却到室温后，打开包装，把水倒出至少5小杯，由至少5个评价员通过喝水味觉感受水的味道，根据自己的感受来判定水的异味级别。
硅胶件通用检验标准(总2页)
1、目的：规范公司产品使用的密封圈、硅胶垫等硅胶材料零件的测试、检验。
2、适用范围：适用于公司所有产品使用的密封圈、硅胶垫等硅胶材料零件检验，属通用
标准，如图纸要求与本标准有不同之处，依图纸要求。
3、参照标准及引用文件：
下列文件中的条款引用而成为本部分的条款，其最新版本适用于本部分
GB2702-2763-81《食品卫生标准》
DGCCRF和NO1227《法国食品条例测试法规》
FDA《美国食品等级法规》
LFGB《德国食用品与日用品法》
4、基本测试环境：环境温度20±5℃；相对湿度≤70%
5、检测项目：
5.1外观
5.1.1零件外观颜色需符合图纸要求。
5.1.2产品表面清洁，无油污。
5.3性能
5.3.1零件上材质硬度：邵氏硬度55±3（或按图纸要求）。
5.3.2异味测试：
5.3.2.1选取一个样品，将样品用纯净水清洗后，在什么都不放的情况下，用保鲜膜密封好，注意不能有漏气，放置24小时后，将样品打开，立即由至少5个评价员通过嗅觉感受，评价员根据自己的感受来判定异味级别。

硅胶出货检验报告

出货检验报告OQC Inspection Report编号客户名称Customer产品型号Type检验项目Inspection硬度 Hardness （Shore A)黑粒 /电阻Conductive Pills （Ω）外观Appearance印刷Silk Screening荷重（弹性）Actuation Force （cN ）尺寸Dimension （mm ）耐磨Abrasion包装Packing检验规则InspectionRules2个硬度块 / 批2Hardnesspieces / Lot10片 /批10pcs / LotC=0, AQL0.065C=0, AQL0.065C=0, AQL0.0652M/ 批次2M /Lot20片 /批20 pcs / Lot1片/批1 pc / Lot订单号 P/O No.硬度块编号Hardnesspiece No.出货日期Date检验标准Inspection Standard规格值：The specification value:电阻值（ Resistance ）：缺、双黑粒（Missing or Doubled）黑粒倾斜、破裂（Slant or Split ）溢料 (Material Overflow)色差 (Color Deviation)气迹 (Gas Mark)刮痕 (Scratches)杂物 (Dirt or Stain)变形 /死键 (Deformed or Dead Key)色差（ Color Deviation）字体不良 (Font)导电不良 (Conduction)F1 ：F3 ：Snap Ratio ：长 (Length) ：宽 (Wide):厚 (Thickness) ：行程 (Stroke )：RCA 纸带 (Paper Strip) ：酒精 (ETHANOL):数量 /箱 (Qty/Carton)净重 (N.W)No ：物料号 P/N生产批号 Lot No批次总数Lot Size出货数DeliverySize检验结果 Inspection Results实际结果Max MinPractical Results结论 Conclusion□ Passed合格特殊原因说明Remark检验员 /日期Inspector/Date□Rejection 不合格核准 /日期Approve/Date检验员/日期核准 /日期Inspector/Date Approve/Date。

硅胶检验标准书

5
耐高温测试
±2分钟后测试开关不可有按压手感、荷重
品，继续做6、7、8、9项目分区各1PC； 2.依烤箱操作规范作业,试验结束后在常
烤箱/手感/荷重测试仪
P
MA
不良。
温、常湿中放置1小时后测试.
6
开关按压寿命测试
寿命10万次不可有手感、性能、荷重不良
。
1.成品做开关按压寿命3万次OK来料可入库； 2.开关按压寿命继续做10万极限测试并保留记录和测试样品。
按硅胶零件图纸要求，不可有荷重不良
。
1.来料分区各取1PCS到FQC做荷重测试； 2.依荷重-位移曲线测试仪操作规范作业, 测试后必要时打印存档.
荷重位移曲线测试仪
P
MA
检验图示
修改记号核准
修改内容审核
修改依据
签名及日期
编制
A.0 010/11/1
1/1
零件 C=0
异常判定处理权限 IQC组长
IQC组长 IQC组长 IQC组长 IQC组长 IQC组长/ 品质主管 IQC组长
IQC组长
IQC组长 IQC组长
日期
林积为实业有限公司
文件编号版次A.0来自文件名称进料零件检验标准书
生效日期页数
2010/11/1 1/1
产品系列
RE/RS
产品名称
硅胶
厂商名称
使用材质
硅胶
模穴数
400
图纸编码
林远
厂商品名
1105I00/I01/I02
制程巡回检验抽样标准
/
颜色绿色类别
允收标准
C=0
NO
检验项目
判定标准

硅胶承认检验规格书

五、内容：
1、相关的证明及文件：
1.1、相关的COC内容及出货报告与RR单以及供应商提供的规格承认书。
1.2、根据图纸检查该物料是否有ROHS要求，如有，则需要查询该供应商是否有ROHS协议或相关的分析报告，如没有则需要供应商提供。
2、.外观要求：
2.1、产品必须符合图纸要求。
2.2、产品应该是无色透明液体，应无杂质，杂色等不良现象存在。
适用于本公司所有连接器产品使用的硅胶。
三、检验流程
1、进行测量和实验前的准备工作。
2、委派经培训合格的检验人员进行测量和实验工作。
3、配备合适且经过校对合格的检验仪器和相关的工具和夹具。
4、准备所需要的文件、资料(如图纸、规格书、数据记录表格等等)，理解清楚后方可进行检验工作。
四、一般规格：
1、功能要求：零件的设计、结构和尺寸按照相应的零件图纸；
标题：硅胶承认检验规格书
Title:Silicon gluespecificationand inspection standard
一、目的：
本标准规定了硅胶(Silicon)的检验方法、要求可以接受的程度确保检验员按正确的方法检验样品，以及为IQC制定QI（来料检验规范)提供参考依据。
二、适用范围：
2、工作环境：根据客户要求，①温度在0-70℃范围内，②工业温度在-40℃至85℃，相对湿度最大95%；
3、存储环境：密封包装，温度35℃以下，阴凉通风，避免强光直射，密闭，专用仓储，相对湿度：75%以下；开封后物料保存环境参考MSDS或材料说明书。
4、测试环境：室内温度：20℃至30℃，相对湿度：20-70%。